Resin bonding to root canal dentin: Effect of the application of an experimental hydrophobic resin coating after an all-in-one adhesive

Aim: Based on the hypothesis the application of a low-viscosity hydrophobic resin coating improves the bond of all-in-one adhesive, the purpose of the study was to evaluate the bond strength of four adhesive systems to bovine root dentin using the push-out test method. Methods and Materials: The root canals of 32 bovine roots (16 mm) were prepared to a length of 12 mm using a FRC Postec Plus preparation drill. The specimens were allocated into four groups according to the adhesive system used: (Group 1) All-in-one Xeno III; (Group 2) All-in-one Xeno III+ScotchBond Multi-Purpose Plus Adhesive; (Group 3) Simplified Etch & Rinse One Step Plus; and (Group 4) Multi-Bottle Etch & Rinse All-Bond 2. A fiber-reinforced composite retention post was reproduced using an additional silicon impression and fabricated with DuoLink resin cement. The root specimens were treated with the selected adhesive systems, and the resin posts were luted in the canals with DuoLink resin cement. Each root specimen was cross sectioned into four samples (±1.8 mm in thickness), and the post sections were pushed-out to determine the bond strength to dentin. Results: Group 2 (2.9±1.2) was statistically higher than Group 1 (1.1±0.5) and Group 3 (1.1±0.5). Groups 1 and 3 showed no statistically significant difference while Group 4 (2.0±0.7) presented similar values (p>0.05) to Groups 1, 2, and 3 [(one-way analysis of variance (ANOVA)] and Tukey test, α=0.05). Conclusion: The hypothesis was accepted since the application of the additional layer of a low-viscosity bonding resin improved the bond of the all-in-one adhesive. Further studies must be conducted to evaluate the long-term bond.

Influence of voids in the hybrid layer based on self-etching adhesive systems: a 3-D FE analysis

The presence of porosities at the dentin/adhesive interface has been observed with the use of new generation dentin bonding systems. These porosities tend to contradict the concept that etching and hybridization processes occur equally and simultaneously. Therefore, the aim of this study was to evaluate the micromechanical behavior of the hybrid layer (HL) with voids based on a self-etching adhesive system using 3-D finite element (FE) analysis. Three FE models (Mr) were built: Mr, dentin specimen (41x41x82 μm) with a regular and perfect (i.e. pore-free) HL based on a self-etching adhesive system, restored with composite resin; Mp, similar to M, but containing 25% (v/v) voids in the HL; Mpp, similar to Mr, but containing 50% (v/v) voids in the HL. A tensile load (0.03N) was applied on top of the composite resin. The stress field was obtained by using Ansys Workbench 10.0. The nodes of the base of the specimen were constrained in the x, y and z axes. The maximum principal stress (σmax) was obtained for all structures at the dentin/adhesive interface. The Mpp showed the highest peak of σmax in the HL (32.2 MPa), followed by Mp (30 MPa) and Mr (28.4 MPa). The stress concentration in the peritubular dentin was high in all models (120 MPa). All other structures positioned far from voids showed similar increase of stress. Voids incorporated into the HL raised the σmax in this region by 13.5%. This behavior might be responsible for lower bond strengths of self-etching and single-bottle adhesives, as reported in the literature.

Temperature rise during adhesive and composite polymerization with different light-curing sources

AIM: This study evaluated the temperature rise of the adhesive system Single Bond (SB) and the composite resins Filtek Z350 flow (Z) and Filtek Supreme (S), when polymerized by light-emitting diode (LED XL 3000) and quartz-tungsten halogen (QTH Biolux). METHODS: Class V cavities (3 yen2 mm) were prepared in 80 bovine incisors under standardized conditions. The patients were divided as follows: G1: Control; G2: SB; G3: SB + Z; G4: SB + S. The groups were subdivided into two groups for polymerization (A: QTH, B: LED). Light curing was performed for 40 s and measurement of temperature changes during polymerization was performed with a thermocouple positioned inside the pulp chamber. Data were statistically analyzed using ANOVA and Tukey tests. RESULTS: The factors material (P<0.00001) and curing unit (P<0.00001) had significant influence on temperature rise. The lowest temperature increase (0.15 degrees C) was recorded in G2 B and the highest was induced in G1 A (0.75 degrees C, P<0.05). In all groups, lower pulp chamber temperature measurements were obtained when using LED compared to QTH (P<0.05). CONCLUSION: QTH caused greater increases in tooth temperature than LED. However, both sources did not increase pulpal temperature above the critical value that may cause pulpal damage.

