DEVELOPMENT OF POROUS CONCRETE GEOPOLYMER USING HYDROGEN PEROXIDE AS BLOWING AGENT.

Metakaolin and volcanic ashes respectively called MK and ZG were used as aluminosilicate raw materials for the synthesis of porous geopolymers. The hydrogen peroxide was used as a blowing agent. The geopolymer prepared were characterized by Spectroscopy Fourier Transform Infrared (SFTI), X-ray Diffraction (XRD), Scanning Electron Microscopy (SEM) and the determination of some physical properties such as bulk density, total porosity, volume shrinkage, compressive strength and thermal conductivity was also carried out. The presence of pores in the geopolymer obtained is function of the percentage of hydrogen peroxide added, causing the concomitantly decrease in compressive strength, apparent density and thermal conductivity. The use of hydrogen peroxide as a blowing agent gave some thermal insulation properties to these geopolymers which could be close to the properties of some commercial insulation materials.

Study of the Influence of Fines on a Self-Compacting Concrete

The paper presents the results of the tests of a self-compacting concrete made with fines which include Portland cement and three fillers: hornfels, limestone and metakaolin, in a weight proportion between 23% and 45% of the admixtures. The first mix proportions were designed with a high proportion of Portland cement (720-750kg/m3), and are compared to those having a smaller content of cement and more fillers. The results obtained show that the limestone filler percentage should be higher than the hornfels one, and both of them significantly higher than that of the metakaolin so as to facilitate the fluidity and self-compactability. AIso, the higher proportion of fillers causes a rounded porosity in the mixing which has a bearing on better compressive strength results.

Desarrollo y caracterización de un material celular de alta porosidad con base cementicia activada mediante agentes inorgánicos

Esta tesis ha estudiado los morteros celulares, centrándose en la experimentación con pastas de cemento aireadas (PCA) con polvo de aluminio como agente expansor. El objetivo es el desarrollo de un material cementicio con una baja conductividad térmica que sirva como aislamiento térmico. La naturaleza inorgánica del material lo hace incombustible, en contraste con las espumas poliméricas existentes en el mercado, cuya aplicación en cámaras ventiladas ha sido prohibida por normativas de construcción tanto a nivel nacional como internacional. Las posibles aplicaciones son con proyección neumática o en paneles prefabricados. Se han ensayado dos series de pastas de cemento con polvo de aluminio: - Serie WPC/CAC/CH. Mezcla de referencia con cemento blanco (WPC), cemento de aluminato cálcico (CAC) y cal aérea (CH) en proporción 5:1:4. - Serie OPC/CH. Mezcla de referencia con cemento portland con cenizas volantes (OPC) y cal aérea (CH) en proporción OPC/CH de 4:1 A las mezclas de referencia se le han añadido adiciones de metacaolín (MK) (10 y 20%) o sepiolita (SP) (1 y 2%) para observar el efecto que producen tanto en el mortero fresco como en el mortero endurecido. Se ha estudiado la reología de las pastas en estado fresco, analizando el proceso de expansión de las pastas, registrando los valores de tensión de fluencia, aire ocluido y temperatura durante la expansión. Con los valores obtenidos se ha discutido la influencia de las adiciones utilizadas en la cinética de corrosión del polvo de aluminio que genera la expansión, concluyendo que las adiciones puzolánicas (CV y MK) y la SP reducen mucho el periodo de inducción, lo que provoca poros más grandes y mayor cantidad de aire ocluido. Asimismo se ha analizado la relación entre la tensión de fluencia y el contenido de aire ocluido, deduciendo que a mayor tensión de fluencia en el momento de iniciarse la expansión, menor tamaño de poros y contenido de aire ocluido. Finalmente, se han obtenido las densidades y capacidades de retención de agua de los morteros frescos. Para caracterizar la red porosa de las pastas aireadas endurecidas, se obtuvieron tanto las densidades reales, netas, aparentes y relativas como las porosidades abiertas, cerradas y totales con ensayos hídricos. Finalmente se obtuvieron imágenes de los poros con tomografía axial computerizada para obtener las porosimetrías de las muestras. La caracterización de la red porosa ha servido para terminar de analizar lo observado en la evolución de la expansión del mortero fresco. Se ha analizado la influencia de la red porosa en la conductividad térmica, obtenida con caja caliente, comparándola con la existente en la literatura existente tanto de morteros celulares como de espumas poliméricas. Se concluye que los valores de conductividad térmica conseguida están en el mínimo posible para un material celular de base cementicia. La microestructura se ha estudiado con microscopía electrónica de barrido, difracción de rayos X y ensayos térmicos TG/ATD, observando que los productos de hidratación encontrados coinciden con los que se producen en morteros sin airear. Las imágenes SEM y los resultados de ultrasonidos han servido para analizar la presencia de microfisuras de retracción en las pastas aireadas, observando que en las muestras con adiciones de MK y SP, se reduce la presencia de microfisuras. ABSTRACT This thesis has studied cellular mortars, focusing in testing aerated cement pastes with aluminum powder as expansive agent. The purpose is the development of a cementitious material with low thermal conductivity that can be used as thermal isolation. Inorganic nature of this material makes it non-combustible, in contrast with polymeric foams in market, whose application in ventilated double skin façade systems has been banned by building standards, both domestically and internationally. Possible uses for this material are pneumatically sprayed applications and precast panels. Two series of batches with aluminum powder have been tested: - WPC/CAC/CH series. Reference paste with white portland cement (WPC), calcium aluminate cement (CAC) and lime (CH) with 5:1:4 ratio. - OPC/CH series. Reference paste with portland cement with fly ash (OPC) and lime (CH) with 4:1 ratio. Metakaolin (MK) (10 and 20%) or sepiolite (SP) (1 and 2%) additions were used in reference pastes to characterize the effect in fresh and hardened mortar. Rheology in fresh pastes was studied, expansion process of pastes was analyzed, recording yield stress, entrained air and temperature values during expansion. Recorded values were used to discuss influence of additions on reaction kinetics of aluminum powder corrosion, that produces expansion.. Conclusion is that pozzolanic additions (FA and MK) and SP greatly reduce induction period, producing bigger pores and more entrained air. Relation between yield stress and entrained air has been also analyzed, observing that the bigger yield stress at beginning of expansion, the smaller pores size and the lower entrained air values. Finally density and water retention of fresh mortars were obtained. Pore network in hardened aerated cement pastes was characterized by imbibition methods providing true, bulk and relative density, and providing also open, closed and total porosity. Finally, pore system imaging were obtained with computerized axial tomography to study porosimetry of specimens. Pore network characterization was useful to complete facts analysis observed in expansion of fresh mortars. Influence of pore network in thermal conductivity, checked in hot box, was analyzed comparing with those existing values in cellular mortar and polymeric foams researches. It was concluded that thermal conductivity values achieved are close to minimum possible in a cementitious cellular material. Microstructure was studied with Scanning Electron Microscopy, X-Ray Diffractometry and TG-DTA analysis, observing that hydration phases found, are those produced in non aerated mortar. SEM imaging and ultrasound results were useful to analyze shrinkage microcracks in aerated cement pastes, concluding that microcrack presence in specimens with MK and SP additions were reduced.

