In vitro penetration of bleaching agents into the pulp chamber

Aim: To investigate pulp chamber penetration of bleaching agents in teeth following restorative procedures. Methodology: Bovine lateral incisors were sectioned 3 mm apical to the cemento-enamel junction and the coronal pulpal tissue was removed. Teeth were divided into six groups (n = 10): G1, G2 and G3 were not submitted to any restorative procedure, while G4, G5 and G6 were submitted to Class V preparations and restored with composite resin. Acetate buffer was placed in the pulp chamber and treatment agents were applied for 60 min at 37°C as follows: G1 and G4, immersion into distilled water; G2 and G5, 10% carbamide peroxide (CP) exposure; G3 and G6, 35% CP bleaching. The buffer solution was removed and transferred to a glass tube where leuco crystal violet and horseradish peroxidase were added, producing a blue solution. The optical density of the blue solution was determined spectrophotometrically at 596 nm. A standard curve made with known amounts of hydrogen peroxide was used to convert the optical density values of the coloured samples into microgram equivalents of hydrogen peroxide. Data were submitted to ANOVA and Tukey's test (5%). Results: Amounts of hydrogen peroxide found in the pulp chamber of G2 and G5 specimens (0.1833 ± 0.2003 μg) were significantly lower (P = 0.001) when compared to G3 and G6 specimens (0.4604 ± 0.3981 μg). Restored teeth held significantly higher (P = 0.001) hydrogen peroxide concentrations in the pulp chamber than intact teeth. Conclusion: Higher concentrations of the bleaching agent produced higher levels of hydrogen peroxide in the pulp chamber, especially in restored teeth.

Surface roughness of packable composite resins polished with various systems

Purpose: The aim of this study was to evaluate the surface roughness of four packable composite resins, SureFil™ (Dentsply, Petrópolis, Rio de Janeiro, Brazil), Prodigy Condensable™ (Kerr Co., Orange, CA, USA), Filtek P60™ (3M do Brasil, São Paulo, Brazil), and ALERT® (Jeneric/Pentron, Inc., Wallingford, CT, USA) and one microhybrid composite resin (Filtek Z250™, 3M do Brasil) after polishing with four finishing systems. Materials and Methods: Twenty specimens were made of each material (5 mm in diameter and 4 mm high) and were analyzed with a profilometer (Perthometer® S8P, Perthen, Mahr, Germany) to measure the mean surface roughness (Ra). The specimens were then divided into four groups according to the polishing system: group 1 - Sof-Lex™ (3M do Brasil), group 2 - Enhance™ (Dentsply), group 3 - Composite Finishing Kit (KG Sorensen, Barueri, São Paulo, Brazil), and group 4 - Jiffy Polisher Cups® (Ultradent Products, Inc., South Jordan, UT, USA). The specimens were polished and then evaluated for Ra, and the data were subjected to analysis of variance, analysis of covariance, and Tukey's test (p = .05). Results: The mean Ra of SureFil polished with Sof-Lex was significantly lower than that of KG points. Prodigy Condensable polished with Enhance showed a significantly less rough surface than when polished with Sof-Lex. Filtek P60 did not exhibit a significant difference with the various polishing systems. For ALERT the lowest mean Ra was obtained with Sof-Lex and the highest mean Ra with KG points. Regarding Filtek Z250, polishing with KG and Jiffy points resulted in a significantly lower mean Ra than when polished with Enhance. Conclusions: Packable composite resins display variable roughness depending on the polishing system used; the Sof-Lex disks and Jiffy points resulted in the best Ra values for the majority of the materials tested.

Treatment options for the occlusal surface of first permanent molars

Restorative dentistry has been increasingly concerned with preservation of the dental structure. For that reason, ultraconservative cavity preparations have been performed with air abrasion systems. The aim of this study was to present treatment options for the occlusal surface of first permanent molars with employment of the conventional method and the air abrasion system for accomplishment of the cavity preparation and a composite occlusal matrix for an accurate reproduction of the tooth surface.

