Flexural Strength of Four Adhesive Fixed Dental Prostheses of Composite Resin Reinforced with Glass Fiber

Purpose: To evaluate the flexural strength of two fixed dental prosthesis (FDP) designs simulating frameworks of adhesive fixed partial prostheses, reinforced or not by glass fiber.Materials and Methods: Forty specimens, made with composite resin, were divided into 4 groups according to the framework design and the presence of fiber reinforcement: A1 - occlusal support; A2: occlusal support + glass fiber; B1: occlusal and proximal supports; B2: occlusal and proximal supports + glass fiber. The specimens were subjected to the three-point bending test, and the data were submitted to two-way ANOVA and Tukey's test (5%).Results: Group A2 (97.9 +/- 38 N) was statistically significantly different from all other experimental groups, presenting a significantly lower mean flexural strength.Conclusion: The use of glass fibers did not improve the flexural strength of composite resin, and designs with occlusal and proximal supports presented better results than designs simulating only occlusal support.

Design of dental implants, influence on the osteogenesis and fixation

The fixation and the bone ingrowth at the interface of porous cylindrical implants (total porosity of 37% and average pores diameter of 480 mu m) were compared in vivo to rough cylindrical implants (R-a = 5.3 mu m), both of commercially pure titanium, made by powder metallurgy. The implants were inserted into the tibias of 20 rabbits and the animals were sacrificed 4 and 8 weeks after surgery. The percentage of bone-implant contact observed in porous implant was significantly larger than in the rough ones for all of sacrifice periods, respectively, 57% vs. 46% after 4 weeks, and 59% vs. 50% after 8 weeks. The mechanical tests showed a significant increase in the shear strength of the porous implants for the two analyzed periods, 4 and 8 weeks (14 and 20 MPa), when compared with rough ones (4 and 13 MPa). These results suggest that porous implants improve the contact at the implant-bone interface and increase the fixation to the bone, improving the osseointegration. Thus, the porous implant might be an alternative to dental implant in less favorable conditions, and appear to be better fixed to bone, offering promising alternatives.

Evaluation of thermal compatibility between core and veneer dental ceramics using shear bond strength test and contact angle measurement

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Dental fluorosis: Exposure, prevention and management

Dental fluorosis is a developmental disturbance of dental enamel, caused by successive exposures to high concentrations of fluoride during tooth development, leading to enamel with lower mineral content and increased porosity. The severity of dental fluorosis depends on when and for how long the overexposure to fluoride occurs, the individual response, weight, degree of physical activity, nutritional factors and bone growth. The risk period for esthetic changes in permanent teeth is between 20 and 30 months of age. The recommended level for daily fluoride intake is 0.05 - 0.07 mg F/Kg/day, which is considered of great help in preventing dental caries, acting in remineralization. A daily intake above this safe level leads to an increased risk of dental fluorosis. Currently recommended procedures for diagnosis of fluorosis should discriminate between symmetrical and asymmetrical and/or discrete patterns of opaque defects. Fluorosis can be prevented by having an adequate knowledge of the fluoride sources, knowing how to manage this issue and therefore, avoid overexposure.

Y-TZP ceramic processing from coprecipitated powders: A comparative study with three commercial dental ceramics

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of Carbamide Peroxide Bleaching Gel Concentration on the Bond Strength of Dental Substrates and Resin Composite