Determinación del contenido de alúmina reactiva de las adiciones puzolánicas naturales y artificiales, por termogravimetría y por el método de Rietveld

Tanto el tema de esta investigación, como sus objetivos, fundamentos, materiales seleccionados y parte experimental para alcanzarlos, han sido promovidos por la situación y el estado de las construcciones de hormigón armado que se comenzaron a realizar en España a partir del año 1975, con hormigones y morteros de cemento que contenían cenizas volantes hasta un 20 %, en principio, y hasta un 35 %, más tarde, de su dosificación de cemento Portland (CP), los cuales y en contra de lo esperado, han demandado y continúan demandando, muy a pesar de sus aparentes bondades de todo tipo que se les atribuían, una necesidad de mejora de sus prestaciones, especialmente, debido a un nivel inesperadamente bajo de la durabilidad de algunas obras construidas con los mismos. Todo era debido, en definitiva, a que las adiciones puzolánicas, naturales y artificiales, tales como las cenizas volantes, referidas antes, se vienen utilizando reglamentariamente para la fabricación de cementos y/o de sus productos derivados, hormigones, morteros y pastas, en la mayor parte de los países industrializados, desde hace ya más de tres décadas aproximadamente, en las mismas condiciones e idénticos usos constructivos que los hormigones y morteros de CP puro, viniendo además, dictada dicha utilización de estos materiales residuales, hoy sub-productos industriales, por cuestiones medioambientales y/o económicas, principalmente, motivo por el cual esta Tesis Doctoral ha pretendido responder también, adecuadamente y de manera esquemática (en forma de diagrama de flujo), a los criterios que deben de tenerse en cuenta a la hora de su selección y caracterización normalizada y reglamentada de estas adiciones minerales activas, sobre todo, antes de su dosificación y uso en forma del denominado cemento Portland con puzolana, o con ceniza volante, o con esquistos calcinados o con puzolanas calcinadas o con humo de sílice, cemento Portland mixto, cemento puzolánico o cemento compuesto, para que dichos problemas no se le produzcan al hormigón armado ni en masa. De aquí el enfoque tan particular y especial de esta investigación, al haberla circunscrito únicamente a las puzolanas naturales y artificiales, por considerarlas todas ellas, independientemente de por su origen, como materiales constituidos por pequeñas fracciones cristalinas distribuidas aleatoriamente en una matriz mayoritariamente vítrea y/o amorfa, la cual es la que le confiere su reactividad con el hidróxido de calcio en forma de cal apagada o de portlandita procedente de la hidratación del CP. A su vez, dichas fracciones vítreas y/o amorfas están constituidas, en su mayor parte, por sílice reactiva, SiO2r-, alúmina reactiva, Al2O3r-, y óxido de hierro reactivo, Fe2O3r-, recibiendo además, en conjunto, el nombre específico de "factores hidráulicos" de la puzolana, los cuales, por lo común, difieren cuantitativamente de sus contenidos totales, determinados por fusión alcalina mediante procedimientos normalizados. De los tres óxidos reactivos mencionados y desde el punto de vista técnico, los más importantes por su mayor presencia en casi todas las puzolanas naturales y artificiales y, también, transcendencia en la durabilidad química que les pueden llegar a conferir al hormigón armado y en masa, mortero o pasta de cemento que las contenga, son la SiO2r- y la Al2O3r-. El primero de los dos, la SiO2r-, reacciona nada más que con la portlandita (y el Ca(OH)2) para formar geles C-S-H, más tarde transformados en tobermoritas o en jennitas, semejantes a los que originan la alita y la belita del CP en su hidratación. Y desde el punto de vista normativo, la presencia de esta fracción silícica reactiva en las puzolanas viene regulada por la norma EN 197-1, de modo general, siendo además referida por la norma EN 450-1:2006, en el contexto de las cenizas volantes en su adición al hormigón, como "un polvo fino de partículas principalmente de forma esférica y cristalina, procedentes de la combustión de carbón pulverizado, que tiene propiedades puzolánicas y que está compuesto fundamentalmente de SiO2 y Al2O3". Además y de acuerdo con la primera de las dos normas, "El contenido de dióxido de silicio reactivo (definido y determinado según la norma EN 196-2 o su equivalente la UNE 80225) no debe ser inferior al 25 % en masa". Por su parte, cuantiosos estudios experimentales realizados por Talero solo y con otros investigadores, han demostrado que si la puzolana no es adecuada en calidad ni en cantidad, la durabilidad del cemento del que forme parte, y, por consiguiente, de los productos derivados que con él se fabriquen, hormigones, morteros, pastas y prefabricados, puede llegar a ser anormalmente baja, porque la alúmina reactiva, Al2O3r-, o alúmina tetra- o penta-coordinada que la constituye, se implica como tal, de una forma muy directa y con resultados totalmente contrapuestos incluso, en los ataques químicos agresivos naturales que se les producen, provenientes de terrenos y aguas selenitosas (sulfatos, que atacan en su caso al propio material hormigón, mortero y pasta que la contiene para formar ettringita de rápida formación, ett-rf, la cual puede llegar incluso a provocar un ataque rápido del yeso), del rocío marino y de las sales de deshielo (cloruros, que atacan, en cambio, a las armaduras de acero del hormigón provocándoles su corrosión electroquímica por "picadura", si bien, en este otro ataque químico, dicha Al2O3r- lo que origina es sal de Friedel de rápida formación, sF-rf, también, cuyo efecto es, en cambio, colmatador y protector, en definitiva, de dicha corrosión electroquímica), del agua de mar (acción agresiva mutua de cloruros y sulfatos), de la carbonatación, de la reactividad árido-álcali, además de intervenir en la liberación del calor de hidratación, así como también, en el comportamiento reológico de sus pastas, etc., acortándoles de este modo su durabilidad prevista y, en ocasiones, muy seriamente incluso. Pero lo más paradójico de todo es, que a pesar de su referido comportamiento totalmente contrapuesto, frente a sulfatos y cloruros, - aún no se dispone de un método de análisis químico para su determinación cuantitativa, que sea además relativamente sencillo en su operatividad, veraz, preciso, de respuesta rápida, desde el punto de vista técnico de la construcción (no más de 28 días), repetible, reproducible, que no implique peligro alguno para la seguridad vital de las personas que lo tengan que manipular y poner en práctica, económico, y que sirva también tanto para investigación -vertiente científica-, como, sobre todo, para control de calidad -vertiente técnica-, - y ni mucho menos tampoco se dispone todavía, de especificación química alguna que precise el contenido máximo de Al2O3r- (%) que tiene que poseer una puzolana natural o artificial, para poder ser añadida al cemento Portland y/o al hormigón que va a estar sometido a un determinado ataque químico agresivo de los mencionados antes, y, en especial, a sulfatos, a cloruros o al agua de mar. Y para mayor justificación de ambas necesidades, se ha de decir también que la vigente Instrucción de Hormigón Estructural EHE-08 no contempla tampoco especificación química alguna sobre los "factores hidráulicos", en general, ni del contenido de Al2O3r-(%) de las cenizas volantes, muy en particular, en su Artículo 30º "Adiciones", ni en ningún otro Artículo, a pesar de que sí contempla, en cambio, - otras especificaciones químicas que carecen del necesario significado en cuanto a la necesidad de llevar explícita o implícitamente, el mensaje de la Durabilidad Química deseado, y - el Artículo 37º, el cual y para mayor abundamiento se titula paradójicamente "Durabilidad del hormigón y de las armaduras". Asimismo, tampoco se contempla en la última versión que acaba de publicarse de la norma EN 197-1 titulada: "Cementos. Parte 1: Composición, especificaciones y criterios de conformidad de los cementos comunes". Ni tampoco, en la norma EN 450-1:2006 titulada "Cenizas volantes para hormigón. Parte 1: Definiciones, especificaciones y criterios de conformidad", ni en la vigente Instrucción española para la Recepción de Cementos, RC-08, ni en la norma ASTM C618-03 tampoco. La única especificación química que ambas normas, la europea y la norteamericana, refieren es aquella que dice que la suma de los contenidos porcentuales de SiO2 total, Al2O3 total y Fe2O3 total, de la puzolana natural o artificial, ha de ser mayor o igual que 70 %, definiendo, además, a las puzolanas de este modo tan genérico: "materiales silíceos o silíceos y aluminosos, que por sí mismos no poseen valor cementante alguno, pero que finamente divididos y en presencia de humedad, reaccionarán químicamente con hidróxido de calcio a temperaturas ordinarias para formar compuestos que poseen propiedades cementantes". Por consiguiente y de acuerdo con todo lo anterior, el objetivo primordial de esta Tesis Doctoral ha sido: Diseñar y poner a punto un nuevo método analítico de utilidad técnica (que la duración máxima del ensayo no sea mayor de 28 días), para determinar el contenido de alúmina reactiva, vítrea o amorfa, Al2O3r-, de las puzolanas naturales y artificiales. Y una vez puesto a punto, validarlo a nivel de su repetibilidad, de acuerdo con parámetros estadísticos apropiados, poniendo especial énfasis en los criterios de aceptación establecidos por la American Association of Official Analytical Chemists (AOAC). Y para conseguirlo, la innovación de esta investigación se ha basado en los siguientes fundamentos generales, a saber: - Toda la alúmina de cualquier puzolana natural o artificial, capaz de ser atacada, disuelta y lixiviada en 28 días, por la portlandita o por el hidróxido de calcio, Ca(OH)2, en medio acuoso, es considerada como alúmina reactiva, Al2O3r-. - Dicha fracción alumínica reactiva de la puzolana natural o artificial se tiene que encontrar, además, en el estado físico-químico de poder reaccionar químicamente también, en presencia de hidróxido de calcio, cloruro de sodio y agua, para originar monocloro¿aluminato de calcio hidratado, C3A·CaCl2·10H2O, o sal de Friedel. Además, dicho estado físico-químico de la puzolana ha de ser acorde con la definición de alúmina reactiva adoptada en esta investigación en razón de las prestaciones reales de durabilidad química que le puede llegar a conferir a los cementos de mezcla y a sus productos derivados, hormigones, morteros y pastas, que se fabriquen con la misma. - La originalidad de este nuevo método analítico, respecto a los demás métodos ya existentes, reside en que la cuantificación de dicha fracción alumínica reactiva de la puzolana natural o artificial, se realiza mediante cálculo estequiométrico, basándose, para ello, en dicha reacción química de formación de sal de Friedel precisamente, tras 28 días de hidratación básica-salina acelerada de la puzolana natural o artificial, habiéndose realizado, además, en esta investigación dicha determinación cuantitativa de la cantidad de sal de Friedel originada por cada puzolana, mediante dos técnicas analíticas instrumentales que fueron las siguientes: el análisis termogravimétrico (variante I ó I-I en su caso) y el método de Rietveld con la difracción de Rayos X en polvo (variante II). - La reacción química de formación de sal de Friedel tras 28 días de hidratación básica-salina acelerada de las puzolanas que se analicen, se optimizó para asegurar que el único compuesto químico de aluminio y cloro formado fuese sal de Friedel nada más (dosificando para ello en cantidad adecuada los reactivos químicos necesarios: Ca(OH)2, NaCl y agua destilada), manteniendo, además y por otra parte, el compromiso apropiado entre el máximo rendimiento de dicha reacción química (ataque, disolución y lixiviación en 28 días, de toda la alúmina reactiva de la puzolana) y el modo y medios más adecuados de acelerarlo para conseguirlo fue a 40°C de temperatura, con agitación constante y cierre hermético del reactor. - La aplicabilidad y selectividad del nuevo método analítico, objeto de esta Tesis Doctoral, fue estudiada con una serie de puzolanas naturales y artificiales españolas, silíceas y/o silíceas y