Solution Polymerization of N-vinylcaprolactam in 1,4-dioxane. Kinetic Dependence on Temperature, Monomer, and Initiator Concentrations

The kinetics of the solution free radical polymerization of N-vinylcaprolactam, in 1,4-dioxane and under various polymerization conditions was studied. Azobisisobutyronitrile and 3-mercaptopropionic acid were used as initiator and as chain transfer agent (CTA), respectively. The influence of monomer and initiator concentrations and polymerization temperature on the rate of polymerizations (R(p)) was investigated. In general, high conversions were obtained. The order with respect to initiator was consistent with the classical kinetic rate equation, while the order with respect to the monomer was greater than unity. The overall activation energy of 53.6 kJ mol(-1) was obtained in the temperature range 60-80 degrees C. The decreasing of the absolute molecular weights when increasing the CIA concentration was confirmed by GPC/SEC/LALS analyses. It was confirmed by UV-visible analyses the effect of molecular weights on the lower critical solution temperature of the polymers. It was also verified that the addition of the CTA influenced the kinetic of the polymerizations. (C) 2010 Wiley Periodicals, Inc. J Appl Polym Sci 118: 229-240, 2010

Obtaining and stability verification of superconducting phases of the Nb-Al and Nb-Sn systems by mechanical alloying and low-temperature heat treatments

The development of Nb(3)Al and Nb(3)Sn superconductors is of great interest for the applied superconductivity area. These intermetallics composites are obtained normally by heat treatment reactions at high temperature. Processes that allow formation of the superconducting phases at lower temperatures (<1000 degrees C), particularly for Nb(3)Al, are of great interest. The present work studies phase formation and stability of Nb(3)Al and Nb(3)Sn superconducting phases using mechanical alloying (high energy ball milling). Our main objective was to form composites near stoichiometry, which could be transformed into the superconducting phases using low-temperature heat treatments. High purity Nb-Sn and Nb-Al powders were mixed to generate the required superconducting phases (Nb-25at.%Sn and Nb-25at.%Al) in an argon atmosphere glove-box. After milling in a Fritsch mill, the samples were compressed in a hydraulic uniaxial press and encapsulated in evacuated quartz tubes for heat treatment. The compressed and heat treated samples were characterized using X-ray diffractometry. Microstructure and chemical analysis were accomplished using scanning electron microscopy and energy dispersive spectrometry. Nb(3)Al XRD peaks were observed after the sintering at 800 degrees C for the sample milled for 30 h. Nb(3)Sn XRD peaks could be observed even before the heat treatment. (C) 2009 Elsevier B.V. All rights reserved.

Thermal expansion of the V(5)Si(3) and T(2) phases of the V-Si-B system investigated by high-temperature X-ray diffraction

The thermal expansion anisotropy of the V(5)Si(3) and T(2)-phase of the V-Si-B system were determined by high-temperature X-ray diffraction from 298 to 1273 K. Alloys with nominal compositions V(62.5)Si(37.5) (V5Si3 phase) and V(63)Si(12)B(25) (T(2)-phase) were prepared from high-purity materials through arc-melting followed by heat-treatment at 1873 K by 24 h, under argon atmosphere. The V(5)Si(3) phase exhibits thermal expansion anisotropy equals to 1.3, with thermal expansion coefficients along the a and c-axis equal to 9.3 x 10(-6) K(-1) and 11.7 x 10(-6) K(-1), respectively. Similarly, the thermal expansion anisotropy value of the T(2)-phase is 0.9 with thermal expansion coefficients equal to 8.8 x 10(-6) K(-1) and 8.3 x 10(-6) K(-1) along the, a and c-axis respectively. Compared to other isostructural silicides of the 5:3 type and the Ti(5)Si(3) phase, the V(5)Si(3) phase presents lower thermal expansion anisotropy. The T(2)-phase present in the V-Si-B system exhibits low thermal expansion anisotropy, as the T(2)-phase of the Mo-Si-B, Nb-Si-B and W-Si-B systems. (C) 2009 Elsevier Ltd. All rights reserved.

Contribution to dynamic characteristics of the cutting temperature in the drilling process considering one dimension heat flow

The machining of hardened steels has always been a great challenge in metal cutting, particularly for drilling operations. Generally, drilling is the machining process that is most difficult to cool due to the tool`s geometry. The aim of this work is to determine the heat flux and the coefficient of convection in drilling using the inverse heat conduction method. Temperature was assessed during the drilling of hardened AISI H13 steel using the embedded thermocouple technique. Dry machining and two cooling/lubrication systems were used, and thermocouples were fixed at distances very close to the hole`s wall. Tests were replicated for each condition, and were carried out with new and worn drills. An analytical heat conduction model was used to calculate the temperature at tool-workpiece interface and to define the heat flux and the coefficient of convection. In all tests using new and worn out drills, the lowest temperatures and decrease of heat flux were observed using the flooded system, followed by the MQL, considering the dry condition as reference. The decrease of temperature was directly proportional to the amount of lubricant applied and was significant in the MQL system when compared to dry cutting. (C) 2011 Elsevier Ltd. All rights reserved.

