Adição de vermiculita expandida mícron em pastas de baixa densidade para cimentação de poços de petróleo

The northeastern region of Brazil has a large number of wells producing oil using a method of secondary recovery steam injection, since the oil produced in this region is essentially viscous. This recovery method puts the cement / coating on thermal cycling, due to the difference in coefficient of thermal expansion between cement and metal coating causes the appearance of cracks at this interface, allowing the passage of the annular fluid, which is associated with serious risk socioeconomic and environmental. In view of these cracks, a correction operation is required, resulting in more costs and temporary halt of production of the well. Alternatively, the oil industry has developed technology for adding new materials in cement pastes, oil well, providing high ductility and low density in order to withstand the thermo-mechanical loads generated by the injection of water vapor. In this context, vermiculite, a clay mineral found in abundance in Brazil has been applied in its expanded form in the construction industry for the manufacture of lightweight concrete with excellent insulation and noise due to its high melting point and the presence of air in their layers lamellar. Therefore, the vermiculite is used for the purpose of providing low-density cement paste and withstand high temperatures caused by steam injection. Thus, the present study compared the default folder containing cement and water with the folders with 6%, 8% and 10% vermiculite micron conducting tests of free water, rheology and compressive strength where it obtained the concentration of 8 % with the best results. Subsequently, the selected concentration, was compared with the results recommended by the API standard tests of filtered and stability. And finally, analyzed the results from tests of specific gravity and time of thickening. Before the study we were able to make a folder with a low density that can be used in cementing oil well in order to withstand the thermo-mechanical loads generated by steam injection

Estudos de Durabilidade Frente ao Ataque Ácido de Compósitos Portland-Polímero para Cimentação de Poços de Petróleo

Portland-polymers composites are promising candidates to be used as cementing material in Northeastern oil wells of Brazil containing heavy oils submitted to steam injection. In this way, it is necessary to evaluate its degradation in the commonly acidizind agents. In addition, to identify how aggressive are the different hostile environments it is an important contribution on the decision of the acidic systems to be used in. It was investigated the performance of the Portland-polymer composites using powdered polyurethane, aqueous polyurethane, rubber tire residues and a biopolymer, those were reinforced with polished carbon steel SAE 1045 to make the electrochemical measurements. HCl 15,0 %, HCl 6,0 % + HF 1,5 % (soft mud acid), HCl 12,0 % + HF 3,0 % (regular mud acid) and HAc 10 % + HF 1,5 % were used as degrading environment and electrolytes. The more aggressive acid solution to the plain Portland hardened cement paste was the regular mud acid, that showed loss of weight around 23.0 %, followed by the soft mud acid, the showed 11.0 %, 15.0 % HCl with 7,0 % and, at last the 10.0 % HAc plus HF 1.5 % with just 1.0 %. The powdered polyurethane-composite and the aqueous polyurethane one showed larger durability, with reduction around 87.0 % on the loss of weight in regular mud acid. The acid attack is superficial and it occurs as an action layer, where the degraded layer is responsible for the decrease on the kinetic of the degrading process. This behavior can be seen mainly on the Portland- aqueous polyurethane composite, because the degraded layer is impregnated with chemically modified polymer. The fact of the acid attack does not have influence on the compressive strength or fratography of the samples, in a general way, confirms that theory. The mechanism of the efficiency of the Portland-polymers composites subjected to acid attack is due to decreased porosity and permeability related with the plain Portland paste, minor quantity of Ca+2, element preferentially leached to the acidic solution, wave effect and to substitute part of the degrading bulk for the polymeric one. The electrolyte HAc 10 % + HF 1,5 % was the least aggressive one to the external corrosion of the casing, showing open circuit potentials around +250 mV compared to -130 mV to the simulated pore solution to the first 24 hours immersion. This behavior has been performed for two months at least. Similar corrosion rates were showed between both of the electrolytes, around 0.01 μA.cm-2. Total impedance values, insipient arcs and big polarization resistance capacitive arcs on the Nyquist plots, indicating passivity process, confirm its efficiency. In this way, Portlandpolymers composites are possible solutions to be succeed applied to oilwell cementing concomitant submitted to steam injection and acidizing operation and the HAc 10,0 % + HF 1,5 % is the less aggressive solution to the external corrosion of the casing

