840 resultados para Ceramic materials.
Resumo:
Objectives: The aim of this research was to evaluate the degree of monomer conversion of different resin cement shades when photocured under different feldspathic ceramic shades. The photocuring time was also evaluated as well as the translucency of each ceramic shade. Methods: Three VITA VM7 ceramic shades (Base Dentin 0M1, Base Dentin 2M2 and Base Dentin 5M3) were used to determine the translucency percentage. A spectrophotometer MiniScan was used to measure the opacity percentage of each specimen (2-mm-thick) and then the translucency was calculated. To measure the degree of conversion (DC), the resin cement (Variolink II; A3 Yellow and transparent) specimens (thickness: 100 μm) were photocured under a ceramic block (2-mm-thick) for 20 or 40 s. Specimens photocured without the ceramic block were used as control. Sixteen groups (n = 3) were evaluated. Micro-ATR/FTIR spectrometry was used to evaluate the extent of polymerization of all specimens after 24 h. The %DC was calculated of experimentally polymerized versus maximally polymerized composite. Results: The translucency percentages of 0M1, 2M2 and 5M3 ceramics were 12.41 (1.02)%, 5.75 (1.91)% and 1.07 (0.03)%, respectively. The %DC of both resin cement shades cured under ceramic 5M3 was significantly lower than the other groups (p < 0.05). The %DC of 0M1 groups exhibited no significant difference from 2M2 groups (p > 0.05), with the exception of the transparent cement photocured for 40 s. Conclusion: Photocuring under 2 mm ceramic showed that the increase in chroma saturation significantly decreased Variolink II resin cement %DC (100-μm-thick). © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.
Resumo:
Objective: To investigate the influence of the convergence angle of tooth preparation on the fracture load of Y-TZP-based ceramic (YZ-Vita YZ) substructure (SB) veneered with a feldspathic porcelain (VM9-Vita VM9). Methods: Finite element stress analysis (FEA) was performed to examine the stress distribution of the system. Eighty YZ SB were fabricated using a CAD-CAM system and divided into four groups (n = 20), according to the total occlusal convergence (TOC) angle: G6-6° TOC; G12-12° TOC; G20-20° TOC; and G20MOD-20° TOC with modified SB. All SB were veneered with VM9, cemented in a fiber reinforced epoxy resin die, and loaded to failure. Half of the specimens from each group (n = 10) were cyclic fatigued (106 cycles) before testing. Failure analysis was performed to determine the fracture origin. Data were statistically analyzed using Anova and Tukey's tests (α = 0.05). Results: The greatest mean load to fracture value was found for the G20MOD, which was predicted by the FEA. Cyclic fatigue did not significantly affect the load of fracture. Catastrophic failure originating from the internal occlusal surface of the SB was the predominant failure mode, except for G20MOD. Significance: The YZ-VM9 restorations resisted greater compression load than the usual physiological occlusal load, regardless of the TOC angle of preparations. Yet, the G20MOD design produced the best performance among the experimental conditions evaluated. © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.
