Synthesis of bis(amine anhydride)s for novel high T(g)s and organosoluble poly(amine imide)s by palladium-catalyzed amination of 4-chlorophthalide anhydride

Two novel bis(amine anhydride)s, NN-bis(3,4-dicarboxyphenyl)aniline dianhydride (I) and N,N-bis(3,4-dicarboxyphenyl)-p-tert-butylaniline (II), were synthesized from the palladium-catalyzed amination reaction of N-methyl-protected 4-chlorophthalic anhydride with arylamines, followed by alkaline hydrolysis of the intermediate bis(amine-phthalimide)s and subsequent dehydration of the resulting tetraacids. The X-ray structures of anhydride I and II were determined. The obtained dianhydride monomers were reacted with various aromatic diamines to produce a series of novel polyimides. Because of the incorporation of bulky, propeller-shaped triphenylamine units along the polymer backbone, all polyimides exhibited good solubility in many aprotic solvents while maintaining their high thermal properties. These polymers had glass transition temperatures in the range of 298-408 degrees C. Thermogravimetric analysis showed that all polymers were stable, with 10% weight loss recorded above 525 degrees C in nitrogen.The tough polymer films, obtained by casting from solution, had tensile strength, elongation at break, and tensile modulus values in the range of 95-164 MPa, 8.8-15.7%, and 1.3-2.2 GPa, respectively.

Water-resistant conducting hybrids from electrostatic interactions

Conductive hybrids were prepared in a water/ethanol solution via the Solgel process from an inorganic sol containing carboxyl groups and water-borne conductive polyaniline (cPANI). The inorganic sol was prepared by the hydrolysis and condensation of methyltriethoxysilane with the condensed product of maleic anhydride and aminopropyltriethoxysilane as a catalyst, for which the carboxyl counterion along the cPANI backbone acted as an electrostatic-interaction moiety. The existence of this electrostatic interaction could improve the compatibility of the two components and contribute to the homogeneous dispersion of cPANI in the silica phase. The electrostaticinteraction hybrids displayed a conductivity percolation threshold as low as 1.1 wt % polyaniline in an emeraldine base, showing 2 orders of magnitude higher electrical conductivity than that without electrostatic interactions. The electrostatic-interaction hybrids also showed good water resistance; the electrical conductivity with a cPANI loading of 16 wt % underwent a slight change after 14 days of soaking in water.

Stimuli-responsive polyelectrolyte block copolymer brushes synthesized from the si wafer via atom-transfer radical polymerization

Surface-tethered oppositely charged weak polyelectrolyte block copolymer brushes composed of poly(2-vinyl pyridine) (P2VP) and poly(acrylic acid) (PAA) were grown from the Si wafer by atom-transfer radical polymerization. The P2VP-b-PAA brushes were prepared through hydrolysis of the second PtBA block to the corresponding acrylic acid. The P2VP-b-PAA brushes with different PAA block length were obtained. The P2VP-b-PAA brushes revealed a unique reversible wetting behavior with pH. The difference between the solubility parameters for P2VP and PAA, the changes of surface chemical composition and surface roughness, and the reversible wetting behavior illustrated that the surface rearrangement occurred during treatment of the P2VP-b-PAA brushes by aqueous solution with different pH value. The reversible properties of the P2VP-b-PAA brushes can be used to regulate the adsorption of the sulfonated PS nanoparticles.

利用电喷雾质谱技术研究复方中药的配伍原则

Traditional Chinese Medicine (TCM) based on natural products is one important part of the Chinese civilization.Owing to the complexity of the composition,the study on medical effective components and curative effects are very difficult;Fuzi (Radix Aconiti Lateralis Praeparata) has been widely used for cardiotonic and analgesics in China,however,the component-aconitine in which is very toxic and may cause some side-effect.This paper reported the application of electrospray iohization mass spectrometric(ESIMS) technique on study of the compound prescriptions containing fuzi,Renshensini concoction and Baweidihuang concoction,to explore the mechanism of synergy between fuzi and other herbs.From chemical point of view,the detoxification mechanism can be attributed to the hydrolysis of the solubility of toxic diester-alkaloids from concoctions of fuzi.Radix Glycyrrhizae Praeparata,Rhizoma Zingiberis,Radix Ginsengp promote the hydrolysis to produce the less toxic monoester-alkaloids and Fructus Corni reduce the solubility of hypaconitine from fuzi.