Effects of temperature at different organic loading levels on the performance of a fluidized-bed anaerobic sequencing batch bioreactor

An investigation was performed on the effect of temperature and organic load on the stability and efficiency of a 1.8-L fluidized-bed anaerobic sequencing batch reactor (ASBR), containing granulated biomass. Assays were carried out employing superficial up How velocity of 7 m/h, total cycle length of 6 h and synthetic wastewater volume of 1.3 L per cycle. The fluidized-bed ASH was operated at 15, 20, 25 and 30 degrees C with influent organic matter concentrations of 500 and 1000 mgCOD/L The system showed stability under all conditions and presented filtered samples removal efficiency ranging from 79 to 86%. A first-order kinetic model could be fitted to the experimental values of the organic matter concentration profiles. The specific kinetic parameter values of this model ranged from 0.0435 to 0.2360 L/(gTVS h) at the implemented operation conditions. in addition, from the slope of an Arrhenius plot, the activation energy values were calculated to be 16,729 and 12,673 cal/mol for operation with 500 and 1000 mgCOD/L, respectively. These results show that treatment of synthetic wastewater. with concentration of 500 mgCOD/L, was more sensitive to temperature variations than treatment of the same residue with concentration of 1000 mgCOD/L. Comparing the activation energy value for operation at 500 mgCOD/L with the value obtained by Agibert et al. (S.A. Agibert, M.B. Moreira, S.M. Ratusznei, J.A.D. Rodrigues, M. Zaiat, E. Foresti. Influence of temperature on performance of an ASBBR with circulation applied to treatment of low-strength wastewater. journal of Applied Biochemistry and Biotechnology, 136 (2007) 193-206) in an ASBBR treating the same wastewater at the same concentration, the value obtained in the fluidized-bed ASBR showed to be superior, indicating that treatment of synthetic wastewater in a reactor containing granulated biomass was more sensitive to temperature variations than the treatment using immobilized biomass. (c) 2008 Elsevier B.V. All rights reserved.

Temperature and feed strategy effects on sulfate and organic matter removal in an AnSBB

The objective of this work was to analyze the interaction effects between temperature, feed strategy and COD/[SO(4)(2-)] levels, maintaining the same ratio, on sulfate and organic matter removal efficiency from a synthetic wastewater. This work is thus a continuation of Archilha et al. (2010) who studied the effect of feed strategy at 30 degrees C using different COD/[SO] ratios and levels. A 3.7-L anaerobic sequencing batch reactor with recirculation of the liquid phase and which contained immobilized biomass on polyurethane foam (AnSBBR) was used to treat 2.0 L synthetic wastewater in 8 h cycles. The temperatures of 15, 22.5 and 30 degrees C with two feed strategies were assessed: (a) batch and (b) batch followed by fed-batch. In strategy (a) the reactor was fed in 10 min with 2 L wastewater containing sulfate and carbon sources. In strategy (b) 1.2 L wastewater (containing only the sulfate source) was fed during the first 10 min of the cycle and the remaining 0.8 L (containing only the carbon source) in 240 min. Based on COD/[SO(4)(2-)] = 1 and on the organic matter (0.5 and 1.5 gCOD/L) and sulfate (0.5 and 1.5 gSO(4)(2-)/L) concentrations, the sulfate and organic matter loading rates applied were 1.5 and 4.5 g/L.d, i.e., same COD/[SO(4)(2-)] ratio (=1) but different levels (1.5/1.5 and 4.5/4.5 gCOD/gSO(4)(2-)). When reactor feed was 1.5 gCOD/L.d and 1.5 gSO(4)(2-)/L.d, gradual feeding (strategy b) showed to favor sulfate and organic matter removal in the investigated temperature range, indicating improved utilization of the electron donor for sulfate reduction. Sulfate removal efficiencies were 87.9; 86.3 and 84.4%, and organic matter removal efficiencies 95.2; 86.5 and 80.8% at operation temperatures of 30; 22.5 and 15 degrees C, respectively. On the other hand, when feeding was 4.5 gCOD/L.d and 4.5 gSO(4)(2-)/L.d, gradual feeding did not favor sulfate removal, indicating that gradual feeding of the electron donor did not improve sulfate reduction. (C) 2011 Elsevier Ltd. All rights reserved.

