Transparent Ni2+-doped silicate glass ceramics for broadband near-infrared emission

Transparent Ni2+-doped MgO-Al2O3-Ga2O3-SiO2-TiO2 glass ceramics were fabricated. The precipitated nanocrystal phase in the glass ceramics was identified by X-ray diffraction and transmission electron microscope. Broadband near-infrared emission centered at 1220 nm with full width at half maximum of about 240 nm and lifetime of about 250 mu s was observed with 980 nm excitation. The longer wavelength emission compared with Ni2+-doped MgAl2O4 crystal was attributed to the low crystal field occupied by Ni2+ in the glass ceramics. The present Ni2+-doped transparent glass ceramics may have potential applications in broadband optical amplifiers. (c) 2007 Elsevier B.V. All rights reserved.

Luminescence properties of bismuth-doped lime silicate glasses

Luminescences from bismuth-doped lime silicate glasses were investigated. Luminescences centered at about 400, 650, and 1300 nm were observed, excited at 280, 532 and 808 nm, respectively. These three luminescence bands arise from three different kinds of bismuth ions in the glasses. The visible luminescences centered at 400 and 650 nm arise from Bi3+, and Bi2+, respectively. The infrared luminescences cover the wavelength range from 1000 to 1600 nm when exited by an 808 nm laser diode. The full width at half maximum (FWHM) of the infrared luminescences is more than 205 urn. The intensity of the infrared luminescence decreases with the increment in CaO content. We suggest that the infrared luminescences might arise from Bi+. Such broadband luminescences indicate that the glasses may be potential candidate material for broadband fiber amplifiers and tunable lasers. (C) 2007 Elsevier B.V. All rights reserved.

Broadband infrared luminescence from bismuth-doped GeS2-Ga2S3 chalcogenide glasses

Near-infrared luminescence is observed from bismuth-doped GeS2-Ga2S3 chalcogenide glasses excited by an 808 nm laser diode. The emission peak with a maximum at about 1260 nm is observed in 80GeS(2)-20Ga(2)S(3):0.5Bi glass and it shifts toward the long wavelength with the addition of Bi gradually. The full width of half maximum (FWHM) is about 200 nm. The broadband infrared luminescence of Bi-doped GeS2-Ga2S3 chalcogenide glasses may be predominantly originated from the low valence state of Bi, such as Bi+. Raman scattering is also conducted to clarify the structure of glasses. These Bi-doped GeS2-Ga2S3 chalcogenide glasses can be applied potentially in novel broadband optical fibre amplifiers and broadly tunable laser in optical communication system.

Broadband infrared luminescence of bismuth-doped borosilicate glasses

We prepare bismuth-doped borosilicate glasses and the luminescence properties in infrared wavelength region are investigated. Transmission spectrum, fluorescence spectrum and fluorescence decay curve are measured. The glasses exhibit a broad infrared luminescence peaking at 1340nm with the full width at half maximum of about 205nm, and lifetime of 273 mu s when excited by an 808-nm laser diode. The glasses are promising materials for broadband optical amplifiers and tunable lasers.

GeO2 : Bi, M (M = Ga, B) glasses with super-wide infrared luminescence

Broadband infrared luminescence covering the optical telecommunication wavelength region of 0, E and S bands was observed in GeO2: Bi, M (M = Ga, B) glasses prepared by conventional melting-quenching technique. The luminescence with a maximum at around 1320 nm possesses a full width at half maximum larger than 300 nm and mean fluorescent lifetime longer than 500 mus when excited by an 808 nm-laser. These glasses may have potential applications in widely tunable laser and super-broadband optical amplifier for the optical communications. (C) 2005 Elsevier B.V. All rights reserved.

