Influence of Different Ceramics on Resin Cement Knoop Hardness Number

This study evaluated: 1) the effect of different ceramics on light attenuation that could affect microhardness, measured as the Knoop Hardness Number (KHN), of a resin cement immediately and 24 hours after polymerization and 2) the effect of different activation modes (direct light-activation, light activation through ceramics and chemical activation) on the KHN of a resin cement.Resin cement Rely X ARC (3M ESPE) specimens 5.0 mm in diameter and 1.0 nun thick were made in a Teflon mold covered with a polyester film. The cement was directly light activated for 40 seconds with an XL 2500 curing unit (3M ESPE) with 650 mW/cm(2), light activated through ceramic discs of Duceram Plus (DeguDent), Cergogold (DeguDent), IPS Empress (Ivoclar), IPS Empress 2 (Ivoclar), Procera. (NobelBiocare), In Ceram Alumina (Vita) and Cercon (DeguDent), having a 1.2 mm thickness or chemically activated without light application. The resin cement specimens were flattened, and KHN was obtained using an HMV 2 microhardness tester (Shimadzu) with a load of 50 g applied for 15 seconds 100 pin from the irradiated surface immediately and after storage at 37 degrees C for 24 hours. Ten measurements were made for each specimen, with three specimens for each group at each time. The data were submitted to ANOVA and Tukey's test (p=0.05). The KHN of the resin cement was not only affected by the mode of activation, but also by the post-activation testing time. The mean KHN of the resin cement for chemical activation and through all ceramics showed statistically significant lower values compared to direct activation immediately and at 24 hours. The KHN for 24 hours post-activation was always superior to the immediate post-activation test except with direct activation. The most opaque ceramics resulted in the lowest KHN values.

Influence of human dentine on the antibacterial activity of self-etching adhesive systems against cariogenic bacteria

Objectives: The incorporation of antibacterial agents into adhesive systems has been proposed to eliminate residual bacteria from dentine. This study used the agar diffusion method to evaluate the antibacterial activity of Clearfil Protect Bond (CPB), Clearfil SE Bond (CSEB), Clearfil Tri-S Bond (C3SB) and Xeno-III (XIII) self-etching adhesive systems, with or without light-activation, against cariogenic bacteria, and to assess the influence of human dentine on the antibacterial activity of these materials.Methods: An aliquot of 10 mu l per material (and individual components) were pipetted onto paper and dentine discs distributed in Petri dishes containing bacterial culture in BHI agar. Positive control was 0.2% chlorhexidine digluconate (CHX).Results: After incubation, the adhesive components of CPB and CSEB, liquid A of XIII and C3SB did not present antibacterial activity when applied to paper discs. The non-light-activated CPB primer + adhesive promoted the greatest inhibition of Streptococcus mutans (p < 0.05), whereas with light-activation, there was no significant difference between primer + adhesive and primer alone. For Lactobacillus acidophilus, CPB primer presented the greatest antibacterial activity in both light-activation conditions (p < 0.05). Regarding the dentine discs, only CHX promoted an inhibitory effect, though less intense than on paper discs (p < 0.05). CHX presented greater antibacterial activity against S. mutans than against L. acidophilus (p < 0.05).Conclusions: Light-activation significantly reduced the antibacterial activity of the self-etching adhesive systems; MDPB incorporation contributed to the effect of adhesive systems against cariogenic bacteria; the components eluted from the adhesive systems were not capable to diffuse through 400 mu m-thick dentine disc to exert their antibacterial activity against cariogenic bacteria. (C) 2008 Elsevier Ltd. All rights reserved.