Desenvolvimento de um sistema misto de pasta à base de geopolímero e cimento portland para correção de perda de circulação

The materials engineering includes processes and products involving several areas of engineering, allowing them to prepare materials that fulfill the needs of various new products. In this case, this work aims to study a system composed of cement paste and geopolymers, which can contribute to solving an engineering problem that directly involves the exploitation of oil wells subject to loss of circulation. To correct it, has been already proposed the use of granular materials, fibers, reducing the drilling fluid or cement paste density and even surface and downhole mixed systems. In this work, we proposed the development of a slurry mixed system, the first was a cement-based slurry and the second a geopolymer-based slurry. The cement-based slurry was formulated with low density and extenders, 12.0 ppg (1.438 g/cm ³), showing great thixotropic characteristics. It was added nano silica at concentrations of 0.5, 1.0 and 1.5 gps (66.88, 133.76 and 200.64 L/m3) and CaCl2 at concentrations of 0.5, 1, 0 and 1.5%. The second system is a geopolymer-based paste formulated from molar ratios of 3.5 (nSiO2/nAl2O3), 0.27 (nK2O/nSiO2), 1.07 (nK2O/nAl2O3) and 13.99 (nH2O/nK2O). Finally, we performed a mixture of these two systems, for their application for correction of circulation lost. To characterize the raw materials, XRD, XRF, FTIR analysis and titration were performed. The both systems were characterized in tests based on API RP10B. Compressive strength tests were conducted after curing for 24 hours, 7 and 28 days at 58 °C on the cement-based system and the geopolymer-based system. From the mixtures have been performed mixability tests and micro structural characterizations (XRD, SEM and TG). The results showed that the nano silica, when combined with CaCl2 modified the rheological properties of the cement slurry and from the concentration of 1.5 gpc (200.64 L / m³) it was possible to obtain stable systems. The system mixture caused a change in the microstructure of the material by favoring the rate of geopolymer formation to hinder the C3S phase hydration, thus, the production of CSH phases and Portlandite were harmed. Through the mixability tests it can be concluded that the system, due to reduced setting time of the mixture, can be applied to plug lost circulation zones when mixed downhole

Influência da vermiculita expandida na formulação de pastas leves para evitar a migração de gás em cimentação de poços petrolíferos

The gas migration during the cementing of wells is one of the main problems of oil wells engineering. Its occurrence can cause severe problems since shortly to loss of control of the well after cementation. Recently, 20/04/2010 In an accident of major proportions in the Gulf of Mexico, among other factors, faulty cementing operation provided the gas migration, causing the accident, in which 11 people died and 17 were injured occurred. Besides the serious consequences that can be caused by gas migration, remediation of the problem, which is made by injecting cement in damaged areas, usually involves additional costs and is not always effective. Therefore, preventing gas migration to be preferred. Some methods are used to prevent the migration of the pressurized gas as the annular space, application of pressure pulses, reducing the height of the cement column compressible cement pastes of low permeability, pastes and to control free filtered water, and binders of thixotropic cement expandable and flexible. Thus, the cement pastes used to prevent gas migration must meet the maximum these methods. Thus, this study aimed to formulate a cement paste to prevent gas migration, using the expanded vermiculite, and evaluate the behavior of the folder trials necessary for use in oil wells. Free water content, rheological properties, compressive strength, loss of liquid phase sedimentation of solids, specific weight, thickening time and gas migration: The following tests were performed. The results show that meets the specifications paste formulated for use in oil wells and the use of expanded vermiculite contribute to the absorption of free water, thixotropy and low density. The absorption of free water is proven to result in zero percentage test free water content, thixotropy is observed with the high value of the initial gel strength (Gi) in testing rheological properties and low density is proven in test weight specific

Influência da adição de gres porcelanato no comportamento mecânico e microestrutural em pastas de cimento portland para cimentação de poços de petróleo