Bond strength of a composite resin to an adhesive luting cement

This study evaluated the influence of surface treatment on the shear bond strength of a composite resin (CR), previously submitted to the application of a temporary cement (TC), to an adhesive luting cement. Eight-four CR cylinders (5 mm diameter and 3 mm high) were fabricated and embedded in acrylic resin. The sets were divided into 6 groups (G1 to G6) (n=12). Groups 2 to 6 received a coat of TC. After 24 h, TC was removed and the CR surfaces received the following treatments: G2: ethanol; G3: rotary brush and pumice; G4: air-abrasion; G5: air-abrasion and adhesive system; G6: air-abrasion, acid etching and adhesive system. G1 (control) did not receive TC or any surface treatment. The sets were adapted to a matrix and received an increment of an adhesive luting cement. The specimens were subjected to the shear bond strength test. ANOVA and Tukey's tests showed that G3 (8.53 MPa) and G4 (8.63 MPa) differed significantly (p=0.001) from G1 (13.34 MPa). The highest mean shear bond strength values were found in G5 (14.78 MPa) and G6 (15.86 MPa). Air-abrasion of CR surface associated with an adhesive system provided an effective bond of the CR to the adhesive luting cement, regardless the pre-treatment with the phosphoric acid.

Evaluating the bonding of two adhesive systems to enamel submitted to whitening dentifrices.

The aim of this study was to evaluate by micro-shear bond strength test, the bond strength of composite resin restoration to enamel submitted to whitening dentifrices. Forty bovine teeth were embedded in polystyrene resin and polished. The specimens were randomly divided into eight groups (n=5), according to the dentifrice (carbamide peroxide, hydrogen peroxide and conventional dentifrice) and the adhesive system (Prime & Bond 2.1 and Adper Single Bond 2). Dentifrice was applied for 15 minutes a day, for 21 days. Thirty minutes after the last exposure to dentifrice, the samples were submitted to a bonding procedure with the respective adhesive system. After that, four buttons of resin were bonded in each sample using transparent cylindrical molds. After 24 hours, the teeth were submitted to the micro-shear bond strength test and subsequent analysis of the fracture mode. Data were submitted to analysis of variance and Fisher's PLSD test (alpha = 0.05). The micro-shear bond strength showed no difference between adhesives systems but a significant reduction was found between the control and carbamide groups (p = 0.0145) and the control and hydrogen groups (p = 0.0370). The evaluation of the failures modes showed that adhesive failures were predominant. Cohesive failures were predominant in group IV The use of dentifrice with peroxides can decrease bonding strength in enamel.

A comparative study of the physical properties of conventional and Grander-modified adhesive systems

Purpose: The objective of this study was to evaluate the influence of the Grander technology in reducing the surface tension and contact angle of a self-etch adhesive system. Methods: Distilled water and Xeno III self-etch adhesive system (Dentsply) were modified by physical contact with the Flexible unit Grander system to revitalize water, for 48 hours, resulting in four groups: Group 1 - Xeno III under normal conditions; Group 2 - Xeno III modified by Grander; Group 3 - distilled water under normal conditions; Group 4 - distilled water system modified by the Grander system;. Surface tension and contact angle (dentin substrate and titanium plate) of the adhesive system and water in normal and Grander-modified conditions was measured with a goniometer. Data were analyzed by ANOVA and Tukey test (5%). Results: Grander technology reduced the surface tension of water but not of the adhesive system Xeno III. The contact angle property of the adhesive ystem was not affected. Conclusion: Grander technology did not interfere with the surface tension and contact angle physical properties of the Xeno III self-etch adhesive system. Copyright: © 2011 Gonçalves et al.;.

Analysis of hybrid layer thickness, resin tag length and their correlation with microtensile bond strength using a total etch adhesive to intact dentin.

