Weight loss and surface roughness of hard chairside reline resins after toothbrushing: Influence of postpolymerization treatments

Purpose: To evaluate the effect of 2 postpolymerization treatments on toothbrushing wear (weight loss) and surface roughness of 3 autopolymerized reline resins-Duraliner II (D) (Reliance Dental), Kooliner (K) (Coe Laboratories), and Tokuso Rebase Fast (T) (Tokuyama Dental)-and 1 heat-polymerized resin, Lucitone 550 (L) (Dentsply International). Materials and Methods: Specimens (40 x 10 x 2mm) of each material (n = 24) were prepared and divided into 3 groups: control (no postpolymerization treatment); water bath (immersion in water at 55°C); and microwave (microwave irradiation). Specimens were dried until constant weight was achieved and the surface roughness (Ra) was measured. Tests were performed in a toothbrush machine using 20,000 strokes of brushing at a weight of 200 g, with the specimens immersed in 1:1 dentifrice/water slurry. Specimens were reconditioned to constant weight and the weight loss (mg) and surface roughness were evaluated. Data were analyzed by 2-way analysis of variance and followed by Tukey test (α = .05). Results: In the control group, the weight loss of materials D and T was lower (P < .05) than that of L. No differences among materials were found after postpolymerization treatments (P > .05). The weight loss of material T (control = 0.5 mg) was significantly increased (P < .05) after postpolymerization treatments (water bath = 1.9 mg; microwave = 1.8 mg). For materials K and T, the toothbrushed surface roughness was higher (P < .05) after microwave and waterbath postpolymerization treatments. Material L showed increased surface roughness after microwave postpolymerization treatment. Conclusion: The toothbrushing wear resistance of L was not superior to the reline resins. The postpolymerization treatments did not improve the toothbrushing wear resistance of the materials and produced an increased surface roughness for materials L, K, and T.

Effectiveness of microwave irradiation on the disinfection of complete dentures

Purpose: The purpose of this study was to evaluate the effectiveness of microwave irradiation on the disinfection of simulated complete dentures. Materials and Methods: Eighty dentures were fabricated in a standardized procedure and subjected to ethylene oxide sterilization. The dentures were individually inoculated (10 7 cfu/mL) with tryptic soy broth (TSB) media containing one of the tested microorganisms (Candida albicans, Streptoccus aureus, Bacillus subtilis, and Pseudomonas aeruginosa). After 48 hours of incubation at 37°C, 40 dentures were individually immersed in 200 mL of water and submitted to microwave irradiation at 650 W for 6 minutes. Forty nonirradiated dentures were used as positive controls. Replicate aliquots (25 μL) of suspensions were plated at dilutions of 10 -3 to 10 -6 on plates of selective media appropriate for each organism. All plates were incubated at 37°C for 48 hours. TSB beakers with the microwaved dentures were incubated at 37°C for 7 more days. After incubation, the number of colony-forming units was counted and the data were statistically analyzed by Kruskal-Wallis test (α = .05). Results: No evidence of growth was observed at 48 hours for S aureus, B subtilis, and C albicans. Dentures contaminated with P aeruginosa showed small growth on 2 plates. After 7 days incubation at 37°C, no growth was visible in the TSB beakers of S aureus and C albicans. Turbidity was observed in 3 broth beakers, 2 from P aeruginosa and 1 from B subtilis. Conclusion: Microwave irradiation for 6 minutes at 650 W produced sterilization of complete dentures contaminated with S aureus and C albicans and disinfection of those contaminated with P aeruginosa and B subtilis.