aluminosas en naturaleza, que fueron las siguientes: M0 (metacaolín 0), M1 (M0 con 50 % de cuarzo), C y L (puzolanas naturales de las Islas Canarias), CV10 y CV17 (cenizas volantes), A (puzolana natural de Almagro), O (puzolana natural de Olot) y HS (humo de sílice). - Todas las adiciones minerales anteriores cumplieron con los principales requisitos físicos y químicos que son preceptivos para poder considerarlas, antes de todo, como puzolanas, lo que era indispensable y de obligado cumplimiento, para poderles determinar su contenido total de Al2O3r- (%) mediante el nuevo método analítico. Estos condicionantes fueron los siguientes: grado adecuado de finura de molido o tamaño medio de partícula (según la norma EN 451-2), haber sido analizadas químicamente antes de todo (según la norma EN 196-2 ó la ASTM C311), con el fin de determinarles especialmente, sus contenidos totales de SiO2 (%), Al2O3 (%) y Fe2O3 (%), haberles determinado, además, su contenido de sílice reactiva, SiO2r- (%) (según la norma UNE 80225), y haber cumplido con el ensayo de puzolanicidad o de Frattini (según la norma EN 196-5) a la edad de 28 días al menos. Este último requisito, otrora de obligado cumplimiento hasta el año 1988, para cualquier puzolana natural y artificial que una fábrica de cementos pretendiera introducir en el proceso de fabricación de un nuevo cemento puzolánico o cemento tipo CEM IV, ha logrado así, que se tenga que volver utilizar de nuevo de forma obligada con esta Tesis Doctoral. Y los resultados obtenidos con el nuevo método analítico de los contenidos de Al2O3r-(%) de las puzolanas seleccionadas, fueron los siguientes: - Mediante su variante I: M0 29.9 %, M1 16.9 %, CV10 11.4 %, L 12.3 %, C 12.6 %, A 8.0 %, CV17 9.5 % y O 6.3 % de Al2O3r-, y - Mediante su variante II: M0 30.7 %, M1 15.4 %, CV10 14.7%, L 11.8 %, C 11.1 %, A 8.9 %, CV17 9.6 % y O 6.8 % de Al2O3r-. Finalmente, todos ellos fueron contrastados, además, mediante la calibración y validación del nuevo método analítico, con los valores de referencia obtenidos de esas mismas puzolanas, los cuales se les habían determinado mediante el método de Florentín, consistente en atacar, disolver y lixiviar también toda la fracción alumínica soluble de la puzolana (y además, aquella silícica y férrica que la constituyen a la par), pero, en especial, su contenido total de alúmina reactiva, mediante un ataque básico (con Ca(OH)2 en medio acuoso a temperatura del laboratorio, habiendo sido, además, su duración hasta 1 año), seguido de otro ácido (con HCl, d = 1.12), habiéndose obtenido esta vez los siguientes resultados de sus contenidos de Al2O3r- (%): M0 28.8 %, M1 16.7 %, CV10 9.7 %, L 11.2 %, C 12.2 %, A 13.0 %, CV17 10.6 % y O 9.5 %. Dicha validación realizada ha puesto de manifiesto, en términos generales, que el nuevo método analítico es más fidedigno que el de Florentín, por lo que resulta ser totalmente apropiado para obtener los resultados que se han pretendido, además de proporcionarlos en un espacio de tiempo relativamente corto (28 días a lo sumo) y a un coste económico razonable por no elevado (salvo error u omisión y libre de impuestos directos e indirectos, el coste económico estimado de la variante I estaría en torno a 800.00 - 900.00 €/puzolana -caso más probable-, y aproximadamente una tercera parte nada más, en el caso de que la edad máxima del ensayo acelerado sea 7 días nada más -caso menos probable-), y, por consiguiente, técnicamente aceptable, al cumplir, además, en todo el rango considerado de variabilidad posible de concentraciones o contenidos del analito buscado en la puzolana, con tales parámetros de validación como son: linealidad (los resultados obtenidos son directamente proporcionales a la señal-respuesta instrumental recibida), sensibilidad, precisión excelente, repetibilidad satisfactoria de los valores obtenidos de los contenidos de Al2O3r- de todas y cada una de las adiciones puzolánicas seleccionadas, confirmando, por ello, la universalidad de su uso. Finalmente, las ventajas del nuevo método analítico, respecto a los métodos ya existentes recopilados de la bibliografía (el método de Florentín, el método de López Ruiz -HF 40 % y HNO3 2N-, el método de Murat y Driouche para arcillas -HF 0.5M-, el método de Arjuan, Silbee y Roy para cenizas volantes -HF 1 %- y su modificación por Fernández-Jiménez y cols. -HF 1 %, 27Al NMR MAS y XRD (método de Rietveld)-, y el método de determinación de la relación SiO2r-/Al2O3r- para arcillas y cenizas volantes por Ruiz-Santaquiteria y cols. -HF 1 %, NaOH 8M y ICP-AES-) son, principalmente, estar exento de peligro alguno para la seguridad vital de las personas que lo tengan que manipular y poner en práctica, ser bastante apropiado para control de calidad además de para investigación, su considerable menor coste económico, su relativamente corto espacio de tiempo que se necesita para obtener la respuesta-resultado pretendida (28 días a lo sumo), así como su universalidad y selectividad, puesto que además, su aplicabilidad es para todo tipo de adiciones puzolánicas naturales o artificiales, como así lo demuestran los resultados obtenidos de los materiales puzolánicos naturales y artificiales seleccionados y analizados, en un rango de concentraciones del analito -contenido de alúmina reactiva, Al2O3r- (%)-, desde el 5 % hasta el 30 % en masa, rango éste que, por otra parte, comprende prácticamente TODAS las adiciones puzolanas naturales y artificiales existentes en el mercado transnacional y las aún por existir. Por consiguiente y de acuerdo con lo anterior, el nuevo método analítico, ya sea realizado mediante su variante I o la II, debido, - en primer lugar, a los fundamentados planteamientos relativos a su procedimiento experimental -modus operandi- el cual ha sido aplicado a una amplia gama de puzolanas naturales y artificiales, y - en segundo lugar, debido a la calidad de los resultados obtenidos con un grado de precisión y repetibilidad excelentes, ha demostrado poseer una gran utilidad científica -para investigación-, pero, sobre todo, técnica -para control de calidad de adiciones puzolánicas naturales y artificiales que se adicionan habitualmente al cemento Portland en fábrica y/o a sus hormigones y morteros en planta-, además de ser representativos los valores obtenidos mediante el mismo respecto a la más que probable durabilidad química que cada una de ellas puede llegarle a conferir al hormigón armado y en masa, mortero y pasta del que forme parte, así como también su cantidad adecuada de sustitución parcial de cada cemento Portland para conseguirla, acorde con sus propias prestaciones químico-físicas o físico-químicas que puede llegarle a conferir, según sea su carácter químico (alumínico, alumínico-silícico, silícico-alumínico, silícico-férrico-alumínico o silícico), forma y tamaño medio de su partícula. Por último, el nuevo método analítico ha demostrado cumplir además, con todos los requisitos de obligado cumplimiento que establece la norma ISO/IEC 17025 sobre la calidad y fiabilidad de nuevos métodos o procedimientos analíticos no normalizados todavía, para poder ser propuesto en un futuro próximo, ante la Comisión de AENOR correspondiente, con objeto de comenzar un expediente para su certificación y normalización. ________________________________________________________________________________ Both the subject of this research, its objectives, fundamentals, materials selected and experimental part to achieve, have all been promoted by the situation and the state of reinforced concrete constructions that began performing in Spain from 1975, with concrete and mortars cement containing fly ash up to 20 %, in principle, and later, up to 35 % to its content of Portland cement, which and against expected, demanded a need to improve their performance, especially due to an unexpectedly low level of durability of some works built with them, despite, however, its apparent benefits of all kinds are ascribed to them. Ultimately, the natural or artificial pozzolanic additions, such as fly ash specially, referred to above, have been used with regulation to manufacture cements and/or its derivatives, concretes, mortars, cement pastes, in the most industrialized countries. More than three decades ago, under the same conditions and identical construction mainly uses concretes and mortars plain Portland cement, besides coming, given that use of these waste materials, industrial by-products today for environmental and/or economic issues. For this reason, this Doctoral Thesis aims to answer properly and schematically (in the form of flow chart), the criteria to be taken into account when selection and characterization standardized for these active mineral additions, especially prior to choosing and use in the so-called Portland Cement (PC) pozzolan, or with fly ash or with calcined shales or with calcined pozzolans or with silica fume or PC mixed or pozzolanic cement or compound cement, for that such pathology problems will not occur when reinforced concretes nor mass concretes are used for building. Hence the very particular and special focus about this research, having confined only to the natural or artificial pozzolans, considering them all, regardless of their origin, approach as materials consisting of small crystalline fractions randomly distributed in a largely vitreous and/or amorphous matrix, which confers their reactivity with calcium hydroxide in the form of slaked lime or portlandite from PC. In turn, these vitreous and/or amorphous fractions consist in its greater part, by reactive silica, SiO2r-, reactive alumina, Al2O3r-, and reactive iron oxide, Fe2O3r-, which also receive, in conjunction, the specific name of "hydraulic factors" of the pozzolan. Usually, they all differs in quantity of their respective total contents of the SiO2 (%), Al2O3 (%) and Fe2O3 (%) determined the pozzolan by alkaline fusion by means of standard procedures. Of the three above-mentioned oxides reagents and from the technical point of view, the most important for its increased presence in every one of the natural or artificial pozzolans and also significance in the chemical durability that can get them to give the concrete mortar or cement paste which contain them, are SiO2r- and Al2O3r-. From the first two, the SiO2r- reacts with portlandite only, released in the hydration of the PC (and with Ca(OH)2), to form C-S-H gels, transformed in tobermorites or jennites later on, similar to C-S-H gels also originating from the alite and belite hydration in the CP. From the standardization criteria point of view, the presence of this silicic fraction in pozzolans is regulated at first, by the European standard EN 197-1, in general, also being referred by the EN 450-1:2006, in the context of the fly ash in addition to the concrete, as a "fine powder of spherical particles mainly crystalline form. It is from the combustion of pulverized coal, which have pozzolanic properties and is mainly composed of SiO2 and Al2O3". In addition and according to the EN 197-1 standard, the reactive silica content (which can be defined and determined in accordance with EN 197-1 standard or its UNE 80225 standard) must not be lower than 25 % of its mass. Meanwhile, considerable experimental studies by Talero and Talero et al, have shown that if the pozzolan is not adequate in quality nor quantity, the durability of cement that is part and, therefore, of its derivative products, concretes, mortars and pastes cement, can become abnormally low because its reactive alumina, Al2O3r- (%), content or tetra- or penta-coordinated alumina which involves itself in a very direct and totally mixed and conflicting results even at all aggressive chemical attack natural to produce to the concrete, mortar and paste with inadequate natural and/or artificial pozzolans, such as those from the selenitous land and waters (sulfates, strikes if the material itself concrete, mortar and paste that contain them, for rapid forming ettringite form, ett-rf, which can even cause rapid gypsum attack to said concrete). In contrast, sea spray and de-icing salts (chlorides strikes the reinforced steel concrete causing them electrochemical corrosion by "bite", although in that other chemical attack, such Al2O3r- causes rapid Friedel's salt