The objective of this study was to evaluate the use of a two-step total etch and rinse adhesive, the correlation between the hyybrid layer thickness (HL) and bond strength (BS), and between resin tag length (RT) and bond strength in the same teeth, and also to evaluate the fracture patterns of the tested specimens. Ten human molars were used for the restorative procedure and then sectioned in two halves (mesio-distally). The materials used were Adper Single Bond 2, 3M ESPE, Ultra etch gel, Ultradent and Filtek Z250, 3M ESPE. One half were utilized to measure the HL thickness and RT length through light microscopy analysis (400x), and the other half was subject to a microtensile test to measure the BS. The fractured surfaces were analyzed by scanning electron microscopy and fracture patterns classified. The Pearson correlation test was applied (p = 0.05). The results of the analyses of each specimen then were correlated: mean HL thickness = 4.39 (0.48) microm, mean length of RT = 9.94 (1.69) microm, mean BS = 23.98 (10.24) MPa. A statistically significant correlation between HL thickness and bond strength was found (r = 0.93). The two step etch and rinse adhesive system, showed a strong correlation between HL thickness and bond strength. The most common fractures were adhesive, followed by cohesive in resin.

Influence of cutting instruments and adhesive systems on hybrid layer formation.

Influence of cutting instruments and The aim of this study was to analyze the hybrid layer in noncarious dentin prepared by different cutting instruments and restored with composite resin. The cavities were randomly prepared in 40 specimens using a high-speed diamond bur (KG Sorensen 1013) and an ultrasonic tip (CVDentus C22). The cavities were restored with composite resin by varying the adhesive system between the Adper™ Single Bond (2 x 1 system, primer+adhesive) and the Prompt L-Pop™ (3 x 1 system, self-etching). The restorations were hemisected longitudinally and analyzed in the SEM (Scanning electron microscopy) in order to evaluate the hybrid layer and resinous tags characteristics, using scores ranging from 1 to 6. The Pearson test revealed a high correlation coefficient and good significance levels for both intra- and inter-raters values (r=0.90). The data were statistically analyzed using the Mann-Whitney test (P≤0.05). A larger proportion of regular hybrid layers with numerous tags were observed in the dentin prepared using the high-speed diamond burs and restored with a 2 × 1 adhesive system. Alternatively, the 3 × 1 adhesive system promoted the generation of a thin hybrid layer with few tags. After preparation using an ultrasonic tip revealed few or no tags after the preparation and 2 × 1 or 3 × 1 adhesive system application. The high-speed diamond burs produced a dentin surface that was more favorable to restorative material adhesion than the ultrasonic tips, regardless of the adhesive system used.

One-year clinical evaluation of composite restorations in posterior teeth: Effect of adhesive systems

This clinical study assessed the performance of posterior composite resins applied with the Adper™ Single Bond Plus (SB) and Adper ™ Scotchbond SE (SE) adhesive systems and Filtek ™ Supreme Plus composite resin, using modified US Public Health Service criteria. A total of 97 restorations were placed in posterior teeth by two calibrated operators. Application of the materials followed manufacturers' instructions. The restorations were evaluated by two examiners at baseline and after one year. Statistical analyses were conducted using the proportion test at a significance level of 5% (p<0.05). All the restorations evaluated (ie, 100%) received an alpha rating for the criteria of marginal discoloration and marginal integrity at baseline. At one year, for marginal discoloration, 64.6% of SB and 61.2% of SE received an alpha rating. For marginal integrity, 72.9% of SB and 77.6% of SE received an alpha rating. The other restorations received bravo ratings for both criteria. None of the teeth that received the restorative systems presented caries lesions around the restorations. A total of eight teeth presented postoperative sensitivity one week after baseline, five with SB and three with SE; the symptom had disappeared one year later. One year later, composite resin restorations using either adhesive system showed satisfactory clinical performance.

Influence of CVD diamond tips and Er:YAG laser irradiation on bonding of different adhesive systems to dentin

