Electric and dielectric behavior of CaCu3Ti4O12-based thin films obtained by soft chemical method

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effects of crystallization conditions on dielectric and ferroelectric properties of PZT thin films

This paper reports studies on dielectric and ferroelectric properties of lead zirconate titanate (PZT) thin films crystallized by conventional thermal annealing (CTA) and rapid thermal annealing (RTA) in air, oxygen and nitrogen atmospheres to better understand, control and optimize these properties. The dielectric constant (epsilon) and dissipation factor (tan delta) values, at a frequency of 100 kHz; for film crystallized in air by CTA process, were 358 and 0.039, respectively. Considering the same frequency for film crystallized in air by RTA, these values were 611 and 0.026, respectively. The different dielectric values were justified by a space-charge or interfacial polarization in films, often characterized as Maxwell-Wagner type. This effect was also responsible to dispersion at frequencies above 1 MHz in film crystallized in air by CTA process and film crystallized by RTA in oxygen atmosphere. The film crystallized by RTA under nitrogen atmosphere presented an evident dispersion at frequencies around 100 Hz, characterized by an increase in both epsilon and tan delta. This dispersion was attributed to conductivity effects. The remanent polarization (P-r) and coercive field (E-c) were also obtained for all films. Films obtained from RTA in air presented higher P-r (17.8 muC cm(-2)) than film crystallized from CTA (7.8 muC cm(-2)). As a function of the crystallization atmospheres, films crystallized by RTA in air and nitrogen presented essentially the same P-r values (around 18 muC cm(-2)) but the P-r (3.9 muC cm(-2)) obtained from film crystallized under oxygen atmosphere was profoundly influenced.

Dielectric investigations in Sr0.75Ba0.25Nb2O6 relaxor ferroelectric thin films

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Mesoscopic structure evidenced by AC dielectric nonlinearities in Sr(0.75)Ba(0.25)Nb(2)O(6) relaxor ferroelectric thin films

The AC electric field and temperature dependences of the dielectric permittivity for strontium barium niobate (Sr(0.75)Ba(0.25)Nb(2)O(6)) relaxor ferroelectric thin films have been investigated. The results indicate the existence of a true mesoscopic structure evidenced by the nonlinear dielectric response of these films, which is similar to those observed for bulk relaxor ferroelectrics. A tendency for a temperature dependent crossover from a linear to a quadratic behaviour of the dielectric nonlinearity was observed, indicating an evolution from paraelectric to glass-like behaviour on cooling the samples towards the freezing temperature transition.

DC Electric Field Dependence of the Dielectric Constant of Pzt Thin Films Prepared by Polymeric Precursor Method

This work reports dielectric measurements performed on Pb(Zr0.53Ti0.47)O3 (PZT) thin films prepared by a polymeric precursor method. The -E curves obtained for the PZT film measured at 100 kHz, under a small ac 0.2 kV/cm signal-test and a dc scan featured a typical butterfly curve. However, the -E curves obtained for PZT film under a dc scan, with a scan rate of 0.003 V/s, shows a pronounced asymmetry. The absence of a symmetric secondary peak in -E curves could be an indication of essentially 180 domain switching.

Investigation of nonlinear dielectric properties in Sr0.75Ba0.25Nb2O6 relaxor ferroelectric thin films

The ac and dc driving fields dependence of the dielectric permittivity for the strontium barium niobate relaxor ferroelectric thin films has been investigated. The nonlinear dielectric properties were obtained by using the measurements of the dielectric permittivity of the material as a function of the ac and dc "bias" electric field amplitude in wide frequency (100 Hz-10 MHz) and temperature (50-450 K) intervals. The results hint the existence of a true mesoscopic dielectric relaxor response in the ferroelectric thin film, which is very similar to those observed in bulk relaxor ferroelectrics. An anomalous behavior of the NL dielectric response was observed when submitted to moderate dc electric fields levels,,indicating a crossover from paraelectric to a glasslike behavior on cooling the sample toward the freezing transition. The obtained results were analyzed within the framework of the models proposed in the current literature.