Factors affecting on bond strength of glass fiber post cemented with different resin cements to root canal

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Fundamental Limits on Wavelength, Efficiency and Yield of the Charge Separation Triad

In an attempt to optimize a high yield, high efficiency artificial photosynthetic protein we have discovered unique energy and spatial architecture limits which apply to all light-activated photosynthetic systems. We have generated an analytical solution for the time behavior of the core three cofactor charge separation element in photosynthesis, the photosynthetic cofactor triad, and explored the functional consequences of its makeup including its architecture, the reduction potentials of its components, and the absorption energy of the light absorbing primary-donor cofactor. Our primary findings are two: First, that a high efficiency, high yield triad will have an absorption frequency more than twice the reorganization energy of the first electron transfer, and second, that the relative distance of the acceptor and the donor from the primary-donor plays an important role in determining the yields, with the highest efficiency, highest yield architecture having the light absorbing cofactor closest to the acceptor. Surprisingly, despite the increased complexity found in natural solar energy conversion proteins, we find that the construction of this central triad in natural systems matches these predictions. Our analysis thus not only suggests explanations for some aspects of the makeup of natural photosynthetic systems, it also provides specific design criteria necessary to create high efficiency, high yield artificial protein-based triads.

Effectiveness of surface protection for resin-modified glass-ionomer materials

Objective: the purpose of this study was to evaluate the effectiveness of various surface treatments for resin-modified glass-ionomer restorative materials by determining dye uptake spectrophotometrically. Method and materials: Two hundred twenty-four specimens, 4.1 mm in diameter and 2.0 mm thick, were made of 3 materials: Vitremer, Fuji II LC, and Photac-Fil Aplicap. Specimens were divided into 15 groups. The positive and negative control specimens remained unprotected, while the experimental specimens were protected with Heliobond light-activated bonding resin, Colorama nail varnish, or surface coatings indicated by the manufacturers of the glass-ionomer materials. Finishing Gloss for Vitremer, Fuji Varnish for Fuji II LC, and Ketac Glaze for Photac-Fil. The disks were immersed in 0.05% methylene blue for 24 hours except for the negative control group, which was immersed in deionized water. After 24 hours, the disks were removed, washed, and individually placed in 1 mL of 65% nitric acid for 24 hours. The solutions were centrifuged and the spectrophotometric absorbance was determined at 606 nm. The dye uptake was expressed in micrograms of dye per milliliter, and the results were analyzed with the Kruskal-Wallis test. Results: There were no differences in dye uptake among the 3 resin-modified glass-ionomer restorative materials, however, all of them required surface protection. Conclusion: the best surface protection for the 3 evaluated materials was obtained with Heliobond light-activated bonding resin.

Effect of Surface Treatments on the Bond Strength between Composite Resin and Acrylic Resin Denture Teeth

Purpose: This investigation studied the effects of 3 surface treatments on the shear bond strength of a light-activated composite resin bonded to acrylic resin denture teeth. Materials and Methods: The occlusal surfaces of 30 acrylic resin denture teeth were ground flat with up to 400-grit silicon carbide paper. Three different surface treatments were evaluated: (1) the flat ground surfaces were primed with methyl methacrylate (MMA) monomer for 180 seconds; (2) light-cured adhesive resin was applied and light polymerized according to the manufacturer's instructions; and (3) treatment 1 followed by treatment 2. The composite resin was packed on the prepared surfaces using a split mold. The interface between tooth and composite was loaded at a cross-head speed of 0.5 mm/min until failure. Results: Analysis of variance indicated significant differences between the surface treatments. Results of mean comparisons using Tukey's test showed that significantly higher shear bond strengths were developed by bonding composite resin to the surfaces that were previously treated with MMA and then with the bonding agent when compared to the other treatments. Conclusion: Combined surface treatment of MMA monomer followed by application of light-cured adhesive resin provided the highest shear bond strength between composite resin and acrylic resin denture teeth.