Aim: The aim of this study was to compare the microtensile bond strength of three adhesive systems, using different methods of dentin preparation. Materials and methods: A hundred and eight bovine teeth were used. The dentin from buccal face was exposed and prepared with three different methods, divided in 3 groups: Group 1 (DT)- diamond tip on a high-speed handpiece; Group 2 (CVD)-CVD tip on a ultrasonic handpiece; Group 3 (LA)-Er: YAG laser. The teeth were divided into 3 subgroups, according adhesive systems used: Subgroup 1-Adper Single Bond Plus/3M ESPE (SB) total-etch adhesive; Subgroup 2-Adper Scotchbond SE/3M ESPE (AS) selfetching adhesive; Subgroup 3-Clearfil SE Bond/Kuraray (CS) selfetching adhesive. Blocks of composite (Filtek Z250-3M ESPE) 4 mm high were built up and specimens were stored in deionized water for 24 hours at 37°C. Serial mesiodistal and buccolingual cuts were made and stick-like specimens were obtained, with transversal section of 1.0 mm2. The samples were submitted to microtensile test at 1 mm/min and load of 10 kg in a universal testing machine. Data (MPa) were subjected to ANOVA and Tukey's tests (p < 0.05). Results and conclusion: Surface treatment with Diamond or CVD tips associated with Clearfil SE Bond adhesive produced significantly lower bond strength values compared to other groups. Surface treatment with Er: YAG laser associated with Single Bond Plus or Clearfil SE Bond adhesives and surface treatment with CVD tip associated with Adper Scotchbond SE adhesive produced significantly lower bond strength values compared to surface treatment with diamond or CVD tips associated with Single Bond Plus or Adper Scotchbond SE adhesives. Clinical significance: Interactions between laser and the CVD tip technologies and the different adhesive systems can produce a satisfactory bonding strength result, so that these associations may be beneficial and enhance the clinical outcomes.

Effects of dentin dry/moist condition on the immediate adhesive performance of different solvent-based etch-and-rinse adhesivesystems

Purpose: The purpose of this research was to analyze and measure, under optical microscopy, the hybrid layer thickness and resin tags length, as well as the microtensile bond strength of two conventional adhesive systems when applied to dry and moist dentinal substrate. Methods: Thirty-two extracted human molars were randomly distributed into four groups according to the adhesive systems (XP Bond and Prime&Bond 2.1) and moisture condition (dry and moist). In Groups I and II, XP adhesive system was applied on dry and moist dentin, respectively; while Groups III and IV received PB adhesive system, in the same way as was done in Groups I and II, respectively. After adhesive and restorative procedures, all specimens were sectioned along their long axes; one hemi-tooth sample was subjected to the microtensile bond strength test while the other was decalcified and serially sectioned into six micron thick slices and sequentially mounted on glass slides. These sections were stained by the Brown and Brenn method for posterior analysis and measurement of the hybrid layer and resin tags under a light microscope with a micrometric ocular 40/075. Results: Data were analyzed using two-way ANOVA and Tukey's test (α=0.05). For the variable hybrid layer thickness, XP showed no significant differences between dry and moist dentin (5.2 μm and 5.5 μm, respectively), but for PB, hybrid layer was significantly thicker for moist (4.0 μm) than for dry dentin (3.0 μm). For the variable resin tags length XP showed 17.9 μm length for dry dentin and 20.8 μm for moist dentin; PB 11.7 μm for dry and 12.69 μm for moist dentin;there was no significant differences between them, independent of the moisture condition. For the variable microtensile bond strength, XP showed 38.0 MPa for dry dentin and 44.5 MPa for moist dentin; and PB showed 22.7 MPa for dry dentin and 20.8 MPa for dry dentin no significant difference was observed between moist and dry dentin for XP (p=0.2) and PB (p=0.7), but XP was presented significantly higher bond strength values than PB in both moisture conditions (p=0.003 for dry and p=0.002 for moist). Conclusion: The two-step butanol-based etch-and-rinse adhesive XP Bond presented a superior behavior with regard to the hybrid layer thickness, length of resin tags and bond strength to dry and moist dentin substrates when compared with two-step acetone-based adhesive system Prime&Bond2.1. © 2013 Elsevier Ltd.

Cytotoxicity of adhesive systems of different hydrophilicities on cultured odontoblast-like cells