Dielectric properties of Ca(Zr0.05Ti0.95)O-3 thin films prepared by chemical solution deposition

Ca(Zr0.05Ti0.95)O-3 (CZT) thin films were grown on Pt(1 1 1)/Ti/SiO2/Si(1 0 0) substrates by the soft chemical method. The films were deposited from spin-coating technique and annealed at 928 K for 4 h under oxygen atmosphere. CZT films present orthorhombic structure with a crack free and granular microstructure. Atomic force microscopy and field-emission scanning electron microscopy showed that CZT present grains with about 47 nm and thickness about 450 nm. Dielectric constant and dielectric loss of the films was approximately 210 at 100 kHz and 0.032 at 1 MHz. The Au/CZT/Pt capacitor shows a hysteresis loop with remnant polarization of 2.5 mu C/cm(2), and coercive field of 18 kV/cm, at an applied voltage of 6 V. The leakage current density was about 4.6 x 10(-8) A/cm(2) at 3 V. Dielectric constant-voltage curve is located at zero bias field suggesting the absence of internal electric fields. (c) 2006 Elsevier B.V. All rights reserved.

Temperature dependence of dielectric properties for Ba(Zr0.25Ti0.75)O-3 thin films obtained from the soft chemical method

Ba(Zr0.25Ti0.75)O-3(BZT) thin films prepared by the polymeric precursor method (PPM) were annealed at 500, 600, and 700 degrees C for 4h. All films crystallized in the perovskite structure present a crack-free microstructure. Dielectric properties of the BZT thin films were investigated as a function of frequency and applied voltage. The dielectric constant of the films were 36, 152 and 145 at 1 kHz, while the dielectric loss were 0.08, 0.08, and 0.12 at 1 MHz. (c) 2007 Elsevier B.V. All rights reserved.

Ferroelectric and dielectric properties of Ba0.5Sr0.5(Ti0.80Sn0.20)O-3 thin films grown by the soft chemical method

Polycrystalline Ba0.5Sr0.5(Ti0.80Sn0.20)O-3 (BST:Sn) thin films with a perovskite structure were prepared by the soft chemical method on a platinum-coated silicon substrate from spin-coating technique. The resulting thin films showed a dense structure with uniform grain size distribution. The dielectric constant of the films estimated from C-V curve is around 1134 and can be ascribed to a reduction in the oxygen vacancy concentration. The ferroelectric nature of the film indicated by butterfly-shaped C-V curves and confirmed by the hysteresis curve, showed remnant polarization of 14 mu C/cm(2) and coercive field of 74 kV/cm at frequency of 1 MHz. At the same frequency, the leakage current density at 1.0 V is equal to 1.5 x 10(-7) A/cm(2). This work clearly reveals the highly promising potential of BST:Sn for application in memory devices. (c) 2006 Elsevier B.V. All rights reserved.

Ferroelectric and dielectric behaviour of Bi0.92La0.08FeO3 multiferroic thin films prepared by soft chemistry route

Bi0.92La0.08FeO3 (BLFO) thin films were grown on platine substrates by the soft chemical route. Ferroelectric and dielectric behaviors of BLFO films deposited by spin-coating technique and annealed at 773 K for 2 h in air atmosphere were explained. BLFO thin films obtained presents a rhombohedral structure. The BLFO films present dielectric and ferroelectric behaviors with dielectric permittivity and dielectric loss of approximately 81 and 0.0144 at 1 kHz. The Au/BLFO/Pt capacitor shows a hysteresis loop with remnant polarization of 20.6 mu C/cm(2) and coercive field of 53.88 kV/cm. The polarization switching and the fatigue behavior of the BLFO films were significantly enhanced.

Study of the dielectric and ferroelectric properties of chemically processed BaxSr1-xTiO3 thin films

Polycrystalline BaxSr1-xTiO3 (x = 0.4 and 0.8) thin films with a perovskite structure were prepared by the polymeric precursor method on a platinum-coated silicon substrate. High-quality thin films with uniform composition and thickness were successfully produced by dip-coating and spin-coating techniques. The resulting thin films prepared by dip and spin-coating showed a well-developed dense polycrystalline structure with uniform grain size distribution. The metal-BST-metal structure of the thin films displays good dielectric and ferroelectric properties. The ferroelectric nature to BaxSr1-xTiO3 (x = 0.8) thin film, indicated by butterfly-shaped C-V curves and confirmed by the hysteresis curve, showed 2P(r) = 5.0 muC/cm(2) and E-c = 20 kV/cm. The capacitance-frequency curve reveals that the dielectric constant may reach a value of up to 794 at 1 kHz. on the other hand, the BaxSr1-xTiO3 (x = 0.4) thin films had paraelectric nature and dielectric constant and the dissipation factor at a frequency of 100 kHz were 680 and 0.01, respectively, for film annealed at 700 degreesC. In addition, an examination of the film's I-V curve at room temperature revealed the presence of two conduction regions in the BaxSr1-xTiO3 (x = 0.4 and 0.8) thin films, showing ohmic-like behavior at low voltage and a Schottky-emission or Poole-Frenkel mechanism at high voltage. (C) 2001 Elsevier B.V. B.V. All rights reserved.

