Resistance of an epoxy coating with an organic inhibitor to cathodic disbondment in sea water

In this study, the effect of anti-corrosion inhibitor addition to epoxy coating, on the disbanding rate was evaluated. First to determination of mechanism, the bare steel substrates were immersed in the 3.5% NaCl solution and the solution containing 1 mM anti corrosion. The Electrochemical Impedance Spectroscopy was performed after 5 and 24 hour. The results indicated a lower corrosion rate in the presence of inhibitor. During the time, charge transfer resistance, was decreased for the substrates immersed in NaCl solution, and increased for the substrates immersed in NaCl solution containing 1 mM anti corrosion. This result can be related to more stability of corrosion products in presence of anti-corrosion and film formation. The coated substrates, with four different concentration of anticorrosion in coating, were protected under -1.2 voltage in the 3.5% NaCl solution. After 12 and 24 hour, the EIS test and disbanding area measurement, were evaluate. The lower disbanding rate, more charge transfer resistance and less double layer capacitance for the coating containing 0.75w% inhibitor, were observed. The result of Pull-off test after 1 day immersion in 3.5% NaCl solution, showed more wet adhesion for the coating containing 0.75w% inhibitor. The images of FE-SEM electron microscope and surface analyses EDX on the coated substrate after disbanding and the bare substrate immersed in 3.5w% NaCl containing 1 mM inhibitor, were proved the formation of stabilized film.

Atributos de qualidade de solos sob dois diferentes tipos de manejo no município de Ibiúna/SP, Brazil

Agricultural activity has direct consequences on the soil and water quality. Thus, assessing environmental impacts of this vital economic activity, through soil attribute analysis, is essential to the proposal of alternatives. The aim of this study was to analyze soil quality under different land management practices, conventional and organic. The study was carried out in a watershed of the Ibiuna municipality, SP, Brazil, an important supplier of agricultural products for the São Paulo metropolitan area. A hundred samples were collected, 20 in each type of land use: reforested areas, native vegetation, pasture, conventional cultivation and organic cultivation. The soil resistance to penetration, its pH (in water and KO), electrical conductivity, bulk density, particle density, porosity, soil color, soil texture and the percentages of carbon and nitrogen were analyzed. The data were statistically analyzed, searching for significant differences. The results of soil analysis showed great similarity between the organic and conventional culture, with no statistical differences. However, organic cultivation showed greater similarity to the soil of native vegetation in the percentage of carbon and nitrogen in soils compared to conventional culture. Thus, the discussion begins on a topic very little explored so far, and the results obtained should be further studied.

Electrical characterization of the rectifying contact between aluminium and electrodeposited poly(3-methylthiophene)

A detailed investigation both of the DC and of the AC electrical properties of the Schottky barrier formed between aluminium and electrodeposited poly(3-methylthiophene) is reported. The devices show rectification ratios up to 2 x 10(4) which can be increased further after post-metal annealing. The reverse characteristics of the devices follow predictions based on the image-force lowering of the Schottky barrier, from which the doping density can be estimated, As the forward voltage increases, the device current is limited by the bulk resistance of the polymer with some evidence for injection limitation at the gold counter-electrode at high bias. In the bulk-limited regime, the device current is thermally activated near room temperature with an activation energy in the range 0.2-0.3 eV. Below about 150 K the device current is almost independent of temperature. Capacitance-voltage plots obtained at frequencies well below the device relaxation frequency indicate the presence of two distinct acceptor states, A set of shallow acceptor states are active in forward bias and are believed to determine the bulk conductivity of the polymer. A set of deeper accepters are active only for very small forward voltages and for all reverse voltages, namely when band banding causes the Fermi energy to cross these states. The density of these deeper states is approximately an order of magnitude greater than that of the shallow states. Evidence is presented also for the influence of fabrication conditions on the formation of an insulating interfacial layer at the rectifying interface. The presence of such a layer leads to inversion at the polymer surface and a modification of the I-V characteristics.