Resumo:
Purpose: Adhesive cementation is an important step for restorations made of feldspathic ceramic as it increases the strength of such materials. Incorrect selection of the adhesive resin and the resin cement to adhere to the ceramic surface and their durability against aging can affect the adhesion between these materials and the clinical performance. This study evaluated the effect of adhesive resins with different pHs, resin cements with different polymerization modes, and aging on the bond strength to feldspathic ceramic. Materials and Methods: One surface of feldspathic ceramic blocks (VM7) (N = 90) (6.4 × 6.4 × 4.8 mm3) was conditioned with 10% hydrofluoric acid for 20 seconds, washed/dried, and silanized. Three adhesive resins (Scotchbond Multi-Purpose Plus [SBMP], pH: 5.6; Single Bond [SB], pH: 3.4; and Prime&Bond NT [NT], pH: 1.7) were applied on the ceramic surfaces (n = 30 per adhesive). For each adhesive group, three resin cements with different polymerization modes were applied (n = 10 per cement): photo-polymerized (Variolink II base), dual polymerized (Variolink II base + catalyst), and chemically polymerized (C&B). The bonded ceramic blocks were stored in water (37°C) for 24 hours and sectioned to produce beam specimens (cross-sectional bonded area: 1 ± 0.1 mm2). The beams of each block were randomly divided into two conditions: Dry, microtensile test immediately after cutting; TC, test was performed after thermocycling (12,000×, 5°C to 55°C) and water storage at 37°C for 150 days. Considering the three factors of the study (adhesive [3 levels], resin cement [3 levels], aging [2 levels]), 18 groups were studied. The microtensile bond strength data were analyzed using 3-way ANOVA and Tukey's post hoc test (α= 0.05). Results: Adhesive resin type (p < 0.001) and the resin cement affected the mean bond strength (p= 0.0003) (3-way ANOVA). The NT adhesive associated with the chemically polymerized resin cement in both dry (8.8 ± 6.8 MPa) and aged conditions (6.9 ± 5.9 MPa) presented statistically lower bond strength results, while the SBMP adhesive resin, regardless of the resin cement type, presented the highest results (15.4 to 18.5 and 14.3 to 18.9 MPa) in both dry and aged conditions, respectively (Tukey's test). Conclusion: Application of a low-pH adhesive resin onto a hydrofluoric acid etched and silanized feldspathic ceramic surface in combination with chemically polymerized resin cement did not deliver favorable results. The use of adhesive resin with high pH could be clinically advised for the photo-, dual-, and chemically polymerized resin cements tested. © 2012 by the American College of Prosthodontists.
Resumo:
This study evaluated the effect of different air-particle abrasion protocols on the biaxial flexural strength and structural stability of zirconia ceramics. Zirconia ceramic specimens (ISO 6872) (Lava, 3M ESPE) were obtained (N=336). The specimens (N=118, n=20 per group) were randomly assigned to one of the air-abrasion protocols: Gr1: Control (as-sintered); Gr2: 50 μm Al2O3 (2.5 bar); Gr3: 50 μm Al2O3 (3.5 bar); Gr4: 110 μm Al2O3(2.5 bar); Gr5: 110 μm Al2O3 (3.5 bar); Gr6: 30 μm SiO2 (2.5 bar) (CoJet); Gr7: 30 μm SiO2(3.5 bar); Gr8: 110 μm SiO2 (2.5 bar) (Rocatec Plus); and Gr9: 110 μm SiO2 (3.5 bar) (duration: 20 s, distance: 10 mm). While half of the specimens were tested immediately, the other half was subjected to cyclic loading in water (100,000 cycles; 50 N, 4 Hz, 37 °°C) prior to biaxial flexural strength test (ISO 6872). Phase transformation (t→m), relative amount of transformed monoclinic zirconia (FM), transformed zone depth (TZD) and surface roughness were measured. Particle type (p=0.2746), pressure (p=0.5084) and cyclic loading (p=0.1610) did not influence the flexural strength. Except for the air-abraded group with 110 μm Al2O3 at 3.5 bar, all air-abrasion protocols increased the biaxial flexural strength (MPa) (Controlnon-aged: 1030±153, Controlaged: 1138±138; Experimentalnon-aged: 1307±184-1554±124; Experimentalaged: 1308±118-1451±135) in both non-aged and aged conditions, respectively. Surface roughness (Ra) was the highest with 110 μm Al2O3(0.84 μm. FM values ranged from 0% to 27.21%, higher value for the Rocatec Plus (110 μm SiO2) and 110 μm Al2O3 groups at 3.5 bar pressure. TZD ranged between 0 and 1.43 μm, with the highest values for Rocatec Plus and 110 μm Al2O3 groups at 3.5 bar pressure. © 2013 Elsevier Ltd.