formation, Fs-rf, too, to cause protector effect of the electrochemical corrosion of reinforcements for these chlorides), seawater (mutual aggressive action of chlorides and sulfates), carbonation, alkali-silica reaction, and, in addition, to influence the release of hydration heat, as well as in the rheological behavior of the pastes, etc., decreasing/shorting them thus their expected durability and sometimes even very seriously. But the most ironic thing is, that despite its referral totally opposed, compared to sulfates and chlorides, behaviour, - far not available is, a chemical analysis method for its quantitative determination, which is also relatively simple in operation, accurate, precise, rapid response, from a technical point of view for building (no more than 28 days), repeatable, reproducible, not involving danger to life safety of the people who need to manipulate and implement, economic, and also serve for both scientific research and technical side, and - has yet to be any chemical specification that sets maximum levels for Al2O3r-(%) in the natural or artificial pozzolan to be added to the cement and/or to the concrete that will be subject to a particularly aggressive chemical attack from those mentioned above, and in particular, to sulphates, chlorides or sea water. And for the sake of and justification of this need, it has to be said that the current Spanish Instruction for Structural Concrete EHE-08 does not provide any specification on "hydraulic factors" in general, nor the content of Al2O3r- (%) in fly ash, very particular, as Article 30º "Additions", or any other Article, although does provide, however, other chemical specifications lacking the necessary meaning in terms of the message Chemical Durability mentioned, nor the Article 37º which and for greater sake, is paradoxically entitled "Durability of the concrete and of their reinforcements". It has also not contemplated in the latest version just released from EN 197-1 standard entitled "Cement Part 1: Composition, specifications and conformity criteria for common cements". Nor, in EN 450-1:2006 entitled "Fly ash for concrete Part 1: Definitions, specifications and conformity criteria", nor by current Spanish Instruction for Cement Reception, RC-08, nor the ASTM C618-03 Standard either. The only chemical specification that both Standards, European and American, refer is one that says that the sum of the total contents of SiO2 (%), Al2O3 (%) and Fe2O3 (%) of natural and artificial pozzolan, must be greater than or equal to 70 % , defining pozzolans thus: "siliceous or aluminous and siliceous materials, which themselves do not have any cementitious value but finely divided and in the presence of moisture it reacts with calcium hydroxide at ordinary temperatures to form compounds possessing cementitious properties". Consequently and according to everything related before, the primary objective of this Doctoral Thesis has been: To design and start-up a new quantitative analytical method of technical utility (the maximum test duration is not more than 28 days), to determine the content of reactive alumina content, Al2O3r- (%), vitreous or amorphous alumina, of natural and artificial pozzolans. And once designed, validate at repeatability level and in accordance with appropriate statistical parameters with special emphasis on the acceptance criteria established by the American Association of Official Analytical Chemists (AOAC). And to achieve this, the innovation of this research has been based on the following general principles, namely: - All the alumina in any pozzolan, natural or artificial, that can be attacked, dissolved and leached by portlandite or calcium hydroxide, Ca(OH)2, in aqueous medium, is considered reactive alumina, Al2O3r-. - This aluminic fraction of natural or artificial pozzolan to analyze and study, has to be in such physical-chemical state that it can react in the presence of calcium hydroxide, sodium chloride and water status and to cause monochloro-aluminate hydrated calcium, C3A·CaCl2·10H2O or Friedel's salt. Moreover, such physical-chemical state of the pozzolan must be consistent with the definition of reactive alumina adopted in this research because of the actual performance of chemical durability that can reach confer on blended cements and their derivatives, concretes, mortars and pastes that are manufactured with the same. - The originality of this new analytical method, compared to the other methods for determining reactive alumina existing (collected in abbreviated form in the state of the art of this report), is the quantification of such aluminic fraction of natural or artificial pozzolans is performed by stoichiometric calculation based on this, in the chemical reaction of Friedel's salt formation after 28 days of the analysis of saline-basic hydration accelerated natural or artificial pozzolan also performed in this research, and the quantitative determination of the Friedel's salt has been performed by two instrumental analytical techniques known as thermogravimetric analysis (variant I), and Rietveld method with X-ray powder diffraction (variant II). - The chemical reaction of Friedel's salt formation after 28 days of accelerated saline-basic hydration of the selected natural and artificial pozzolan, was optimized to ensure that the single chemical compound of aluminium and chlorine formed was Friedel's salt only (dosing for this purpose in amount suitable chemical reagents: Ca(OH)2, NaCl and distilled water), and, on the other hand, maintaining the appropriate compromise between the highest yield from the chemical reaction (attack, dissolution and leaching in 28 days, all reactive alumina of pozzolan) and to accelerate the etching media, which were 40°C temperature, constant stirring and sealing the reactor. - The applicability and selectivity of the new analytical method, the subject of this Doctoral Thesis, was studied with a series of Spanish natural and artificial pozzolans, siliceous or siliceous and aluminous in nature, which were as follows: M0 (metakaolin 0), M1 (M0 with 50 % quartz), L and C (natural pozzolans of the Canary Islands), CV10 (fly ash 10), CV17 (fly ash 17), A (natural pozzolan of Almagro), O (natural pozzolan of Olot), and HS (silica fume). - All mineral admixtures were selected satisfied the physical and chemical requirements proposed to consider them as pozzolan, which was mandatory, so its Al2O3r- (%) content can determine by the new analytical method. These conditions were as follows: adequate degree of fineness of grind or average particle size (according to EN 451-2 standard), have been analyzed chemically (according to EN 196-2 or ASTM C311 standards), in order to determine their total contents of SiO2 (%), Al2O3 (%) and Fe2O3 (%), mainly, having also determined its reactive silica content, SiO2r- (%) (UNE 80225 standard), and fulfilled with testing of pozzolanicity or Frattini test (according to EN 196-5 standard) at 28 days age at least. The last criteria was mandatory until 1988, for any natural and artificial pozzolan to a factory intended to introduce cements in the manufacturing process of a new Portland cement type CEM IV pozzolanic additions, and with this Doctoral Thesis has made is to be used once again mandatory. And the results obtained using the new analytical method, of the Al2O3r- (%) content for each selected pozzolan, were as follows: - by its variant I: M0 29.9 % , M1 16.9 % , CV10 11.4 % , L 12.3 % , C 12.6 % , A 8.0 % , CV17 9.5 % and O 6.3 % of Al2O3r-, and - by its variant II: M0 30.7 % , M1 15.4 % , CV10 14.7% % , L 11.8 % , C 11.1 % , A 8.9 % , CV17 9.6 % and O 6.8 % of Al2O3r-. Finally, they would all be further contrasted by the calibration and validation of new analytical method, with reference values obtained from these same natural and artificial pozzolans, which had been given by the method of Florentin, consisting of attack, dissolve and leached with a basic attack (with Ca(OH)2 in aqueous medium and laboratory temperature, having also been its duration up to 1 year), followed by another acid attack (HCl, d = 1.12), all soluble aluminic fraction of pozzolan, and in particular their total content of reactive alumina, Al2O3r-(%), was this time as follows: M0 28.8 %, M1 16.7 %, CV10 9.7 %, L 11.2 %, C 12.2 %, A 13.0 %, CV17 10.6 % and O 9.5 % (and their siliceous and iron contents that are at par). This validation has shown on the new analytical method is more reliable than Florentin method, so it turns out to be entirely appropriate to get the results that have been tried by the same, besides providing them a relatively short space of time (28 days at most) and reasonably no high economic cost (unless mistake -free direct and indirect taxes, such economic cost would be between 800.00 - 900.00 €/pozzolan (most likely case), and about an one-third part around, in the event that the maximum age of the accelerated test is 7 days only (less likely case). So it is technically acceptable, to consider the range of possible variability of concentrations or contents pozzolan analyte with validation parameters such as: linearity (the results obtained are directly proportional to the instrumental response signal received), excellent sensitivity and accuracy, satisfactory repeatability values from the contents of each and Al2O3r- (%) each selected pozzolan, confirming therefore universal use. Finally, the advantages of the new analytical method over existing methods compiled from literature (Florentin method , the Lopez Ruiz method -HF and HNO3 40 % 2N-, the method of Murat and Driouche for clays -0.5M HF-, the method of Arjuan, Roy and Silbee for fly ash -HF 1 %- and its modification by Fernández-Jiménez et al -HF 1 %, 27Al MAS NMR and XRD (Rietveld method)-, and the method for determining the SiO2r-/Al2O3r- clay and fly ash ratio of Santaquiteria Ruiz et al -HF 1 %, NaOH 8M and ICP-AES-) are primarily and relatively short time get the result intended answer (28 days at most), its considerable lower cost, free from danger to the life safety of the people who need to manipulate and put in practice as well as its universality and selectivity, since it is applicable for all types of natural or artificial pozzolans, as it has been shown by the results of selected natural and artificial pozzolanic materials and analyzed in a range of analyte concentrations -reactive alumina, Al2O3r- (%) content- from 5 % to 30 % by mass, this range, on the other hand, includes virtually ALL existing transnational market in natural and artificial pozzolans and still exist. Therefore and in accordance with the above, the new analytical method is already performed by the variant I or II, because, - firstly, grounded to experimental approaches concerning its experimental procedure -"modus operandi"- which has been applied to a wide range of natural and artificial pozzolans, and - secondly, due to the quality of the results obtained with a great degree of accuracy and repeatability, it has been shown to possess significant scientific value in the research, but especially technical value -for quality control of natural and artificial pozzolans commonly added to Portland cement factory and/or directly to their concrete and mortar in plant-, and also be representative enough of the values obtained by the same probable chemical durability that each of them can reach out to give the concrete mortar and paste to which it belongs, as well as proper amount of partial replacement of Portland cement. To get in line with their own chemical-physical or physical-chemical features which can come to confer, as its chemical character (aluminic, silicic-aluminic, aluminic-silicic, aluminic-ferric-silicic or ferric-silicic), form and medium size of its particle is. Finally, the new analytical method has proven to meet all mandatory requirements established by ISO/IEC 17025 on the quality and reliability of new methods or analytical procedures are not standardized yet, in order to be considered appropriate this new analytical method, in this Doctoral Thesis it is to be proposed in the near future, before the corresponding AENOR (Spanish Association for Standardization and Certification) Commission, to start a procedure for certification and standardization.

