Effect of bleaching agents containing fluoride or calcium on enamel microhardness, roughness and permeability

Aim: To evaluate the effect of different in-office bleaching agents on the permeability, roughness and surface microhardness of human enamel. Methods: For evaluation of roughness and microhardness, 40 hemi-faces of 20 premolars were subjected to initial roughness (Ra parameter) and microhardness (VHN) measurements. Thirty-two premolar’s crowns were used for permeability test. Then, all specimens were randomly divided into four groups: C - without bleaching (control), HP35 - bleaching with 35% hydrogen peroxide (HP), HPF38 - 38% HP+fluoride, HPC35 - 35% HP+calcium. Final roughness (FR) and microhardness (FM) measurements were evaluated. For permeability, the 32 crowns were immersed in 1% sodium hypochlorite (20 min) and silver nitrate solutions (2 h) and subjected to developing solution under fluorescent light (16 h). Three sections from the crowns were analyzed in light microscope (100x) to evaluate the scores of permeability: Score 0 - no tracer agent penetration; Score 1 - less than half the thickness of enamel penetration; Score 2 - tracer agent reaching half the enamel thickness; Score 3 - entire enamel depth penetration, without reaching dentin and Score 4 - tracer agent reaching dentin. For roughness and microhardness evaluation were used one-way ANOVA and Dunnet post-test for independent samples, and t test for paired samples. For permeability, the data were analyzed by Kruskal Wallis and Dunn tests. Results: A significantly higher permeability and surface roughness were observed in groups HP35, HPF38 and HPC35 compared to the C group, as well as decreased microhardness (p<0.05). Conclusions: All bleaching agents increased permeability and surface roughness, and decreased microhardness of human enamel; thus, the addition of fluoride or calcium was not beneficial.

The Cratylia Mollis Seed Lectin Induces Membrane Permeability Transition In Isolated Rat Liver Mitochondria And A Cyclosporine A-insensitive Permeability Transition In Trypanosoma Cruzi Mitochondria.

Previous results provided evidence that Cratylia mollis seed lectin (Cramoll 1,4) promotes Trypanosoma cruzi epimastigotes death by necrosis via a mechanism involving plasma membrane permeabilization to Ca(2+) and mitochondrial dysfunction due to matrix Ca(2+) overload. In order to investigate the mechanism of Ca(2+) -induced mitochondrial impairment, experiments were performed analyzing the effects of this lectin on T. cruzi mitochondrial fraction and in isolated rat liver mitochondria (RLM), as a control. Confocal microscopy of T. cruzi whole cell revealed that Cramoll 1,4 binding to the plasma membrane glycoconjugates is followed by its internalization and binding to the mitochondrion. Electrical membrane potential (∆Ψm ) of T. cruzi mitochondrial fraction suspended in a reaction medium containing 10 μM Ca(2+) was significantly decreased by 50 μg/ml Cramoll 1,4 via a mechanism insensitive to cyclosporine A (CsA, membrane permeability transition (MPT) inhibitor), but sensitive to catalase or 125 mM glucose. In RLM suspended in a medium containing 10 μM Ca(2+) this lectin, at 50 μg/ml, induced increase in the rate of hydrogen peroxide release, mitochondrial swelling, and ∆Ψm disruption. All these mitochondrial alterations were sensitive to CsA, catalase, and EGTA. These results indicate that Cramoll 1, 4 leads to inner mitochondrial membrane permeabilization through Ca(2+) dependent mechanisms in both mitochondria. The sensitivity to CsA in RLM characterizes this lectin as a MPT inducer and the lack of CsA effect identifies a CsA-insensitive MPT in T. cruzi mitochondria.

Oxidative Stress And Susceptibility To Mitochondrial Permeability Transition Precedes The Onset Of Diabetes In Autoimmune Non-obese Diabetic Mice.

