Effect of dentine surface treatment on leakage of root fillings with a glass ionomer sealer.

The purpose of this study was to observe the quality of seal of the glass ionomer cement, Ketac-Endo, after treatment of the root canal wall. The root canals of 140 extracted human teeth were prepared biomechanically. The root canals were treated with either EDTA or received an intracanal dressing of calcium hydroxide or camphorated paramonochlorphenol. The root canals were filled by the lateral condensation technique with gutta-percha points and the sealer Ketac-Endo, or zinc oxide-eugenol cement or Sealapex. The teeth were placed into a 2% methylene blue dye solution inside a flask, which was attached to a vacuum pump. Leakage was measured linearly. Sealapex exhibited significantly less leakage than Ketac-Endo or zinc oxide-eugenol cement (P<0.01). The use of EDTA and intermediary dressings reduced significantly (P<0.01) the leakage observed with the zinc oxide-eugenol sealer and Ketac-Endo.

Surface finishing of glass ionomer

Purpose: To evaluate the surface roughness and staining of a glass ionomer cement when subjected to different finishing procedures. Materials and Methods: Sixty-four discs of Chem-Fil II glass ionomer cement were submitted to staining test with methylene blue by spectrophotometry and roughness test by profilometry. Four groups were evaluated: Mylar matrix (control), Sof-Lex discs, Enhance points, and diamond bur. Results: Staining and roughness test, analyzed by ANOVA and Tukey's test, showed that the best surface was obtained when the material cured in contact with the Mylar matrix strip or when treated with Sof-Lex discs. The poorest results were obtained after using the diamond bur.

Reaction of dogs' teeth to root canal filling with mineral trioxide aggregate or a glass ionomer sealer

This study was conducted to observe the reaction of apical tissues of dogs' teeth after root canal filling with gutta-percha and mineral trioxide aggregate (MTA) or a glass ionomer (Ketac-Endo) as a sealer. The root canals were instrumented and filled by the lateral condensation technique with the sealers studied. Animals were killed 6 months later, and the specimens were removed and prepared for histological analysis. Results showed no inflammatory reaction of apical tissue and total closure of the apical foramen of all the teeth sealed with MTA. The teeth sealed with Ketac-Endo showed two cases of partial closure and different degrees of chronic inflammatory reaction. In conclusion, MTA exhibited better biological properties than Ketac-Endo. Copyright © 1999 by The American Association of Endodontists.

Cytotoxic effects of hard-setting cements applied on the odontoblast cell line MDPC-23

Objective: The present study evaluated the cytotoxic effects of hard setting applied on the odontoblastlike cells MDPC-23. Study design: Eighty round-shaped samples were prepared with the following experimental materials: calcium hydroxide, Vitrebond, RelyX Luting, and RelyX Unicem. The samples were placed in serum-free culture medium and incubated for 24 hours or 7 days at 37°C with 5% CO 2 and 95% air. The odontoblast cells were plated in the wells and incubated for 72 hours. After this period, the complete culture medium was replaced by the extracts obtained from every sample, and the methyltetrazolium assay was carried out to evaluate the cell metabolism. Results: For the 24-hour period, the experimental materials calcium hydroxide, Vitrebond, RelyX Luting, and RelyX Unicem decreased the cell metabolic activity by 91.52%, 81.14%, 78.17%, and 2.64%, respectively. For the 7-day period, calcium hydroxide, Vitrebond, RelyX Luting, and RelyX Unicem decreased the metabolic activity of the MDPC-23 cells by 91.13%, 87.27%, 79.04%, and 10.51%, respectively. Conclusion: RelyX Unicem presented the lowest cytopathic effects to the cultured odontoblast cell line. © 2007 Mosby, Inc. All rights reserved.

Randomized controlled clinical trial evaluating connective tissue graft plus resin-modified glass ionomer restoration for the treatment of gingival recession associated with non-carious cervical lesion: 2-year follow-up