Energía de fractura de morteros de cemento reforzados con fibras de vidrio (GRC)

En este trabajo se presenta el estudio de la energía de fractura de dos tipos de morteros de cemento reforzados con fibras de vidrio (GRC). El primer tipo es un GRC normal y en el segundo se ha realizado una adición de un 25% en peso de cemento de metacaolín de alta reactividad. El estudio de la energía de fractura de este tipo de material es de especial relevancia puesto que las normas que rigen su utilización no proporcionan datos sobre esta propiedad del material. Para solventar estos problemas se ha planteado una modificación de la recomendación RILEM TC-187-SOC. Se han modificado las dimensiones de las probetas y se han adaptado el resto de características. Los ensayos han mostrado como el GRC de control y el GRC con metacaolín tienen respectivamente una energía de 455 N/m y 1824 N/m.This work presents the evaluation of the fracture energy of two types of glass fiber reinforced cement (GRC). The first type of GRC had a normal composition and the second type had a 25% of the cement weight metakaolin addition. This metakaolin had high reactivity. The study of the fracture energy in GRC is essential due to the lack of data about this mechanical property. Also the usual test method recommendations of this material do not provide any mean to obtain it. To solve these problems a modification of recommendation RILEM TC-187-SOC has been performed. Sample geometry has been modified to adapt it to GRC while the rest of the test parameters were maintained. Tests results showed that GRC without additions has a fracture energy of 455 N/m and GRC with 25% metakaolin addition has a fracture energy of 1824 N/m.