Purpose: This study evaluated the effect of bleaching gel containing 10%, 15% and 20% carbamide peroxide (CP) on the bond strength of dental enamel or dentin and resin composite restorations.Methods: The buccal surfaces of 12 bovine tooth crowns were conditioned with 37% phosphoric acid, and the adhesive resin Single Bond 2 and the resin composite Filtek Z350 were used to perform the restorations. The blocks were sectioned to obtain bar specimens. Each specimen group (enamel-E, dentin-D) was divided into four subgroups (n=15): S-artificial saliva; 10-10% CP bleaching; 15-15% CP bleaching; 20-20% CP bleaching. CP was applied for six hours daily for two weeks. The specimens were submitted to the a test in a universal testing machine. The data were analyzed by one-way ANOVA and the Tukey post-hoc test and a correlation analysis (r) was performed.Results: For Group E, the mean value (+/- standard-deviation) was 21.86 (+/- 6.03)a, 18.91 (+/- 8.31)ab, 15.43 (+/- 7.44)b and 10.6 (+/- 4.94)c for ES, E10, E15 and E20, respectively. For Group D, the alpha values were 34.73 (+/- 4.68)a, 35.12 (+/- 13.43)a, 29.67 (+/- 6.84)ab and 24.56 (+/- 6.54)b for DS, D10, D15 and D20, respectively. A negative correlation between the CP concentration and mean values was observed for both the enamel (r=-0.95) and dentin (r=-0.85) groups.Conclusion: In the current study, the bond strength of the restoration to enamel and the restoration to dentin were influenced by the application of CP and was dependent on the CP concentration in the bleaching gel.

Effect of Cement Shade and Light-curing Unit on Bond Strength of a Ceramic Cemented to Dentin

Purpose: To evaluate the effect of cement shade, light-curing unit, and water storage on tensile bond strength (a) of a feldspathic ceramic resin bonded to dentin.Materials and Methods: The dentin surface of 40 molars was exposed and etched with 37% phosphoric acid, then an adhesive system was applied. Forty blocks of feldspathic ceramic (Vita VM7) were produced. The ceramic surface was etched with 10% hydrofluoric acid for 60 s, followed by the application of a silane agent and a dual-curing resin cement (Variolink II). Ceramic blocks were cemented to the treated dentin using either A3 or transparent (Tr) shade cement that was activated using either halogen or LED light for 40 s. All blocks were stored in 37 degrees C distilled water for 24 h before cutting to obtain non-trimmed bar-shaped specimens (adhesive area = 1 mm(2) +/- 0.1) for the microtensile bond strength test. The specimens were randomly grouped according to the storage time: no storage or stored for 150 days in 37 degrees C distilled water. Eight experimental groups were obtained (n = 30). The specimens were submitted to the tensile bond strength test using a universal testing machine at a crosshead speed of 1 mm/min. The data were statistically analyzed using ANOVA and Tukey's post-hoc tests (alpha = 0.05).Results: The mean bond strength values were significantly lower for the corresponding water stored groups, except for the specimens using A3 resin cement activated by halogen light. There was no significance difference in mean bond strength values among all groups after water storage.Conclusion: Water storage had a detrimental effect under most experimental conditions. For both cement shades investigated (Tr and A3) under the same storage condition, the light-curing units (QTH and LED) did not affect the mean microtensile bond strengths of resin-cemented ceramic to dentin.

Hardening of a dual-cure resin cement using QTH and LED curing units

Objective: This study evaluated the surface hardness of a resin cement (RelyX ARC) photoactivated through indirect composite resin (Cristobal) disks of different thicknesses using either a light- emitting diode (LED) or quartz tungsten halogen (QTH) light source. Material and Methods: Eighteen resin cement specimens were prepared and divided into 6 groups according to the type of curing unit and the thickness of resin disks interposed between the cement surface and light source. Three indentations (50 g for 15 s) were performed on the top and bottom surface of each specimen and a mean Vickers hardness number (VHN) was calculated for each specimen. The data were analyzed using two-way ANOVA and Tukey-Kramer test was used for post-hoc pairwise comparisons. Results: Increased indirect resin disk thickness resulted in decreased mean VHN values. Mean VHN values for the top surfaces of the resin cement specimens ranged from 23.2 to 46.1 (QTH) and 32.3 to 41.7 (LED). The LED curing light source produced higher hardness values compared to the QTH light source for 2- and 3-mm-thick indirect resin disks. The differences were clinically, but not statistically significant. Increased indirect resin disk thickness also resulted in decreased mean VHN values for the bottom surfaces of the resin cement: 5.8 to 19.1 (QTH) and 7.5 to 32.0 (LED). For the bottom surfaces, a statistically significant interaction was also found between the type of curing light source and the indirect resin disk thickness. Conclusions: Mean surface hardness values of resin cement specimens decreased with the increase of indirect resin disk thickness. The LED curing light source generally produced higher surface hardness values.