Resumo:
Purpose: To evaluate the influence of heat treatment (HT) procedures of a pre-hydrolyzed silane on bond strength of resin cement to a feldspathic ceramic.Materials and Methods: Ceramic and composite blocks (N = 30) were divided into six groups (n = 5) and subjected to the following conditioning procedures: G1: 9.6% hydrofluoric acid (HF) for 20 s + silane (RelyX Ceramic Primer, 3M ESPE) + resin cement (Panavia F2.0, Kuraray) (control); G2: HF (20 s) + silane + heat treatment in furnace (HTF) (100 degrees C, 2 min) + resin cement; G3: silane + HTF + resin cement; G4-HF (20 s) + silane + heat treatment with hot air (HTA) (50 +/- 5 degrees C for 1 min) + resin cement; G5: silane + HTA + resin cement; G6: silane + resin cement. The microtensile bond strength (MTBS) test was performed using a universal testing machine (1 mm/min). After debonding, the substrate and adherent surfaces were analyzed using a stereomicroscope and SEM to categorize the failure types. The data were statistically evaluated using one-way ANOVA and Tukey's test (5%).Results: The control group (G1) showed no pre-test failures and presented significantly higher mean MTBS (16.01 +/- 1.12 MPa) than did other groups (2.63 +/- 1.05 to 12.55 +/- 1.52 MPa) (p = 0.0001). In the groups where HF was not used, HTF (G3: 12.55 +/- 1.52 MPa) showed significantly higher MTBS than did HTA (G5: 2.63 +/- 1.05 MPa) (p < 0.05). All failure types were mixed, ie, adhesive between the resin cement and ceramic accompanied by cohesive failure in the cement.Conclusion: Heat treatment procedures for the pre-hydrolyzed silane either in a furnace or with the application of hot air cannot replace the use of HF gel for the adhesion of resin cement to feldspathic ceramic. Yet when mean bond strengths and incidence of pre-test failures are considered, furnace heat treatment delivered the second best results after the control group, being considerably better than hot air application.
Resumo:
Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)
Resumo:
Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)
Resumo:
Since the discovery of YBaCuO, experiments have shown that its superconducting properties are strongly affected by the oxygen content. More recently, anelastic relaxation measurements in La2CuO4+δ, showed that the decrease in the oxygen content can be related to two events. One is the decrease in mobility between two adjacent CuO planes, and the other is the increase in the number of tilting patterns of the CuO6 octahedra. In the case of the bismuth-based ceramic, it is known that the oxygen content, within some limits, does not affect its superconducting properties. In order to evaluate the mobility and the effect of the oxygen content on this material we have prepared BSCCO ceramic and tested regarding its internal friction and electrical resistivity as a function of the temperature while the oxygen content was being reduced by a sequence of vacuum annelaing at 620 K. The samples were prepared in the Bi:Sr:Ca:Cu = 2212 and 2223 proportion, using powder obtained by the sol-gel route and conventional solid state reaction. The anelastic relaxation measurements were performed using a torsion pendulum operating with frequency about 15-35 Hz between 77 to 700 K. The diffraction pattern of the as sintered and the vacuum annealed material were also presented. The results have shown complex anelastic relaxation structures that were associated to the jump of interstitial oxygen atoms between two adjacent CuO planes. The vacuum annealing showed to be deleterious to the critical temperature of the superconducting ceramic.
Resumo:
