Facile preparation of ZnTiO3 ceramic powders in sodium/potassium chloride melts

A facile molten salt synthesis route was developed to prepare ZnTiO3 ceramic powders with simple oxides ZnO and TiO2 using sodium and potassium chloride eutectic salts as flux. The role of calcination temperature and time and the amount of salt addition to ZnTiO3 formation was investigated by thermogravimetry-differential thermal analysis, X-ray diffraction and Fourier transformation-infrared spectroscopy measurements. Pure hexagonal phase of ZnTiO3 could be obtained from the mixture of the simple oxides and the chlorides (50 mol% KCl, 20 times to oxides in molar ratio) heating at 800 degrees C for 6 h. The scanning electron microscopy images revealed the products were hexagonal sheets of about 1-3 mu m size. Increasing the amount of salt aids in reducing the crystal sizes of final ceramic powders because of diluting the solution.

Synthesis of nanocrystalline Ba(CoxZn1-x)(2)Fe16O27 by sol-gel auto-combustion method

The synthesis of nanocrystalline W-type hexaferrites Ba(CoxZn1-x)(2)Fe16O27 powders by sol-gel auto-combustion method has been investigated. The thermal decomposition process of dried gel was studied by thermogravimetry (TG), differential thermal analysis (DTA) and infrared spectra (IR). The structural and magnetic properties of resultant particles were investigated by X-ray diffraction (XRD), transmission electron microscope (TEM), and vibrating sample magnetometer (VSM). The results reveal that the dried gel exhibits auto-combustion behavior. After combustion, pure nanocrystalline W-type hexaferrite phase starts to appear at the calcination temperature of 800 degrees C. The crystallinity and the grain size increase at higher temperature. The saturation magnetization and coercivity clearly depend on calcination temperature and Co content X.

Thermal stability of double-ceramic-layer thermal barrier coatings with various coating thickness

Double-ceramic-layer (DCL) coatings with various thickness ratios composed of YSZ (6-8 wt.% Y2O3 + ZrO2) and lanthanum zirconate (LZ, La2Zr2O7) were produced by the atmospheric plasma spraying. Chemical stability of LZ in contact with YSZ in DCL coatings was investigated by calcining powder blends at different temperatures. No obvious reaction was observed when the calcination temperature was lower than 1250 degrees C, implying that LZ and YSZ had good chemical applicability for producing DCL coating. The thermal cycling test indicate that the cycling lives of the DCL coatings are strongly dependent on the thickness ratio of LZ and YSZ, and the coatings with YSZ thickness between 150 and 200 mu m have even longer lives than the single-layer YSZ coating. When the YSZ layer is thinner than 100 mu m, the DCL coatings failed in the LZ layer close to the interface of YSZ layer and LZ layer. For the coatings with the YSZ thickness above 150 mu m, the failure mainly occurs at the interface of the YSZ layer and the bond coat.

Preparation and characterization of nanocrystalline CeO2 by precipitation method

CeO2 nanocrystalline particulates with different sizes were prepared by precipitation method using ethanol as dispersive and protective reagent. XRD spectra show that the synthesized CeO2 has cubic crystalline structure of space group O-H(5)-F-M3M, when calcination temperature is in the range of 250 similar to 800 degreesC. TEM images reveal that CeO2 particles are spherical in shape. The average size of the particles increases with the increase of calcination temperature. Thermogravimetric analysis indicates that the weight loss of precursor mainly depends on the calcination temperature, and little depends on the calcination time. Measurements of CeO2 relative density show that the relative density of CeO2 nanocrystalline powders increases with increasing CeO2 particle size.

焙烧温度对CeO2改性Pd/Al2O3甲醇分解催化剂性能的影响

中国科学院山西煤炭化学研究所

Nanocrystalline SnO2 synthesised by means of hydrothermal precipitation

Nanocrystalline SnO2 with different particle sizes has been prepared by means of hydrothermal precipitation. The resulting SnO2 nanometer size powders, which are basically spherical in shape according to TEM, are tetragonal in structure with space group P4/mnm. Calculation shows that the crystallite size of SnO2 increases with increase of the calcination temperature, but that the average crystal lattice distortion rate decreases with increase of crystallite size. The smaller the particle, the bigger the crystal lattice distortion and the slower the crystal growth rate. Weight loss analysis indicates the prepared SnO2 is very slightly impure.