Cementation operation consists in an extremely important work for the phases of perforation and completion of oil wells, causing a great impact on the well productivity. Several problems can occur with the cement during the primary cementation, as well as throughout the productive period. The corrective operations are frequent, but they are expensive and demands production time. Besides the direct cost, prejudices from the interruption of oil and gas production till the implementation of a corrective operation must be also taken into account. The purpose of this work is the development of an alternative cement paste constituted of Portland cement and porcelainized stoneware residue produced by ceramic industry in order to achieve characteristics as low permeability, high tenacity, and high mechanical resistance, capable of supporting various operations as production or oil wells recuperation. Four different concentration measures of hydrated paste were evaluated: a reference paste, and three additional ones with ceramic residue in concentrations of the order of 10%, 20% and 30% in relation to cement dough. High resistance and low permeability were found in high concentration of residues, as well as it was proved the pozolanic reactivity of the residue in relation to Portland cement, which was characterized through x-ray and thermogravimetry assays. It was evident the decrease of calcium hydroxide content, once it was substituted by formation of new hydrated products as it was added ceramic residue

Desenvolvimento de sistemas de aditivos químicos para aplicação em cimentações de poços de petróleo

The primary cementing is an important step in the oilwell drilling process, ensuring the mechanical stability of the well and the hydraulic isolation between casing and formation. For slurries to meet the requirements for application in a certain well, some care in the project should be taken into account to obtain a cement paste with the proper composition. In most cases, it is necessary to add chemicals to the cement to modify its properties, according to the operation conditions and thus obtain slurries that can move inside the jacket providing a good displacement to the interest area. New technologies of preparation and use of chemicals and modernization of technological standards in the construction industry have resulted in the development of new chemical additives for optimizing the properties of building materials. Products such as polycarboxylate superplasticizers provide improved fluidity and cohesion of the cement grains, in addition to improving the dispersion with respect to slurries without additives. This study aimed at adapting chemical additives used in civil construction to be used use in oilwell cement slurries systems, using Portland cement CPP-Special Class as the hydraulic binder. The chemical additives classified as defoamer, dispersant, fluid loss controller and retarder were characterized by infrared absorption spectroscopy, thermogravimetric analyses and technological tests set by the API (American Petroleum Institute). These additives showed satisfactory results for its application in cement slurries systems for oil wells. The silicone-based defoamer promoted the reduction of air bubbles incorporated during the stirring of the slurries. The dispersant significantly reduced the rheological parameters of the systems studied. The tests performed with the fluid loss controller and the retarder also resulted in suitable properties for application as chemical additives in cement slurries

Desenvolvimento de sistemas de pastas leves para aplicação em cimentação de poços petrolíferos com baixo gradiente de fratura

All around the world, naturally occurring hydrocarbon deposits, consisting of oil and gas contained within rocks called reservoir rocks , generally sandstone or carbonate exists. These deposits are in varying conditions of pressure and depth from a few hundred to several thousand meters. In general, shallow reservoirs have greater tendency to fracture, since they have low fracture gradient, ie fractures are formed even with relatively low hydrostatic columns of fluid. These low fracture gradient areas are particularly common in onshore areas, like the Rio Grande do Norte basin. During a well drilling, one of the most favorable phases for the occurrence of fractures is during cementing, since the cement slurry used can have greater densities than the maximum allowed by the rock structure. Furthermore, in areas which are already naturally fractured, the use of regular cement slurries causes fluid loss into the formation, which may give rise to failures cementations and formation damages. Commercially, there are alternatives to the development of lightweight cement slurries, but these fail either because of their enormous cost, or because the cement properties were not good enough for most general applications, being restricted to each transaction for which the cement paste was made, or both reasons. In this work a statistical design was made to determine the influence of three variables, defined as the calcium chloride concentration, vermiculite concentration and nanosilica concentration in the various properties of the cement. The use of vermiculite, a low density ore present in large amounts in northeastern Brazil, as extensor for cementing slurries, enabled the production of stable cements, with high water/cement ratio, excellent rheological properties and low densities, which were set at 12.5 lb / gal, despite the fact that lower densities could be achieved. It is also seen that the calcium chloride is very useful as gelling and thickening agent, and their use in combination with nanosilica has a great effect on gel strength of the cement. Hydrothermal Stability studies showed that the pastes were stable in these conditions, and mechanical resistance tests showed values of the order of up to 10 MPa