This study evaluated the five-year clinical performance of ceramic inlays and onlays made with two systems: sintered Duceram (Dentsply-Degussa) and pressable IPS Empress (Ivoclar Vivadent). Eighty-six restorations were placed by a single operator in 35 patients with a median age of 33 years. The restorations were cemented with dual-cured resin cement (Variolink II, Ivoclar Vivadent) and Syntac Classic adhesive under rubber dam. The evaluations were conducted by two independent investigators at baseline, and at one, two, three, and five years using the modified United States Public Health Service (USPHS) criteria. At the five-year recall, 26 patients were evaluated (74.28%), totalling 62 (72.09%) restorations. Four IPS restorations were fractured, two restorations presented secondary caries (one from IPS and one from Duceram), and two restorations showed unacceptable defects at the restoration margin and needed replacement (one restoration from each ceramic system). A general success rate of 87% was recorded. The Fisher exact test revealed no significant difference between Duceram and IPS Empress ceramic systems for all aspects evaluated at different recall appointments (p>0.05). The McNemar chi-square test showed significant differences in relation to marginal discoloration, marginal integrity, and surface texture between the baseline and five-year recall for both systems (p<0.001), with an increased percentage of Bravo scores. However, few Charlie or Delta scores were attributed to these restorations. In conclusion, these two types of ceramic materials demonstrated acceptable clinical performance after five years
Resumo:
Thermoelektrizität beschreibt die reversible Beeinflussung und Wechselwirkung von Elektrizität und Temperatur T in Systemen abseits des thermischen Gleichgewichtes. In diesen führt ein Temperaturgradient entlang eines thermoelektrischen Materials zu einem kontinuierlichen Ungleichgewicht in der Energieverteilung der Ladungsträger. Dies hat einen Diffusionsstrom der energiereichen Ladungsträger zum kalten Ende und der energiearmen Ladungsträger zum heißen Ende zur Folge. Da in offenen Stromkreisen kein Strom fließt, wird ein Ungleichgewicht der Ströme über das Ausbilden eines elektrischen Feldes kompensiert. Die dadurch entstehende Spannung wird als Seebeck Spannung bezeichnet. Über einen geeigneten Verbraucher, folgend aus dem Ohm'schen Gesetz, kann nun ein Strom fließen und elektrische Energie gewonnen werden. Den umgekehrten Fall beschreibt der sogenannte Peltier Effekt, bei dem ein Stromfluss durch zwei unterschiedliche miteinander verbundene Materialien ein Erwärmen oder Abkühlen der Kontaktstelle zur Folge hat. Die Effizienz eines thermoelektrischen Materials kann über die dimensionslose Größe ZT=S^2*sigma/kappa*T charakterisiert werden. Diese setzt sich zusammen aus den materialspezifischen Größen der elektrischen Leitfähigkeit sigma, der thermischen Leitfähigkeit kappa und dem Seebeck Koeffizienten S als Maß der erzeugten Spannung bei gegebener Temperaturdifferenz. Diese Arbeit verfolgt den Ansatz glaskeramische Materialien mit thermoelektrischen Kristallphasen zu synthetisieren, sie strukturell zu charakterisieren und ihre thermoelektrischen Eigenschaften zu messen, um eine Struktur-Eigenschaft Korrelation zu erarbeiten. Hierbei werden im Detail eine elektronenleitende (Hauptphase SrTi_xNb_{1-x}O_3) sowie eine löcherleitende Glaskeramik (Hauptphase Bi_2Sr_2Co_2O_y) untersucht. Unter dem Begriff Glaskeramiken sind teilkristalline Materialien zu verstehen, die aus Glasschmelzen durch gesteuerte Kristallisation hergestellt werden können. Über den Grad der Kristallisation und die Art der ausgeschiedenen Spezies an Kristallen lassen sich die physikalischen Eigenschaften dieser Systeme gezielt beeinflussen. Glaskeramiken bieten, verursacht durch ihre Restglasphase, eine niedrige thermische Leitfähigkeit und die Fermi Energie lässt sich durch Dotierungen in Richtung des Leitungs- oder Valenzbands verschieben. Ebenso besitzen glaskeramische Materialien durch ihre Porenfreiheit verbesserte mechanische Eigenschaften gegenüber Keramiken und sind weniger anfällig für den Einfluss des Sauerstoffpartialdruckes p_{O_2} auf die Parameter. Ein glaskeramisches und ein gemischt keramisch/glaskeramisches thermoelektrisches Modul aus den entwickelten Materialien werden konzipiert, präpariert, kontaktiert und bezüglich ihrer Leistung vermessen.
Resumo:
Carbon and carbonaceous material have been known to have a deleterious effect upon the cyanidation of gold and silver ores since the very beginning of the process. Organic matter is a common source of impurities in cyanide solution, its reducing effect being notorious.