Effect of microwave disinfection procedures on torsional bond strengths of two hard chairside denture reline materials

Purpose: This study evaluated the potential effects of denture base resin water storage time and an effective denture disinfection method (microwave irradiation at 650 W for 6 minutes) on the torsional bond strength between two hard chairside reline resins (GC Reline and New Truliner) and one heat-polymerizing denture base acrylic resin (Lucitone 199). Materials and Methods: Cylindrical (30 x 3.9 mm) denture base specimens (n = 160) were stored in water at 37°C (2 or 30 days) before bonding. A section (3.0 mm) was removed from the center of the specimens, surfaces prepared, and the reline materials packed into the space. After polymerization, specimens were divided into four groups (n = 10): Group 1 (G1) - tests performed after bonding; Group 2 (G2) - specimens immersed in water (200 ml) and irradiated twice (650 W for 6 minutes); Group 3 (G3) - specimens irradiated daily until seven cycles of disinfection; Group 4 (G4) - specimens immersed in water (37°C) for 7 days. Specimens were submitted to a torsional test (0.1 Nm/min), and the torsional strengths (MPa) and the mode of failure were recorded. Data from each reline material were analyzed by a two-way analysis of variance, followed by Neuman-Keuls test (p = 0.05). Results: For both Lucitone 199 water storage periods, before bonding to GC Reline resin, the mean torsional strengths of G2 (2 days - 138 MPa; 30 days - 132 MPa), G3 (2 days - 126 MPa; 30 days - 130 MPa), and G4 (2 days - 130 MPa; 30 days - 137 MPa) were significantly higher (p < 0.05) than G1 (2 days - 108 MPa; 30 days - 115 MPa). Similar results were found for Lucitone 199 specimens bonded to New Truliner resin, with G1 specimens (2 days - 73 MPa; 30 days - 71 MPa) exhibiting significantly lower mean torsional bond strength (p < 0.05) than G2 (2 day - 86 MPa; 30 days - 90 MPa), G3 (2 days - 82 MPa; 30 days - 82 MPa), and G4 specimens (2 days - 78 MPa; 30 days - 79 MPa). The adhesion of both materials was not affected by water storage time of Lucitone 199 (p > 0.05). GC reline showed a mixed mode of failure (adhesive/cohesive) and New Truliner failed adhesively. Conclusions: Up to seven microwave disinfection cycles did not decrease the torsional bond strengths between the hard reline resins, GC Reline and New Truliner to the denture base resin Lucitone 199. The effect of additional disinfection cycles on reline material may be clinically significant and requires further study. Copyright © 2006 by The American College of Prosthodontists.

Bond strength of hard chairside reline resins to a rapid polymerizing denture base resin before and after thermal cycling

Purpose: This study assessed the shear bond strength of 4 hard chairside reline resins (Kooliner, Tokuso Rebase Fast, Duraliner II, Ufi Gel Hard) to a rapid polymerizing denture base resin (QC-20) processed using 2 polymerization cycles (A or B), before and after thermal cycling. Materials and Methods: Cylinders (3.5 mm x 5.0 mm) of the reline resins were bonded to cylinders of QC-20 polymerized using cycle A (boiling water-20 minutes) or B (boiling water; remove heat-20 minutes; boiling water-20 minutes). For each reline resin/polymerization cycle combination, 10 specimens (groups CAt e CBt) were thermally cycled (5 and 55°C; dwell time 30 seconds; 2,000 cycles); the other 10 were tested without thermal cycling (groups CAwt ad CBwt). Shear bond tests (0.5 mm/min) were performed on the specimens and the failure mode was assessed. Data were analyzed by 3-way ANOVA and Newman-Keuls post-hoc test (α=.05). Results: QC-20 resin demonstrated the lowest bond strengths among the reline materials (P<.05) and mainly failed cohesively. Overall, the bond strength of the hard chairside reline resins were similar (10.09±1.40 to 15.17±1.73 MPa) and most of the failures were adhesive/cohesive (mixed mode). However, Ufi Gel Hard bonded to QC-20 polymerized using cycle A and not thermally cycled showed the highest bond strength (P<.001). When Tokuso Rebase Fast and Duraliner II were bonded to QC-20 resin polymerized using cycle A, the bond strength was increased (P=.043) after thermal cycling. Conclusions: QC-20 displayed the lowest bond strength values in all groups. In general, the bond strengths of the hard chairside reline resins were comparable and not affected by polymerization cycle of QC-20 resin and thermal cycling.

