Effect of carbon fibres on the mechanical properties and corrosion levels of reinforced portland cement mortars

The changes in mechanical properties of portland cement mortars due to the addition of carbon fibres (CF) to the mix have been studied. Compression and flexural strengths have been determined in relation to the amount of fibres added to the mix, water/binder ratio, curing time and porosity. Additionally, the corrosion level of reinforcing steel bars embedded in portland cement mortars containing CF and silica fume (SF) have also been investigated and reinforcing steel corrosion rates have been determined. As a consequence of the large concentration of oxygen groups in CF surface, a good interaction between the CF and the water of the mortar paste is to be expected. A CF content of 0.5% of cement weight implies an optimum increase in flexural strength and an increase in embedded steel corrosion.

Corrosion of stainless steel components in seawater reverse osmosis desalination plants-investigations on adapted internal cathodic protection

Stainless steel is widely used in seawater reverse osmosis units (SWRO) for both good mechanical and corrosion resistance properties. However, many corrosion failures of stainless steel in SWRO desalination units have been reported. These failures may often be attributed to un-adapted stainless steel grade selection and/or to the particular aggressive seawater conditions in "warm" regions (high ambient temperature, severe biofouling, etc.). Cathodic protection (CP) is a well-known efficient system to prevent corrosion of metallic materials in seawater. It is successfully used in the oil and gas industry to protect carbon steel structures exposed in open-sea. However, the specific service conditions of SWRO units may seriously affect the efficiency of such anti-corrosion system (high flow rates, large stainless steel surfaces affected by biofouling, confinement limiting protective cathodic current flow, etc.). Hence, CP in SWRO units should be considered with special care and modeling appears as useful tool to assess an appropriate CP design. However, there is a clear lack of CP data that could be transposed to SWRO service conditions (i.e. stainless steel, effect of biofouling, high flow rate, etc.). From this background a Join Industry Program was initiated including laboratory exposures, field measurements in a full scale SWRO desalination plant, and modeling work using PROCOR software. The present paper reviews the main parameters affecting corrosion of stainless steel alloys in seawater reverse osmosis units. CP on specific stainless steel devices was investigated in order to assess its actual efficiency for SWRO units. Severe environmental conditions were intentionally used to promote corrosion on the tested stainless steel products in order to evaluate the efficiency of CP. The study includes a modeling work aiming at predicting and designing adapted CP protection to modeled stainless steel units. An excellent correlation between modeling work and field measurements was found.

Estudo da corrosão e inibição dos aços carbono AISI 1010, inoxidável AISI 316 e duplex UNS S31803 em meio de solução de íons cloreto

O comportamento da corrosão e inibição à corrosão dos aços carbono AISI 1010, inox AISI 316 e duplex UNS S31803 foi estudado em meio de solução de íons cloreto à 3,0% (m/v), na ausência e presença do benzimidazol e imidazol como inibidores. A caracterização química e morfológica dos aços foi realizada por meio das técnicas de espectrometria de emissão ótica, difração de raios X (DRX), microscopia ótica, microscopia eletrônica de varredura (MEV) e energia dispersiva de raios X (EDX). As análises eletroquímicas foram realizadas através das técnicas de polarização potenciodinâmica e espectroscopia de impedância eletroquímica. As análises de DRX e de metalografia mostraram as fases presentes em cada aço, sendo o aço AISI 1010 composto pela fase ferrita, o aço AISI 316 pelas fases de FeNi e Cr e o aço UNS S31803 pelas fases austenita e ferrita. Além disso, a metalografia e as análises de MEV e EDX permitiram identificar regiões e certos elementos presentes nos aços que propiciam à ocorrência da corrosão, tais como inclusões. Os inibidores foram testados em diferentes concentrações (25 ppm, 50 ppm, 100 ppm, 500 ppm e 1000 ppm) para os três aços, através das curvas de polarização e impedância eletroquímica, e verificou-se que para todas as concentrações houve aumento da resistência à corrosão dos aços. Pelas curvas de polarização verificou-se que o benzimidazol proporcionou aos aços AISI 1010, AISI 316 e UNS S31803, eficiências de inibição de cerca de 51%, 71% e 75%, respectivamente. Enquanto que o imidazol apresentou eficiência de cerca de 73%, 95% e 86%, respectivamente. Os resultados de impedância eletroquímica mostraram que as eficiências de inibição do benzimidazol foram de aproximadamente 52%, 73% e 71%, respectivamente, para os aços AISI 1010, AISI 316 e UNS S31803. E por sua vez, o imidazol apresentou eficiências de aproximadamente 96% para os aços AISI 1010 e AISI 316 e 85% para o aço UNS S31803. O teste de perda de massa mostrou que para o aço AISI 1010 tanto o benzimidazol quanto e o imidazol inibiram a corrosão, sendo que reduziram a corrosão em cerca de 17% e 24%, respectivamente. Nas análises das curvas de polarização em estudos com a água do mar observou-se que os inibidores foram menos eficientes do que em meio de solução de cloreto. O benzimidazol obteve eficiências de cerca de 14%, 50% e 33%, respectivamente, para os aços AISI 1010, AISI 316 e UNS S31803. Enquanto que o imidazol apresentou eficiências de aproximadamente 21%, 59% e 34%, respectivamente. Em todas as análises eletroquímicas e análise de perda de massa, o imidazol se mostrou o melhor inibidor para os aços estudados.