The effect of adhesive and flowable composite on postoperative sensitivity: 2-Week results

Objective: To measure 2-week postoperative sensitivity in Class II composite restorations placed with a self-etching adhesive (Clearfil SE Bond) or a total-etch adhesive (Prime&Bond NT) with or without a flowable composite as cervical increment. Method and materials: Upon approval by the University of Guarulhos Committee on Human Subjects, 100 restorations were inserted in 46 patients who required Class II restorations in their molars and premolars. Enamel and dentin walls were conditioned with a self-etching primer (for Clearfil SE Bond) or etched with 34% phosphoric acid (for Prime&Bond NT). A 1- to 2-mm-thick increment of a flowable composite (Filtek Flow) was used in the proximal box in 50% of the restorations of each adhesive. Preparations were restored with a packable composite (Surefil). The restorations were evaluated preoperatively and 2 weeks postoperatively for sensitivity to cold, air, and masticatory forces using a visual analog scale. Marginal integrity of the accessible margins was also evaluated. Statistical analysis used a mixed linear model with subject as a random effect. Results: Ninety-eight teeth from 44 subjects were observed at 2 weeks. The type of adhesive and use of flowable composite had no significant effects or interaction for any of the four outcomes of interest, ie, change from baseline to 2 weeks in sensitivity and response time for the cold or air stimulus. For the air stimulus, the overall average change from baseline was not significant for either sensitivity or response time. For the cold stimulus, the overall average change from baseline was significant for both sensitivity and response time. No case of sensitivity to masticatory forces was observed. Conclusion: No differences in postoperative sensitivity were observed between a self-etch adhesive and a total-etch adhesive at 2 weeks. The use of flowable composite did not decrease postoperative sensitivity.

Clinical evaluation of proximal contacts of Class II esthetic direct restorations

Objective: This study evaluated the effectiveness of proximal contacts in Class II restorations using two types of matrix bands (steel and polyester) with two different restoration techniques (incremental and with prepolymerized particles). Method and materials: Eighty-eight Class II adjacent restorations using Prodigy resin composite were performed: 44 with the incremental technique (22 with steel matrix bands, 22 with polyester matrix bands) and 44 utilizing prepolymerized resin particles (22 steel matrix, 22 polyester matrix). The restorations were clinically evaluated at baseline and at 6, 12, and 18 months. Proximal contacts obtained immediately after restoration procedure in all restorations were satisfactory. Results: No statistically significant alterations were found in 18 months of evaluation. Conclusion: Regardless of the utilized resin composite, there were no differences in the amount of proximal contact variations with respect to tested techniques and matrices.

The effect of CO 2 laser irradiation on failed implant surfaces

The aim of this investigation was to evaluate the cleaning effect of CO 2 on surface topography and composition of failed dental implant surfaces. Ten failed dental implants were retrieved from nine patients (mean age, 46.33 ± 5.81 years) as a result of early or late failure. The implants were divided into two parts: one side of the implant was irradiated with a CO 2 laser (test side), while the other side did not receive irradiation (control side). The CO 2 laser was operated at 1.2 W in a continuous wave for 40 seconds (40 J energy). The handpiece of the CO 2 laser was kept at a distance of 30 mm from the implant surface, resulting in a spot area of 0.031415 cm 2 (38.20 W/cm 2; 1559 J/cm 2) in scanning mode (cervical-apical). One unused dental implant was used as a negative control for both groups. All implant surfaces were examined by scanning electron mi croscopy (SEM) and energy-dispersive spectrometer x-ray (EDS) for element analysis. SEM showed that the surface of the test sides consisted of different degrees of organic residues, appearing mainly as dark stains similar to those observed on the control sides. None of the test surfaces presented alterations such as crater-like alterations, lava-like layers, or melting compared with the nonirradiated surfaces. Foreign elements such as carbon, oxygen, sodium, calcium, and aluminum were detected on both sides. These results suggest that CO 2 laser irradiation does not modify the implant surface, although the cleaning effect was not satisfactory.

Histomorphometric evaluation of a threaded, sandblasted, acid-etched implant retrieved from a human lower jaw: A case report

The purpose of this study was to histomorphometrically evaluate the bone-to-implant contact and bone area around a titanium implant retrieved from a human lower jaw. A screw-shaped titanium implant (sandblasted and acid-etched surface) was removed from a 68-year-old male after having been in function for 40 months because of a fracture of the abutment screw. Following the implant removal, an undecalcified section was obtained. The histomorphometric analysis showed a rate of 75.40% of bone-to-implant contact and 89.30% of bone area filling within the limits of the implant threads. The surrounding bone healed in a well-organized pattern and could not be differentiated from the anginal alveolus. The histologic evidence showed a high degree of osseointegration in a threaded, sandblasted, and acid-etched implant retrieved from a human lower jaw after functional loading for 40 months. Copyright © 2005 by Lippincott Williams & Wilkins.