Novel acidic porous clay heterostructure with highly ordered organic-inorganic hybrid structure: one-pot synthesis of mesoporous organosilica in the galleries of clay

A new class of organic-inorganic hybrid porous clay heterostructures (HPCHs) have been prepared through the surfactant-directed assembly of organosilica in the galleries of montmorillonite. The reaction involved hydrolysis and condensation of phenyltriethoxysilane and tetraethoxysilane in the presence of intragallery surfactant templates (dodecylame and cetyltrimethylammonium ion). The surfactant templates were removed from the pores by solvent-extraction. The products were characterized by X-ray diffraction (XRD), N-2 adsorption, solid-state Si-29 and C-13 NMR, and FTIR. XRD patterns indicated a regular interstratification of the clay layers for HPCHs. Depending on loading of phenyl groups, HPCHs had BET surface areas of 390-771 m(2) g(-1), pore volumes of 0.3-0.59 cm(3) g(-1), and the framework pore sizes in the supermicropore to small mesopore range (1.2-2.6 nm). HPCHs were hydrophobic and acidic.

A facile synthetic method for biphenyltetracarhoxylic dianhydrides

We report a facile and high-yielding procedure for preparing biphenyltetracarboxylic dianhydrides (BPDAs). This method relies on a nickel-catalyzed electroreductive coupling reaction of dimethyl 3-chorophthalate (3-DMCP) and/or dimethyl 4-chorophthalate (4-DMCP) with subsequent hydrolysis of tetra-ester and dehydration of tetra-acid.

Preparation and luminescence properties of in situ formed lanthanide complexes covalently grafted to a silica network

Lanthanide-doped sol-gel-derived materials are an attractive type of luminescent materials that can be processed at ambient temperatures. However, the solubility of the lanthanide complexes in the matrix is a problem and it is difficult to obtain a uniform distribution of the complexes. Fortunately, these problems can be solved by covalently linking the lanthanide complex to the sol-gel-derived matrix. In this study, luminescent Eu3+ and Tb3+ bipyridine complexes were immobilized on sol-gel-derived silica. FT-IR, DTA-TG and luminescence spectra, as well as luminescence decay analysis, were used to characterize the obtained hybrid materials. The organic groups from the bipyridine-Si moiety were mostly destroyed between 220 and 600 degreesC. The luminescence properties of lanthanide bipyridine complexes anchored to the backbone of the silica network and the corresponding pure complexes were comparatively investigated, which indicates that the lanthanide bipyridine complex was formed during the hydrolysis and co-condensation of TEOS and modified bipyridine. Excitation at the ligand absorption wavelength (336 nm for the hybrid materials and 350 nm for the pure complexes) resulted in strong emission of the lanthanide ions: Eu3+ D-5(0)-F-7(J) (J = 0, 1, 2, 3, 4) and Tb3+ D-5(4)-F-7(J) (J = 6, 5, 4, 3) emission lines due to efficient energy transfer from the ligands to the lanthanide ions.

Enzymatic degradation of poly(L-lactide) and poly (epsilon-caprolactone) electrospun fibers

Poly(L-lactide) (PLLA) and poly(epsilon-caprolactone) (PCL) ultrafine fibers were prepared by electrospinning. The influence of cationic and anionic surfactants on their enzymatic degradation behavior was investigated by measuring weight loss, molecular weight, crystallinity, and melting temperature of the fibers as a function of degradation time. Under the catalysis of proteinase K, the PLLA fibers containing the anionic surfactant sodium docecyl sulfate (SDS) exhibited a faster degradation rate than those containing cationic surfactant triethylbenzylammonium chloride (TEBAC), indicating that surface electric charge on the fibers is a critical factor for an enzymatic degradation. Similarly, TEBAC-containing PCL fibers exhibited a 47% weight loss within 8.5 h whereas SDS-containing PCL fibers showed little degradation in the presence of lipase PS. By analyzing the charge status of proteinase K and lipase PS under the experimental conditions, the importance of the surface charges of the fibers and their interactions with the charges on the enzymes were revealed. Consequently, a "two-step" degradation mechanism was proposed: (1) the enzyme approaches the fiber surface; (2) the enzyme initiates hydrolysis of the polymer.