The effect of the angle of incidence on the aqueous corrosion of ion implanted M50 steel substrates

Following work on tantalum and chromium implanted flat M50 steel substrates, this work reports on the electrochemical behaviour of M50 steel implanted with tantalum and chromium and the effect of the angle of incidence. Proposed optimum doses for resistance to chloride attack were based on the interpretation of results obtained during long-term and accelerated electrochemical testing. After dose optimization from the corrosion viewpoint, substrates were implanted at different angles of incidence (15°, 30°, 45°, 60°, 75°, 90°) and their susceptibility to localized corrosion assessed using open-circuit measurements, step by step polarization and cyclic voltammetry at several scan rates (5–50 mV s-1). Results showed, for tantalum implanted samples, an ennoblement of the pitting potential of approximately 0.5 V for an angle of incidence of 90°. A retained dose of 5 × 1016 atoms cm-2 was found by depth profiling with Rutherford backscattering spectrometry. The retained dose decreases rapidly with angle of incidence. The breakdown potential varies roughly linearly with the angle of incidence up to 30° falling fast to reach -0.1 V (vs. a saturated calomel electrode (SCE)) for 15°. Chromium was found to behave differently. Maximum corrosion resistance was found for angles of 45°–60° according to current densities and breakdown potentials. Cr+ depth profiles ((p,γ) resonance broadening method), showed that retained doses up to an angle of 60° did not change much from the implanted dose at 90°, 2 × 1017 Cr atoms cm-2. The retained implantation dose for tantalum and chromium was found to follow a (cos θ)8/3 dependence where θ is the angle between the sample normal and the beam direction.

Avaliação de indicadores de uso diverso como inibidores de corrosão

Very often hydrochloric acid is employed in acidification operations aiming to dissolve the mineral matrix in petroleum wheel operations, which always require intense use of corrosion inhibitors. This work presents an evaluation of common indicators, phenolfthaleine, fluorescein, methylene blue, alizarine S and methyl orange, as corrosion inhibitors for carbon steel in HCl 15% w/v at temperatures of 26, 40 and 60 ºC. Fluorescein and methyl orange show excelent corrosion inhibition efficiencies at 26 ºC; however at 60 ºC only fluorescein shows good corrosion inhibition when employed with alcohol and/or formaldehyde. For the fluorescein 1% w/v + formaldehyde 0.6% w/v mixture we present polarization and impedance curves and adsorption isotherms.

Corrosion by sulfate reducing bacteria that utilize nitrate

16S rRNA gene sequencing was used to identify a sulfate-reducing bacterium (SRB) from a Danish North Sea oilfield water injection system. This species was cultivated, purified and subsequently identified as being >97% similar to Desulfovibrio gracilis. Like some other Desulfovibrio species this SRB, strain OP102, could reduce nitrate as an electron acceptor and produce ammonia in the absence of sulfate. In addition, in the presence of sulfate, when nitrate was dosed at 100 mg/l it was again reduced by the bacterium, with some ammonium production. Therefore, this mechanism could be important in oilfield systems where nitrate is applied to prevent sulfide generation by SRB which leads to reservoir souring. In static tests the influence of this Desulfovibrio on corrosion was assessed using carbon steel coupons, in the presence of sulfate and in the presence of sulfate with 100 mg/l nitrate. Corrosion rates were less than 1.5 mpy when coupons were incubated in the same water, with sulfate and with nitrate. Furthermore, the occurrence of pitting corrosion was fairly low under all circumstances.

