Electronic structure origin of conductivity and oxygen reduction activity changes in low-level Cr-substituted (La, Sr)MnO3

The electronic structure of the (La0.8Sr0.2)(0.98)Mn1-xCrxO3 model series (x = 0, 0.05, or 0.1) was measured using soft X-ray synchrotron radiation at room and elevated temperature. O K-edge near-edge X-ray absorption fine structure (NEXAFS) spectra showed that low-level chromium substitution of (La, Sr)MnO3 resulted in lowered hybridisation between O 2p orbitals and M 3d and M 4sp valance orbitals. Mn L-3-edge resonant photoemission spectroscopy measurements indicated lowered Mn 3d-O 2p hybridisation with chromium substitution. Deconvolution of O K-edge NEXAFS spectra took into account the effects of exchange and crystal field splitting and included a novel approach whereby the pre-peak region was described using the nominally filled t(2g) up arrow state. 10% chromium substitution resulted in a 0.17 eV lowering in the energy of the t(2g) up arrow state, which appears to provide an explanation for the 0.15 eV rise in activation energy for the oxygen reduction reaction, while decreased overlap between hybrid O 2p-Mn 3d states was in qualitative agreement with lowered electronic conductivity. An orbital-level understanding of the thermodynamically predicted solid oxide fuel cell cathode poisoning mechanism involving low-level chromium substitution on the B-site of (La, Sr)MnO3 is presented. (C) 2015 AIP Publishing LLC.

Room temperature ferromagnetism and white light emissive CdS:Cr nanoparticles synthesized by chemical co-precipitation method

Undoped and Cr (3% and 5%) doped CdS nanoparticles were synthesized by chemical co-precipitation method. The synthesized nanocrystalline particles are characterized by energy dispersive X-ray analysis (EDAX), scanning electron microscope (SEM), X-ray Diffraction (XRD), transmission electron microscopy (TEM), diffuse reflectance spectroscopy (DRS), photoluminescence (PL), Electron paramagnetic resonance (EPR), vibrating sample magnetometer (VSM) and Raman spectroscopy. XRD studies indicate that Cr doping in host CdS result a structural change from Cubic phase to mixed (cubic + hexagonal) phase. Due to quantum confinement effect, widening of the band gap is observed for undoped and Cr doped CdS nanoparticles compared to bulk CdS. The average particle size calculated from band gap values is in good agreement with the TEM study calculation and it is around 4-5 nm. A strong violet emission band consisting of two emission peaks is observed for undoped CdS nanoparticles, whereas for CdS:Cr nanoparticles, a broad emission band ranging from 420 nm to 730 nm with a maximum at similar to 587 nm is observed. The broad emission band is due to the overlapped emissions from variety of defects. EPR spectra of CdS:Cr samples reveal resonance signal at g = 2.143 corresponding to interacting Cr3+ ions. VSM studies indicate that the diamagnetic CdS nanoparticles are transform to ferromagnetic for 3% Cr3+ doping and the ferromagnetic nature is diminished with increasing the doping concentration to 5%. (C) 2015 Elsevier B.V. All rights reserved.

Nonequilibrium microstructures and their evolution in a Fe-Cr-W-Ni-C laser clad coating

The laser-solidified microstructural and compositional characterization and phase evolution during tempering at 963 K were investigated using an analytical transmission electron microscope with energy dispersive X-ray analysis. The cladded alloy, a powder mixture of Fe, Cr, W, Ni, and C with a weight ratio of 10:5:1:1:1, was processed with a 3 kW continuous wave CO2 laser. The processing parameters were 16 mm/s beam scanning speed, 3 mm beam diameter. 2 kW laser power, and 0.3 g/s feed rate. The coating was metallurgically bonded to the substrate, with a maximum thickness of 730 mu m, a microhardness of about 860 Hv and a volumetric dilution ratio of about 6%. Microanalyses revealed that the cladded coating possessed the hypoeutectic microstructure comprising the primary dendritic gamma-austenite and interdendritic eutectic consisted of gamma-austenite and M7C3 carbide. The gamma-austenite was a non-equilibrium phase with extended solid solution of alloying elements and a great deal of defect structures, i.e. a high density of dislocations, twins, and stacking faults existed in gamma phase. During high temperature aging, in situ carbide transformation occurred of M7C3 to M23C6 and M6C. The precipitation of M23C6, MC and M2C carbides from austenite was also observed.