Sol-Gel Preparation of Zn2 Si04：Mn Phosphor Layers on Silica Spheres and Their Luminescent Properties

The synthesis and luminescence properties of Zn2SiO4:Mn phosphor layers on spherical silica spheres,i.e.,a kind of core-shell complex phosphor,Zn2SiO4:Mn@SiO2 were described.Firstly,monodisperse silica spheres were obtained via the Stober method by the hydrolysis of tetraethoxysilane(TEOS)Si(OC2H5)4 under base condition (using NH4OH as the catalyst).Secondly,the silica spheres were coated with a Zn2SiO4:Mn phosphor layer by a Pechini sol-gel process.X-ray diffraction(XRD),scanning electron microscope(SEM),energy-dispersive X-ray spectrum(EDS) and photoluminescence(PL) were employed to characterize the resulting complex phosphor.The results comfirm that 1000℃ annealed sample consists of crystalline Zn2SiO4:Mn shells and amorphous SiO2 cores.The phosphor show the green emission of Mn2+ at 521nm corresponding 4T1(4G)-6A1(6S) transition,and the possible luminescence mechanism is proposed.

Specific determination of As(V) by an acid phosphatase-polyphenol oxidase biosensor

An original amperometric biosensor based on the simultaneous entrapment of acid phosphatase (AcP) and polyphenol oxidase (PPO) into anionic clays (layered double hydroxides) was developed for the specific detection of As(V). The functioning principle of the bienzyme electrode consisted of the successive hydrolysis of phenyl phosphate into phenol by AcP, followed by the oxidation of phenol into o-quinone by PPO. The phenyl phosphate concentration was, thus, monitored by potentiostating the biosensor at -0.2 V vs Ag/AgCl to detect amperometrically the generated quinone. The detection of As(V) was based on its inhibitory effect on AcP activity toward the hydrolysis of phenyl phosphate into phenol. The As(V) can be specifically determined in pH 6.0 acetate buffer without any interferences of As(III) or phosphate, the detection limit being 2 nM or 0.15 ppb after an incubation step for 20 min.

PolydA and polyrA self-structured by a europium and amino acid complex

Different DNA selectivity was found for the newly synthesized europium-L-valine complex. Unexpected DNA and RNA selection results showed that europium-L-valine complex can cause single-stranded polydA and polyrA to self-structure. The sigmoidal melting curve profiles indicate the transition is cooperative, similar to the cooperative melting of a duplex DNA. This is different from another europium amino acid complex, europium-L-aspartic acid complex which can induce B-Z transition under the low salt condition. To our knowledge, there is no report to show that a metal-amino acid complex can cause the self-structuring of single-stranded DNA and RNA.

Preparation and properties of ternary polyimide/SiO2/polydiphenyisiloxane composite films

A series of novel ternary polyimide/SiO2/polydiphenylsiloxane (PI/SiO2/PDPhS) composite films were prepared through co-hydrolysis and condensation between tetramethoxysilane, diphenyldimethoxysilane (DDS) and aminopropyltriethoxysilane-terminated polyamic acid, using an in situ sol-gel method. The composite films exhibited good optical transparency up to 30 wt% of total content of DDS and SiO2. SEM analysis showed that the PDPhS and SiO2 were well dispersed in the PI matrix without macroscopic separation of the composite films. TGA analysis indicated that the introduction of SiO2 could improve the thermal stability of the composite films. Dynamic mechanical thermal analysis showed that the composite films with low DDS content (5 wt%) had a higher glass transition temperature (T-g) than pure PI matrix. When the content of DDS was above 10 wt%, the T-g of the composite decreased slightly due to the plasticizing effect of flexible PDPhS linkages on the rigid PI chains. The composite films with high SiO2 content exhibited higher values of storage modulus. Tensile measurements also showed that the modulus and tensile strength of the composite films increased with increasing SiO2 content, and the composite films still retained a high elongation at break due the introduction of DDS.