Yb掺杂的YAlO<3/sub>单晶体的温梯法生长和光谱性能

The dark-brown colored 5 at% Yb-doped YAlO3 (Yb:YAP) single crystal was grown successfully by temperature gradient technique (TGT) for the first time. The TGT-grown Yb:YAP crystal with the perovskite structure and excellent crystallization perfection were confirmed by the X-ray diffractions techniques. The dark-brown color of TGT-Yb:YAP crystal turned into the colorless after annealing in the air at 1200 degrees C for 10h. The absorption spectra, LD-excited infrared emission and X-ray excited luminescence spectra of the air-annealed Yb:YAP single crystal were investigated at the room temperature. The results indicate that the TGT-Yb:YAP single crystals can be used for the laser and scintillation applications. (c) 2005 Elsevier B.V. All rights reserved.

Broadband near-infrared emission from transparent Ni2+-doped sodium aluminosilicate glass ceramics

Broadband neat-infrared emission from transparent Ni2+-doped sodium aluminosilicate glass-cermaics is observed. The broad emission is centered at 1290 nm and covers the whole telecommunication wavelength region (1100-1700 nm) with full width at half maximum of about 340 nm. The observed infrared emission could be attributed to the T-3(2)(F) -> (3)A(2)(F) transition of octahedral Ni2+ ions that occupy high-field sites in nanocrystals. The product of the lifetime and the stimulated emission cross section is 2.15 x 10(-24) cm(2)s. It is suggested that Ni2+-doped sodium aluminosilicate glass ceramics have potential applications in tunable broadband light sources and broadband amplifiers.

Cr4+在Al2O3多晶体中的光谱性能研究

Transparent polycrystalline Cr:Al2O3 ceramics were synthesized by conventional pressureless synthesis processing. The absorption and emission spectra of Cr:Al2O3 ceramics specimens before and after annealing were measured at room temperature. It was discovered that the emission spectra of Cr4+ in Al2O3 octahedral coordination site is in infrared wavelength range of 1100-1600 nm. The emission peak of Cr4+ is centered at 1223 nm, which is similar to that of Cr4+ in tetrahedral site. Al2O3 has smaller lattice constant, resulting in the larger crystal field strength, so there is a blue shift in the peak of Cr4+:Al2O3 ceramics compared to those of other Cr4+-doped crystals. And the emission band is much narrower with full width at half maximum Delta lambda 37 nm.

Influence of vapor transport equilibration on the crystal quality and thermal-expansion coefficients of gamma-LiAlO2

gamma-LiAlO2 (LAO) single crystal has been grown by the Czochralski method. However, its quality was deteriorated due to lithium volatilization during the crystal growth. The full width at half maximum value drops from 116.9 to 44.2 arc sec after the LAO slice was treated by vapor transport equilibration at 1000, 1100, and 1200 degrees C/48 h in sequence. The treated slice shows higher optical transmission than the as-grown one in the measured wavelength range of 190-1900 nm, meanwhile, its absorption edge exhibits a blueshift. According to Raman spectra, the treated slice has homogeneous quality at different depths from surface to 0.01 mm. The expansion coefficient of the treated slice for a axis drops from 17.2398x10(-6)/degrees C to 16.5240x10(-6)/degrees C, and that for c axis drops from 10.7664x10(-6)/degrees C to 10.0786x10(-6)/degrees C.

激光二极管抽运Na，Yb共掺CaF2晶体自调Q激光特性的研究

利用激光二极管（LD）抽运新型Na．Yb共掺CaF2（Na．Yb：CaF2）晶体，获得了1．05μm的自调Q激光输出。利用透射率1％的耦合输出镜，得到最低激光输出的抽运阈值功率仅为70mW。在透射率为2％的输出镜条件下，得到最大输出激光功率为390mw，此时激光的斜度效率达到20%。实验详细记录了自调Q脉冲的周期和宽度随抽运功率的变化关系，随着抽运功率的增加，自调Q脉冲的周期和宽度呈指数衰减。同时，还采用单棱镜进行光谱调谐实验，获得了1036～1059nm的自调Q激光调谐输出。