Background: The aim of this clinical study is to evaluate the 2-year term results of gingival recession (GR) associated with non-carious cervical lesions (NCCLs) treated by connective tissue graft (CTG) alone or in combination with a resin-modified glass ionomer restoration (CTG+R). Methods: Thirty-six patients with Miller Class I buccal GR associated with NCCLs completed the follow-up. The defects were randomly assigned to receive either CTG or CTG+R. Bleeding on probing (BOP), probing depth (PD), relative GR, clinical attachment level (CAL), and cervical lesion height coverage were measured at baseline, 6 months, 1 year, and 2 years after treatment. Results: Both groups showed statistically significant gains in CAL and soft-tissue coverage. The differences between groups were not statistically significant in BOP, PD, relative GR, or CAL after 2 years. Cervical lesion height coverage was 79.31% ± 18.51% for CTG and 71.95% ± 13.25% for CTG+R (P >0.05). Estimated root coverage was 91.56% ± 11.74% for CTG and 93.29% ± 7.97% for CTG+R (P ≥0.05). Conclusions: Within the limits of the present study, it can be concluded that both procedures provide comparable soft tissue coverage after 2 years of follow-up.

Degree of conversion and hardness of two different systems of the vitrebond™ glass ionomer cement light cured with blue LED

This study investigated the physicochemical properties of the new formulation of the glass ionomer cements through hardness test and degree of conversion by infrared spectroscopy (FTIR). Forty specimens (n = 40) were made in a metallic mold (4 mm diameter × 2 mm thickness) with two resin-modified glass ionomer cements, Vitrebond™ and Vitrebond™ Plus (3M/ ESPE). Each specimen was light cured with blue LED with power density of 500 mW/cm2during 30 s. Immediately after light curing, 24h, 48h and 7 days the hardness and degree of conversion was determined. The Vickers hardness was performed by the MMT-3 microhardness tester using load of 50 gm force for 30 seconds. For degree of conversion, the specimens were pulverized, pressed with KBr and analyzed with FT-IR (Nexus 470). The statistical analysis of the data by ANOVA showed that the Vitrebond™ and Vitrebond™ Plus were no difference significant between the same storage times (p > 0.05). For degree of conversion, the Vitrebond™ and Vitrebond™ Plus were statistically different in all storage times after light curing. The Vitrebond™ showed higher values than Vitrebond™ Plus (p < 0.05). The performance of Vitrebond™ had greater results for degree of conversion than Vitrebond™ Plus. The correlation between hardness and degree of conversion was no evidence in this study.

Effect of chlorhexidine gluconate on porosity and compressive strength of a glass ionomer cement

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Influence of the addition of chlorhexidine diacetate on bond strength of a high-viscosity glass ionomer cement to sound and artificial caries-affected dentin

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Influence of ultrasound or halogen light on microleakage and hardness of enamel adjacent to glass ionomer cement

Background. The use of external sources of energy may accelerate the setting rate of glass ionomer cements (GICs) allowing better initial mechanical properties. Aim. To investigate the influence of ultrasound and halogen light on the microleakage and hardness of enamel adjacent to GIC restorations, after artificial caries challenge. Design. Cavities were prepared in 60 primary canines, restored with GIC, and randomly distributed into three groups: control group (CG), light group (LG) - irradiation with a halogen lightcuring unit for 60 s, and ultrasonic group (UG) application of ultrasonic scaler device for 15 s. All specimens were then submitted to a cariogenic challenge in a pH cycling model. Half of sample in each group were immersed in methylene blue for 4 h and sectioned for dye penetration analysis. The remaining specimens were submitted to Knoop cross-sectional microhardness assessments, and mineral changes were calculated for adjacent enamel. Results. Data were compared using Kruskal-Wallis test and two- way ANOVA with 5% significance. Higher dye penetration was observed for the UG (P < 0.01). No significant mineral changes were observed between groups (P = 0.844). Conclusion. The use of halogen light- curing unit does not seem to interfere with the properties of GICs, whereas the use of ultrasound can affect its marginal sealing.

Push-out bond strengths of different dental cements used to cement glass fiber posts

