Influence of the dipolar interactions in the magnetization reversal asymmetry of hard-soft magnetic ribbons

Partial crystallization of the metallic glass Co66Si16B12Fe4Mo2 was performed by annealing at temperatures between 500 and 540°C for 10-20 min, resulting in crystallite volume fractions of (0.7-5)×10¿3 and sizes of 50-100 nm. This two-phase alloy presents a remarkable feature: a hysteresis loop shift that can be tailored by simply premagnetizing the sample in the adequate magnetic field. Shifts as large as five times the coercive field have been obtained which make them interesting for application as magnetic cores in dc pulse transformers. The asymetrical magnetic reversal is explained in terms of the magnetic dipolar field interaction and the observed hysteresis loops have been satisfactorily simulated by a modification of Stoner-Wohlfarth¿s model of coherent rotations.

Synthesis, structure, and magnetic studies on self-assembled BiFeO3-CoFe2O4 nanocomposite thin films

Self-assembled (0.65)BiFeO3-(0.35)CoFe2O4 (BFO-CFO) nanostructures were deposited on SrTiO3 (001) and (111) substrates by pulsed laser deposition at various temperatures from 500 to 800°C. The crystal phases and the lattice strain for the two different substrate orientations have been determined and compared. The films grow epitaxial on both substrates but separation of the spinel and perovskite crystallites, without parasitic phases, is only obtained for growth temperatures of around 600-650°C. The BFO crystallites are out-of-plane expanded on STO(001), whereas they are almost relaxed on (111). In contrast, CFO crystallites grow out-of-plane compressed on both substrates. The asymmetric behavior of the cell parameters of CFO and BFO is discussed on the basis of the role of the epitaxial stress caused by the substrate and the spinel-perovskite interfacial stress. It is concluded that interfacial stress dominates the elastic properties of CFO crystallites and thus it may play a fundamental on the interface magnetoelectric coupling in these nanocomposites.

Properties of non-crystalline EuIG and DyIG obtained from Mossbauer and magnetization data

Non crystalline (nc) EuIG and DyIG have been prepared by dc¿sputtering. Mössbauer data on 57Fe, 151Eu and 161Dy reveal sharp magnetic transitions at 62 K and 70 K for nc EuIG and DyIG, respectively. The 57Fe hyperfine (hf) spectra consist of three superpositioned patterns for Fe3+ in tetrahedral and octahedral and for Fe2+ in tetrahedral oxygen coordination. The saturation hf fields at 4.2 K are reduced compared to the values of the corresponding crystalline materials. The induced hf field at 151Eu is only 1/8 of that for crystalline EuIG

From demagnetizing to magnetizing interactions in CoFe-AgCu granular films

CoFe-AgCu granular films of compositions ranging from 0.17-0.44 ferromagnetic atomic concentration were prepared by rf sputtering. The microstructure and the transport and magnetic properties suggested that this family of samples can be classified into two groups with a crossover concentration at about 32 at. %. The experimental results for samples Co34Fe8Ag54Cu4 and Co18Fe8Ag70Cu4, which are representative of both different behaviors, are discussed. For the as-prepared sample with higher CoFe content, an uncompensated out-of-plane antiferromagneticlike microstructure with dominant demagnetizing interactions was observed. The particle growth through the annealing led to large in-plane ferromagneticlike clusters with dominant magnetizing interactions. The thermal dependence of the remanence-to-saturation ratio of the as-prepared and annealed samples indicated the existence of a high degree of magnetic correlations leading to a very low magnetoresistivity: In none of the cases was a Stoner¿Wohlfarth behavior observed. On the contrary, for the sample with lower CoFe content, the magnetoresistivity change was much higher, and the remanence followed the expected behavior, since magnetic correlations were strongly reduced through dilution.

Magnetic properties of amorphous Fe-Si compositionally modulated thin films

The present paper reports on a magnetometric study of Fe‐Si compositionally modulated thin films. The low‐temperature dependence of the magnetization exhibit Bloch's T3/2 dependence with a minor T5/2 correction term. The spin‐wave stiffness constant deduced from the temperature coefficient depends on the characteristic modulation length and its values are much lower that in glassy alloys.