Addressing wildfire risk in forest management with a wildfire resistance indicator

Mestrado Mediterranean Forestry and Natural Resources Management - Instituto Superior de Agronomia - UL

Motivação e desempenho de tarefas num trabalho de Contact Center

Mestrado em Ciências Empresariais

Electrical characterization of the rectifying contact between aluminium and electrodeposited poly(3-methylthiophene)

A detailed investigation both of the DC and of the AC electrical properties of the Schottky barrier formed between aluminium and electrodeposited poly(3-methylthiophene) is reported. The devices show rectification ratios up to 2 x 10(4) which can be increased further after post-metal annealing. The reverse characteristics of the devices follow predictions based on the image-force lowering of the Schottky barrier, from which the doping density can be estimated, As the forward voltage increases, the device current is limited by the bulk resistance of the polymer with some evidence for injection limitation at the gold counter-electrode at high bias. In the bulk-limited regime, the device current is thermally activated near room temperature with an activation energy in the range 0.2-0.3 eV. Below about 150 K the device current is almost independent of temperature. Capacitance-voltage plots obtained at frequencies well below the device relaxation frequency indicate the presence of two distinct acceptor states, A set of shallow acceptor states are active in forward bias and are believed to determine the bulk conductivity of the polymer. A set of deeper accepters are active only for very small forward voltages and for all reverse voltages, namely when band banding causes the Fermi energy to cross these states. The density of these deeper states is approximately an order of magnitude greater than that of the shallow states. Evidence is presented also for the influence of fabrication conditions on the formation of an insulating interfacial layer at the rectifying interface. The presence of such a layer leads to inversion at the polymer surface and a modification of the I-V characteristics.

MEASURING HEAD IMPACT CONTACT PRESSURE IN COLLEGIATE FOOTBALL GAMES TO CORRELATE HEAD KINEMATICS TO BRAIN KINETICS ELUCIDATING BRAIN INJURY DYNAMICS

Does a brain store thoughts and memories the way a computer saves its files? How can a single hit or a fall erase all those memories? Brain Mapping and traumatic brain injuries (TBIs) have become widely researched fields today. Many researchers have been studying TBIs caused to adult American football players however youth athletes have been rarely considered for these studies, contradicting to the fact that American football enrolls highest number of collegiate and high-school children than adults. This research is an attempt to contribute to the field of youth TBIs. Earlier studies have related head kinematics (linear and angular accelerations) to TBIs. However, fewer studies have dealt with brain kinetics (impact pressures and stresses) occurring during head-on collisions. The National Operating Committee on Standards for Athletic Equipment (NOCSAE) drop tests were conducted for linear impact accelerations and the Head Impact Contact Pressures (HICP) calculated from them were applied to a validated FE model. The results showed lateral region of the head as the most vulnerable region to damage from any drop height or impact distance followed by posterior region. The TBI tolerance levels in terms of Von-Mises and Maximum Principal Stresses deduced for lateral impact were 30 MPa and 18 MPa respectively. These levels were corresponding to 2.625 feet drop height. The drop heights beyond this value will result in TBI causing stress concentrations in human head without any detectable structural damage to the brain tissue. This data can be utilized for designing helmets that provide cushioning to brain along with providing a resistance to shear.

Beech bark disease distribution and resistance in Michigan and fungal endophyte ecology of resistant and susceptible beech (Fagus grandifolia Ehrh.)