Beta cell destruction in type 1 diabetes (TID) is associated with cellular oxidative stress and mitochondrial pathway of cell death. The aim of this study was to determine whether oxidative stress and mitochondrial dysfunction are present in T1D model (non-obese diabetic mouse, NOD) and if they are related to the stages of disease development. NOD mice were studied at three stages: non-diabetic, pre-diabetic, and diabetic and compared with age-matched Balb/c mice. Mitochondria respiration rates measured at phosphorylating and resting states in liver and soleus biopsies and in isolated liver mitochondria were similar in NOD and Balb/c mice at the three disease stages. However, NOD liver mitochondria were more susceptible to calcium-induced mitochondrial permeability transition as determined by cyclosporine-A-sensitive swelling and by decreased calcium retention capacity in all three stages of diabetes development. Mitochondria H2O2 production rate was higher in non-diabetic, but unaltered in pre-diabetic and diabetic NOD mice. The global cell reactive oxygen species (ROS), but not specific mitochondria ROS production, was significantly increased in NOD lymphomononuclear and stem cells in all disease stages. In addition, marked elevated rates of 2',7'-dichlorodihydrofluorescein (H2DCF) oxidation were observed in pancreatic islets from non-diabetic NOD mice. Using matrix-assisted laser desorption/ionization (MALDI) mass spectrometry (MS) and lipidomic approach, we identified oxidized lipid markers in NOD liver mitochondria for each disease stage, most of them being derivatives of diacylglycerols and phospholipids. These results suggest that the cellular oxidative stress precedes the establishment of diabetes and may be the cause of mitochondrial dysfunction that is involved in beta cell death.

Vascular Endothelial Growth Factor Increases During Blood-brain Barrier-enhanced Permeability Caused By Phoneutria Nigriventer Spider Venom.

Phoneutria nigriventer spider accidental envenomation provokes neurotoxic manifestations, which when critical, results in epileptic-like episodes. In rats, P. nigriventer venom (PNV) causes blood-brain barrier breakdown (BBBb). The PNV-induced excitotoxicity results from disturbances on Na(+), K(+) and Ca(2+) channels and glutamate handling. The vascular endothelial growth factor (VEGF), beyond its angiogenic effect, also, interferes on synaptic physiology by affecting the same ion channels and protects neurons from excitotoxicity. However, it is unknown whether VEGF expression is altered following PNV envenomation. We found that adult and neonates rats injected with PNV showed immediate neurotoxic manifestations which paralleled with endothelial occludin, β-catenin, and laminin downregulation indicative of BBBb. In neonate rats, VEGF, VEGF mRNA, and Flt-1 receptors, glutamate decarboxylase, and calbindin-D28k increased in Purkinje neurons, while, in adult rats, the BBBb paralleled with VEGF mRNA, Flk-1, and calbindin-D28k increases and Flt-1 decreases. Statistically, the variable age had a role in such differences, which might be due to age-related unequal maturation of blood-brain barrier (BBB) and thus differential cross-signaling among components of the glial neurovascular unit. The concurrent increases in the VEGF/Flt-1/Flk-1 system in the cerebellar neuron cells and the BBBb following PNV exposure might imply a cytokine modulation of neuronal excitability consequent to homeostatic perturbations induced by ion channels-acting PNV neuropeptides. Whether such modulation represents neuroprotection needs further investigation.

Microtensile Bond Strength Of Methacrylate And Silorane Resins To Enamel And Dentin.