铁基抗高温磨损激光熔覆涂层强韧设计和研究II:Fe-Cr-C-W-Ni激光熔覆层的微观组织及性能

本文以对热工模具进行失效分析的基础上，利用激光熔覆技术，在５ＣｒＭｎＭｏ基础上设计并制备强韧兼备的抗高温磨损涂层。

MATLAB在Cr涂层微裂纹组态分析中的应用

镀Cr身管在使用时普遍存在涂层剥落问题.本文结合我国某新型号机枪枪管的研制工艺,对涂层微裂纹组态、控制因素及其与破坏模式的关系进行研究.鉴于微裂纹的纳米级宽度,本文通过特殊的金相制样方法将其扩宽,从而得到反映微裂纹组态的低倍照片.应用MATLAB对微裂纹特征进行统计分析,得出微裂纹密度、长度等特征参数与涂层失效模式间的对应关系,同时证实基体激光离散预处理对微裂纹组态有控制作用.

Measurement Of Fracture Toughness And Interfacial Shear Strength Of Hard And Brittle Cr Coating On Ductile Steel Substrate

The fracture toughness and interfacial adhesion properties of a coating on its substrate are considered to be crucial intrinsic parameters determining performance and reliability of coating-substrate system. In this work, the fracture toughness and interfacial shear strength of a hard and brittle Cr coating on a normal medium carbon steel substrate were investigated by means of a tensile test. The normal medium carbon steel substrate electroplated with a hard and brittle Cr coating was quasi-statically stretched to induce an array of parallel cracks in the coating. An optical microscope was used to observe the cracking of the coating and the interfacial decohesion between the coating and the substrate during the loading. It was found that the cracking of the coating initiated at critical strain, and then the number of the cracks of the coating per unit axial distance increased with the increase in the tensile strain. At another critical strain, the number of the cracks of the coating became saturated, i.e. the number of cracks per unit axial distance became a constant after this critical strain. Based on the experiment result, the fracture toughness of the brittle coating can be determined using a mechanical model. Interestingly, even when the whole specimen fractured completely under an extreme strain of the substrate, the interfacial decohesion or buckling of the coating on its substrate was completely absent. The test result is different from that appeared in the literature though the identical test method and the brittle coating/ductile metal substrate system are taken. It was found that this difference can be attributed to an important mechanism that the Cr coating on the steel substrate has a good adhesion, and the ultimate interfacial shear strength between the Cr coating and the steel substrate has exceeded the maximum shear flow strength level of the steel substrate. This result also indicates that the maximum shear flow strength level of the ductile steel substrate can be only taken as a lower bound estimate on the ultimate shear strength of the interface. This estimation of the ultimate interfacial shear strength is consistent with the theoretical analysis and prediction presented in the literature.

Quantum Monte Carlo study of the CO interaction with a dimer model surface for Cr(110)

The chemisorption of CO on a Cr( 110) surface is investigated using the quantum Monte Carlo method in the diffusion Monte Carlo (DMC) variant and a model Cr2CO cluster. The present results are consistent with the earlier ab initio HF study with this model that showed the tilted/ near-parallel orientation as energetically favoured over the perpendicular arrangement. The DMC energy difference between the two orientations is larger (1.9 eV) than that computed in the previous study. The distribution and reorganization of electrons during CO adsorption on the model surface are analysed using the topological electron localization function method that yields electron populations, charge transfer and clear insight on the chemical bonding that occurs with CO adsorption and dissociation on the model surface.