Vickers hardness of cast commercially pure titanium and Ti-6Al-4V alloy submitted to heat treatments

The purpose of this study was to evaluate the effect of heat treatments on the Vickers hardness of commercially pure titanium and Ti-6Al-4V cast alloys. Six-millimeter-diameter cylindrical specimens were cast in a Rematitan System. Commercially pure titanium and Ti-6Al-4V alloy specimens were randomly assigned to 3 groups (n=10) that received the following heat treatments: control (no heat treatment); treatment 1 (T1): heating at 750°C for 2 h; and treatment 2 (T2): annealing at 955°C for 1 h and aging at 620°C for 2 h. After heat treatments, the specimens were embedded in acrylic resin and their surface was ground and polished and hardness was measured. Vickers hardness means (VHN) and standard deviations were analyzed statistically by Kruskal-Wallis test at 5% significance level. For commercially pure titanium, Vickers hardness means of group T2 (259.90 VHN) was significantly higher than those of the other groups (control - 200.26 VHN and T1 - 202.23 VHN), which presented similar hardness means to each other (p>0.05). For Ti-6Al-4V alloy, statistically significant differences were observed among the three groups: T2 (369.08 VHN), T1 (351.94 VHN) and control (340.51 VHN) (p<0.05). The results demonstrated different hardness of CP Ti and Ti-6Al-4V when different heat treatments were used. For CP Ti, VHN means of T2 group was remarkably higher than those of control and T1 group, which showed similar VHN means to each other. For Ti-6Al-4V alloy, however, VHN means recorded for each group may be presented as follows: T2>T1>control.

Bond strength of adhesive systems to human tooth enamel

The purpose of this study was to evaluate in vitro three adhesive systems: a total etching single-component system (G1 Prime & Bond 2.1), a self-etching primer (G2 Clearfil SE Bond), and a self-etching adhesive (G3 One Up Bond F), through shear bond strength to enamel of human teeth, evaluating the type of fracture through stereomicroscopy, following the ISO guidance on adhesive testing. Thirty sound premolars were bisected mesiodistally and the buccal and lingual surfaces were embedded in acrylic resin, polished up to 600-grit sandpapers, and randomly assigned to three experimental groups (n = 20). Composite resin cylinders were added to the tested surfaces. The specimens were kept in distilled water (37°C/24 h), thermocycled for 500 cycles (5°C-55°C) and submitted to shear testing at a crosshead speed of 0.5 mm/min. The type of fracture was analyzed under stereomicroscopy and the data were submitted to Anova, Tukey and Chi-squared (5%) statistical analyses. The mean adhesive strengths were G1: 18.13 ± 6.49 MPa, (55% of resin cohesive fractures); G2: 17.12 ± 5.80 MPa (90% of adhesive fractures); and G3: 10.47 ± 3.14 MPa (85% of adhesive fractures). In terms of bond strength, there were no significant differences between G1 and G2, and G3 was significantly different from the other groups. G1 presented a different type of fracture from that of G2 and G3. In conclusion, although the total etching and self-etching systems presented similar shear bond strength values, the types of fracture presented by them were different, which can have clinical implications.

Influence of cavity preparation and curing method on the marginal seal of resin composite restorations: an in vitro evaluation.