Scanning electron microscope analysis of internal adaptation of materials used for pulp protection under composite resin restorations

Purpose: The aim of this study was to evaluate the interfacial microgap with different materials used for pulp protection. The null hypothesis tested was that the combination of calcium hydroxide, resin-modified glass ionomer, and dentin adhesive used as pulp protection in composite restorations would not result in a greater axial gap than that obtained with hybridization only. Materials and Methods: Standardized Class V preparations were performed in buccal and lingual surfaces of 60 caries-free, extracted human third molars. The prepared teeth were randomly assessed in six groups: (1) Single Bond (SB) (3M ESPE, St. Paul, MN, USA); (2) Life (LF) (Kerr Co., Romulus, MI, USA) + SB; (3) LF + Vitrebond (VT) (3M ESPE) + SB; (4) VT + SB; (5) SB + VT; (6) SB + VT + SB. They were restored with microhybrid composite resin Filtek Z250 (3M ESPE), according to the manufacturer's instructions. However, to groups 5 and 6, the dentin bonding adhesive was applied prior to the resin-modified glass ionomer. The specimens were then thermocycled, cross-sectioned through the center of the restoration, fixed, and processed for scanning electron microscopy. The specimens were mounted on stubs and sputter coated. The internal adaptation of the materials to the axial wall was analyzed under SEM with × 1,000 magnification. Results: The data obtained were analyzed with nonparametric tests (Kruskal-Wallis, p ≤ .05). The null hypothesis was rejected. Calcium hydroxide and resin-modified glass ionomer applied alone or in conjunction with each other (p < .001) resulted in statistically wider microgaps than occurred when the dentin was only hybridized prior to the restoration. ©2005 BC Decker Inc.

Interdisciplinary approach to treat dyskeratosis congenita associated with severe aplastic anemia: A case report

This paper reports on a 4-year-old male who had dyskeratosis congenita and who acquired severe aplastic anemia. The patient developed hyperpigmentation of the face, neck and chest region, arms, shoulders and legs. In addition, he had dry skin, deformed fingernails and toenails, sparse hair and eyebrows and hyperkeratosis of the dorsum of the hands and feet. Laboratory and histological analysis revealed severe pancytopenia and dyserythropoiesis of red blood cells, hypocellularity of white blood cells and decreased megakaryocytes with dysplasia. The intraoral examination identified bleeding gums; petechiae of the palate, tongue and cheek mucosa; and an atrophic, smooth and shining dorsal surface of the tongue. There were deep carious lesions in the deciduous mandibular molars and maxillary anterior teeth; as well as mobility of mandibular left canine, which had bone loss. The treatment for oral lesions included diet changes, improved oral hygiene, and extraction of the deciduous teeth destroyed by caries.

Clinical and radiographic evaluation of pulpotomies employing calcium hydroxide and trioxide mineral aggregate

This study utilized clinical and radiographic examinations to compare the effectiveness of calcium hydroxide paste and mineral trioxide aggregate (MTA) for pulpotomies of primary molars in children. Ninety primary molars that showed clinical and radiographic indications for pulpotomy treatment were selected. The pulpotomies were performed in two sessions, using a corticosteroid/ antibiotic solution as therapeutic dressing. The sample was divided into two groups of 45 teeth, in which the pulpal remains were protected with either calcium hydroxide paste (Group 1) or MTA (Group 2). Radiographs were taken immediately and at 3-, 6-, and 12-month follow-up appointments. Three teeth in Group 1 failed after three months, while two cases failed after six months and one more failed at one year. Two failures were found in Group 2 at the 12-month follow-up. These results indicate that both materials may be utilized for pulpotomies in primary teeth.

Surface roughness of glass ionomer cements indicated for atraumatic restorative treatment (ART)

The purpose of this study was to evaluate the surface roughness of four conventional chemically cured glass ionomer cements (Fuji IX, Ketac Molar, Vidrion R and Vitromolar) commonly used in atraumatic restorative treatment (ART) immediately after material preparation. Twenty specimens of each glass ionomer cement were fabricated and surface roughness was measured after material setting. The specimens were further examined under scanning electron microscopy. Data were analyzed statistically by Kruskal-Wallis test and Mann-Whitney test at 5% significance level. Two-by-two comparisons showed statistically significant difference (p<0.05) between all materials, except for Ketac Molar and Vidrion R, which had statically similar results (p>0.05). Regarding their results of surface roughness, the materials can be presented in a crescent order, as follows: Ketac Molar < Vidrion R < Fuji IX < Vitromolar. In conclusion, from the tested glass ionomer cements, Fuji IX, Ketac Molar and Vidrion R presented acceptable surface roughness after setting reaction while Vitromolar showed remarkably higher surface roughness.