Microstructural, dielectric and ferroelectric properties of calcium-modified lead titanate thin films derived by chemical processes

Ferroelectric Pb1-xCaxTiO3 (x = 0.24) thin films were formed on a Pt/Ti/SiO2/Si substrate by the polymeric precursor method using the dip-coating technique for their deposition. Characterization of the films bq X-ray diffraction showed a perovskite single phase with a tetragonal structure after annealing at 700 degreesC. Atomic force microscopy (AFM) analyses showed that the film had a smooth and crack-free surface with low surface roughness. In addition, the PCT thin film had a granular structure with an 80 nm grain size. The thickness of the films observed by the scanning electron microscopy (SEM) is 550 nm and there is a good adhesion between the film and substrate. For the electrical measurements metal-ferroelectric-metal of the type capacitors were obtained, where the thin films showed good dielectric and ferroelectric properties. The dielectric constant and dissipation factor at 1 kHz and measured at room temperature were found to be 457 and 0.03. respectively. The remanent polarization and coercive field for the: deposited films were P-r = 17 muC/cm(2) and E-c = 75 kV/cm, respectively. Moreover. The 550-nm-thick film showed a current density in the order of 10(-8) A/cm(2) at the applied voltage of 2 V. The high values of the thin film's dielectric properties are attributed to its excellent microstructural quality and the chemical homogeneity obtained by the polymeric precursor method. (C) 2001 Elsevier science Ltd. All rights reserved.

Improvement of the dielectric and ferroelectric properties in superlattice structure of Pb(Zr,Ti)O-3 thin films grown by a chemical solution route

Making heterolayered perovskite materials constitutes an approach for the creation of better dielectric and ferroelectric properties. In the experiment reported here, heterolayered PZT40/PZT60 films were grown on Pt/Ti/SiO2/Si (100) by a chemical solution deposition. The dielectric constant of the heterolayered thin film was significantly enhanced compared with that of pure PZT40 and PZT60 thin films. A dielectric constant of 701 at 100 kHz was observed for a stacking periodicity of six layers having a total thickness of 150 nm. The heterolayered film exhibited greater remanent polarization than PZT60 and PZT40 films. The values of remanent polarization were 7.9, 18.5, and 31 muC/cm(2), respectively, for pure PZT60, PZT40, and heterolayered thin films, suggesting that the superior dielectric and ferroelectric properties of the heterolayered thin film resulted from a cooperative interaction between the ferroelectric phases made from alternating tetragonal and rhombohedral phases of PZT, simulating the morphotropic phase boundary of this system. (C) 2004 American Institute of Physics.

High dielectric constant of SrTiO3 thin films prepared by chemical process

SrTiO3 thin films were prepared by the polymeric precursor method and deposited by spin-coating onto Pt/Ti/SiO2/Si(100) substrates. The spin-coated films heat treated at 700 degrees C were crack-free, dense, and homogeneous. Microstructural and morphological evaluations were followed by grazing incident X-ray, scanning electron microscopy and atomic force microscopy. Dielectric studies indicated a dielectric constant of about 475, which is higher than that of ceramic SrTiO3, and a factor dissipation of about 0.050 at 100 kHz. SrTiO3 thin films were found to have paraelectric properties with C-V characteristics. (C) 2000 Kluwer Academic Publishers.

Ferroelectric and dielectric properties of lanthanum-modified bismuth titanate thin films obtained by the polymeric precursor method

Lanthanum-modified bismuth titanate, Bi4-xLaxTi3O12 (BLT), thin films with a La concentration of 0.75 was grown on Pt/Ti/SiO2/Si substrates by using the polymeric precursor solution and spin-coating method. The scanning electron microscopy (SEM) showed rounded grains, which is not typical for these system. The BLT films showed well-saturated polarization-electric field curve which 2P(r) = 41.4 muC/cm(2) and V-c = 0.99 V. The capacitance dependence on the voltage is strongly nonlinear, confirming the ferroelectric properties of the film resulting from the domains switching. These properties make BLT a promising material for FERAM applications.