OBJECTIVE: To evaluate the influence of cavity design and photocuring method on the marginal seal of resin composite restorations. METHOD AND MATERIALS: Seventy-two bovine teeth were divided into 2 groups: group 1 received box-type cavity preparations, and group 2 received plate-type preparations. Each group was divided into 3 subgroups. After etching and bonding, Z250 resin composite (3M Espe) was applied in 2 equal increments and cured with 1 of 3 techniques: (1) conventional curing for 30 seconds at 650 mW/cm2; (2) 2-step photocuring, in which the first step was performed 14 mm from the restoration for 10 seconds at 180 mW/cm2 and the second step was performed in direct contact for 20 seconds at 650 mW/cm2; or (3) progressive curing using Jetlite 4000 (J. Morita) for 8 seconds at 125 mW/cm2 and then 22 seconds at 125 mW/cm2 up to 500 mW/cm2. The specimens were thermocycled for 500 cycles and then submitted to dye penetration with a 50% silver nitrate solution. Microleakage was assessed using a stereomicroscope. Data were analyzed using analysis of variance and Tukey test (5% level of significance). RESULTS: A statistically significant difference was found between groups when a double interaction between photocuring and cavity preparation was considered (P = .029). CONCLUSIONS: No one type of cavity preparation or photocuring method prevented micro-leakage. The plate-type preparation showed the worst dye penetration when conventional and progressive photocuring methods were used. The best results were found using the 2-step photocuring with the plate-type preparation.

In vitro evaluation of the precision of working casts for implant-supported restoration with multiple abutments

Objective: The purpose of this study was to compare the accuracy of two working cast fabrication techniques using strain-gauge analysis. Methods: Two working cast fabrication methods were evaluated. Based on a master model, 20 working casts were fabricated by means of an indirect impression technique using polyether after splinting the square transfer copings with acrylic resin. Specimens were assigned to 2 groups (n=10): Group A (GA): type IV dental stone was poured around the abutment analogs in the conventional way; Group B (GB), the dental stone was poured in two stages. Spacers were used over the abutment analogs (rubber tubes) and type IV dental stone was poured around the abutment analogs in the conventional way. After the stone had hardened completely, the spacers were removed and more stone was inserted in the spaces created. Six strain-gauges (Excel Ltd.), positioned in a cast bar, which was dimensionally accurate (perfect fit) to the master model, recorded the microstrains generated by each specimen. Data were analyzed statistically by the variance analysis (ANOVA) and Tukey's test (α= 5%). Results: The microstrain values (με) were (mean±SD): GA: 263.7±109.07με, and GB: 193.73±78.83με. Conclusion: There was no statistical difference between the two methods studied.

In vitro evaluation of surface roughness of 4 resin composites after the toothbrushing process and methods to recover superficial smoothness.

OBJECTIVE: This study evaluated the efficiency of repolishing, sealing with surface sealant, and the joining of both in decreasing the surface roughness of resin-based composites after a toothbrushing process. METHOD AND MATERIALS: Ten specimens of each composite (Alert, Z100, Definite, and Prodigy Condensable), measuring 2 mm in thickness and 4 mm in diameter, were made and submitted to finishing and polishing processes on both sides of the specimens using the Sof-Lex system. The specimens were then subjected to toothbrushing (30,000 cycles), and surface roughness (Ra) was analyzed with a Surfcorder SE 1700 profilometer. The upper surface of each composite was etched with 37% phosphoric acid, and the surface-penetrating sealant Protect-it was applied on 1 surface. The roughness of these surfaces was again measured. On the other side, the surface of the specimen was repolished, and the efficiency of this procedure was measured using the profilometer. The surface roughness resulting from the joining of the 2 methods was verified by applying, in the final stage, the surface-penetrating sealant on the repolished surface. Data were analyzed with analysis of variance and Tukey test (P <.05). RESULTS: Results showed that the lowest surface roughness values were obtained for Definite, Z100, and Prodigy Condensable after the repolishing process and after the repolishing plus sealing. For Alert, the joining of repolishing plus sealing promoted the lowest values of surface roughness. CONCLUSION: Of the resin-based composites, Alert demonstrated the highest values of surface roughness in all the techniques tested.

