Effect of nanoclay content and compatibilizer on viscoelastic properties of montmorillonite/polypropylene nanocomposites

This paper deals with preparation of nanocomposites using modified nanoclay (organoclay) and polypropylene (PP), with, and without compatibilizer (m-TMI-g-PP) to study the effects of modified nanoclay and compatibilizer on viscoelastic properties. Nanocomposites were prepared in two steps; compounding of master batch of nanoclay, polypropylene and m-TMI-g-PP in a torque rheometer and blending of this master-batch with polypropylene in a twin-screw extruder in the specific proportions to yield 3-9% nanoclay by weight in the composite. Dynamic Mechanical Analysis (DMA) tests were carried out to investigate the viscoelastic behavior of virgin polypropylene and nanocomposites. The dynamic mechanical properties such as storage modulus (E'), loss modulus (E `') and damping coefficient (tand) of PP and nano-composites were investigated with and without compatibilizer in the temperature range of -40 degrees C to 140 degrees C at a step of 5 degrees C and frequency range of 5 Hz to 100 Hz at a step of 10 Hz. Storage modulus and loss modulus of the nano-composites was significantly higher than virgin polypropylene throughout the temperature range. Storage modulus of the composites increased continuously with increasing nano-content from 3% to 9%. Composites prepared with compatibilizer exhibited inferior storage modulus than the composites without compatibilizer. Surface morphology such as dispersion of nanoclay in the composites with and without compatibilizer was analyzed through Atomic Force Microscope (AFM) that explained the differences in viscoelastic behavior of composites. (C) 2011 Elsevier Ltd. All rights reserved.

Use of acoustic emissions in flexural fatigue crack growth studies on concrete

The acoustic emission technique is used for monitoring the fatigue crack growth in plain concrete beams under three-point loading. Variable amplitude loading with step-wise increase in the maximum load is applied. The fatigue crack growth is continuously monitored using six acoustic sensors. The results of load, displacement, crack mouth opening displacement, acoustic events, and acoustic energy are simultaneously acquired during the test. It is seen that a Paris law type of relationship exists between the rate of increase of acoustic emission count per cycle and the stress intensity factor range. Using b-value analysis, different stages of fatigue fracture is explained. (C) 2012 Elsevier Ltd. All rights reserved.

Effect of ``dipolar-biasing'' on the tunability of tunneling magnetoresistance in transition metal oxide systems

We observe an unusual tunneling magnetoresistance (TMR) phenomenon in a composite of La2/3Sr1/3MnO3 with CoFe2O4 where the TMR versus applied magnetic field loop suggests a ``negative coercive field.'' Tracing its origin back to a ``dipolar-biasing'' of La2/3Sr1/3MnO3 by CoFe2O4, we show that the TMR of even a single composite can be tuned continuously so that the resistance peak or the highest sensitivity of the TMR can be positioned anywhere on the magnetic field axis with a suitable magnetic history of the sample. This phenomenon of an unprecedented tunability of the TMR should be present in general in all such composites. (C) 2012 American Institute of Physics.http://dx.doi.org/10.1063/1.4731206]

LOCAL TWO-DIMENSIONAL PARTICLE-IN-CELL SIMULATIONS OF THE COLLISIONLESS MAGNETOROTATIONAL INSTABILITY

The magnetorotational instability (MRI) is a crucial mechanism of angular momentum transport in a variety of astrophysical accretion disks. In systems accreting at well below the Eddington rate, such as the central black hole in the Milky Way (Sgr A*), the plasma in the disk is essentially collisionless. We present a nonlinear study of the collisionless MRI using first-principles particle-in-cell plasma simulations. We focus on local two-dimensional (axisymmetric) simulations, deferring more realistic three-dimensional simulations to future work. For simulations with net vertical magnetic flux, the MRI continuously amplifies the magnetic field, B, until the Alfven velocity, v(A), is comparable to the speed of light, c (independent of the initial value of v(A)/c). This is consistent with the lack of saturation of MRI channel modes in analogous axisymmetric MHD simulations. The amplification of the magnetic field by the MRI generates a significant pressure anisotropy in the plasma (with the pressure perpendicular to B being larger than the parallel pressure). We find that this pressure anisotropy in turn excites mirror modes and that the volume-averaged pressure anisotropy remains near the threshold for mirror mode excitation. Particle energization is due to both reconnection and viscous heating associated with the pressure anisotropy. Reconnection produces a distinctive power-law component in the energy distribution function of the particles, indicating the likelihood of non-thermal ion and electron acceleration in collisionless accretion disks. This has important implications for interpreting the observed emission-from the radio to the gamma-rays-of systems such as Sgr A*.