This study evaluated the cytotoxicity of experimental adhesive systems (EASs) on odontoblast-like cells. Paper discs (n=132) were impregnated with 10 μL of each EAS-R1, R2, R3, R4, and R5 (in an ascending order of hydrophilicity), followed by photoactivation. R1 and R2 are nonsolvated hydrophobic blends, R3 represents a simplified etch-and-rinse adhesive system, and R4 and R5 represent simplified self-etch adhesive systems. Discs were immersed in Dulbecco's modified Eagle's medium for 24 h to obtain eluates applied on MDPC-23 cell cultures. No material was applied on discs used as control (R0). Cell viability [3-(4,5-dimethythiazol-2-yl)-2,5-diphenyl tetrazolium bromide assay], total protein (TP) production, alkaline phosphatase (ALP) activity, type of cell death, and degree of monomer conversion Fourier transform infrared (%DC-FTIR) were evaluated. Data were analyzed by Kruskal-Wallis and Mann-Whitney tests (α=0.05). Considering R0 (control) as having 100% of cell viability, R1, R2, R3, R4, and R5 reduced the metabolic activity of cells by 36.4, 3.1, 0.2, 21.5, and 65.7%, respectively, but only R1 and R5 differed from R0. Comparing with R0, lower TP production was observed for R1, R4, and R5, while ALP activity decreased for R1 and R5. Necrotic cell death was predominant for all EASs, but only R1, R4, and R5 differed from R0. Only R5 presented a different apoptotic cell death ratio from R0. R1 presented the lowest %DC (ca. 37%), whereas R4 and R5 presented the highest (ca. 56%). In conclusion, R2 and R3 were not toxic to the MDPC-23 cells, suggesting that the degree of hydrophilicity or %DC of the EASs alone were not responsible for their cytopathic effects. © 2013 Wiley Periodicals, Inc.

Transdentinal cytotoxicity of experimental adhesive systems of different hydrophilicity applied to ethanol-saturated dentin

The aim of this study was to evaluate the transdentinal cytotoxicity of experimental adhesive systems (EASs) with different hydrophilicity and dentin saturation solutions on odontoblast-like cells. One hundred 0.4-mm-thick dentin discs were mounted in in vitro pulp chambers and assigned to 10 groups. MDPC-23 cells were seeded onto the pulpal side of the discs, incubated for 48 h. The EASs with increasing hydrophilicity (R1, R2, R3 and R4) were applied to the occlusal side after etching and saturation of etched dentin with water or ethanol. R0 (no adhesive) served as controls. R1 is a non-solvated hydrophobic blend, R2 is similar to a simplified etch-and-rinse adhesive system and R3 and R4 are similar to self-etching adhesives. After 24 h, cell metabolism was evaluated by MTT assay (n = 8 discs) and cell morphology was examined by SEM (n = 2 discs). Type of cell death was identified by flow cytometry and the degree of monomer conversion (%DC) was determined by infrared spectroscopy (FTIR) after 10 s or 20 s of photoactivation. Data were analyzed by the Kruskal-Wallis and Mann-Whitney tests (α = 0.05). Dentin saturation with ethanol resulted in higher necrotic cell death ratios for R2, R3 and R4 compared with water saturation, although R2 and R3 induced higher SDH production. Photoactivation for 20 s significantly improved the %DC of all EASs compared with 10 s. A significant positive correlation was observed between the degree of hydrophilicity and %DC. In conclusion, except for R1, dentin saturation with ethanol increased the cytotoxicity of EASs, as expressed by the induction of necrotic cell death. © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Avaliação da eficiência de adesão de um cimento resinoso autocondicionante (self-adhesive) sobre esmalte e dentina: efeito termociclagem e condicionamento dental : estudo in vitro

Pós-graduação em Odontologia Restauradora - ICT

Adhesive systems: important aspects related to their composition and clinical use

This literature review article addresses the types and the main components of different etch-and-rinse and self-etch adhesive systems available in the market, and relates them to their function, possible chemical interactions and influence of handling characteristics. Scanning electron microscopy (SEM) images are presented to characterize the interface between adhesives and dentin. Adhesive systems have been recently classifed according to their adhesion approaches in etch-and-rinse, self-etch and glass ionomer. The etch-and-rinse systems require a specifc acid-etch procedure and may be performed in two or three steps. Self-etch systems employ acidic monomers that demineralize and impregnate dental substrates almost at the same time. These systems are separated in one or two steps. Some advantages and defciencies were noted for etch-and-rinse and self-etch approaches, mainly for the simplifed ones due to some chemical associations and interactions. The SEM micrographs illustrate different relationships between adhesive systems and dental structures, particularly dentin. The knowledge of composition, characteristics and mechanisms of adhesion of each adhesive system is of fundamental importance to permit the adoption of ideal bonding strategies under clinical conditions.