Deposition of SiOx Thin Films on Y-TZP by Reactive Magnetron Sputtering: Influence of Plasma Parameters on the Adhesion Properties Between Y-TZP and Resin Cement for Application in Dental Prosthesis

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

In vitro study of the Nd : YAG laser effect on human dental enamel: Optical and scanning electron microscope analysis

Objective: the Nd:YAG laser irradiation of dental enamel was evaluated in enamel demineralization experiments in a Streptococcus mutans culture media. Summary Background Data: Previous studies had shown that a continuous wave Nd:YAG laser at an energy of approximately 67 mJ may induce an increased acid resistance in human dental enamel when exposed to severe demineralization conditions. Methods: Enamel windows of 3 x 4 cm in the buccal surface were irradiated with a continuous wave Nd:YAG laser at a wavelength of 1,064 Ecm using energy densities of from 83.75 to 187.50 J/cm(2), Enamel windows of 3 x 4 cm on the lingual surface served as control (without the laser irradiation). The enamel windows were then exposed to a Streptococcus mutans culture media at a temperature of 37 degrees C for 15 and 21 days. The laser effects and demineralization were examined both by optical microscopy and scanning electron microscopy (SEM), Results: A comparison between the lased and the unlased windows of enamel showed fusion and recrystalization of the enamel and increased acid-resistance in all groups irradiated with the Nd:YAG laser, on the other hand, the 3 x 4 delimited enamel surfaces from the control group (not irradiated with the Nd:YAG laser) showed 100% deminerization, Conclusions: These findings are consistent with the finding that laser irradiation of dental results in significant reduction of the effective solubility of enamel mineral.

Effect of dental surface treatment with Nd:YAG and Er:YAG lasers on bond strength of resin composite to recently bleached enamel

The aim of this work is to evaluate the effect of surface treatment with Er:YAG and Nd:YAG lasers on resin composite bond strength to recently bleached enamel. In this study, 120 bovine incisors were distributed into two groups: group C: without bleaching treatment; group B: bleached with 35% hydrogen peroxide. Each group was divided into three subgroups: subgroup N: without laser treatment; subgroup Nd: irradiation with Nd:YAG laser; subgroup Er: irradiation with Er:YAG laser. The adhesive system (Adper Single Bond 2) was then applied and composite buildups were constructed with Filtek Supreme composite. The teeth were sectioned to obtain enamel-resin sticks (1 x 1 mm) and submitted to microtensile bond testing. The data were statistically analyzed by the ANOVA and Tukey tests. The bond strength values in the bleached control group (5.57 MPa) presented a significant difference in comparison to the group bleached and irradiated with Er:YAG laser (13.18 MPa) or Nd:YAG (25.67 MPa). The non-bleached control group presented mean values of 30.92 MPa, with statistical difference of all the others groups. The use of Nd:YAG and Er:YAG lasers on bleached specimens was able to improve the bond strengths of them.

Effects of Self-Etching Adhesive Systems Used in the Dental Modelling Technique on the Cohesive Strength of Composite Resin

This study evaluated the cohesive strength of composite using self-etching adhesive systems (SE) in the lubrication of instruments between layers of composite. The specimens were made by using a Teflon (R) device. SE were used at the interface to lubricate the instruments: Group 1(G1) - control group, no lubricant was used; Group 2(G2) -Futurabond (R) M; Group 3(G3) - Optibond (R) All-In-One; Group 4(G4) - Clearfil (R) SE Bond; Group 5(G5) - Futurabond (R) NR; Group 6(G6) - Adper (R) SE Plus; Group 7(G7) - One Up Bond (R) F. Specimens were submitted to the tensile test to evaluate the cohesive strength. Data were submitted to the ANOVA and Tukey tests. ANOVA showed a value of p = 0.00. The average means (SD): G2 = 11.33(+/-3.44) a, G3 = 15.36(+/-4.06) ab, G4 = 18.9(+/-4.72) bc, G7 = 19.62(+/-4.46) bc, G5 = 21.02(+/-5.09) bc, G6 = 23.39(+/-4.17) cd, and G1 = 28.49(+/-2.89) d. All SE decreased the cohesive strength of the composite, except for Adper (R) SE Plus.

