E and H regimes of plasma enhanced chemical vapor deposition of diamond-like carbon film in low frequency inductively coupled plasma reactor

This paper reports on the efficient deposition of hydrogenated diamond-like carbon (DLC) film in a plasma reactor that features both the capacitively and inductively coupled operation regimes. The hydrogenated DLC films have been prepared on silicon wafers using a low-frequency (500 kHz) inductively coupled plasma (ICP) chemical vapor deposition (CVD) system. At low RF powers, the system operates as an asymmetric capacitively coupled plasma source, and the film deposition process is undertaken in the electrostatic (E) discharge regime. Above the mode transition threshold, the high-density inductively coupled plasma is produced in the electromagnetic (H) discharge regime. It has been shown that the deposition rate and hardness of the DLC film are much higher in the H-mode deposition regime. For a 2.66-Pa H-mode CH4 + Ar gas mixture discharge, the deposited DLC film exhibits a mechanical hardness of 18 GPa, Young's modulus of 170 GPa, and compressive stress of 1.3 GPa.

Synthesis and characterization of ternary AL-C-N compound

Efficient hydrogenated diamond-like carbon (DLC) film deposition in a plasma reactor that features both the capacitive and inductively coupled operation regimes is reported. The hydrogenated DLC films have been prepared on silicon wafers using a low-frequency (500 kHz) inductively coupled plasma (LF ICP) chemical vapor deposition (CVD) system. At low RF powers, the system operates as an asymmetric capacitively coupled plasma source, and the film deposition process is undertaken in the electrostatic (E) discharge regime. The films deposited in the electrostatic mode feature graphite-like structure. Above the mode transition threshold, the high-density inductively coupled plasma is produced in the electromagnetic (H) discharge regime. Raman spectrometry suggests the possibility to control relative proportions of sp2 and sp3 hybridized carbon. Variation of the DC substrate bias results in dramatic modification of the film structure from the polymeric (unbiased substrates) to the diamond-like (optimized bias). It has been shown that the deposition rate and hardness of the DLC film are much higher in the H-mode deposition regime. For a 20 m Torr H-mode CH4+Ar gas mixture discharge, the DLC film exhibits mechanical hardness of 18 GPa, Young's modulus of 170 GPa, and compressive stress of 1.3 GPa.

New reaction paths for metal diborides at low temperature and pressure

Attention has recently focussed on MgB2 superconductors (Tc~39K) which can be formed into wires with high material density and viable critical current densities (Jc)1. However, broader utilisation of this diboride and many others is likely to occur when facile synthesis for bulk applications is developed. To date, common synthesis methods include high temperature sintering of mixed elemental powders2, combustion synthesis3, mechano-chemical mixing with high temperature sintering4 and high pressure (~GPa region) with high temperature. In this work, we report on a lower temperature, moderate (<4MPa) pressure method to synthesise metal diborides.

Mechanical bending properties of sodium titanate (Na2Ti3O7) nanowires

We report on the mechanical properties of sodium titanate nanowires (Na2Ti3O7 NW) through a combination of bending experiments and theoretical analysis. Na2Ti3O7 NWs with lateral dimensions ranging from 20–700 nm were synthesized by a hydrothermal approach. A focused ion beam (FIB) was used to manipulate the selected Na2Ti3O7 NW over a hole drilled in an indium tin oxide substrate. After welding the nanowire, a series of bending tests was performed. It was observed that the Na2Ti3O7 NW exhibits a brittle behavior, and a nonlinear elastic deformation was observed before failure. By using the modified Euler–Bernoulli beam theory, such nonlinear elastic deformation is found to originate from a combination of surface effects and axial elongation (arising from the bending deformation). The effective Young's modulus of the Na2Ti3O7 NW was found to be independent of the wire length, and ranges from 21.4 GPa to 45.5 GPa, with an average value of 33 ± 7 GPa. The yield strength of the Na2Ti3O7 NW is measured at 2.7 ± 0.7 GPa.