Desenvolvimento de misturas ternárias para remoção de reboco de fluido de perfuração sintético

The construction of wells is one of the most important activities of the oil industry. The drilling process is the set of activities and operations to design, program and perform the opening thereof. During this process, the cuttings are removed by the drilling fluid, or mud, and carted to the surface. This fluid is injected into the drill string and returns to the surface through the annular space between the well walls and the drill string. After the descent of the column casing, the annular space between the casing string and the walls of the borehole is filled with cement so as to secure the spine and prevent any migration of fluids between the various permeable zones traversed by the well behind of the coating. To ensure the good quality of the cementation scrubbers are used mattresses which are pumped ahead of the cement slurry so as to avoid contamination of the drilling fluid paste, or vice versa, and assist in the removal of plaster, formed by drilling fluid of the borehole walls, thus enabling a better cement bond to the well. Within this context, this work aims to evaluate the efficiency of mattresses scrubbers, the basis of ionic and nonionic surfactants, on the removal of nonaqueous drilling fluid, based on n-paraffin in oil wells, and the compatibility between the Mattress relations washer / drilling fluid bed scrubber / cement paste mattress washer / cement slurry / drilling fluid and the drilling fluid / cement slurry using laboratory tests rheology, thickening time and compressive strength. Also technique was performed X-ray diffraction (XRD) for a more detailed analysis of these mixtures with hydrated cement paste. In compatibility tests the conditions of temperature and pressure used in the same laboratory procedure simulating the conditions of oil wells, the well is considered the depth of 800 m. The results showed that the compositions of the mattress washer nonionic, KMS obtained a 100% efficient in removing the non-aqueous drilling fluid, and the best formulation showed good results with respect to compliance testing

Investigação de compósitos cimentícios para preenchimento de juntas da interface e de nichos em ligações de estruturas pré- moldadas

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Compósito de argamassa de cimento reforçada por fibra de sisal com entalhe definidos: caracterização mecânica e mecanismo de falha

Neste trabalho, foi desenvolvido um novo material compósito utilizando-se como matriz a argamassa de cimento reforçado com fibra de sisal a 1% em peso, que foram cortadas manualmente nos comprimentos de 15 mm e 25 mm utilizadas sem tratamento superficial utilizando-se o menor nível possível de processamento tecnológico nas etapas de fabricação. A pesquisa foi direcionada para estudar os mecanismos de falha desse novo material. Os compósitos foram produzidos com moldagem manual utilizando-se vibrador de imersão para melhor adensamento. Foram confeccionados corpos de prova da matriz pura e do compósito com fibra de sisal, com entalhes pré definidos, de 1,7 mm, 3,0 mm e 5,0 mm. As propriedades mecânicas foram avaliadas por ensaio de flexão em três pontos e correlacionadas com o aspecto fractográfico realizados no Microscópio Eletrônico de Varredura. Os resultados mostraram que a presença das fibras de sisal, inseridas na pasta de cimento, provocou restrição à retração plástica da mistura fresca, possivelmente pela elevada capacidade de absorção de água do reforço fibroso, um incremento na resistência mecânica e aumento da tenacidade do compósito em relação a matriz entre as séries de entalhes, diminuindo a tendência de fratura brusca.

Avaliação do comportamento reológico na retração plástica e na fissuração de argamassas de concreto auto-adensável

This paper investigated the influence of the amount of superplasticizer and mineral adding - silica fume and basaltic filer - in plastic shrinkage and cracking of self-compacting concrete (SCC) mortars. Initially analysis was performed of the rheological behavior of cement paste and mortars phases of the compositions of SCC. Then the deformations of mortars were measured by the effect of shrinkage and evaluation of cracking. On plastic shrinkage and cracking, the composition with silica fume showed superior results, independent of wind and superplasticizer content, relative to the composition with addition of basalt filler. However, the composition with silica fume showed superior results only in the tests with imposed ventilation at vertical plastic deformation. The rheological behavior affected directly the plastic shrinkage and cracking at early ages, fact confirmed by the analysis of capillary pressures of mortars tested.