Resumo:
Objectives: To investigate surface roughness and microhardness of two recent resin-ceramic materials for computer-aided design/computer-aided manufacturing (CAD/CAM) after polishing with three polishing systems. Surface roughness and microhardness were measured immediately after polishing and after six months storage including monthly artificial toothbrushing. Methods: Sixty specimens of Lava Ultimate (3M ESPE) and 60 specimens of VITA ENAMIC (VITA Zahnfabrik) were roughened in a standardized manner and polished with one of three polishing systems (n=20/group): Sof-Lex XT discs (SOFLEX; three-step (medium-superfine); 3M ESPE), VITA Polishing Set Clinical (VITA; two-step; VITA Zahnfabrik), or KENDA Unicus (KENDA; one-step; KENDA Dental). Surface roughness (Ra; μm) was measured with a profilometer and microhardness (Vickers; VHN) with a surface hardness indentation device. Ra and VHN were measured immediately after polishing and after six months storage (tap water, 37°C) including monthly artificial toothbrushing (500 cycles/month, toothpaste RDA ~70). Ra- and VHN-values were analysed with nonparametric ANOVA followed by Wilcoxon rank sum tests (α=0.05). Results: For Lava Ultimate, Ra (mean [standard deviation] before/after storage) remained the same when polished with SOFLEX (0.18 [0.09]/0.19 [0.10]; p=0.18), increased significantly with VITA (1.10 [0.44]/1.27 [0.39]; p=0.0001), and decreased significantly with KENDA (0.35 [0.07]/0.33 [0.08]; p=0.03). VHN (mean [standard deviation] before/after storage) decreased significantly regardless of polishing system (SOFLEX: 134.1 [5.6]/116.4 [3.6], VITA: 138.2 [10.5]/115.4 [5.9], KENDA: 135.1 [6.2]/116.7 [6.3]; all p<0.0001). For VITA ENAMIC, Ra (mean [standard deviation] before/after storage) increased significantly when polished with SOFLEX (0.37 [0.18]/0.41 [0.14]; p=0.01) and remained the same with VITA (1.32 [0.37]/1.31 [0.40]; p=0.58) and with KENDA (0.81 [0.35]/0.78 [0.32]; p=0.21). VHN (mean [standard deviation] before/after storage) remained the same regardless of polishing system (SOFLEX: 284.9 [24.6]/282.4 [31.8], VITA: 284.6 [28.5]/276.4 [25.8], KENDA: 292.6 [26.9]/282.9 [24.3]; p=0.42-1.00). Conclusion: Surface roughness and microhardness of Lava Ultimate was more affected by storage and artificial toothbrushing than was VITA ENAMIC.
Resumo:
Purpose: To investigate the bond strength to dentin of two recent resin-ceramic materials for computer-aided design/computer-aided manufacturing (CAD/CAM) after 24 hours and after six months storage. Methods and Materials: Ninety cylinders were milled out of Lava Ultimate (3M ESPE) and 90 cylinders out of VITA ENAMIC (VITA Zahnfabrik) (dimension of cylinders: ∅=3.6 mm, h=2 mm). All Lava Ultimate cylinders were sandblasted (aluminium oxide, grain size: 27 μm) and cleaned with ethanol, whereas all VITA ENAMIC cylinders were acid-etched (5% hydrofluoric acid) and cleaned with water-spray. According to the three groups of cements used, the cylinders (n=30/resin-ceramic material) were further pretreated with 1) Scotchbond Universal for RelyX Ultimate (3M ESPE), 2) CLEARFIL Ceramic Primer for PANAVIA F2.0 (Kuraray), or 3) no further pretreatment for Ketac Cem Plus (3M ESPE). The cylinders were then bonded to ground human dentin specimens with 1) Scotchbond Universal and RelyX Ultimate (light-cured), 2) ED PRIMER II and PANAVIA F2.0 (light-cured), or 3) no adhesive system; Ketac Cem Plus (self-cured). Shear bond strength (SBS) was measured after 24 hours for 15 specimens/group and after six months (37°C, 100% humidity) for the other 15 specimens/group. SBS-values were statistically analysed with nonparametric ANOVA followed by exact Wilcoxon rank sum tests (α=0.05). Results: SBS of the two resin-ceramic materials and the three cements after 24 hours and after six months storage are shown in Figure 1. The statistical analysis showed that the duration of storage had a significant effect on SBS of Lava Ultimate for all three cements but had no significant effect on SBS of VITA ENAMIC. For Lava Ultimate SBS-values were (MPa; medians after 24 hours/six months): 13.5/22.5 (p=0.04) for RelyX Ultimate, 11.4/5.8 (p=0.0006) for PANAVIA F2.0, and 0.34/0.09 (p=0.04) for Ketac Cem Plus (Fig. 1). For VITA ENAMIC SBS-values were (MPa; medians after 24 hours/six months): 16.0/21.2 (p=0.10) for RelyX Ultimate, 11.4/14.4 (p=0.06) for PANAVIA F2.0, and 0.43/0.41 (p=0.32) for Ketac Cem Plus (Fig. 1). After 24 hours, there was no significant difference in SBS between Lava Ultimate and VITA ENAMIC for all three cements (p≥0.37). After six months, there was no significant difference in SBS between Lava Ultimate and VITA ENAMIC for RelyX Ultimate and Ketac Cem Plus (p≥0.07) whereas for PANAVIA F2.0, SBS was significantly lower for Lava Ultimate than for VITA ENAMIC (p<0.0001). Conclusion: SBS of Lava Ultimate was more affected by six months storage and by the cement used than was VITA ENAMIC.