Variation in parental magmas of Mt Rouse, a complex polymagmatic monogenetic volcano in the basaltic intraplate Newer Volcanics Province, southeast Australia

Monogenetic volcanoes have long been regarded as simple in nature, involving single magma batches and uncomplicated evolutions; however, recent detailed research into individual centres is challenging that assumption. Mt Rouse (Kolor) is the volumetrically largest volcano in the monogenetic Newer Volcanics Province of southeast Australia. This study presents new major, trace and Sr–Nd–Pb isotope data for samples selected on the basis of a detailed stratigraphic framework analysis of the volcanic products from Mt Rouse. The volcano is the product of three magma batches geochemically similar to Ocean–Island basalts, featuring increasing LREE enrichment with each magma batch (batches A, B and C) but no evidence of crustal contamination; the Sr–Nd–Pb isotopes define two groupings. Modelling suggests that the magmas were sourced from a zone of partial melting crossing the lithosphere–asthenosphere boundary, with batch A forming a large volume partial melt in the deep lithosphere (1.7 GPa/55.5 km); and batches B and C from similar areas within the shallow asthenosphere (1.88 GPa/61 km and 1.94 GPa/63 km, respectively). The formation and extraction of these magmas may have been due to high deformation rates in the mantle caused by edge-driven convection and asthenospheric upwelling. The lithosphere– asthenosphere boundary is important with respect to NVP volcanism. An eruption chronology involves sequential eruption of magma batches A, C and B, followed by simultaneous eruption of batches A and B. Mt Rouse is a complex polymagmatic monogenetic volcano that illustrates the complexity of monogenetic volcanism and demonstrates the importance of combining detailed stratigraphic analysis alongside systematic geochemical sampling.

Phonon anomalies predict superconducting Tc for AlB2-type structures

We show that the well-known Kohn anomaly predicts Tc for ordered AlB2-type structures. We use ab initio Density Functional Theory to calculate phonon dispersions for Mg1-xAlxB2 compositions and identify a phonon anomaly with magnitude that predicts experimental values of Tc for all x. Key features of these anomalies correlate with the electronic structure of Mg1-xAlxB2. This approach predicts Tc for other known AlB2-type structures as well as new compositions. We predict that Mg0.5Ba0.5B2 will show Tc = 63.6 ± 6.6 K. Other forms of the Mg1-xBaxB2 series will also be superconductors when successfully synthesised. Our calculations predict that the end-member composition, BaB2, is likely to show a Tc significantly higher than currently achieved by other diborides although an applied pressure ~16 GPa may be required to stabilise the structure.

Lowering of relaxor transition temperature in Lead-based perovskites under pressure

The dielectric constants of lead iron niobate (PFN) and 40% lead zinc niobate (PZN) added to lead iron niobate (PFN0.6-PZN(0.4)) have been measured as a function of pressure up to 6 GPa under isothermal conditions between room temperature and 348 K. The relaxer transition temperature measured at 1 kHz excitation frequency varies at a rate -24.5 K/GPa for PFN and at a rate of - 28.8 K/GPa for the PFN0.6-PZN(0.4) composition.

Electrical and mechanical properties of diluted magnetic semiconductor Zn1-xMnxS nanocrystalline films

Nanostructured Zn1-xMnxS films (0 less-than-or-equals, slant x less-than-or-equals, slant 0.25) were deposited on glass substrates by simple resistive thermal evaporation technique. All the films were deposited at 300 K in a vacuum of 2*10-6 m bar. All the films temperature dependence of resistivity revealed semiconducting behaviour of the samples. Hot probe test revealed that all the samples exhibited n-type conductivity. The nanohardness of the films ranges from 4.7 to 9.9 GPa, Young's modulus value ranging 69.7-94.2 GPa.

Frictional response of fatty acids on steel

Self-assembled monolayers of fatty acids were formed on stainless steel by room-temperature solution deposition. The acids are covalently bound to the Surface as carboxylate in a bidentate manner. To explore the effect Of Saturation in the carbon backbone on friction in sliding tribology, we Study the response of saturated stearic acid (SA) and unsaturated linoleic acid (LA) as self-assembled monolayers using lateral force microscopy and nanotribometry and when the molecules are dispersed in hexadecane, using pin-on-disc tribometry. Over a very wide range (10 MPa-2.5 GPa) of contact pressures it is consistently demonstrated that the unsaturated linoleic acid molecules yield friction which is significantly lower than that of the saturated stearic acid. it is argued, using density functional theory predictions and XPS of slid track, that when the molecular backbone of unsaturated fatty acids are tilted and pressed strongly by a probe, in tribological contact, the high charge density of the double bond region of the backbone allows coupling with the steel Substrate. The interaction yields a low friction carboxylate soap film on the substrate. The saturated fatty acid does not show this effect.