Preparation and properties of nanocrystalline Yb2O3

Nanocrystalline Yb2O3 of various particle sizes was prepared using sol-gel method. XRD analysis shows that the prepared nanocrystalline Yb2O3 is cubic in structure with space group Ia3. TEM photographs indicate that Yb2O3 nanoparticles are basically spherical in shape. Calculation of crystallite size indicates that the average crystallite size of Yb2O3 increases with increasing calcination temperature, but the average crystal lattice distortion rate decreases with increasing calcination temperature and crystallite size. This result shows that the smaller the crystallite size, the bigger the crystal lattice distortion, and the worse crystal growth. Solubility test of Yb2O3 in nitric acid shows that the surface activity of Yb2O3 increases with decreasing crystallite size. Fourier Transform Infrared Spectrometer (FTIR) spectra reveal that nanocrystalline Yb2O3 has higher surface activity; than that of ordinary Yb2O3. Absorbance intensity of Yb-O bond of nanocrystalline Yb2O3 is weaker than that of ordinary Yb2O3, and the absorbance of Yb-O bond of nanocrystalline Yb2O3 is small blue-shifted.

Catalytic reduction of NO by CO with hydrotalcite derived mixed oxides

Catalysts with spinel structure derived from Hydrotalcite-like Compounds (HTLcs) containing cobalt have been investigated in NO catalytic reduction by Co. It was found that catalysts with spinel structures derived from HTLcs had obviously higher activity than that prepared from general methods. A two-step reaction was observed during the reaction curse: NO was first reduced to N2O by Co, and with the increase of temperature, the N2O was reduced to N-2. The reactivity of the catalysts studied increased with the amount of cobalt-content in the catalyst, and decreased with the calcination temperature. The crystal defect would play an important role in the reaction.

Synthesis and properties of cerium oxide nanometer powders by pyrolysis of amorphous citrate

CeO2 nanometer powders of different sizes were prepared at low temperature by pyrolysis of amorphous citrate. XRD patterns show that CeO2 is cubic in structure, space group O-h(5)-F-M3M. TEM indicates that the prepared CeO2 is spherical in shape, and the particle size distribution is in narrow range. It was found that calcination temperature is a more important factor affecting the crystallite size of CeO2 than calcining time, the smaller the particle, the bigger the crystal lattice distortion, the worse the crystal growth. Solubility test of CeO2 in nitric acid reveals that the surface activity of CeO2 decreases with the increasing particle sizes. IR spectra analysis shows that the absorption of Ce-O bond is shifted to higher energy with the decrease of CeO2 particle sizes.

Easy fabrication of dense ceramic membrane for oxygen separation

A combined EDTA-citrate complexing method was developed for the easy preparation of mixed oxygen-ionic and electronic conducting dense ceramic membrane for oxygen separation. The nea method takes the advantage of lower calcination temperature for phase formation. lower membrane sintering temperature and higher relative density over the standard ceramic method.

Structure and base properties of calcined hydrotalcites

Five hydrotalcites with Mg/Al molar ratio range of 3-15 were prepared. The structure and basicity of Mg-Al mixed oxides (Mg(Al)O) transformed from hydrotalcites were investigated by TPD, XPS, XRD, FT-IR and NMR techniques. The results of elemental analysis and XPS indicate that Al is enriched in the surface regions of Mg(Al)O, and its amount increases with the Mg/Al molar ratio and, the calcination temperature. Al-27-MAS-NMR results show that Al exists in two chemical environments: tetrahedral aluminium (Al(t)) and octahedral aluminium (Al(o)) in Mg(AI)O. The amount of Al(t) increases with the Mg/Al molar ratio and the calcination temperature. It is assumed that Al(t) may be mainly from the surface Al. Temperature-programmed desorption (TPD) of CO2 shows that the number of basic sites of Mg(Al)O samples increases with the Mg/Al molar ratio, and the maximum number of basic sites is obtained for hydrotalcite calcined at 773 K. Infrared spectra of adsorbed CO2 and B(OCH3)(3) reveal that there are two kinds of basic sites: weak basic OH- sites and strong basic O2- sites on the Mg(AI)O samples, the base strength depends on the Mg/Al molar ratio and calcination temperature.