Resumo:
En este trabajo, materiales de tipo alúmina/Y-TZP (ZrO2 tetragonal, estabilizada con 3 mol. % Y2O3), como sistema cerámico popular por sus mejoradas propiedades mecánicas en comparación con las cerámicas de alúmina puras, han sido estudiados en términos de propiedades mecánicas y tensiones residuales. El novedoso método de colado en cinta, consistente en el apilamiento de cintas de cerámica verde a temperatura ambiente y el uso de bajas presiones, se ha escogido para la presente investigación con el fin de poder aprovechar al máximo el futuro desarrollo de materiales laminados de alúmina-óxido de circonio. Se han determinado las propiedades de los materiales obtenidos por este nuevo método de procesamiento comparándolas con las de los materiales obtenidos por “slip casting”, con el fin de analizar si el método propuesto afecta a la microestructura y, por tanto, a las propiedades mecánicas y tensiones residuales propias de estos materiales. Para analizar la idoneidad del proceso de fabricación, utilizado para evitar la presencia de discontinuidades en las intercaras entre las láminas así como otros fenómenos que puedan interferir con las propiedades mecánicas, se estudiaron materiales cerámicos con la misma composición en cintas. Por otra parte también se analizó el efecto de la adición de óxido de circonio sobre la aparición de tensiónes residuales en cerámicas Al2O3/Y-TZP, teniendo en cuenta su notable influencia sobre las propiedades microestructurales y mecánicas de los materiales, así como el requisito de co-sinterización de capas con diferentes materiales compuestos en materiales laminados. La caracterización del material incluye la determinación de la densidad, el análisis de la microestructura, la obtención de las propiedades mecánicas (módulo de elasticidad, dureza, resistencia a la flexión y tenacidad de fractura) así como de las tensiones residuales. En combinación con otros métodos de medida tradicionales, la nanoindentación también se empleó como una técnica adicional para la medida del módulo de elasticidad y de la dureza. Por otro lado, diferentes técnicas de difracción con neutrones, tanto las basadas en longitud de onda constante (CW) como en tiempo de vuelo (TOF), han sido empleadas para la medición fiable de la deformación residual a través del grosor en muestras a granel. Las tensiones residuales fueron determinadas con elevada precisión, aplicando además métodos de análisis apropiados, como por ejemplo el refinamiento de Rietveld. Las diferentes fases en cerámicas sinterizadas, especialmente las de zirconia, se examinaron con detalle mediante el análisis de Rietveld, teniendo en cuenta el complicado polimorfismo del Óxido de Zirconio (ZrO2) así como las posibles transformaciones de fase durante el proceso de fabricación. Los efectos del contenido de Y-TZP en combinación con el nuevo método de procesamiento sobre la microestructura, el rendimiento mecánico y las tensiones residuales de los materiales estudiados (Al2O3/Y-TZP) se resumen en el presente trabajo. Finalmente, los mecanismos de endurecimiento, especialmente los relacionados con las tensiones residuales, son igualmente discutidos. In present work, Alumina/Y-TZP (tetragonal ZrO2 stabilized with 3 mol% Y2O3) materials, as an popular ceramic system with improved mechanical properties compared with the pure alumina ceramics, have been studied in terms of mechanical properties and residual stresses. The novel tape casting method, which involved the stacking of green ceramics tapes at room temperature and using low pressures, is selected for manufacturing and investigation, in order to take full advantage of the future development of alumina-zirconia laminated materials. Features of materials obtained by the new processing method are determined and compared with those of materials obtained by conventional slip casting in a plaster mold, in order to study whether the proposed method of processing affects microstructure and thereby the mechanical properties and residual stresses characteristics of materials. To analyse the adequacy of the manufacturing process used to avoid the presence of discontinuities at the interfaces between the sheets and other phenomena that interfere with the mechanical properties, ceramic materials with the same composition in tapes were investigated. Moreover, the effect of addition of zirconia on residual stress development of Al2O3/Y-TZP ceramics were taken into investigations, considering its significantly influence on the microstructure and mechanical