Pressure-Induced transitions in amorphous TlxSe100-x alloys

The electrical resistivity of bulk semiconducting amorphous TlxSe100-x alloys with 0 ≤ x ≤ 25 has been investigated up to a pressure of 14 GPa and down to liquidnitrogen temperature by use of a Bridgman anvil device. All the glasses undergo a discontinuous pressure-induced semiconducting-to-metal transition. X-ray diffraction studies on the pressure-recovered samples show that the high-pressure phase is the crystalline phase. The pressure-induced crystalline products are identified to be a mixture of Se having a hexagonal structure with a = 4·37 Aring and c = 4·95 Aring and TlSe having a tetragonal structure with a = 8·0 Aring and c = 7·0 Aring

Low-temperature and high-pressure Raman and x-ray studies of pyrochlore Tb2Ti2O7: Phonon anomalies and possible phase transition

We have carried out temperature- and pressure-dependent Raman and x-ray measurements on single crystals of Tb2Ti2O7. We attribute the observed anomalous temperature dependence of phonons to phonon-phonon anharmonic interactions. The quasiharmonic and anharmonic contributions to the temperature-dependent changes in phonon frequencies are estimated quantitatively using mode Grüneisen parameters derived from pressure-dependent Raman experiments and bulk modulus from high-pressure x-ray measurements. Further, our Raman and x-ray data suggest a subtle structural deformation of the pyrochlore lattice at ~9 GPa. We discuss possible implications of our results on the spin-liquid behavior of Tb2Ti2O7.

Electrical transport and crystallization studies of glassy semiconducting Si20Te80 alloy at high pressure

The effect of pressure on the electrical resistivity of bulk Si20Te80 glass is reported. Results of calorimetric, X-ray and transmission electron microscopy investigations at different stages of crystallization of bulk Si20Te80 glass are also presented. A pressure induced glass-to-crystal transition occurs at a pressure of 7 GPa. Pressure and temperature dependence of the electrical resistivity of Si20Te80 glass show the observed transition is a pressure induced glassy semiconductor to crystalline metal transition. The glass also exhibits a double Tg effect and double stage crystallization, under heating. The differences between the temperature induced crystallization (primary crystallization) and pressure induced congruent crystallization are discussed.

High-Pressure Nmr And Compressibility Evidence For A Phase-Transition In The Protonic Conductor (NH4)4Fe(CN)6.1.5H2o

1H NMR at high hydrostatic pressures and compressibility studies show that the protonic conductor (NH4)4Fe(CN)6·1.5H2O undergoes a phase transition around 0.45 GPa. The transition is characterized by a large hysteresis. From the NMR studies, an activation volume of 6% is obtained below the phase transition, indicating the dominance of Frenkel defects.

Pressure induced polymorphous crystallization in bulk Ge20Te80 glass

The pressure and temperature dependence of the electrical resistivity of bulk glassy Ge20Te80 is reported. The effect of annealing is also studied. The glass undergoes a polymorphous or congruent crystallization under high pressures. The high pressure phase is found to have fcc structure with Image . Under thermal treatment the glass undergoes the double stage crystallization. The sample annealed at the first crystallization temperature shows a pressure induced semiconductor-to-metal transition at 4.0 GPa pressure and the crystalline Ge20Te80 samples show the transition at 7 GPa pressure.

Stress-induced phase transformation and pseudo-elastic/pseudo-plastic recovery in intermetallic Ni-Al nanowires

Extensive molecular dynamics (MD) simulations have been performed in a B2-NiAl nanowire using an embedded atom method (EAM) potential. We show a stress induced B2 -> body-centered-tetragonal (BCT) phase transformation and a novel temperature and cross-section dependent pseudo-elastic/pseudo-plastic recovery from such an unstable BCT phase with a recoverable strain of similar to 30% as compared to 5-8% in polycrystalline materials. Such a temperature and cross-section dependent pseudo-elastic/pseudo-plastic strain recovery can be useful in various interesting applications of shape memory and strain sensing in nanoscale devices. Effects of size, temperature, and strain rate on the structural and mechanical properties have also been analyzed in detail. For a given size of the nanowire the yield stress of both the B2 and the BCT phases is found to decrease with increasing temperature, whereas for a given temperature and strain rate the yield stress of both the B2 and the BCT phase is found to increase with increase in the cross-sectional dimensions of the nanowire. A constant elastic modulus of similar to 80 GPa of the B2 phase is observed in the temperature range of 200-500 K for nanowires of cross-sectional dimensions in the range of 17.22-28.712 angstrom, whereas the elastic modulus of the BCT phase shows a decreasing trend with an increase in the temperature.