Statement of problem: Since the introduction of glass fiber posts, irreversible vertical root fractures have become a rare occurrence; however, adhesive failure has become the primary failure mode. Purpose: The purpose of this study was to evaluate the push-out bond strength of glass fiber posts cemented with different luting agents on 3 segments of the root. Material and methods: Eighty human maxillary canines with similar root lengths were randomly divided into 8 groups (n=10) according to the cement assessed (Rely X luting, Luting and Lining, Ketac Cem, Rely X ARC, Biscem, Duo-link, Rely X U100, and Variolink II). After standardized post space preparation, the root dentin was pretreated for dualpolymerizing resin cements and untreated for the other cements. The mixed luting cement paste was inserted into post spaces with a spiral file and applied to the post surface that was seated into the canal. After 7 days, the teeth were sectioned perpendicular to their long axis into 1-mm-thick sections. The push-out test was performed at a speed of 0.5 mm/min until extrusion of the post occurred. The results were evaluated by 2-way ANOVA and the all pairwise multiple comparison procedures (Tukey test) (?=.05). Results: ANOVA showed that the type of interaction between cement and root location significantly influenced the push-out strength (P<.05). The highest push-out strength results with root location were obtained with Luting and Lining (S3) (19.5 ±4.9 MPa), Ketac Cem (S2) (18.6 ±5.5 MPa), and Luting and Lining (S1) (18.0 ±7.6 MPa). The lowest mean values were recorded with Variolink II (S1) (4.6 ±4.0 MPa), Variolink II (S2) (1.6 ±1.5 MPa), and Rely X ARC (S3) (0.9 ±1.1 MPa). Conclusions: Self-adhesive cements and glass ionomer cements showed significantly higher values compared to dual-polymerizing resin cements. In all root segments, dual-polymerizing resin cements provided significantly lower bond strength. Significant differences among root segments were found only for Duo-link cement.

Immediate shear bond strengths of a composite, a compomer and a glass ionomer to a ceramic substrate.

PURPOSE To determine the best-performing combination of three core buildup materials and three bonding materials based on their bond strength to ceramic blocks in vitro. MATERIALS AND METHODS The materials used for core buildup were a composite (Tetric EvoCeram), a compomer (Compoglass F), and a glass-ionomer cement (Ketac Fil Plus), and for bonding, a three-step etch-and-rinse adhesive (Syntac), a two-step etch-and-rinse adhesive (ExciTE), and a single-step system (RelyX Unicem). Bond strength to ceramic blocks was determined by shear bond strength testing. Fracture behavior was evaluated by scanning electron microscopy. RESULTS The highest adhesive values between buildup and ceramic were obtained using the materials Compoglass F and Syntac, followed by Compoglass F and ExciTE. Among the two other core buildups, Tetric EvoCeram performed better than Ketac Fil Plus, which was independent of the bonding materials. Adhesive fractures were characteristically observed with Syntac and ExciTE, and cohesive fractures were characteristically observed with RelyX Unicem. CONCLUSION These data show that compomers bonded with a multistep adhesive system achieved statistically significantly higher shear bond strength than composites and glass-ionomer cements. Within the limitations inherent to this in vitro study, the use of compomers for core buildup can be recommended.

Rugosidade e pigmentação superficial de materiais ionoméricos

The aim of this study was to compare two methods of surface roughness analysis, perfilometry and spectrophotometry, applied to the surface of ionomeric materials (Chelon Fil, Vitremer and Dyract), submitted to different surface finishing treatments. For the perfilometric analysis, sixty specimens of each material were made and randomly separated into three experimental groups. The average surface roughness (Ra, mm) was measured on each specimen by a surface perfilometer (Mitutoyo Surftest 211). The spectrophotometric analysis consisted in quantifying the dye impregnated in the samples. The dyes used were 0.5% fuchsin and 0.5% erythrosin. Data were submitted to variance analysis (ANOVA) and t-Student test at a 0.05 significance level. There was no linear correlation between average roughness and superficial deposition of dye. Perfilometric analysis revealed that 12- and 30-bladed carbide burs caused the roughest surface of Chelon Fil, followed by Sof-Lex discs and mylar band. There were no significant differences between the specimens submitted to finishing and polishing with Sof-Lex discs and the control group (mylar band) for Vitremer, nevertheless, the highest Ra values were obtained when 12- and 30-bladed burs were used. For Dyract, there was no significant difference between the three treatments. The mean values of superficial deposition of dye for Chelon Fil, Vitremer and Dyract were: 1.7261, 1.4759, 1.3318, respectively. There were no significant differences between the restorative materials when different finishing and polishing systems were used.