Desarrollo de conglomerantes basados en hipótesis constructivas de pirámides egipcias del Reino Antiguo

En la presente tesis doctoral se revisan las principales hipótesis que intentan aclarar los procesos constructivos llevados a cabo para edificar las pirámides egipcias de las Dinastías III y IV, organizándose dichas teorías desde el punto de vista de los posibles materiales constituyentes. La investigación se ha centrado en la hipótesis heterodoxa que propone, como medio para ejecutar estas construcciones, la manufactura completa de la pirámide con piedra caliza conglomerada. Con este fin, se profundiza en artículos que tienen por objeto el análisis de muestras de material de estos monumentos, de piedras calizas naturales y de piedras calizas geopoliméricas, con objeto de determinar si la hipótesis constructiva mencionada es viable. Tomando como referencia la hipótesis constructiva estudiada, se adicionan morteros de cal aérea con carbonato de sodio (natrón) y metacaolín, analizando posteriormente las nuevas características de estos conglomerantes. El cementante descrito en la teoría constructiva se enmarca dentro de la química y tecnología de los polímeros sintéticos inorgánicos activados alcalinamente, también denominados geopolímeros. Se desarrolla una primera mezcla basada en los datos extraídos de la investigación precedente. Posteriormente, se realizan varios grupos de mezclas, en las que se parte de unas proporciones iniciales correspondientes al geopolímero teórico de la hipótesis constructiva. Sobre dichas proporciones se realizan incrementos en la cantidad de cal, y los productos obtenidos son ensayados, tomando datos de: dureza Shore C, velocidad de ultrasonidos, densidades, resistencia a compresión y a flexión, difracción de rayos X, análisis térmicos y microscopía electrónica de barrido. Los resultados derivados de introducir las adiciones, en las proporciones estudiadas, mejoran notablemente algunas características de los morteros de cal convencionales. ABSTRACT In the present PhD thesis the main hypotheses about the construction processes to build the Egyptian pyramids of Dynasties III and IV are reviewed. These theories are addressed from the point of view of their possible constituent materials. The research focuses on the heterodox hypothesis that proposes, as a means to perform these constructions, the complete manufacturing of the pyramid with limestone conglomerate. In this regard, a state of the art is set on the analysis of samples of material of these monuments, natural limestone and limestone geopolymeric, to determine if the constructive hypothesis is viable. Using this constructive hypothesis as a reference, aerial lime mortars are added with sodium carbonate (natron) and metakaolin, and the new characteristics of these resulting binders are then analyzed. The cementing described in the constructive theory belongs to the chemistry and the technology of synthetic inorganic alkali-activated polymers, also called geopolymer. Based on data obtained from previous research, a first mix is prepared. Subsequently, several groups of mixes are made, starting from theoretical initial ratios corresponding to the geopolymer that was presumably used in the constructive hypothesis. Increments in the amount of lime are made upon such proportion, and the resulting products are tested for data collection about: Shore C hardness, ultrasound velocity, densities, compressive and flexural strength, X-ray diffraction, thermal analysis and scanning electron microscopy. The results allow to conclude that, if in the studied proportions, additions improve significantly some of the characteristics of conventional lime mortars.