Avaliação de inibidores verdes microemulsionados na inibição à corrosão do aço carbono AISI 1020

In general, among the corrosion inhibitors surfactants are the most commonly used compounds, because they are significantly effective by forming protective films on anodic and cathodic areas. In this study, microemulsions containing he biodegradable saponified coconut oil as surfactant (SME-OCS) was used as green corrosion inhibitors. With this purpose, methanolic extracts of Ixora coccinea Linn (IC) and a polar fraction rich in alkaloids (FA) obtained from Croton cajucara Benth solubilized in the SME-OCS system were examined in the presence of AISI 1020 carbon steel, in saline solution (NaCl 3,5 %). The efficiency of corrosion inhibition of IC and FA were evaluated in the following microemulsions: SME-OCS-IC and SME-OCS-FA. The microemulsion system SME-OCS in the presence and absence of IC and FA was assessed by measurements of weight loss and the electrochemical method of polarization resistance, with variation in the concentration of IC and FA (50 - 400 ppm), showing significant results of corrosion inhibition (83,6 % SME-OCS; 92,2 % SME-OCS-FA; and 95,3 % SME-OCS-IC)

Utilização de matérias primas vegetais para aplicabilidade como inibidores de corrosão

In the search for products that act as corrosion inhibitors and do not cause environmental, impact the use of plant extracts as corrosion inhibitors is becoming a promising alternative. In this work the efficiency of polar extracts (ethanol extracts) obtained from the plants Anacardium occidentale Linn (AO) and Phyllantus amarus Schum. & Thonn (PA) as corrosion inhibitors were evaluated in different concentrations. For that AO and PA extracts were solubilized in the microemulsion systems (SME) containing saponified coconut oil as surfactant (SME -OCS and SME-OCS-1) in saline (NaCl 3,5 %) solution, which was also used as electrolyte. Both SME-OCS and SME-OCS-1 were characterized by surface tension and viscosity methods showing a Newtonian fluid behavior. The SME-OCS and SME-OCS-1 systems satisfactorily solubilized the polar extracts AO and PA with measurements carried out by ultraviolet spectroscopy. The measurements of corrosion inhibition efficiencies were performed by the electrochemical linear polarization resistance (LPR) technique as well as weight loss, on the surface of AISI 1020 carbon steel. The maximum corrosion inhibition efficiencies were determined by extrapolation of Tafel plots, showing the following values: 95,6 % for the system SME-OCS-AO, 98,9 % for the system SME-OCS-AO-1 and 93,4 % for the system SME-OCS-PA

Avaliação da espécie vegetal Croton cajucara Benth como inibidor de biocorrosão em aço carbono Aisi 1020

Actually in the oil industry biotechnological approaches represent a challenge. In that, attention to metal structures affected by electrochemical corrosive processes, as well as by the interference of microorganisms (biocorrosion) which affect the kinetics of the environment / metal interface. Regarding to economical and environmental impacts reduction let to the use of natural products as an alternative to toxic synthetic inhibitors. This study aims the employment of green chemistry by evaluating the stem bark extracts (EHC, hydroalcoholic extract) and leaves (ECF, chloroform extract) of plant species Croton cajucara Benth as a corrosion inhibitor. In addition the effectiveness of corrosion inhibition of bioactive trans-clerodane dehydrocrotonin (DCTN) isolated from the stem bark of this Croton was also evaluated. For this purpose, carbon steel AISI 1020 was immersed in saline media (3,5 % NaCl) in the presence and absence of a microorganism recovered from a pipeline oil sample. Corrosion inhibition efficiency and its mechanisms were investigated by linear sweep voltammetry and electrochemical impedance. Culture-dependent and molecular biology techniques were used to characterize and identify bacterial species present in oil samples. The tested natural products EHC, ECF and DCTN (DMSO as solvent) in abiotic environment presented respectively, corrosion inhibition efficiencies of 57.6% (500 ppm), 86.1% (500 ppm) and 54.5% (62.5 ppm). Adsorption phenomena showed that EHC best fit Frumkin isotherm and ECF to Temkin isotherm. EHC extract (250 ppm) dissolved in a polar microemulsion system (MES-EHC) showed significant maximum inhibition efficiency (93.8%) fitting Langmuir isotherm. In the presence of the isolated Pseudomonas sp, EHC and ECF were able to form eco-compatible organic films with anti-corrosive properties