Beech bark disease (BBD), a non-native association of the fungal pathogen Neonectria faginata and the beech scale insect Cryptococcus fagisuga, has dramatically affected American beech within North American forests. To monitor the spread and effects of BBD in Michigan, a network of forest health monitoring plots was established in 2001 following the disease discovery in Ludington State Park (Mason County). Forest health canopy condition and basic forestry measurements including basal area were reassessed on beech trees in these plots in 2011 and 2012. The influence of bark-inhabiting fungal endophytes on BBD resistance was investigated by collecting cambium tissue from apparently resistant and susceptible beech. Vigor rating showed significant influences of BBD in sample beech resulting in reduced health and substantiated by significant increases of dead beech basal area over time. C. fagisuga distribution was found to be spatially clustered and widespread in the 22 counties in Michigan's Lower Peninsula which contained monitoring plots. Neonectria has been found in Emmet, Cheboygan and Wexford in the Lower Peninsula which may coincide with additional BBD introduction locations. Surveys for BBD resistance resulted in five apparently resistant beech which were added to a BBD resistance database. The most frequently isolated endophytes from cambium tissue were identified by DNA sequencing primarily as Deuteromycetes and Ascomycetes including Chaetomium globosum, Neohendersonia kickxii and Fusarium flocciferum. N. faginata in antagonism trials showed significant growth reduction when paired with three beech fungal endophytes. The results of the antagonism trial and decay tests indicate that N. faginata may be a relatively poor competitor in vivo with limited ability to degrade cellulose.

Effect of cattle on Salmonella carriage, diversity and antimicrobial resistance in free-ranging wild boar (Sus scrofa) in northeastern Spain

Salmonella is distributed worldwide and is a pathogen of economic and public health importance. As a multi-host pathogen with a long environmental persistence, it is a suitable model for the study of wildlife-livestock interactions. In this work, we aim to explore the spill-over of Salmonella between free-ranging wild boar and livestock in a protected natural area in NE Spain and the presence of antimicrobial resistance. Salmonella prevalence, serotypes and diversity were compared between wild boars, sympatric cattle and wild boars from cattle-free areas. The effect of age, sex, cattle presence and cattle herd size on Salmonella probability of infection in wild boars was explored by means of Generalized Linear Models and a model selection based on the Akaike's Information Criterion. Prevalence was higher in wild boars co-habiting with cattle (35.67%, CI 95% 28.19-43.70) than in wild boar from cattle-free areas (17.54%, CI 95% 8.74-29.91). Probability of a wild boar being a Salmonella carrier increased with cattle herd size but decreased with the host age. Serotypes Meleagridis, Anatum and Othmarschen were isolated concurrently from cattle and sympatric wild boars. Apart from serotypes shared with cattle, wild boars appear to have their own serotypes, which are also found in wild boars from cattle-free areas (Enteritidis, Mikawasima, 4:b:- and 35:r:z35). Serotype richness (diversity) was higher in wild boars co-habiting with cattle, but evenness was not altered by the introduction of serotypes from cattle. The finding of a S. Mbandaka strain resistant to sulfamethoxazole, streptomycin and chloramphenicol and a S. Enteritidis strain resistant to ciprofloxacin and nalidixic acid in wild boars is cause for public health concern.

An investigation of contact transmission of methicillin-resistant staphylococcus aureus

Hand hygiene is critical in the healthcare setting and it is believed that methicillin-resistant Staphylococcus aureus (MRSA), for example, is transmitted from patient to patient largely via the hands of health professionals. A study has been carried out at a large teaching hospital to estimate how often the gloves of a healthcare worker are contaminated with MRSA after contact with a colonized patient. The effectiveness of handwashing procedures to decontaminate the health professionals' hands was also investigated, together with how well different healthcare professional groups complied with handwashing procedures. The study showed that about 17% (9–25%) of contacts between a healthcare worker and a MRSA-colonized patient results in transmission of MRSA from a patient to the gloves of a healthcare worker. Different health professional groups have different rates of compliance with infection control procedures. Non-contact staff (cleaners, food services) had the shortest handwashing times. In this study, glove use compliance rates were 75% or above in all healthcare worker groups except doctors whose compliance was only 27%.

Texture for Script identification

The problem of determining the script and language of a document image has a number of important applications in the field of document analysis, such as indexing and sorting of large collections of such images, or as a precursor to optical character recognition (OCR). In this paper, we investigate the use of texture as a tool for determining the script of a document image, based on the observation that text has a distinct visual texture. An experimental evaluation of a number of commonly used texture features is conducted on a newly created script database, providing a qualitative measure of which features are most appropriate for this task. Strategies for improving classification results in situations with limited training data and multiple font types are also proposed.