Viscosidade cinemática de pastas cimentícias com incorporadores de ar avaliadas em diferentes temperaturas

A presença de aditivos incorporadores de ar (AIA) em suspensões cimentícias torna esses materiais sensíveis às etapas de processamento e às condições ambientais de preparo das composições. Diversos estudos têm sido reportados em literatura avaliando o efeito de incorporadores de ar nas propriedades de materiais cimentícios, sobretudo no estado endurecido. Porém o efeito da temperatura na incorporação de ar e nas propriedades reológicas dessas composições tem sido menos investigado, sendo este o objetivo do presente trabalho. Para tanto, foram avaliadas as características de pastas cimentícias, compostas por cimentos CPIIF ou CPIIE e dois tipos de AIA, em função da variação da temperatura. O conceito de viscosidade cinemática foi adotado na análise dos resultados para compensar diferenças de inércia das pastas com densidades distintas. Os resultados mostraram que o tipo de cimento, a presença do aditivo e a temperatura influenciaram significativamente na incorporação de ar e nas propriedades reológicas.

Surface layer formation in polymer melts and in solutions

In this work the surface layer formation in polymer melts and in polymer solutions have been investigated with the atomic force microscope (AFM). In polymer melts, the formation of an immobile surface layer results in a steric repulsion, which can be measured by the AFM. From former work it is know, that polydimethyl siloxane (PDMS) forms a stable surface layer for molecular weights above 12 kDa. In the present thesis, polyisoprene (PI) was investigated apart from PDMS, by a)measuring the steric surface interactions and b)measuring the surface slip in hydrodynamic experiments. If a polymer flows over a surface, the flow velocity at the surface is larger then zero. If case of a surface layer formation the flow plane changes to the top of the adsorbed layer and the surface slip is reduced to zero. By measuring the surface slip in hydrodynamic experiments, it is therefore possible to determine the presence of a stable surface layer. The results show no stable repulsion for PI and only a small decrease of the surface slip. This indicates that PI does not form a stable surface layer, but is only adsorbed weakly to the surface. Furthermore for 8 kDa PDMS the timescale of the formation of a surface layer was investigated by changing themaximal force the tip applied to the surface. With a repulsive force present, applying a higher force than 15 nN resulted in a destruction of the surface layer, indicated by attractive forces. Reducing the applied force below 15 nN then resulted in an increase of the repulsion to the former state during one minute, thus indicating that a surface layer can be formed within one minute even under the influence of continuous measurements. As a next step, mixtures of two PDMS homopolymers with different chain lengths have been investigated. The aim was to verify theoretical predictions that shorter chains should predominate at the surface due to their smaller loss in conformational entropy. The measurements where done in dependence of the volume fractions of short and long chain PMDS. The results confirmed the short chain dominance for all mixtures with less then 90 vol.% long chain PDMS. Surface layer formation in solution was investigated for superplasticizers which are industrially used as an additive to cement. They change the surface interaction between the cement grains from attractive to repulsive and the freshlymixed cement paste therefore becomes liquid. The aimin this part of the thesis was, to investigate cement particle interactions in a close to real environment. Therefore calcium silicate hydrate phases have been precipitated onto an AFM tip and onto a calcite crystal and the interaction between these surfaces have beenmeasured with and without addition of superplasticizers. The measurements confirmed the change from attraction to repulsion upon addition of superplasticizers. The repulsive steric interaction increased with the length of the sidechain of the superplasticizer, and the dependence of the range of the steric interactions on the sidechain length indicated that the sidechains are in a coiled conformation.

Integration of computational models and experimental characterization to study internal frost damage in cementitious materials