The aim of this study was to evaluate the microtensile bond strength (µTBS) of two substrates (enamel and dentin) considering two study factors: type of composite resin [methacrylate-based (Filtek Supreme) or silorane-based (Filtek LS)] and aging time (24 h or 3 months). Twenty human molars were selected and divided into 2 groups (n=10) considering two dental substrates, enamel or dentin. The enamel and dentin of each tooth was divided into two halves separated by a glass plate. Each tooth was restored using both tested composite resins following the manufacturer's instructions. The samples were sectioned, producing 4 sticks for each composite resin. Half of them were tested after 24 h and half after 3 months. µTBS testing was carried out at 0.05 mm/s. Data were analyzed by three-way ANOVA and Tukey's HSD tests at α=0.05. Significant differences between composite resins and substrates were found (p<0.05), but no statistically significant difference was found for aging time and interactions among study factors. The methacrylate-based resin showed higher µTBS than the silorane-based resin. The µTBS for enamel was significantly higher than for dentin, irrespective of the composite resin and storage time. Three months of storage was not sufficient time to cause degradation of the bonding interaction of either of the composite resins to enamel and dentin.

Radiotherapy Does Not Impair Dentin Adhesive Properties In Head And Neck Cancer Patients.

This study evaluated the influence of radiotherapy on the dentin bond strength of teeth extracted from patients who had undergone head and neck radiotherapy. A total of 36 samples were divided into two experimental groups: group I (control group, n = 18) and group II (in vivo irradiated group, n = 18). Groups I and II were further separated into three subgroups (six specimens per subgroup), which were further assigned to the three adhesive system protocols employed: Single Bond 2 (SB) (3M ESPE), Easy Bond (EB) (3M ESPE) and Clearfil SE Bond (CSE) (Kuraray). The adhesive systems were applied to the prepared surface according to the manufacturers' instructions and restored using composite resin (Filtek Supreme, 3M ESPE). After 24 h in deionised water (37(o)C), teeth were horizontally and vertically cut to obtain beam specimens with a cross-section area of 0.8 ± 1.0 mm(2). Specimens were tested in tension using a universal testing machine at a cross-speed of 0.5 mm/min. Fracture patterns were observed under SEM. Data was analysed by two-way analysis of variance (p ≤ 0.05). No statistically significant difference was found between the irradiated (R/SB = 44.66 ± 10.12 MPa; R/EB = 41.48 ± 12.71 MPa; and R/CSE = 46.01 ± 6.98 MPa) and control group (C/SB = 39.12 ± 9.51 MPa; C/EB = 42.40 ± 6.66 MPa; and C/CSE = 36.58 ± 7.06 MPa) for any of the adhesive systems. All groups presented a predominance of mixed fracture modes. Head and neck radiotherapy did not affect dentin bond strength for the adhesive materials tested in this study.

Dentin Bond Strength Of A Fluoride-releasing Adhesive System Submitted To Ph-cycling.

To evaluate the microtensile bond strength (µTBS) of a fluoride-containing adhesive system submitted to a pH-cycling and storage time regimen for primary outcomes. As secondary outcomes the fluoride released amount was evaluated. Twelve dentin surfaces from sound third molar were divided into 2 groups according to adhesive systems: Clearfil SE Protect (PB) and Clearfil SE Bond (SE). Sticks obtained (1.0 mm2) from teeth were randomly divided into 3 subgroups according to storage regimen model: immediate (24h); 5-month deionized water (W); and pH-cycling model (C). All sticks were tested for µTBS in a universal testing machine. Fluoride concentration was obtained from 1-4 days and 30-day in W and 1-4 days in demineralization (DE)/remineralization (RE) solutions from C, using a fluoride-specific electrode. µTBS and fluoride released data were, respectively, submitted to ANOVA in a split plot design and Tukey, and Friedman' tests (a=0.05). There was no significant interaction between adhesive system and storage regimen for µTBS. W showed the lowest µTBS values. There was no significant difference between 24 h and C models for µTBS. There was no significant difference between adhesive systems. Failure mode was predominantly cohesive within composite for the 24 h and W, for the C group it was mixed for SE and cohesive within composite for PB adhesive system. Fluoride concentrations in the DE/RE solutions were less than 0.03125 ppm and not detected in W. In conclusion, the fluoride-containing adhesive system performed similarly to the regular one. Hydrolytic degradation is the main problem with both adhesive systems, regardless of fluoride contents.