Factors affecting the strength of denture repairs: Topics of interest

Fracture of dentures is a common clinical finding in daily prosthodontic practice, resulting in great inconvenience to both patient and dentist. A satisfactory repair should be cost-effective, simple to perform, and quick; it should also match the original color and not cause distortion to the existing denture. Different repair materials, surface designs, and mechanical and chemical surface treatments have been recommended in order to obtain stronger repairs. This article reviews some of the available literature with regard to the most important factors that may influence the strength of denture repairs. © 2007 by The American College of Prosthodontists.

Regional odontodysplasia: Case report

Regional odontodysplasia (RO) is a rare developmental anomaly involving both mesodermal and ectodermal dental components in a group of contiguous teeth. It affects the primary and permanent dentitions in the maxilla and mandible or both jaws. Generally it is localized in only one arch. The etiology of this dental anomaly is uncertain. Clinically, affected teeth have an abnormal morphology, are soft on probing and typically discolored, yellow or yellowish-brown. Radiographically, the affected teeth show a ghostlike appearance. This paper reports the case of a 5-year-old girl presenting this rare anomaly on the left side of the maxillary arch, which crossed the midline. The primary maxillary left teeth (except for the canine) and the primary maxillary right central incisor were missing due to previous extractions. The permanent teeth had a ghostlike appearance radiographically. The treatment performed was rehabilitation with temporary partial acrylic denture and periodic controls. In the future, the extraction of affected permanent teeth and rehabilitation with dental implants will be evaluated. The presentation of this case adds valuable information to pediatric dentists to review special clinical and radiographic features of RO, which will facilitate the diagnosis and treatment of patients with this condition.

Influence of resin composite insertion technique in preparations with a high C-factor

Objective: To evaluate the marginal microleakage in enamel and dentin/cementum walls in preparations with a high C-factor, using 3 resin composite insertion techniques. The null hypothesis was that there is no difference among the 3 resin composite insertion techniques. Method and Materials: Standardized Class 5 cavities were prepared in the lingual and buccal aspects of 30 caries-free, extracted third molars. The prepared teeth were randomly assigned to 3 groups: (1) oblique incremental placement technique, (2) horizontal incremental placement technique, and (3) bulk insertion (single increment). The preparations were restored with a 1-bottle adhesive (Single Bond, 3M ESPE) and microhybrid resin composite (Z100, 3M ESPE). Specimens were isolated with nail varnish except for a 2-mm-wide rim around the restoration and thermocycled (1,000 thermal cycles, 5°C/55°C; 30-second dwell time). The specimens were immersed in an aqueous solution of 50 wt% silver nitrate for 24 hours, followed by 8 hours in a photo-developing solution and evaluated for microleakage using an ordinal scale of 0 to 4. The microleakage scores obtained from occlusal and gingival walls were analyzed with Wilcoxon and Kruskal-Wallis nonparametric tests. Results: The null hypothesis was accepted. The horizontal incremental placement technique, the oblique incremental technique, and bulk insertion resulted in statistically similar enamel and dentin microleakage scores. Conclusion: Neither the incremental techniques nor the bulk placement technique were capable of eliminating the marginal microleakage in preparations with a high C-factor.

Anticariogenic effect of fluoride-releasing elastomers in orthodontic patients

This in vivo experimental study evaluated the efficacy of fluoride-releasing elastomers in the control of Streptococcus mutans levels in the oral cavity. Forty orthodontic patients were recruited and divided into two groups of 20. Fluoride-releasing elastomeric ligature ties (Fluor-I-Ties, Ortho Arch Co. Inc., USA) were used in the experimental group, and conventional elastomeric ligature ties (D. Morelli, Brazil), in the control group. Two initial samples of saliva were collected at a 14-day interval to determine the number of colony forming units (CFU) of Streptococcus mutans. Immediately after collecting the second sample, fluoride-releasing elastomeric ligature ties were placed in the patients of the experimental group, and conventional ligature ties, in the patients of the control group. Seven, 14 and 28 days after placement of the elastomeric ligature ties, saliva and plaque surrounding the orthodontic appliance were collected for microbiologic analysis. There were no significant differences in the number of Streptococcus mutans CFUs in saliva or plaque in the area surrounding the fluoride-releasing or conventional elastomeric ligature ties. Thus, fluoride-releasing elastomeric ligature ties should not be indicated to reduce the incidence of enamel decalcification in orthodontic patients. Since there was no significant reduction in S. mutans in saliva or plaque, other means of prevention against enamel decalcification should be indicated for these patients.

