Bond strength of denture teeth to acrylic resin: effect of thermocycling and polymerisation methods

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influence of Different Ceramics on Resin Cement Knoop Hardness Number

This study evaluated: 1) the effect of different ceramics on light attenuation that could affect microhardness, measured as the Knoop Hardness Number (KHN), of a resin cement immediately and 24 hours after polymerization and 2) the effect of different activation modes (direct light-activation, light activation through ceramics and chemical activation) on the KHN of a resin cement.Resin cement Rely X ARC (3M ESPE) specimens 5.0 mm in diameter and 1.0 nun thick were made in a Teflon mold covered with a polyester film. The cement was directly light activated for 40 seconds with an XL 2500 curing unit (3M ESPE) with 650 mW/cm(2), light activated through ceramic discs of Duceram Plus (DeguDent), Cergogold (DeguDent), IPS Empress (Ivoclar), IPS Empress 2 (Ivoclar), Procera. (NobelBiocare), In Ceram Alumina (Vita) and Cercon (DeguDent), having a 1.2 mm thickness or chemically activated without light application. The resin cement specimens were flattened, and KHN was obtained using an HMV 2 microhardness tester (Shimadzu) with a load of 50 g applied for 15 seconds 100 pin from the irradiated surface immediately and after storage at 37 degrees C for 24 hours. Ten measurements were made for each specimen, with three specimens for each group at each time. The data were submitted to ANOVA and Tukey's test (p=0.05). The KHN of the resin cement was not only affected by the mode of activation, but also by the post-activation testing time. The mean KHN of the resin cement for chemical activation and through all ceramics showed statistically significant lower values compared to direct activation immediately and at 24 hours. The KHN for 24 hours post-activation was always superior to the immediate post-activation test except with direct activation. The most opaque ceramics resulted in the lowest KHN values.

Silver Distribution and Release from an Antimicrobial Denture Base Resin Containing Silver Colloidal Nanoparticles

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Effect of weathering and thickness on the superficial microhardness of acrylic resin and ocular button

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of different concentrations of fluoride in dentifrices on dentin erosion subjected or not to abrasion in situ/ex vivo

This in situ/ex vivo study assessed the effect of different concentrations of fluoride in dentifrices on dentin subjected to erosion or to erosion plus abrasion. Ten volunteers took part in this crossover and double-blind study performed in 3 phases (7 days). They wore acrylic palatal appliances containing 4 bovine dentin blocks divided in two rows: erosion and erosion plus abrasion. The blocks were subjected to erosion by immersion ex vivo in a cola drink (60 s, pH 2.6) 4 times daily. During this step, the volunteers brushed their teeth with one of three dentifrices D (5,000 ppm F, NaF, silica); C (1,100 ppm F, NaF, silica) and placebo (22 ppm F, silica). Then, the respective dentifrice slurry (1: 3) was dripped on dentin surfaces. While no further treatment was performed in one row, the other row was brushed using an electric toothbrush for 30 s ex vivo. The appliances were replaced in the mouth and the volunteers rinsed with water. Dentin loss was determined by profilometry and analyzed by 2-way ANOVA/Bonferroni test (alpha = 0.05). Dentin loss after erosive-abrasive wear was significantly greater than after erosion alone. Wear was significantly higher for the placebo than for the D and C dentifrices, which were not significantly different from each other. It can be concluded that the presence of fluoride concentrations around 1,100 ppm in dentifrices is important to reduce dentin wear by erosion and erosion + abrasion, but the protective effect does not increase with fluoride concentration. Copyright (C) 2008 S. Karger AG, Basel.

Enamel microabrasion followed by dental bleaching for patients after orthodontic treatment - Case reports

This article reports clinical procedures used to remove residual bonded resin and enamel stains following bracket debonding at the conclusion of orthodontic treatment. A water-cooled fine-tapered diamond bur was used for resin removal, followed by enamel surface finishing using a commercially available microabrasion paste. It was noted that residual tooth coloration remained yellowish because of enamel translucency; the yellow dentin shade showed through. Additional tooth shade lightening was achieved using carbamide peroxide dental bleaching solution in custom-formed trays. This report describes a safe and effective technique that optimizes tooth appearance at the conclusion of orthodontic therapy. Mechanical resin removal, enamel microabrasion, and tooth bleaching are employed.