A novel process for converting coalmine-drained methane gas to syngas over nickel-magnesia solid solution catalysts

A novel process is developed in this paper for utilizing the coalmine-drained methane gas that is usually vented straight into the atmosphere in most coalmines worldwide. It is expected that low-cost syngas can be produced by the combined air partial oxidation and CO2 reforming of methane, because this process utilizes directly the methane, air, and carbon dioxide in the coalmine-drained gas without going through the separation step. For this purpose, a nickel-magnesia solid solution catalyst was prepared and its catalytic performance for the proposed process was investigated. It was found that calcination temperature has significant influence on the catalytic performance due to the different extent of solid solution formation in the catalysts. A uniform nickel-magnesia solid solution catalyst exhibits higher stability than the catalysts in which NiO has not completely formed solid solution with MgO. Its catalytic activity and selectivity remain stable during 120 h of reaction. The product H-2/CO ratio is mainly dependent on the feed gas composition. By changing CO2/air ratio of the feed gases, syngas with a H-2/CO ratio between 1 and 1.9 can be obtained. The influences of reaction temperature and nickel loading on the catalytic performance were also investigated. (c) 2004 Elsevier B.V All rights reserved.

Factors influencing the catalytic activity of SBA-15-supported copper nanoparticles in CO oxidation

Copper nanoparticles were deposited onto mesoporous SBA-15 support via two different routes: post-grafting method and incipient wet impregnation method. Both XRD and TEM reveal that the post-grafting can make Cu particles very small in size and highly dispersed into channels of SBA-15, while the impregnation method mainly forms large Cu particles on the external surface of SBA-15. TPR experiments show that CuO species formed by the post-grafting method is more reducible than that prepared by the impregnation method. The catalytic activity tests for CO oxidation manifests that the sample prepared by the post-grafting method has a much higher activity than that prepared by the impregnation method, with a lowering of 50 degrees C for T-50, showing a strong dependence of catalytic activity on the size and dispersion of Cu particles. Besides the preparation procedure, other factors including calcination temperature, reduction treatment, copper loading as well as the feed composition, have an important effect on the catalytic activity. The best performance was obtained when the catalyst was calcined at 500 degrees C and reduced at 550 degrees C. The calcination and reduction treatment at high temperature have been found to be necessary to completely remove the organic residue and to generate active metallic copper particles. (c) 2005 Elsevier B.V. All rights reserved.

Structural investigations and magnetic properties of sol-gel Ni0.5Zn0.5Fe2O4 thin films for microwave heating

Nanocrystalline Ni0.5Zn0.5Fe2O4 thin films have been synthesized with various grain sizes by a sol-gel method on polycrystalline silicon substrates. The morphology, magnetic, and microwave absorption properties of the films calcined in the 673-1073 K range were studied with x-ray diffraction, scanning electron microscopy, x-ray photoelectron spectroscopy, atomic force microscopy, vibrating sample magnetometry, and evanescent microwave microscopy. All films were uniform without microcracks. Increasing the calcination temperature from 873 to 1073 K and time from 1 to 3 h resulted in an increase of the grain size from 12 to 27 nm. The saturation and remnant magnetization increased with increasing the grain size, while the coercivity demonstrated a maximum near a critical grain size of 21 nm due to the transition from monodomain to multidomain behavior. The complex permittivity of the Ni-Zn ferrite films was measured in the frequency range of 2-15 GHz. The heating behavior was studied in a multimode microwave cavity at 2.4 GHz. The highest microwave heating rate in the temperature range of 315-355 K was observed in the film close to the critical grain size.

Transformation of vaterite into calcite in the absence and the presence of copper(II) species. Thermal analysis, IR and EPR study

The transformation of vaterite into calcite may be performed by heating in the presence and the absence of oxygen. Vaterite remains thermally stable until a calcination temperature of 450°C. It transforms progressively to calcite up to 500°C giving two exothermic peaks: 1) at 481°C due to the transformation of vaterite surface which is in contact with a small amount of calcite phase already formed with the time on the solid surface from the humidity atmosphere; 2) at 491°C due to the transformation of pure vaterite bulk. The calcite phase remains stable until 700°C. Above this temperature the formation of CaO is observed.