Spectrophotometric Evaluation Of Dental Bleaching Under Orthodontic Bracket In Enamel And Dentin.

Aware of the diffusion capacity of bleaching in the dental tissues, many orthodontists are subjecting their patients to dental bleaching during orthodontic treatment for esthetic purposes or to anticipate the exchange of esthetic restorations after the orthodontic treatment. For this purpose specific products have been developed in pre-loaded whitening trays designed to fit over and around brackets and wires, with clinical efficacy proven. The objective of this study was to evaluate, through spectrophotometric reflectance, the effectiveness of dental bleaching under orthodontic bracket. Thirty-two bovine incisors crown blocks of 8 mm x 8 mm height lengths were used. Staining of tooth blocks with black tea was performed for six days. They were distributed randomly into 4 groups (1-home bleaching with bracket, 2- home bleaching without bracket, 3- office bleaching with bracket, 4 office bleaching without bracket). The color evaluation was performed (CIE L * a * b *) using color reflectance spectrophotometer. Metal brackets were bonded in groups 1 and 3. The groups 1 and 2 samples were subjected to the carbamide peroxide at 15%, 4 hours daily for 21 days. Groups 3 and 4 were subjected to 3 in-office bleaching treatment sessions, hydrogen peroxide 38%. After removal of the brackets, the second color evaluation was performed in tooth block, difference between the area under the bracket and around it, and after 7 days to verified color stability. Data analysis was performed using the paired t-test and two-way variance analysis and Tukey's. The home bleaching technique proved to be more effective compared to the office bleaching. There was a significant difference between the margin and center color values of the specimens that were subjected to bracket bonding. The bracket bond presence affected the effectiveness of both the home and office bleaching treatments. Key words:Tooth bleaching, spectrophotometry, orthodontics.

Shear bond strength of self-etch and total-etch bonding systems at different dentin depths

The purpose of this study was to evaluate the dentin shear bond strength of four adhesive systems (Adper Single Bond 2, Adper Prompt L-Pop, Magic Bond DE and Self Etch Bond) in regards to buccal and lingual surfaces and dentin depth. Forty extracted third molars had roots removed and crowns bisected in the mesiodistal direction. The buccal and lingual surfaces were fixed in a PVC/acrylic resin ring and were divided into buccal and lingual groups assigned to each selected adhesive. The same specimens prepared for the evaluation of superficial dentin shear resistance were used to evaluate the different depths of dentin. The specimens were identified and abraded at depths of 0.5, 1.0, 1.5 and 2.0 mm. Each depth was evaluated by ISO TR 11405 using an EMIC-2000 machine regulated at 0.5 mm/min with a 200 Kgf load cell. We performed statistical analyses on the results (ANOVA, Tukey and Scheffé tests). Data revealed statistical differences (p < 0.01) in the adhesive and depth variation as well as adhesive/depth interactions. The Adper Single Bond 2 demonstrated the highest mean values of shear bond strength. The Prompt L-Pop product, a self-etching adhesive, revealed higher mean values compared with Magic Bond DE and Self Etch Bond adhesives, a total and self-etching adhesive respectively. It may be concluded that the shear bond strength of dentin is dependent on material (adhesive system), substrate depth and adhesive/depth interaction.