properties of materials as well as the requirement of co-sintering of layers with different composites in laminated materials. The characterization includes density, microstructure, mechanical properties (elastic modulus, hardness, flexure strength and fracture toughness) and residual stresses. Except of the traditional measurement methods, nanoindentation technique was also used as an additional measurement of the elastic modulus and hardness. Neutron diffraction, both the constant-wavelength (CW) and time-of-flight (TOF) neutron diffraction techniques, has been used for reliable through-thickness residual strain measurement in bulk samples. Residual stresses were precisely determined combined with appropriate analysis methods, e.g. the Rietveld refinement. The phase compositions in sintered ceramics especially the ones of zirconia were accurately examined by Rietveld analysis, considering the complex polymorph of ZrO2 and the possible phase transformation during manufacturing process. Effects of Y-TZP content and the new processing method on the microstructure, mechanical performance and residual stresses were finally summarized in present studied Al2O3/Y-TZP materials. The toughening mechanisms, especially the residual stresses related toughening, were theoretically discussed.
Resumo:
El presente trabajo de investigación determina las características de la cerámica que más eficientemente se comporta a evaporación y a enfriamiento. Con el objeto de ser empleado como material integrado en la envolvente de los edificios para reducir su carga de refrigeración. La cerámica es un buen material para ser empleado para la refrigeración por evaporación. Es un sólido poroso inerte que, tras ser sometido a cocción a temperaturas por encima de los 900ºC, resulta uno de los materiales que mejor se comportan como contenedor de agua en su red capilar para, posteriormente, ir liberándola por evaporación al mismo tiempo que se enfría su superficie. La metodología general de investigación, se divide en tres etapas: Búsqueda y análisis del estado de la técnica y de la investigación. Estudio teórico de la eficacia del enfriamiento evaporativo como estrategia de enfriamiento pasivo en la arquitectura. Etapa experimental, desarrollada en tres fases: una primera de definición de los parámetros determinantes del Enfriamiento Evaporativo en piezas cerámicas, una segunda de selección cerámica y diseño de ensayos experimentales y una tercera de caracterización de la cerámica bajo criterios de evaporación y de enfriamiento. El recorrido por el estado de la cuestión ha identificado las aplicaciones tecnológicas y las investigaciones científicas que emplean el Enfriamiento Evaporativo con piezas cerámicas como técnica de enfriamiento. Como resultado se ha obtenido una tabla de clasificación de sistemas de enfriamiento evaporativo y se ha constatado que el conjunto de las aplicaciones están centradas en el diseño de piezas o sistemas pero que, sin embargo, no existe una definición de las características de la cerámica para su empleo como material de enfriamiento por evaporación. El estudio teórico de la eficacia del empleo del enfriamiento evaporativo como estrategia de enfriamiento pasivo en la arquitectura se ha realizado mediante cálculos de porcentaje de ampliación de horas en confort con empleo de técnicas de enfriamiento evaporativo directo e indirecto (EED y EEI). Como resultado se obtienen unos mapas para el ámbito español de potencial de aplicación del EED y EEI. Los resultados permiten afirmar que mediante EE se puede llegar a confort en prácticamente la totalidad de las horas de los días más cálidos del año en muchas localidades. La metodología experimental se ha desarrollado en tres fases. En la fase inicial, se han definido los parámetros determinantes del enfriamiento evaporativo en un medio cerámico mediante ensayos experimentales de capacidad de evaporación y de caracterización. Se realizaron un total de 12 ensayos. Se determinó que el material cerámico tiene una gran influencia en la capacidad de evaporación y enfriamiento en las piezas cerámicas, apoyando la hipótesis inicial y la necesidad de caracterizar el material. La primera fase empírica se centró en la selección cerámica y el diseño de los ensayos experimentales de comportamiento hídrico. Se seleccionaron muestras de 5 tipos de cerámica. Se realizaron 4 tipos de ensayos de caracterización y 6 tipos de ensayos experimentales de comportamiento hídrico (total 123 muestras ensayadas). Los resultados obtenidos son