Luminescence and energy transfer of organically modified silica xerogels (OMSX) doped and undoped with Eu3+ and Tb3+

Organically modified silica xerogels (OMSX) and Eu3+ (Tb3+)-doped OMSX were prepared by the reaction of (3-aminopropyl) triethoxysilane (APS) with 3-isocyanatepropyltriethoxysilane (ICPTES) followed by the subsequent hydrolysis and condensation in the presence of Eu3+ (Tb3+) via sol-gel method, which were characterized by FT-IR, XRD, fluorescence excitation and emission spectra. The as-formed OMSX shows a strong blue emission with the maximum excitation and emission wavelength at 351 and 420 nm, respectively. Due to the spectral overlap between the emission band of OMSX and f-f absorption lines of Eu3+ and Tb3+ in the UV-blue region, an energy transfer was observed from OMSX host to Eu3+ and Tb3+ in OMSX/Eu3+ and OMSX/Tb3+, respectively. Excitation at 350-360 nm resulted in a very weak emission around 420 nm from OMSX host and strong emission of Eu3+ and Tb3+ in OMSX/Eu3+ and OMSX/Tb3+, respectively. The emission spectra of Eu3+ and Tb3+ consist of D-5(0)-F-7(J) (J = 0, 1, 2, 3, 4) and D-5(4)-F-7(J) (J = 6, 5, 4, 3), respectively. Furthermore, the predicted structure of OMSX/Eu3+ and OMSX/Tb3+ is presented.

Preparation and characterization of novel luminescent sol-gel films containing a RE3+ carboxylic acid complex

RE3+ (Eu3+, Tb3+) complexes with carboxylic acid (salicylic acid and benzoic acid) were introduced into the sol, which was prepared by the hydrolysis of tetraethoxysilane (TEOS). A sol-gel luminescent thin film (SG-LTF) was then prepared by dispersing the sol onto a silica substrate by a spin coating method. Multi-layer luminescent thin films were prepared by repeating the same process. The luminescent spectra, fluorescence lifetime and thermal stability of the SG-LTFs were investigated. For the reason of comparison polyvinylbutyral (PVB) was added into a N,N-dimethylformamide (DMF) solution in which the comparative RE3+ carboxylic acid complexes were previously dissolved to form the DMF/PVB solution and the PVB luminescent thin film (PVB-LTF) was prepared. The results show that a broad excitation band indicates the formation of RE complexes in the solid SG-LTFs. RE ions, which are restrained in the silica matrix, present longer lifetimes and higher thermal stability than that in the PVB-LTF containing the corresponding pure complexes. The different doping concentration of RE (III) complexes in the SG-LTFs and the different change of the emission intensities with the heat treatment temperature in the sol-gel thin film and the sol-gel bulk gel were also discussed in this paper.

Preparation and characterization of PSt-b-PHEMA metal hybrids

The block copolymer polystyrene-b-poly[2-(trimethylsilyloxy)ethylene methacrylate] (PSt-b-PTMSEMA) was synthesized using atom-transfer radical polymerization (ATRP). The hydrolysis of PSt-b-PTMSEMA led to the formation of an amphiphilic block copolymer, polystyrene-b-poly(2-hydroxylethyl methacrylate) (PSt-b-PHEMA), which was characterized by GPC and H-1-NMR. TEM showed that the PSt-b-PHEMA formed a micelle, which is PSt as the core and PHEMA as the shell. Under appropriate conditions, the nickel or cobalt ion cause chemical reactions in these micelles and could be reduced easily. ESCA analysis showed that before reduction the metal existed as a hydroxide; after reduction, the metal existed as an oxide, and the metal content of these materials on the surface is more than that on the surface of the copolymer metal ion. XRD analysis showed that the metal existed as a hydroxide before reduction and existed as a metal after reduction.