Influence of brush type as a carrier of adhesive solutions and paper points as an adhesive-excess remover on the resin bond to root dentin

Purpose: To evaluate the influence of the brush type as a earner of priming adhesive solutions and the use of paper points as a remover of the excess of these solutions on the push-out bond strength of resin cement to bovine root dentin. The null hypotheses were that brush type and the use of paper points do not affect the bond strength. Materials and Methods: The canals of 80 single-root bovine roots (16 mm in length) were prepared at 12 mm using the preparation drill (FRC Postec Plus, Ivoclar). Half of each root was embedded in acrylic resin and the specimens were divided into 8 groups, considering the factors brush type (4 levels) and paper point (2 levels) (n = 10): Gr 1: small microbrush (Cavi-Tip, SDI); Gr 2: Microbrush (Dentsply); Gr 3: Endobrush (Bisco); Gr 4: conventional brush (Bisco); Gr 5: Cavi-Tip (SDI) + paper points; Gr 6: Microbrush (Dentsply) + paper points; Gr 7: Endobrush (Bisco) + paper points; Gr 8: conventional brush (Bisco) + paper points. The root dentin was treated with a multistep total-etch adhesive system (All Bond 2). The adhesive system was applied using each microbrush, with and without using paper points. One fiber post was molded with addition silicon and 80 posts were made of resin cement (Duolink), The resin posts were luted (Duolink resin cement), and the specimens were stored for 24 h in water at 37°C. Each specimen was cut into 4 disk-shaped samples (1.8 mm in thickness), which were submitted to the push-out test. Results: The brush type (p < 0.0001) (small microbrush > microbrush = endobrush = conventional brush) and the use of paper points (p = 0.0001) (with > without) influenced the bond strength significantly (two-way ANOVA). The null hypotheses were rejected. Conclusion: The smallest brush (Cavi-Tip) and the use of paper points significantly improved the resin bond to bovine root dentin.

In vitro evaluation of the abrasiveness of a commercial low-abrasive dentifrice and an experimental dentifrice containing vegetable oil

Toothpastes usually contain detergents, humectants, water colorant, fluoride and thickeners (e.g. silica). Tooth wear has a multi-factorial etilology and the use of abrasive dentifrices is related to abrasion of dental tissues during toothbrushing. This study evaluated in vitro the abrasiveness of a commercial silica gel low-abrasive dentrifice compared to an experimental dentifrice containing vegetable (almond) oil. Distilled water served as a control group. Acrylic specimens (8 per group) were submitted to simulated toothbrushing with slurries of the commercial dentifrice experimental dentifrice, almond oil and water in an automatic brushing machine programmed to 30,000 brush strokes for each specimen which is equivalent to 2 years of manual toothbrushing. Thereafter, surface roughness (Ra) of the specimens was analyzed with a Surfcorder SE 1700 profilometer. Data were analyzed statistically by ANOVA and Tukey's test at 5% significance level. There was no statistically significant differences (p>0.05) in the surface roughness after brushing with water almond oil experimental dentifrice. The commercial dentifrice produced rougher surfaces compared to the control and abrasive free products (p<0.05). Further studies are necessary in confirm the potential benefits of using vegetable oil in toothpaste as an alternative in abrasives in an attempt to minimize the tooth wear caused by toothbrushing.