The durability of glass fibre reinforced cements made with new cementitious matrices

Widespread use of glass fibre reinforced cement (GRC) has been impeded by concerns over its durability. Three degradation mechanisms are proposed - fibre corrosion, Ca(OHh precipitation and matrix densification - although their relative importance is debated. Matrices with reduced alkalinities and Ca(OH)2 contents are being developed; the aim of this study was to investigate their hydration and interaction with alkali-resistant fibres to determine the factors controlling their long-term durability, and assess the relevancy of accelerated ageing. The matrices studied were: OPC/calcium-sulphoaluminate cement plus metakaolin (C); OPC plus metakaolin (M); blast-furnace slag cement plus a micro-silica based additive (D); and OPC (O). Accelerated ageing included hot water and cyclic regimes prior to tensile testing. Investigations included pore solution expression, XRD, DTA/TG, SEM and optical petrography. Bond strength was determined from crack spacings using microstructural parameters obtained from a unique image analysis technique. It was found that, for the new matrices - pore solution alkalinities were lower; Ca(OH)2 was absent or quickly consumed; different hydrates were formed at higher immersion temperatures; degradation under 65°C immersion was an order of magnitude slower, and no interfilamental Ca(OH)2 was observed .It was concluded that: fibre weakening caused by flaw growth was the primary degradation mechanism and was successfully modelled on stress corrosion/static fatigue principles. OPC inferiority was attributed partly to its higher alkalinity but chiefly to the growth of Ca(OH)2 aggravating the degradation; and hot water ageing although useful in model formulation and contrasting the matrices, changed the intrinsic nature of the composites rather than simply accelerating the degradation mechanisms.

Alkali-Activated Natural Pozzolan Concrete as New Construction Material

In the near future, geopolymers or alkali-activated cementitious materials will be used as new high-performance construction materials of low environmental impact with a reasonable cost. This material is a good candidate to partially replace ordinary portland cement (OPC) in concrete as a major construction material that plays an outstanding role in the construction industry of different structures. Geopolymer materials are inorganic polymers based on alumina and silica units; they are synthesized from a wide range of dehydroxylated alumina-silicate powders condensed with alkaline silicate in a highly alkaline environment. Geopolymeric materials can be produced from a wide range of alumina-silica, including natural products--such as natural pozzolan and metakaolin--or coproducts--such as fly ash (coal and lignite), oil fuel ash, blast furnace or steel slag, and silica fume--and provide a route toward sustainable development. Using lesser amounts of calcium-based raw materials, lower manufacturing temperature, and lower amounts of fuel result in reduced carbon emissions for geopolymer cement manufacture up to 22 to 72% in comparison with portland cement. A study has been done by the authors to investigate the intrinsic nature of different types of Iranian natural pozzolans to determine the activators and methods that could be used to produce a geopolymer concrete based on alkali-activated natural pozzolan (AANP) and optimize mixture design. The mechanical behavior and durability of these types of geopolymer concrete were investigated and compared with normal OPC concrete mixtures cast by the authors and also reported in the literature. This paper summarizes the main conclusions of the research regarding pozzolanic activity, activator properties, engineering and durability properties, applications and evaluation of carbon footprint, and cost for AANP concrete.

Chemical resistance of lime-based grouts for masonry strengthening

The stone masonry walls are present in many buildings and historical monuments, with undeniable asset value, but also in old buildings housing both in Portugal and in Europe. Most of these buildings in masonry are in certain cases in a high state of degradation needing urgent intervention. This requires the identification of deficiencies and the application of appropriate intervention techniques. One of the possible techniques for structural consolidation works of stone masonry walls is the injection of fluid mortars currently called grouts. The choice of grouts is very important with regard in particular to their chemical and physical properties. In this study, carried out under the Master of Chemical Engineering, two types of lime-based grouts were used, in order to evaluate and compare their chemical resistance due to the crystallization of soluble salts. One of the grouts is a pre-dosed blend commercially available, Mape-Antique I from company Mapei (CA), and the second grout is a mixture prepared in the laboratory (LB), comprising metakaolin, cement, hydrated lime, water and superplasticizer. With the purpose of evaluating the action of sulphates on these grouts, a series of samples underwent several wetting-drying cycles using two different temperatures, 20 °C and 50 °C. During the experiment it was determined the change of weight and compressive strength in the analyzed grouts, as well as the sulphate ion concentration and pH of the solution in which the samples were dipped. The commercial grout (CA) apparently has a greater chemical resistance to sulphates. However grout LB showed to have positive results in some parameters.

Otimização e análise mecânica de pastas geopoliméricas para uso em poços sujeitos à injeção cíclica de vapor

Oil wells subjected to cyclic steam injection present important challenges for the development of well cementing systems, mainly due to tensile stresses caused by thermal gradients during its useful life. Cement sheath failures in wells using conventional high compressive strength systems lead to the use of cement systems that are more flexible and/or ductile, with emphasis on Portland cement systems with latex addition. Recent research efforts have presented geopolymeric systems as alternatives. These cementing systems are based on alkaline activation of amorphous aluminosilicates such as metakaolin or fly ash and display advantageous properties such as high compressive strength, fast setting and thermal stability. Basic geopolymeric formulations can be found in the literature, which meet basic oil industry specifications such as rheology, compressive strength and thickening time. In this work, new geopolymeric formulations were developed, based on metakaolin, potassium silicate, potassium hydroxide, silica fume and mineral fiber, using the state of the art in chemical composition, mixture modeling and additivation to optimize the most relevant properties for oil well cementing. Starting from molar ratios considered ideal in the literature (SiO2/Al2O3 = 3.8 e K2O/Al2O3 = 1.0), a study of dry mixtures was performed,based on the compressive packing model, resulting in an optimal volume of 6% for the added solid material. This material (silica fume and mineral fiber) works both as an additional silica source (in the case of silica fume) and as mechanical reinforcement, especially in the case of mineral fiber, which incremented the tensile strength. The first triaxial mechanical study of this class of materials was performed. For comparison, a mechanical study of conventional latex-based cementing systems was also carried out. Regardless of differences in the failure mode (brittle for geopolymers, ductile for latex-based systems), the superior uniaxial compressive strength (37 MPa for the geopolymeric slurry P5 versus 18 MPa for the conventional slurry P2), similar triaxial behavior (friction angle 21° for P5 and P2) and lower stifness (in the elastic region 5.1 GPa for P5 versus 6.8 GPa for P2) of the geopolymeric systems allowed them to withstand a similar amount of mechanical energy (155 kJ/m3 for P5 versus 208 kJ/m3 for P2), noting that geopolymers work in the elastic regime, without the microcracking present in the case of latex-based systems. Therefore, the geopolymers studied on this work must be designed for application in the elastic region to avoid brittle failure. Finally, the tensile strength of geopolymers is originally poor (1.3 MPa for the geopolymeric slurry P3) due to its brittle structure. However, after additivation with mineral fiber, the tensile strength became equivalent to that of latex-based systems (2.3 MPa for P5 and 2.1 MPa for P2). The technical viability of conventional and proposed formulations was evaluated for the whole well life, including stresses due to cyclic steam injection. This analysis was performed using finite element-based simulation software. It was verified that conventional slurries are viable up to 204ºF (400ºC) and geopolymeric slurries are viable above 500ºF (260ºC)

Adição de resíduo cerâmico em pastas geopoliméricas para cimentação de poços de petróleo