de dos tipos, por un lado, se determinó cuál es el tipo de cerámica que más eficientemente se comporta a EE y, por otro, se rediseñaron los ensayos de la última fase experimental. Para la segunda fase experimental se seleccionaron cerámicas de fabricación manual abarcando el mayor número de localidades del ámbito español. Se realizaron ensayos de caracterización de 7 tipos y ensayos de comportamiento hídrico de 5 tipos (total 197 muestras ensayadas). Los resultados de caracterización han permitido aportar unos rangos de las características de la cerámica que más eficientemente se comporta en los ensayos de comportamiento hídrico. Al final de la investigación se ha caracterizado el material cerámico aportando características acerca de su porosidad, capacidad de absorción, color, rugosidad y mineralogía. Así como datos de referencia de su comportamiento hídrico. Además se ha desarrollado una metodología de ensayo específica que permite evaluar la capacidad de enfriamiento eficiente de una pieza cerámica. ABSTRACT The purpose of this research is to determine the characteristics of ceramic materials having the most efficient performance in terms of evaporation and cooling, so that they can be integrated in building envelopes to reduce cooling loads. Ceramics are suitable materials for cooling through passive evaporation. After being fired at temperatures over 900 °C (1,652 °F), the capillary network of this inert porous medium turns to be excellent to retain water, which is progressively liberated by evaporation while the material surface gets colder. Research methodology has involved the following steps: Search and analysis on the state of the art in technology and research. Theoretical study on the efficiency of evaporation as passive cooling strategies in buildings. Experimental stage developed in three phases, namely: definition of parameters determining evaporative cooling in ceramic elements; ceramic selection and design of experimental tests; characterization of ceramic materials under evaporation and cooling criteria. Search and analysis on the state of the art in this field have been useful to identify technology applications and scientific research where ceramics are employed for evaporative cooling. The resulting table shows that applications are wholly focused on the design of pieces and systems. Nonetheless, there is lack of definition of material characteristics in this scope. The theoretical study on efficiency of the passive strategy applied to buildings has been realized by calculation of the percentage increase in comfort hours through direct/indirect evaporative cooling techniques (DEC/IEC). The mapping of their potential application in Spain clearly shows that comfort conditions can be reached in almost all the hours of the hottest days in many towns. In the initial phase of the experimental stage, parameters determining evaporative cooling in ceramic media have been defined. For this purpose, characterization tests and evaporation and cooling rates experiments have been carried out; the number of samples tested amounted to 12. It has been concluded that material characteristics have great influence on these rates, which supports the initial hypothesis and the need for their characterization. The first empirical phase has focused on ceramic selection and design of water behaviour experimental methods. The samples covered five different kinds of ceramic materials. Four different characterization tests and six different water behaviour experiments were carried out; the number of samples tested amounted to 123. The experimental testing procedures served to determine the most efficient types of ceramic materials in terms of evaporative cooling efficiency and, at the same time, made it necessary to change the original designed experimental test for the last phase. In the second phase, a number of varied hand-made ceramic tiles have been selected. Seven different characterization tests and five different water behaviour tests were carried out; the number of samples amounted to 197. The results of characterization served to establish a range of features in ceramic materials according to their efficiency in water behaviour experiments. Finally, ceramic materials have been characterized according to porosity, water absorption, colour, surface roughness and mineralogy. Also, reference data regarding water behaviour have been included. Moreover, an innovative and specific experimental test to evaluate cooling efficiency of ceramic tiles has been developed.