A novel bioactive glass-ceramic for treating dentin hypersensitivity

Dentin hypersensitivity (DH) is a painful response to stimulus applied to the open dentinal tubules of a vital tooth. It's a common oral condition, however, without an ideal treatment available yet. This work evaluated in vitro the effect of micron-sized particles from a novel bioactive glass-ceramic (Biosilicate) in occluding open dentinal tubules. A dentin disc model was employed to observe comparatively, using scanning electron microscopy (SEM), dentinal tubule occlusion by different products and deposition of hydroxyl carbonate apatite (HCA) on dentin surface by Biosilicate, after a single application: G1 - Dentifrice with potassium nitrate and fluoride; G2 - Two-step calcium phosphate precipitation treatment; G3 - Water-free gel containing Biosilicate particles (1%); G4 - Biosilicate particles mixed with distilled water in a 1:10 ratio; all of them after 1, 12 and 24 hours of immersion in artificial saliva. Fourier transform infrared spectroscopy (FTIR) was performed to detect HCA formation on dentin discs filled with Biosilicate after 2 minutes, 30 minutes and 12 hours of immersion in artificial saliva. SEM showed a layer of HCA formed on dentin surface after 24 hours by G4. G1, G2 and G3 promoted not total occlusion of open dentinal tubules after 24 hours. FTIR showed HCA precipitation on the dentin surface induced by Biosilicate after 30 minutes. The micron-sized particles from the bioactive glass-ceramic thus were able to induce HCA deposition in open dentinal tubules in vitro. This finding suggests that Biosilicate may provide a new option for treating DH.

Viability of using enamel and dentin from bovine origin as a substitute for human counterparts in an intraoral erosion model

This study ascertained whether under dental erosion models that closely mimics the real-life situation enamel and root dentin from bovine origin would be reliable substitutes for human counterparts. Through a 2x2 crossover design, in a first trial, 14 volunteers wore a palatal device containing slabs of bovine and human enamel. Half of the participants ingested (4x daily, for 10 days) orange juice first, crossing over to mineral water, while the remainder received the reverse sequence. In a second trial, volunteers wore devices with slabs of bovine and human root dentin. Except for the duration of each intraoral phase, which lasted 2 rather 10 days, the experiment with root dentin run exactly as for enamel. Dental substrates were analyzed for surface microhardness. Two-way ANOVAs (α=0.05) indicated no difference between the microhardness values recorded for human and bovine enamel (p=0.1350), but bovine root dentin had lower microhardness compared to its human counterpart (p=0.0432). While bovine enamel can reliably substitute its human counterpart in in situ dental erosion models, bovine root dentin does not seem to be a viable alternative to the corresponding human tissue.

Adhesion of Epiphany and AH Plus sealers to human root dentin treated with different solutions

This study evaluated comparatively the adhesion of Epiphany and AH Plus endodontic sealers to human root dentin treated with 1% NaOCl and 1% NaOCl+17% EDTA, using the push-out test. Sixty root cylinders obtained from maxillary canines had the canals prepared and were randomly assigned to 3 groups (n=20), according to root dentin treatment: GI - distilled water (control), GII - 1% NaOCl and GIII - 1% NaOCl+17% EDTA. Each group was divided into 2 subgroups (n=10) filled with either Epiphany or AH Plus. Bond strength push-out test data (kN) were obtained and analyzed statistically by ANOVA and Tukey's post-hoc test. There was statistically significant difference between sealers (AH Plus: 0.78 ± 0.13; Epiphany: 0.61 ± 0.19; p<0.01) and among root dentin treatments (distilled water: 0.58 ± 0.19; 1% NaOCl: 0.71 ± 0.12; 1% NaOCl+17% EDTA: 0.80 ± 0.17; p<0.05). In conclusion, AH Plus sealer presented greater adhesion to dentin than Epiphany, regardless of the treatment of root canal walls.

Adhesion of an endodontic sealer to dentin and gutta-percha: shear and push-out bond strength measurements and SEM analysis