FeNbP in ultra-low carbon Nb-added steel containing high P

Precipitation of FeTiP is reported to occur in Ti-added IF steels containing high P during thermomechanical processing. An ultra-low carbon (ULC) Nb-added steel ingot containing a higher P content (< 0.8 wt-%) was produced via aluminothermic reduction of Fe2O3 followed by double electron beam melting (EBM). FeNbP coarse precipitates were observed in the as-cast microstructure. After soaking at 1050C for 1 h, the plate was hot rolled from 31 mm down to 7 mm in thickness (total reduction of 77%). During cold rolling of these hot bands we observed embrittlement. We believe that this embrittlement can be attributed to the presence of the FeNbP precipitates. Light optical and scanning electron microscopy (SEM/EDS) were used to characterize the microstructure of this ULC steel. (C) 2000 Elsevier B.V. All rights reserved.

Obtenção de novos sistemas nanoautoemulsificantes a partir do óleo das sementes de Azadirachta indica A Juss e suas aplicações como inibidores de corrosão

Corrosion is a natural process that causes progressive deterioration of materials, so, reducing the corrosive effects is a major objective of development of scientific studies. In this work, the efficiency of corrosion inhibition on a AISI 1018 carbon steel of the nanoemulsion system containing the oil of the seeds of Azadirachta indica A. Juss (SNEOAI) was evaluated by the techniques of linear polarization resistance (LPR) and weight loss (CPM), a instrumented cell. For that, hydroalcoholic extract of leaves of A. indica (EAI) was solubilized in a nanoemulsion system (SNEOAI) of which O/W system (rich in aqueous phase). This nanoemulsion system (tested in different concentrations) was obtained with oil from the seeds of this plant species (OAI) (oil phase), dodecylammonium chloride (DDAC) (surfactant), butanol (cosurfactant) and water, using 30 % of C/T (cosurfactant/surfactant), 0.5 % of oil phase and 69.5 % of aqueous phase, and characterized by surface tension, rheology and droplet sizes. This systems SNEOAI and SNEOAI-EAI (nanoemulsion containing hydroalcoholic extract - EAI) showed inhibition efficiencies in corrosive environment in saline (1 %), for the method of LPR with significant value of 70.58 % (300 ppm) to SNEOAI, 74.17 % (100 ppm) and 72.51 % (150 ppm) to SNEOAI-EAI. The best efficiencies inhibitions were observed for the method of CPM with 85.41 % for the SNEOAI (300 ppm) and 83.19 % SNEOAI-EAI (500 ppm). The results show that this formulation could be used commercially for use as a corrosion inhibitor, this research contributed to the biotechnological applicability of Azadirachta indica, considering the large use of this plant species rich in limonoids (tetranortriterpenoids), especially azadirachtin

Highly corrosion resistant siloxane-polymethyl methacrylate hybrid coatings

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

SAE 1045 steel/WC-Co/Ni-Cu-Ni/SAE 1045 steel joints prepared by dynamic diffusion bonding: Microelectrochemical studies in 0.6 M NaCl solution

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influence of ethanol, acidity and chloride concentration on the corrosion resistance of AISI 316L stainless steel

The influence of ethanol, sulfuric acid and chloride on the corrosion resistance of 316L stainless steel was investigated by means of polarization curves and electrochemical impedance spectroscopy measurements. Over the studied range, the steel corrosion potential was independent of H2SO 4 and NaCl concentrations in aqueous solution. On the other hand, in solution containing 65 wt.% ethanol and 35 wt.% water, the corrosion potentials were higher than those obtained in aqueous solution. Besides, the steel corrosion potential was affected by the addition of H2SO4 and NaCl in solution. In solutions with and without ethanol, plus 0.35 wt.% NaCl, the presence of 1 wt.% H2SO4 inhibited the appearance of pitting corrosion. © 2013 Sociedade Brasileira de Química.

Fracture propagation and stress corrosion in the case of dissimilar laser hybrid welded joints

The paper addresses the fracture propagation and stress corrosion behaviour of laser hybrid welds achieved between low carbon steel and stainless steel thin sheets. The crack propagation within these overmatched in strength welds was investigated by crack tip opening displacement (CTOD) on CT specimens notched transverse to the weld. A Digital Image Correlation System was used to qualify and estimate the initial crack length obtained by fatigue. The results are associated with the fractographic examinations of various regions of laser hybrid joints. Stress corrosion behaviour of the joint is also discussed.