Femtosecond laser ablation on dental hard tissues-Analysis of ablated profile near an interface using local effective intensity

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Evaluation of the Cohesive Strength Between Resin Composite and Light-curing Characterizing Materials

Purpose: To evaluate the cohesive strength between composite and different light-curing characterizing materials (LCCM), which were prepared using the intrinsic technique.Materials and Methods: One hundred composite specimens were made by using a prefabricated Teflon device, and a layer of LCCM was applied at the interface. The specimens were divided into 5 groups (n = 20): group 1 (control), no LCCM was used; group 2: application of White Kolor Plus Pigment (Kerr) LCCM; group 3: White Tetric Color Pigment (Ivoclar/Vivadent) LCCM; group 4: Brown Kolor Plus Pigment (Kerr) LCCM; group 5: Black Tetric Color Pigment (Ivoclar/Vivadent) LCCM. All materials were used according to the manufacturers' instructions. Specimens were submitted to a tensile test in a universal testing machine (EMIC DL-200MF) to evaluate the cohesive strength at the composite interface. Data were subjected to one-way ANOVA and Tukey's test (alpha = 5%).Results: ANOVA showed a p-value = 0.0001, indicating that there were significant differences among the groups. The mean values in MPa (+/- standard deviation) obtained for the groups were: G1: 28.5 (+/-2.74)a; G2: 23.5 (+/-2.47)b; G3: 20.3 (+/-2.49)b; G4: 10.5 (+/-2.40)c; G5: 9.66 (+/-3.06)c. The groups with the same letters presented no significant differences. The control group presented statistically significantly higher cohesive strengths when compared to the other groups. The groups in which Brown Kolor Plus Pigment and Black Tetric Color Pigment LCCM were used showed significantly lower cohesive strengths when compared to the groups in which White Kolor Plus Pigment and White Tetric Color Pigment LCMM were used.Conclusion: The use of LCCM produced with the intrinsic technique reduced the cohesive strength of composite.

Assessment of the effectiveness of light-emitting diode and diode laser hybrid light sources to intensify dental bleaching treatment

Objective. To evaluate the effectiveness of the color change of hybrid light-emitting diode (LED) and low-intensity infrared diode laser devices for activating dental bleaching and to verify the occurrence of a color regression with time. Material and methods. A total of 180 specimens obtained from human premolars were immersed in a coffee solution for 15 days for darkening and then divided into eight experimental groups (n = 20 in each) as follows: G1, bleaching without light; G2, bleaching with halogen light; G3, bleaching with a blue LED (1000 mW/470 nm) and a laser device (120 mW/795 nm) simultaneously; G4, bleaching with an LED emitting blue light (1000 mW/470 nm); G5, bleaching with a blue LED (800 mW/470 nm) and a laser device (500 mW/830 nm) simultaneously; G6, bleaching with a blue LED device (800 mW); G7, bleaching with a green LED (600 mW/530 nm) and a laser device (120 mW/795 nm) simultaneously; and G8, bleaching with a green LED (600 mW). Three measurements were performed (at baseline and 14 days and 12 months after bleaching) using a Vita Easyshade spectrophotometer. The data were submitted to two-way ANOVA and a Tukey test. Results. All groups showed significantly higher Delta E values than Group G1, with the exception of Group G8. Variations in the Delta E values at 14 days were significant when compared with those obtained at baseline and after 12 months. Conclusions. Light activation of the bleaching gel provided faster and more intense bleaching than use of the bleaching gel without light activation. Combinations of low-intensity diode lasers are ineffective as a bleaching gel activator. Color regression was observed after 12 months of storage.