Avaliação de Diferentes Compósitos na Resistência à Fratura de Núcleos de Preenchimento

Objective: To evaluate and compare the fracture strength of different composite resins used for core buildup. Method: Thirty-six bovine teeth were decoronated at the cervical third to standardize the length of specimens at 20 mm. Under constant irrigation, the canals were prepared with #5 Largo drills corresponding to the size and diameter of #3 Reforpost fiberglass post. The posts were cemented with Enforce resin sealer, being 16 mm inside the root canal and 4 mm outside the root canal, and the material was light-activated for 30 seconds at each side. The specimens were divided into 3 groups (n=12), in which cores (4 mm diameter and 5 mm high) were prepared from a prefabricated standard with three types of composite resins: Group 1: Z100 (3M), Group 2: Z250 (3M) and Group 3: P60 (3M). The specimens were fixed in a cylindrical device with an adaptor at 45o inclination. This device was adapted to a universal testing machine (EMIC) to simulate the force until fracture of the specimen. Data were subjected to ANOVA (p<0.05). Results: The Z250 resin cores presented the highest mean fracture strength (45.453 kgf), while the mean fracture strengths in Group 1 and Group 3 were 38.014 and 39.506 kgf, respectively. P60 caused the largest number of root fractures. Conclusion: Considering the characteristics and properties of the tested resins, Z250 appears as the most indicated for core buildup.

Dentin hypersensitivity after teeth bleaching with in-office systems. randomized clinical trial

Purpose: To comparatively and prospectively compare in a randomized clinical trial, dentin hypersensitivity after treatment with three in-office bleaching systems, based on hydrogen peroxide at different concentrations, with and without light source activation. Methods: 88 individuals were included according to inclusion and exclusion criteria. Subjects were randomly divided into the following three treatment groups: Group 1 was treated with three 15-minute applications of hydrogen peroxide at 15% with titanium dioxide (Lase Peroxide Lite) that was light-activated (Light Plus Whitening Lase) with five cycles of 1 minute and 30 seconds each cycle, giving a total treatment time of 45 minutes; Group 2 was treated with three 10-minute applications of hydrogen peroxide at 35% (Lase Peroxide Sensy), activated by light (LPWL) same activation cycles than Group 1, with a total treatment time of 30 minutes; Group 3 was treated with only one application for 45 minutes of hydrogen peroxide at 35% (Whitegold Office) without light activation. Each subject underwent one session of bleaching on the anterior teeth according to the manufacturers' instructions. Dentin sensitivity was recorded with a visual analogue scale (VAS) at baseline, immediately after, and at 7 and 30 days after treatment using a stimulus of an evaporative blowing triple syringe for 3 seconds on the upper central incisors from a distance of 1 cm. A Kruskal-Wallis test followed by Mann-Whitney test was performed for statistical analysis. Results: All groups showed increased sensitivity immediately after treatment. Group 1 displayed less changes relative to baseline with no significant differences (P= 0.104). At 7 and 30 days after treatment, a comparison of VAS values indicated no significant differences between all groups (P= 0.598 and 0.489, respectively).

Avaliação das propriedades mecânicas e químicas em função de diferentes cimentos resinosos e pinos não-metálicos

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Caracterização de resinas para base de prótese e reembasamento: propriedades físico-químicas e mecânicas

Pós-graduação em Reabilitação Oral - FOAR

Profundidade de polimerização de cimentos resinosos utilizados na cimentação de pinos translúcidos e sua influência sobre a resistência adesiva antes e após ciclagem mecânica

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Evaluation of bond strength and thickness of adhesive layer according to the techniques of applying adhesives in composite resin restorations

Adhesive restorations have increasingly been used in dentistry, and the adhesive system application technique may determine the success of the restorative procedure. The aim of this study was to evaluate the influence of the application technique of two adhesive systems (Clearfil SE Bond and Adper Scotchbond MultiPurpose) on the bond strength and adhesive layer of composite resin restorations. Eight human third molars were selected and prepared with Class I occlusal cavities. The teeth were restored with composite using various application techniques for both adhesives, according to the following groups (n = 10): group 1 (control), systems were applied and adhesive was immediately light activated for 20 seconds without removing excesses; group 2, excess adhesive was removed with a gentle jet of air for 5 seconds; group 3, excess was removed with a dry microbrush-type device; and group 4, a gentle jet of air was applied after the microbrush and then light activation was performed. After this, the teeth were submitted to microtensile testing. For the two systems tested, no statistical differences were observed between groups 1 and 2. Groups 3 and 4 presented higher bond strength values compared with the other studied groups, allowing the conclusion that excess adhesive removal with a dry micro-brush could improve bond strength in composite restorations. Predominance of adhesive fracture and thicker adhesive layer were observed via scanning electron microscopy (SEM) in groups 1 and 2. For groups 3 and 4, a mixed failure pattern and thinner adhesive layer were verified. Clinicians should be aware that excess adhesive may negatively affect bond strength, whereas a thin, uniform adhesive layer appears to be favorable. (Quintessence Int 2013;44:9-15)