The objective of this doctoral research is to investigate the internal frost damage due to crystallization pore pressure in porous cement-based materials by developing computational and experimental characterization tools. As an essential component of the U.S. infrastructure system, the durability of concrete has significant impact on maintenance costs. In cold climates, freeze-thaw damage is a major issue affecting the durability of concrete. The deleterious effects of the freeze-thaw cycle depend on the microscale characteristics of concrete such as the pore sizes and the pore distribution, as well as the environmental conditions. Recent theories attribute internal frost damage of concrete is caused by crystallization pore pressure in the cold environment. The pore structures have significant impact on freeze-thaw durability of cement/concrete samples. The scanning electron microscope (SEM) and transmission X-ray microscopy (TXM) techniques were applied to characterize freeze-thaw damage within pore structure. In the microscale pore system, the crystallization pressures at sub-cooling temperatures were calculated using interface energy balance with thermodynamic analysis. The multi-phase Extended Finite Element Modeling (XFEM) and bilinear Cohesive Zone Modeling (CZM) were developed to simulate the internal frost damage of heterogeneous cement-based material samples. The fracture simulation with these two techniques were validated by comparing the predicted fracture behavior with the captured damage from compact tension (CT) and single-edge notched beam (SEB) bending tests. The study applied the developed computational tools to simulate the internal frost damage caused by ice crystallization with the two dimensional (2-D) SEM and three dimensional (3-D) reconstructed SEM and TXM digital samples. The pore pressure calculated from thermodynamic analysis was input for model simulation. The 2-D and 3-D bilinear CZM predicted the crack initiation and propagation within cement paste microstructure. The favorably predicted crack paths in concrete/cement samples indicate the developed bilinear CZM techniques have the ability to capture crack nucleation and propagation in cement-based material samples with multiphase and associated interface. By comparing the computational prediction with the actual damaged samples, it also indicates that the ice crystallization pressure is the main mechanism for the internal frost damage in cementitious materials.

Optimización granulométrica de morteros de base cemento

En la práctica habitual, para la elaboración de morteros se recomienda la utilización de granulometrías continuas. El requisito de continuidad y que los tamaños de partícula se encuentren dentro de los límites establecidos por “husos granulométricos” surge de las teorías clásicas de Fuller – Thompson y se apoya en la necesidad de obtener mezclas con adecuada docilidad en el estado fresco. Sin embargo, las distribuciones continuas de árido no representan las únicas alternativas para obtener mezclas que tengan una adecuada docilidad en estado fresco y mediante nuevos criterios de interferencia de partículas es posible demostrar que las distribuciones discontinuas aun siendo más compactas y con menor requerimientos de volumen de pasta pueden ser igual de dóciles en estado fresco. Aunque el volumen mínimo de pasta está condicionado por su fluidez y viscosidad estos parámetros pueden modificarse mediante la incorporación de filler de distinta naturaleza y aditivos químicos de reciente desarrollo. En consecuencia, se propone analizar la posibilidad de minimizar el contenido de pasta de morteros de base cemento, manteniendo las prestaciones en el estado fresco, con el objetivo de obtener una mejor estabilidad volumétrica, posibilitando mejor control de la retracción y de la fisuración. Para ello se emplearán criterios de interferencia de partículas, combinados con el uso de filler de distinta naturaleza La reducción del contenido de pasta conducirá también a mejorar el perfil sostenible de los morteros. El proceso de optimización tiene una base racional y, por lo tanto, será aplicable a distintos tipos de mortero, y las proporciones óptimas podrán adecuarse según las prestaciones requeridas para el material. SUMMARY In common practice, continuous sand gradings are recommended to produce ordinary mortars. This requirement, along with grading limits are based on classical theories, such as Fuller, aimed at achieving a reasonable packing density without compromising workability at the fresh state. Nevertheless, there are other alternatives, such as discontinuous curves based on particle interference criteria, which are capable of having even higher packing density. The less the content of voids in the granular skeleton, the less the amount of cement paste required to fill in these voids and coating the particles. Yet, the minimum volume of paste in a mortar is determined by requirements associated to the fresh state and thus, fluidity and viscosity of the paste play a significant role on the matter. These two properties can be modified by the use of suitable fillers and by the use of last-generation chemical admixtures. As a result, it is proposed to analyse the possibility of combining current particle interference criteria with the use of different types of filler and chemical admixtures to optimise cement-based mortar formulations. This optimisation is aimed at reducing the paste content while maintaining a suitable performance at the fresh state. The reduction in paste content would lead to a better dimensional stability, with better control of shrinkage and cracking behaviour. The foreseen optimisation process will have a strong rational basis and thus, it should be potentially useful to optimise mortar proportions according to a performance-based approach.