Effect of resin luting film thickness on fracture resistance of a ceramic cemented to dentin

Purpose: The aim of this study was to evaluate the fracture resistance of ceramic plates cemented to dentin as a function of the resin cement film thickness. Materials and Methods: Ceramic plates (1 and 2 mm thicknesses) were cemented to bovine dentin using resin composite cement. The film thicknesses used were approximately 100, 200, and 300 μm. Noncemented ceramic plates were used as control. Fracture loads (N) were obtained by compressing a steel indenter in the center of the ceramic plates. ANOVA and Tukey tests (α = 0.05) were used for each ceramic thickness to compare fracture loads among resin cement films used. Results: Mean fracture load (N) for 1-mm ceramic plates were: control - 26 (7); 100 μm - 743 (150); 200 μm - 865 (105); 300 μm - 982 (226). Test groups were significantly different from the control group; there was a statistical difference in fracture load between groups with 100 and 300 μm film thicknesses (p < 0.01). Mean fracture load for 2-mm ceramic plates were: control - 214 (111); 100 μm - 1096 (341); 200 μm - 1067 (226); 300 μm - 1351 (269). Tested groups were also significantly different from the control group (p < 0.01). No statistical difference was shown among different film thicknesses. Conclusions: Unluted specimens presented significantly lower fracture resistance than luted specimens. Higher cement film thickness resulted in increased fracture resistance for the 1-mm ceramic plates. Film thickness did not influence the fracture resistance of 2-mm porcelain plates. Copyright © 2007 by The American College of Prosthodontists.

In vivo preservation of the hybrid layer by chlorhexidine

Host-derived proteases have been reported to degrade the collagen matrix of incompletely-resin-infiltrated dentin. This study tested the hypothesis that interfacial degradation of resin-dentin bonds may be prevented or delayed by the application of chlorhexidine (CHX), a matrix metalloproteinase inhibitor, to dentin after phosphoric acid-etching. Contralateral pairs of resin-bonded Class I restorations in non-carious third molars were kept under intra-oral function for 14 months. Preservation of resin-dentin bonds was assessed by microtensile bond strength tests and TEM examination. In vivo bond strength remained stable in the CHX-treated specimens, while bond strength decreased significantly in control teeth. Resin-infiltrated dentin in CHX-treated specimens exhibited normal structural integrity of the collagen network. Conversely, progressive disintegration of the fibrillar network was identified in control specimens. Auto-degradation of collagen matrices can occur in resin-infiltrated dentin, but may be prevented by the application of a synthetic protease inhibitor, such as chlorhexidine.

In vitro evaluation of marginal leakage in bonded restorations, with mechanical or chemical-mechanical (Carisolv) removal of carious tissue

This study carried out an in vitro evaluation and comparison of the occurrence of marginal leakage in bonded restorations using mechanical or chemical-mechanical (Carisolv) removal of carious tissue. For that purpose, 40 extracted decayed human molars were divided into 4 groups: GI (burs + Prime & Bond NT + TPH), GII (Carisolv + Prime & Bond NT + TPH), GIII (burs + SBMP + Z100) and GIV (Carisolv + SBMP + Z100). After accomplishment of the restorations and thermal cycling, the teeth were exposed to dye, sectioned and qualitatively evaluated. The results demonstrated that the system of removal of carious tissue did not influence the results of microleakage at any of the cavity margins. At dentinal margins, use of the Prime & Bond NT + TPH restorative system allowed the occurrence of less microleakage than the SBMP + Z100 system.

Influence of resin composite insertion technique in preparations with a high C-factor

Objective: To evaluate the marginal microleakage in enamel and dentin/cementum walls in preparations with a high C-factor, using 3 resin composite insertion techniques. The null hypothesis was that there is no difference among the 3 resin composite insertion techniques. Method and Materials: Standardized Class 5 cavities were prepared in the lingual and buccal aspects of 30 caries-free, extracted third molars. The prepared teeth were randomly assigned to 3 groups: (1) oblique incremental placement technique, (2) horizontal incremental placement technique, and (3) bulk insertion (single increment). The preparations were restored with a 1-bottle adhesive (Single Bond, 3M ESPE) and microhybrid resin composite (Z100, 3M ESPE). Specimens were isolated with nail varnish except for a 2-mm-wide rim around the restoration and thermocycled (1,000 thermal cycles, 5°C/55°C; 30-second dwell time). The specimens were immersed in an aqueous solution of 50 wt% silver nitrate for 24 hours, followed by 8 hours in a photo-developing solution and evaluated for microleakage using an ordinal scale of 0 to 4. The microleakage scores obtained from occlusal and gingival walls were analyzed with Wilcoxon and Kruskal-Wallis nonparametric tests. Results: The null hypothesis was accepted. The horizontal incremental placement technique, the oblique incremental technique, and bulk insertion resulted in statistically similar enamel and dentin microleakage scores. Conclusion: Neither the incremental techniques nor the bulk placement technique were capable of eliminating the marginal microleakage in preparations with a high C-factor.