In vitro analysis of inhibitory effects of the antibacterial monomer MDPB-containing restorations on the progression of secondary root caries

Objective: This study aimed to analyze in vitro inhibitory effects of restorative materials containing the antibacterial monomer 12-methacryloyloxydodecylpyridinium bromide (MDPB) on the formation of artificial secondary root caries lesions. Methods: Class V cavities (2 mm x 2 mm) were prepared in 75 human root fragments. Specimens were randomly divided into five groups (n = 15 fragments per group) and restored as follows: (I) MDPB-free adhesive system + MDPB-free composite (negative control); (II) resin modified glass ionomer (RM-GIC; positive control); (III) MDPB-free adhesive system + MDPB-containing composite (2.83% MDPB); (IV) MDPB-containing adhesive system + MDPB-free composite; M MDPB-containing adhesive system + MDPB-containing composite. Artificial secondary root caries lesions were produced by a biological artificial caries challenge. The restored specimens were immersed into a culture medium containing Streptococcus mutans and sucrose for 15 days. Histological slices (80 +/- 20 mu m) of the specimens were used for measuring the mean depths of the artificial lesions produced in both margins of the restorations using polarized light microscopy. Results were expressed in percentage related to the mean depth of the negative control, considered 100%. Data were compared by ANOVA followed by the Tukey`s test (p <= 0.05). Results: The depths of lesions adjacent to cavities filled with RM-GIC (GII; 85.17 +/- 15.2%) were significantly (p < 0.01) shallower than those adjacent to restorations with MDPB-free composite (GI; 100.00 +/- 10.04%), despite the presence of MDPB in the adhesive system (GIV; 101.95 +/- 21.32%). The depths of lesions adjacent to cavities restored with MDPB-containing composite (GIII; 82.68 +/- 12.81% and GV; 85.65 +/- 15.42%), despite the adhesive system used, were similar to those of RM-GIC (GII). Mean lesions depths in these groups decreased from 13% (GV) to 17% (GIII) in relation to the negative control (GI). Conclusions: MDPB-containing composite inhibits the progression of artificial secondary root caries lesions regardless of adhesive systems. (C) 2009 Elsevier Ltd. All rights reserved.

Effect of prolonged erosive pH cycling on different restorative materials

This in vitro study evaluated the effect of a prolonged erosive pH cycling on the superficial microhardness change (SMHC) and the erosive wear of different restorative materials. Eighty enamel specimens with prepared cavities of 1.5 x 1.5 mm were randomly divided into eight groups according to the restorative materials used for the fillings (RMGI - resin-modified glass-ionomer, CGI - conventional glass-ionomer, CR- composite resin, A - amalgam) and immersion media used (ERO - erosive medium or SAL - artificial saliva). During 35 days, half of the specimens were immersed in a cola drink (ERO), for 5 min, three times a day, and they remained in SAL between the erosive cycles. The other half of the specimens was immersed in SAL only, for the entire experimental period (control). Data were tested for significant differences by anova and Tukey`s tests (P < 0.05). Scanning electron microscopy images were made to illustrate the enamel erosive wear and restorative materials alterations. The mean SMHC (%) and mean erosive wear (mu m) of the materials were: RMGI-ERO (30/0.5); CGI-ERO (37/0.5); CR-ERO (-0.3/0.3); A-ERO (-4/0.3); RMGI-SAL (4/0.4); CGI-SAL (-6/0.4); CR-SAL (-3/0.2) and A-SAL (2/0.4). Scanning electron microscopy images showed pronounced enamel erosive wear on groups submitted to erosive pH cycling when compared with groups maintained in saliva. In conclusion, the prolonged pH cycling promoted significantly higher alterations (SMHC and erosive wear) on the glass-ionomer cements than the CR and amalgam.

Six-year evaluation of the atraumatic restorative treatment approach in permanent-tooth Class III restorations

Purpose: The aim of this study was to assess the 6-year performance of the ART (atraumatic restorative treatment) approach in Class III restorations in permanent teeth. Materials and Methods: A total of 127 ART Class III restorations, using Ketac-Molar (3M ESPE) ionomer cement, was performed in 58 adult patients by one experienced operator in 1998. After a 6 years, 34 patients and 65 restorations were evaluated according to ART criteria. Two calibrated examiners carried out the evaluation. Data were analyzed by exact 95% Confidence Interval and Survival Analysis using the Jackknife method for standard error determination. Results: Among assessed restorations, 73.8% (95% CI = 61.5% to 86.2%) were in good condition and classified as successful, with a 67.6% (95% CI = 54.4% to 80.7%) cumulative survival rate. Failed restorations included 13.9% completely or partially missing restorations, 9.2% restorations that had been replaced by other treatment, 1.5% restorations with a large defect at the margin, and 1.5% restorations that presented high wear on the surface. No caries was observed even in those teeth in which restorations were absent. Conclusion: The 6-year success rate of the ART approach in anterior permanent teeth (Class III) was considered high.