Nd：YbVO4晶体的拉曼光谱和荧光光谱研究

用群论的方法计算了Nd：YbVO4晶体的拉曼活性振动模数目，在室温下测得了其极化拉曼谱线，并指认了在不同几何配置下，各振动模式所对应的频率。同时，测得了室温下晶体的吸收谱，得到了中心波长为808am吸收峰的半高宽为12nm，并在J-O理论的基础上计算了晶体的光学参数，其三个晶场参数分别为Ω2=6．88945×10^-20cm^2。Ω4=4．13394×10^-20cm^2、Ω6=4．54503×10^-20cm^2，并由此得到^4F3／2能级的荧光寿命为178．69炉，1062nm处的荧光分支比为48．85％，积分发射截面为2．786710^-18cm^2。分别在808nm、940nm激发下测得晶体室温发射谱，观察到了Nd→Yb以及Nd←Yb间的能量传递现象。

Fabrication and spectral properties of Nd3+-doped yttrium lanthanum oxide transparent ceramics

Transparent 1 at% Nd3+:Y1.9La0.1O3 ceramics were fabricated with nanopowders prepared by carbonate coprecipitation method. The powder compacts were sintered in H-2 atmosphere at 1550 degrees C for 30 h. The Nd3+:Y1.9La0.1O3 ceramics display uniform grains of about 50 mu m and high transparency. The highest transmittance of the ceramics reaches 67%. The strongest absorption peak is in the wavelength of 820 nm with absorption cross section of 2.48 x 10(-20) cm(2). The absorption is still high at LD wavelength 806 nm with absorption cross section of 1.78 x 10(-20) cm(2) and broad full width at half maximum (FWHM) of about 6.3 nm. The strongest emission peak was centered at 1078 nm with large stimulated emission cross section of 9.63 x 10(-20) cm(2) and broad FWHM of about 7.8 nm. The broad absorption and emission bandwidth of Nd3+:y(1.9)La(0.1)O(3) transparent ceramics are favorable to achieve the miniaturized LD pumping apparatus and ultrashort modelocked pulse laser output, respectively. (c) 2007 Elsevier B.V. All rights reserved.

Growth and characterization of high-quality LiAlO2 single crystal

g-LiAlO2 single crystal is a promising substrate for GaN heteroepitaxy. In this paper, we present the growth of large-sized LiAlO2 crystal by modified Czochralski method. The crystal quality was characterized by high-resolution X-ray diffraction and chemical etching. The results show that the as-grown crystal has perfect quality with the full width at half maximum (FWHM) of 17.7-22.6 arcsec and etch pits density of (0.3-2.2) x 10(4) cm(-2) throughout the crystal boule. The bottom of the crystal boule shows the best quality. The optical transmission spectra from UV to IR exhibits that the crystal is transparent from 0.2 to 5.5 mu m and becomes completely absorbing around 6.7 mu m wavelength. The optical absorption edge in near UV region is about 191 nm.

Judd-Oflet analysis of spectrum and laser performance of Ho:YAP crystal end-pumped by 1.91-mu m Tm:YLF laser

The Ho:YAP crystal is grown by the Czochralski technique. The room-temperature polarized absorption spectra of Ho:YAP crystal was measured on a c-cut sample with 1 at% holmium. According to the obtained Judd-Ofelt intensity parameters Omega(2) = 1.42 x 10(-20) cm(2), Omega(4) = 2.92 x 10(-20) cm(2), and Omega(6) = 1.71 x 10(-20) cm(2), this paper calculated the fluorescence lifetime to be 6 ms for I-5(7) -> I-5(8) transition, and the integrated emission cross section to be 2.24 x 10(-18) cm(2). It investigates the room-temperature Ho:YAP laser end-pumped by a 1.91-mu m Tm:YLF laser. The maximum output power was 4.1 W when the incident 1.91-mu m pump power was 14.4W. The slope efficiency is 40.8%, corresponding to an optical-to-optical conversion efficiency of 28.4%. The Ho:YAP output wavelength was centred at 2118 nm with full width at half maximum of about 0.8 nm.