The use of an adequate method for evaluation of the adhesion of root canal filling materials provides more reliable results to allow comparison of the materials and substantiate their clinical choice. The aims of this study were to compare the shear bond strength (SBS) test and push-out test for evaluation of the adhesion of an epoxy-based endodontic sealer (AH Plus) to dentin and gutta-percha, and to assess the failure modes on the debonded surfaces by means of scanning electron microscopy (SEM). Three groups were established (n=7): in group 1, root cylinders obtained from human canines were embedded in acrylic resin and had their canals prepared and filled with sealer; in group 2, longitudinal sections of dentin cylinders were embedded in resin with the canal surface smoothed and turned upwards; in group 3, gutta-percha cylinders were embedded in resin. Polyethylene tubes filled with sealer were positioned on the polished surface of the specimens (groups 2 and 3). The push-out test (group 1) and the SBS test (groups 2 and 3) were performed in an Instron universal testing machine running at crosshead speed of 1 mm/min. Means (±SD) in MPa were: G1 (8.8±1.13), G2 (5.9±1.05) and G3 (3.8±0.55). Statistical analysis by ANOVA and Student's t-test (a=0.05) revealed statistically significant differences (p<0.01) among the groups. SEM analysis showed a predominance of adhesive and mixed failures of AH Plus sealer. The tested surface affected significantly the results with the sealer reaching higher bond strength to dentin than to gutta-percha with the SBS test. The comparison of the employed methodologies showed that the SBS test produced significantly lower bond strength values than the push-out test, was skilful in determining the adhesion of AH Plus sealer to dentin and gutta-percha, and required specimens that could be easily prepared for SEM, presenting as a viable alternative for further experiments.

Clinical evaluation of desensitizing treatments for cervical dentin hypersensitivity

The aim of this study was to compare different treatments for dentin hypersensitivity in a 6-month follow-up. One hundred and one teeth exhibiting non carious cervical lesions were selected. The assessment method used to quantify sensitivity was the cold air syringe, recorded by the visual analogue scale (VAS), prior to treatment (baseline), immediately after topical treatment, after 1 week, 1, 3 and 6 months. Teeth were randomly assigned to five groups (n = 20): G1: Gluma Desensitizer (GD); G2: Seal&Protect (SP); G3: Oxa-gel (OG); G4: Fluoride (F); G5: Low intensity laser-LILT (660 nm/3.8 J/cm²/15 mW). Analysis was based on the non-parametric Kruskal-Wallis test that demonstrated statistical differences immediately after the treatment (p = 0.0165). To observe the individual effects of each treatment, data was submitted to Friedman test. It was observed that GD and SP showed immediate effect after application. Reduction in the pain level throughout the six-month follow-up was also observed. In contrast, LILT presented a gradual reduction of hypersensitivity. OG and F showed effects as of the first and third month respectively. It can be concluded that, after the 6-month clinical evaluation, all therapies showed lower VAS sensitivity values compared with baseline, independently of their different modes of action.

Micromorphological and hardness analyses of human and bovine sclerotic dentin: a comparative study

The purpose of this study was to test the hypothesis that both human and bovine sclerotic dentin have similar hardness properties, in addition to similar micromorphological characteristics. Sixteen teeth (8 human and 8 bovine) exhibiting exposed dentin in the incisal edge and showing characteristics typical of sclerosis were used. Vickers surface microhardness testing was conducted. Three areas of the dentin surface of each specimen were selected. All teeth were processed for scanning electron microscopy in order to estimate the amount (in percentage) of solid dentin on the sclerotic dentin surface. The data were compared by Student's t test (α = 0.05). The micromorphological and microhardness data were compared by Pearson's linear correlation test (α = 0.05). The mean percentages of solid dentin of human and bovine sclerotic dentin were similar (human 90.71 ± 0.83 and bovine 89.08 ± 0.81, p = 0.18). The mean microhardness value (VHN) of human sclerotic dentin was significantly higher than that of bovine sclerotic dentin (human 45.26 ± 2.92 and bovine 29.93 ± 3.83, p = 0.006). No correlation was found between the microhardness values and the amount of solid dentin in the sclerotic dentin, irrespective of the species considered (human R² = 0.0240, p = 0.714; bovine R² = 0.0017, p = 0.923; and combined R² = 0.038, p = 0.46). We concluded that although both bovine and human sclerotic dentin present a similar amount of solid tissue, human sclerotic dentin presents higher microhardness than bovine sclerotic dentin.