The development of activities the of oil and gas sector have promoted the search for suitable materials for cementing oil wells. In the state of the Rio Grande do Norte, the integrity of the cement sheath tends to be impaired during steam injection, a procedure necessary to increase oil recovery in reservoirs with low-viscosity oil. The geopolymer is a material that can be used as alternative cement, since it has been used in the production of fire-resistant components, building structures, and for the control of toxic or radioactive residues. Geopolymers result from condensation polymer alkali aluminosilicates and silicates resulting three-dimensional polymeric structures. They are produced in a manner different from that of Portland cement, which is made an activating solution that is mixed with geopolymer precursor. Among the few works studied allowed us to conclude that the pastes prepared with metakaolin as precursor showed better performance of its properties. Several studies show the addition of waste clay as a means of reducing cost and improving end of the folder properties. On this basis, the goal is to study the influence of the addition of ceramic waste in geopolymer paste. To develop the study of rheology tests were carried out, filtered, thickening time, compressive strength, free water, specific gravity and permeability, according to the American Pretoleum Institute (API). The results for all formulations studied show that the folders have high mechanical strength to a light paste; low filtrate volume, absence of free water, very low permeability, slurry, consistent with a light paste, and thickening time low that can be corrected with the use of a retardant handle. For morphological characterization, microstructural, physical, chemical and thermal tests were carried out by XRD, MEV, DTA, TG, FTIR. In the trial of XRD, it was found that geopolymer is an amorphous material, with a peak of crystalline kaolinite. In tests of TG / DTA, revealed the presence of a significant event, which represents the mass loss related to water, and also observed the reduction of weight loss by increasing the concentration of ceramic waste. In the trial of MEV, we found a uniform matrix without the presence of other phases. In the trial of FT-IR, we observed the presence of the band related to water. From all results it was determined that the optimum concentration range of use is between 2.5 and 5% of waste ceramic

Efeito da adição de fibras da palma do licuri (syagrus coronata) no comportamento físico e mecânico de compósitos de matriz cimentícia

This research was motivated by the requirement of asbestos s replacement in building systems and the need to generate jobs and income in the country side of the state of Bahia, Brazil. The project aimed at using fibers from licuri leaves (syagrus coronata), an abundant palm in the region, to produce composites appropriate for the sustainable production of cement fibre reinforced products in small plants. The composites were produced in laboratory using Portland cement CP-II-F32, sand, water, licuri palm fiber contents of 1.0, 1.5 and 2.0% by weight of binder (two different fiber length) and metakaolin. The latter was chosen as an additional binder for its efficiency to reduce the alkalinity of cementitious matrixes therefore preventing the degradation of vegetable fibers. The characterization of the composite components was carried out by sieving and laser particle size analyses, thermal analysis, fluorescence and X-ray diffraction. The composites performance was evaluated by 3- point-bending tests, compressive strength, ultrasound module of elasticity, free and restrained shrinkage, water capillarity absorption and apparent specific gravity. It has been found that the addition of fibers increased the time to onset of cracking over 200.00% and a 25% reduction in cracks opening in the restrained shrinkage test. The capillary absorption reduced about 25% when compared to fiber-free composites. It was also observed with regard to flexural strength, compressive strength and specific gravity, that the addiction of fibers did not affect the composite performance presenting similar results for compounds with and without fibers. In general it can be stated that the reinforced composite fibers of palm licuri presents physical and mechanical characteristics which enable them to be used in the intended proposals of this research

An Investigation of Waste Glass-Based Geopolymers Supplemented with Alumina

An increased consideration of sustainability throughout society has resulted in a surge of research investigating sustainable alternatives to existing construction materials. A new binder system, called a geopolymer, is being investigated to supplement ordinary portland cement (OPC) concrete, which has come under scrutiny because of the CO2 emissions inherent in its production. Geopolymers are produced from the alkali activation of a powdered aluminosilicate source by an alkaline solution, which results in a dense three-dimensional matrix of tetrahedrally linked aluminosilicates. Geopolymers have shown great potential as a building construction material, offering similar mechanical and durability properties to OPC. Additionally, geopolymers have the added value of a considerably smaller carbon footprint than OPC. This research considered the compressive strength, microstructure and composition of geopolymers made from two types of waste glass with varying aluminum contents. Waste glass shows great potential for mainstream use in geopolymers due to its chemical and physical homogeneity as well as its high content of amorphous silica, which could eliminate the need for sodium silicate. However, the lack of aluminum is thought to negatively affect the mechanical performance and alkali stability of the geopolymer system. Mortars were designed using various combinations of glass and metakaolin or fly ash to supplement the aluminum in the system. Mortar made from the high-Al glass (12% Al2O3) reached over 10,000 psi at six months. Mortar made from the low-Al glass (<1% Al2O3) did not perform as well and remained sticky even after several weeks of curing, most likely due to the lack of Al which is believed to cause hardening in geopolymers. A moderate metakaolin replacement (25-38% by mass) was found to positively affect the compressive strength of mortars made with either type of glass. Though the microstructure of the mortar was quite indicative of mechanical performance, composition was also found to be important. The initial stoichiometry of the bulk mixture was maintained fairly closely, especially in mixtures made with fine glass. This research has shown that glass has great potential for use in geopolymers, when care is given to consider the compositional and physical properties of the glass in mixture design.

Synthesis of Na-PSS geopolymers and analysis of the H2O/Na2O molar ratio influence over their mechanical properties

Geopolymers are solid aluminosilicate material made by mixing an activating solution and a solid precursor. This work studied the mechanisms of synthesis of metakaolin-based geopolymers and the influence of water content, described by the molar ratio H2O/Na2O, on the final product. The samples were tested using a Uniaxial Compressive Test (UCT) to define their compressive resistance. Two geopolymers series were synthetized and let them rest for 7- days and 28-days, each of them composed by six different sets. 7-day rest series showed that water addition had no relevant effect over its resistance while the 28-day rest series almost doubled the compressive resistance, although those with the highest H2O/Na2O molar ratio showed instead a drastic reduction. Two other series were synthesized by adding silt aggregate, a waste material obtained in the production of aggregate for concrete, corresponding to 10wt% and 20wt%of the metakaolin used. After 28 days of aging, these samples were tested via UCT to measure the variation of the compressive resistance after the silt addition. The aggregate has disruptive effects over the compressive resistance, but the 20wt% samples achieved a higher compressive resistance. Samples with highest and lowest compressive resistance have been chosen to carry out an XRD analysis. In all the samples it has been recognized the presence of Anatase (TiO2), a titanium oxide found in the metakaolin and Thermonatrite, a hydrated sodium carbonate [Na2CO3 • (H2O)]. Scanning Electron Microscopy was carried out on the samples with the highest compressive resistance and showed that the samples with lower water content developed a homogeneous geopolymeric texture, while those with higher water content showed instead a spongy-like texture and a higher air or pore solution bubbles presence. Silt/geopolymer composites showed a fracture system developing across the interstitial transition zone between the geopolymer matrix and the aggregate particle.

Synthesis of KOH-based geopolymers for innovative applications

This study presents an evaluation on compressive strength of metakaolin-based geopolymers synthetized by using different activators, KOH and NaOH. The influence of NaOH/KOH concentration ratio together with curing temperature and time were investigated to find the best results from the compressive strength tests of metakaolin-based geopolymers, synthesized with a commercial metakaolin. Aggregates of small grain size referred as fillers, were added to reduce brittleness, and minimize the pore size and shrinkage of the final mixture creating a stronger network. In this work, silt recovered from industrial processes of wash water used for aggregates production was used as a filler in the production of KOH-based geopolymers, examining the possible influence on the mechanical strength of the final product. The curing temperatures chosen for the synthesis were 85°C, 60°C and 40°C. The samples were tested after 7 days and 28 days, according to the UNI EN 1015-11:2019 applied on Ca-based cements, analyzing the differences in mechanical strength comparing samples with similar and different compositions. The study presented in total 72 synthetized geopolymer specimens that were analyzed with unconfined compression test (UCT). The characterization of the starting materials metakaolin and silt was carried out using X- ray diffraction analysis (XRD). Whereas, the formed geopolymers were analyzed using X- ray diffraction (XRD), and scanning electron microscopy (SEM) with energy dispersive X- ray spectroscopy (EDS).