Effect of Different Light-Curing Modes on Degree of Conversion, Staining Susceptibility and Stain's Retention Using Different Beverages in a Nanofilled Composite Resin

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Evaluation of mineral trioxide aggregate and calcium hydroxide cement as pulp-capping agents in human teeth

This study evaluated the histomorphologic response of human dental pulps capped with mineral trioxide aggregate (MTA) and Ca(OH)(2) cement (CH). Pulp exposures were performed on the occlusal floor of 40 human permanent premolars. After that, the pulp was capped either with CH or MTA and restored with composite resin. After 30 and 60 days, teeth were extracted and processed for histologic exam and categorized in a histologic score system. The data were subjected to Kruskal-Wallis and Conover tests (alpha = .05). All groups performed well in terms of hard tissue bridge formation, inflammatory response, and other pulpal findings. However, a lower response of CH30 was observed for the dentin bridge formation, when compared with MTA30 and MTA60 groups. Although the pulp healing with calcium hydroxide was slower than that of MTA, both materials were successful for pulp capping in human teeth.

Biocompatibility of resin-based materials used as pulp-capping agents

Aim To evaluate and compare the response of pulps of rats capped with resin-modified glass-ionomer cement (RMGIC) or self-etching adhesive system.Methodology Class I cavities were prepared on the occlusal surface of 54 maxillary first molars of 27 rats. Pulp exposure was performed on the cavity floor. The following resin-based materials were applied as pulp-capping agents: G1, Clearfil Liner Bond 2V (CLB 2V; Kuraray Co., Japan); G2, Vitrebond (VIT; 3M/ESPE, USA). In group 3 (control group), a calcium hydroxide/saline paste (CH; Labsynth, Brazil) was used. The cavities were restored with amalgam. After 7, 30 and 60 days, the animals were sacrificed and the jaws were processed for microscopic evaluation.Results Despite the inflammatory response caused by the experimental and the control materials at 7 days, pulpal healing associated with calcified barrier formation was observed at 60 days following the pulp therapy. Both resin-based materials promoted a large zone of cell-rich fibrodentine matrix deposition on the pulp horn related to the pulp exposure site, which was larger to VIT than to CLB 2V specimens. Tertiary dentine underneath the fibrodentine matrix was deposited by a layer of elongated pulpal cells. The remaining pulpal tissue exhibited normal histological characteristics. In the control group, healing and dentine-bridge formation was observed at 30 days. Pulpal breakdown occurred only when bacterial infection occurred.Conclusion Both experimental pulp-capping agents allowed pulpal healing characterized by cell-rich fibrodentine and tertiary dentine deposition as well as calcified barrier formation.

Correlation between light transmission and permeability of human dentin

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effects of light-curing time on the cytotoxicity of a restorative composite resin on odontoblast-like cells

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Surface roughness and hardness of a composite resin: influence of finishing and polishing and immersion methods

This study evaluated the finishing and polishing effect on the surface roughness and hardness of the Filtek Supreme XT, in fluoride solutions. Specimens were prepared (n = 140) with half of the samples finished and polished with Super-Snap (R) disks. The experimental groups were divided according to the presence or absence of finishing and polishing and immersion solutions (artificial saliva, sodium fluoride solution at 0.05%-manipulated, Fluordent Reach, Oral B, Fluorgard). The specimens remained immersed in artificial saliva for 24 hours and were then subjected to initial analysis (baseline) of surface roughness and Vickers microhardness. Next, they were immersed in different fluoride solutions for 1 min/day, for 60 days. Afterwards, a new surface roughness and microhardness reading was conducted. The data were submitted to a two-way ANOVA and Tukey's test (5% significance level). For the comparison of mean roughness and hardness at baseline and after 60 days, the paired Student t test was used. The results showed that the surface roughness and microhardness of the Filtek Supreme XT were influenced by the finishing and polishing procedure, independently of the immersion methods.

Clinical and microbiological performance of resin-modified glass-ionomer liners after incomplete dentine caries removal

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Cytotoxicity of resin-based light-cured liners

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)