The effect of polymerization mode on monomer conversion, free radical entrapment, and interaction with hydroxyapatite of commercial self-adhesive cements

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Evaluation of the bleached human enamel by scanning electron microscopy

Since bleaching has become a popular procedure, the effect of peroxides on dental hard tissues is of great interest in research. Purpose: The aim of this in vitro study was to perform a qualitative analysis of the human enamel after the application of in-office bleaching agents, using Scanning Electron Microscopy (SEM). Materials and Methods: Twenty intact human third molars extracted for orthodontic reasons were randomly divided into four groups (n=5) treated as follows: G1- storage in artificial saliva (control group); G2- four 30-minute applications of 35% carbamide peroxide (total exposure: 2h); G3- four 2-hour exposures to 35% carbamide peroxide (total exposure: 8h); G4- two applications of 35% hydrogen peroxide, which was light-activated with halogen lamp at 700mW/cm2 during 7min and remained in contact with enamel for 20min (total exposure: 40min). All bleaching treatments adopted in this study followed the application protocols advised by manufacturers. Evaluation of groups submitted to 35% carbamide peroxide was carried out after two time intervals (30 minutes and 2 hours per session), following the extreme situations recommended by the manufacturer. Specimens were prepared for SEM analysis performing gold sputter coating under vacuum and were examined using 15kV at 500x and 2000x magnification. Results: Morphological alterations on the enamel surface were similarly detected after bleaching with either 35% carbamide peroxide or 35% hydrogen peroxide. Surface porosities were characteristic of an erosive process that took place on human enamel. Depression areas, including the formation of craters, and exposure of enamel rods could also be detected. Conclusion: Bleaching effects on enamel morphology were randomly distributed throughout enamel surface and various degrees of enamel damage could be noticed. Clinical significance: In-office bleaching materials may adversely affect enamel morphology and therefore should be used with caution.

Effectiveness of 6% hydrogen peroxide concentration for tooth bleaching-A double-blind, randomized clinical trial

The aim of this clinical randomized double-blind split-mouth study was to assess the effectiveness of a 6% hydrogen peroxide with nitrogen-doped titanium dioxide light activated bleaching agent. 31 patients were treated with: one upper hemiarcade with a 35% hydrogen peroxide bleaching agent and the other hemiarcade with a 6% hydrogen peroxide. Two applications were completed each treatment session and three sessions were appointed, with one week interval between them. Tooth colour was registered each session and 1 week and 1 months after completing the treatment by spectrophotometer, registering parameters L*, a* and b*, and subjectively using VITA Classic guide. Tooth sensitivity was registered by VAS and patient satisfaction and self-perception result was determined using OHIP-14. Tooth colour variation and sensitivity were compared between both bleaching agents. Both treatment showed a change between baseline colour and all check-points with a ΔE=5.57 for 6% and of ΔE=7.98 for the 35% one month after completing the (p<0.05). No statistical differences were seen when subjective evaluations were compared. Also, no differences were seen in tooth sensitivity between bleaching agents. OHIP-14 questionnaire demonstrated a significant change for all patients after bleaching. A 6% hydrogen peroxide with nitrogen-doped titanium dioxide light activated agent is effective for tooth bleaching, reaching a ΔE of 5.57 one month after completing the treatment, with no clinical differences to a 35% agent neither in colour change or in tooth sensitivity. A low concentration hydrogen peroxide bleaching agent may reach good clinical results with less adverse effects.