铁基抗高温磨损激光熔覆涂层强韧设计和研究 Ⅱ:Fe-Cr-C-W-Ni激光熔覆层的微观组织及性能

利用ＯＭ、ＳＥＭ、ＴＥＭ研究了Ｆｅ－Ｃｒ－Ｃ－Ｗ－Ｎｉ激光熔覆涂层熔覆态及其高温时效态的微观组织结构。结果表明激光熔覆层组织细小，具有强韧两相组成（奥氏体和Ｍ_７Ｃ_３碳化物）的微观结构特征，高温时效处理组织中有Ｍ_（２３）Ｃ_６、Ｍ_６Ｃ、Ｍ_２Ｃ等新碳化物形成。显微硬度和冲击磨损实验证实了激光熔覆态和峰值时效态熔覆层均具有良好的力学性能。

MATLAB在Cr涂层微裂纹组态分析中的应用

镀Cr身管在使用时普遍存在涂层剥落问题。本文结合我国某新型号机枪枪管的研制工艺,对涂层微裂纹组态、控制因素及其与破坏模式的关系进行研究。鉴于微裂纹的纳米级宽度,本文通过特殊的金相制样方法将其扩宽,从而得到反映微裂纹组态的低倍照片。应用MATLAB对微裂纹特征进行统计分析,得出微裂纹密度、长度等特征参数与涂层失效模式间的对应关系,同时证实基体激光离散预处理对微裂纹组态有控制作用。

P-选择素CR结构域功能的模拟预测

国家自然科学基金项目(10702075/30730032)

Development And Characterization Of Composite Ni-Cr-C-Caf2 Laser Cladding On Gamma-Tial Intermetallic Alloy

A process of laser cladding Ni-CF-C-CaF2 mixed powders to form a multifunctional composite coatingd on gamma-TiAl substrate was carried out. The microstructure of the coating was examined using XRD, SEM and EDS. The coating has a unique microstructure consisting of primary dendrite or short-stick TiC and block Al4C3 carbides reinforcement as well as fine isolated spherical CaF2 solid lubrication particles uniformly dispersed in the NiCrAlTi (gamma) matrix. The average microhardness of the composite coatings is approximately HV 650 and it is 2-factor greater than that of the TiAl substrate. (C) 2008 Elsevier B.V. All rights reserved.

Absorption characteristic and nonvolatile holographic recording in LiNbO3 : Cr : Cu crystals

The absorption characteristic of lithium niobate crystals doped with chromium and copper (Cr and Cu) is investigated. We find that there are two apparent absorption bands for LiNbO3:Cr:Cu crystal doped with 0.14 wt.% Cr2O3 and 0.011 wt.% CuO; one is around 480 nm, and the other is around 660 nm. With a decrease in the doping composition of Cr and an increase in the doping composition of Cu, no apparent absorption band in the shorter wavelength range exists. The higher the doping level of Cr, the larger the absorbance around 660 nm. Although a 633 nm red light is located in the absorption band around 660 nm, the absorption at 633 nm does not help the photorefractive process; i.e., unlike other doubly doped crystals, for example, LiNbO3:Fe:Mn crystal, a nonvolatile holographic recording can be realized by a 633 nm red light as the recording light and a 390 nm UV light as the sensitizing light. For LiNbO3:Cr:Cu crystals, by changing the recording light from a 633 nm red light to a 514 nm green light, sensitizing with a 390 nm UV light and a 488 nm blue light, respectively, a nonvolatile holographic recording can be realized. Doping the appropriate Cr (for example, N-Cr = 2.795 X 10(25)m(-3) and N-Cr/N-Cu = 1) benefits the improvement of holographic recording properties. (c) 2005 Optical Society of America.

LiNbO3：Cr：Cu晶体吸收特性及非挥发全息存储研究

研究了LiNbO3：Cr：Cu晶体的吸收特性，发现LiNbO3：Cr：Cu（含0．14wt．％Cr2O3和0．011wt．％CuO）晶体存在两个明显的吸收峰，中心波长分别位于480nm和660nm；随着Cr的含量逐渐减小，Cu的含量逐渐增大，短波段不存在明显吸收峰，掺Cr的含量越大，中心波长在660nm处的吸收越大；633nm红光虽然位于中心波长为660nm的吸收峰内，但它无助于光折变过程．分别采用390nm紫外光和488nm蓝光作为敏化光，514nm绿光作为记录光的记录方案，实现了非挥发全息记录，掺入适