Influence of chloride ion concentration and temperature on the electrochemical properties of passive films formed on a superduplex stainless steel

Polarization measurements were conducted to monitor the corrosion behavior of superduplex stainless steel ASTM A995M-Gr.SA/EN 10283-Mat#1.4469(GX2CrNiMo26-7-4) when exposed to a) an electrolyte containing 22,700 parts per million (ppm) of chloride ions at seven different temperatures and b) an electrolyte at 25 GC and different chloride ion concentrations (5800, 22,700, 58,000 and 80,000 ppm of Cl(-)). The polarization curves indicate that the passive films formed are only slightly affected by NaCl concentration, but the pitting potential decreases drastically increasing the temperature, in particular >60 degrees C. The image analysis of the microstructure after potentiodynamic polarization showed that the pitting number and size vary in function of the temperature of the tested medium. Nyquist diagrams were determined by electrochemical impedance spectroscopy to characterize the resistance of the passive layer. According to Nyquist plots, the arc polarization resistance decreases increasing the temperature due to a catalytic degradation of the oxide passive films. (C) 2009 Elsevier Inc. All rights reserved.

Porous alumina-spinel ceramics for high temperature applications

In order to reduce energy costs, high-temperature insulation porous refractory ceramics have been subjected to increasing demands. Among the techniques used to produce these materials (such as the addition of foaming agents and organic compounds), the pore generation via phase transformation presents key aspects, such as easy processing and the absence of toxic volatiles. In this study, this technique was applied to produce porous ceramics by decomposing an aluminum magnesium hydro-carbonate known as hydrotalcite (Mg(6)Al(2)(CO(3))(OH)(16)center dot 4H(2)O). It was found out that by using this complex compound, a large fraction of pores can be generated and kept at high temperatures (above 1300 degrees C) due to the in situ formation of spinel-like phases (MgAl(2)O(4)). (C) 2011 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Structure and properties of low temperature plasma carburized austenitic stainless steels

Austenitic stainless steels cannot be conventionally surface treated at temperatures close to 550 degrees C due to intense precipitation of nitrides or carbides. Plasma carburizing allows introducing carbon in the steel at temperatures below 500 degrees C without carbide precipitation. Plasma carburizing of AISI 316L was carried out at 480 degrees C and 400 degrees C, during 20 h, using CH(4) as carbon carrier gas. The results show that carbon expanded austenite (gamma(c)), 20 mu m in depth, was formed on the surface after the 480 degrees C treatment. Carbon expanded austenite (gamma(c)), 8 mu m in depth, was formed on the surface after the 400 degrees C treatment. DRX results showed that the austenitic FCC lattice parameter increases from 0.358 nm to 0.363 nm for the 400 degrees C treatment and to 0.369 nm for the 480 degrees C treatment, giving an estimation of circa 10 at.% carbon content for the latter. Lattice distortion, resulting from the expansion and the associated compressive residual stresses increases the surface hardness to 1040 HV(0.025). Micro-scale tensile tests were conducted on specimens prepared with the conditions selected above, which has indicated that the damage imposed to the expanded austenite layer was more easily related to each separated grain than to the overall macro-scale stresses imposed by the tensile test. (C) 2009 Elsevier B.V. All rights reserved.

Tempering temperature effects on abrasive wear of mottled cast iron

The effects of different tempering temperatures (300-600 degrees C) on abrasive wear resistance of mottled cast iron were studied. Abrasive wear tests were carried out using the rubber-wheel test on quartz sand and the pin test on Al(2)O(3) abrasive cloths. The retained austenite content of the matrix was determined by X-ray diffraction. The wear surface of the specimens was examined by scanning electron microscopy for identifying the wear micromechanism. Bulk hardness and matrix hardness before and after the tests were measured. The results showed that in the two-body (pin-on-disc test) system, the main wear mechanism was microcutting and high matrix hardening was presented. The wear rates presented higher correlation with the retained austenite than with the bulk and matrix hardness. In the three-body system (sand-rubber wheel), the wear surfaces presented indentations due to abrasive rolling. The wear rates had better correlation with both the bulk and matrix hardness (before and after the wear test) than with the retained austenite content. There are two groups of results, high and low wear rates corresponding to each tribosystem, two-body abrasive wear and three-body abrasive wear, respectively. (C) 2009 Elsevier B.V. All rights reserved.

Comparison between DC(+) and Square Wave AC SAW Current Outputs to Weld AISI 304 for Low-Temperature Applications

Welded equipment for cryogenic applications is utilized in chemical, petrochemical, and metallurgical industries. One material suitable for cryogenic application is austenitic stainless steel, which usually doesn`t present ductile/brittle transition temperature, except in the weld metal, where the presence of ferrite and micro inclusions can promote a brittle failure, either by ferrite cleavage or dimple nucleation and growth, respectively. A 25-mm- (1-in.-) thick AISI 304 stainless steel base metal was welded with the SAW process using a 308L solid wire and two kinds of fluxes and constant voltage power sources with two types of electrical outputs: direct current electrode positive and balanced square wave alternating current. The welded joints were analyzed by chemical composition, microstructure characterization, room temperature mechanical properties, and CVN impact test at -100 degrees C (-73 degrees F). Results showed that an increase of chromium and nickel content was observed in all weld beads compared to base metal. The chromium and nickel equivalents ratio for the weld beads were always higher for welding with square wave AC for the two types of fluxes than for direct current. The modification in the Cr(eq)/Ni(eq) ratio changes the delta ferrite morphology and, consequently, modifies the weld bead toughness at lower temperatures. The oxygen content can also affect the toughness in the weld bead. The highest absorbed energy in a CVN impact test was obtained for the welding condition with square wave AC electrical output and neutral flux, followed by DC(+) electrical output and neutral flux, and square wave AC electrical output and alloyed flux.

Influence of Water Content, Time, and Temperature on the Rheological Behavior of Polyethylene Terephtalate

In this work, the main factors affecting the rheological behavior of polyethylene terephtalate (PET) in the linear viscoelastic regime (water content, time delay before test, duration of experiment, and temperature) were accessed. Small amplitude oscillatory shear tests were performed after different time delays ranging from 300 to 5000 s for samples with water contents ranging from 0.02 to 0.45 wt %. Time sweep tests were carried out for different durations to explain the changes undergone by PET before and during small amplitude oscillatory shear measurements. Immediately after the time sweep tests, the PET samples were removed from the rheometer, analyzed by differential scanning calorimetry and their molar mass was obtained by viscometry analysis. It was shown that for all the samples, the delay before test and residence time within the rheometer (i.e. duration of experiment) result in structural changes of the PET samples, such as increase or decrease of molar mass, broadening of molar mass distribution, and branching phenomena. (C) 2010 Wiley Periodicals, Inc. J Appl Polym Sci 116: 3525-3533, 2010

High temperature flexural strength and fracture toughness of AlN with Y(2)O(3) ceramic

The effects of temperature on the fast fracture behavior of aluminum nitride with 5 wt% Y(2)O(3) ceramic were investigated. Four-point flexural strength and fracture toughness were measured in air at several temperatures (30-1,300 A degrees C). The flexural strength gradually decreased with the increase of temperature up to 1,000 A degrees C due to the change in the fracture mode from transgranular to intergranular, and then became almost constant up to 1,300 A degrees C. Two main flaw types as fracture origin were identified: small surface flaw and large pores. The volume fraction of the large pores was only 0.01%; however, they limited the strength on about 50% of the specimens. The fracture toughness decreased slightly up to 800 A degrees C controlled by the elastic modulus change, and then decreased significantly at 1,000 A degrees C due to the decrease in the grain-boundary toughness. Above 1,000 A degrees C, the fracture toughness increased significantly, and at 1,300 A degrees C, its value was close to that measured at room temperature.

Study on Iron Formation During the Carbothermic Reduction of Iron Ore in Carbon Composite Pellets in the Temperature Range 1423 K-1623 K

The aim of this work is to study the reaction rate and the morphology of the intermediary reaction products during reduction of iron ore, when iron ore and carbonaceous material are agglomerated together as a carbon composite iron ore pellet. The reaction was performed at high temperatures, and in order to avoid heat transfer constraints small size samples were used. The carbonaceous materials employed were coke breeze and pure graphite. Portland cement was employed as a binder, and the pellets diameter was 5.2 mm. The experimental technique involved the measurement of the pellets weight loss, as well as interruption of the reaction at different stages in order to submit the partially reduced pellet to scanning electron microscopy. It has been observed that above 1523 K there is the formation of liquid slag inside the pellets, which partially dissolves iron oxides. The apparent activation energies obtained were 255 kJ/mol for coke breeze containing pellets, and 230 kJ/mol for those pellets containing graphite. It was possible to avoid heat transfer control of the reaction rate up to 1523 K by employing small composite pellets.

Influence of Temperature, Basiscity and Particle Size on MnO Reduction

The aim of this work is to study MnO reduction by solid carbon. The influence of size of carbon particles, slag basicity, and bath temperature on MnO reduction was investigated. Fine Manganese ore particles were used as a source of MnO. Three sizes of carbon particles were used; 0.230 mm, 0.162 mm and 0.057 mm, binary basicity of 1 and 1.5 and temperatures of 1550, 1550 and 1600 degrees C. Curves were drawn for Mn content in the bath as a function of time and temperature for the several studied parameters. The MnO reduction rates were determined using these data. [doi:10.2320/matertrans.M2011007]