Optimal Control of Markov Processes with Age-Dependent Transition Rates

We study optimal control of Markov processes with age-dependent transition rates. The control policy is chosen continuously over time based on the state of the process and its age. We study infinite horizon discounted cost and infinite horizon average cost problems. Our approach is via the construction of an equivalent semi-Markov decision process. We characterise the value function and optimal controls for both discounted and average cost cases.

Seismic stability of a long unsupported circular tunnel

The stability of a long unsupported circular tunnel (opening) in a cohesive frictional soil has been assessed with the inclusion of pseudo-static horizontal earthquake body forces. The analysis has been performed under plane strain conditions by using upper bound finite element limit analysis in combination with a linear optimization procedure. The results have been presented in the form of a non-dimensional stability number (gamma H-max/c); where H = tunnel cover, c refers to soil cohesion and gamma(max) is the maximum unit weight of soil mass which the tunnel can support without collapse. The results have been obtained for various values of H/D (D = diameter of the tunnel), internal friction angle (phi) of soil, and the horizontal earthquake acceleration coefficient (alpha(h)). The computations reveal that the values of the stability numbers (i) decrease quite significantly with an increase in alpha(h), and (ii) become continuously higher for greater values of H/D and phi. As expected, the failure zones around the periphery of the tunnel becomes always asymmetrical with an inclusion of horizontal seismic body forces. (c) 2012 Elsevier Ltd. All rights reserved.

Signatures of Indian ocean Dipole and El Nino-Southern Oscillation events in sea level variations in the Bay of Bengal

We investigate the impact of the Indian Ocean Dipole (IOD) and El Nino and the Southern Oscillation (ENSO) on sea level variations in the North Indian Ocean during 1957-2008. Using tide-gauge and altimeter data, we show that IOD and ENSO leave characteristic signatures in the sea level anomalies (SLAs) in the Bay of Bengal. During a positive IOD event, negative SLAs are observed during April-December, with the SLAs decreasing continuously to a peak during September-November. During El Nino, negative SLAs are observed twice (April-December and November-July), with a relaxation between the two peaks. SLA signatures during negative IOD and La Nina events are much weaker. We use a linear, continuously stratified model of the Indian Ocean to simulate their sea level patterns of IOD and ENSO events. We then separate solutions into parts that correspond to specific processes: coastal alongshore winds, remote forcing from the equator via reflected Rossby waves, and direct forcing by interior winds within the bay. During pure IOD events, the SLAs are forced both from the equator and by direct wind forcing. During ENSO events, they are primarily equatorially forced, with only a minor contribution from direct wind forcing. Using a lead/lag covariance analysis between the Nino-3.4 SST index and Indian Ocean wind stress, we derive a composite wind field for a typical El Nino event: the resulting solution has two negative SLA peaks. The IOD and ENSO signatures are not evident off the west coast of India.

On the height of fall of dropping mass in SASW measurements for asphaltic road pavements

A number of spectral analysis of surface waves (SASW) tests were performed on asphaltic road pavements by dropping a metallic 6.5 kg sphere, from a height (H) ranging from 1 to 3 m. Various combinations of source to first receiver distance (S) and receiver spacing (X) were employed. By increasing the height of the fall of the dropping mass, the maximum wavelength (lambda(max)), up to which the shear wave velocity profile can be predicted with the usage of the SASW measurements, was found to increase continuously. The height of fall of the dropping mass also seems to affect the admissible range of the wavelength for given combinations of X and S. Irrespective of different chosen combinations of S, X and H, a unique combined dispersion curve was generated in all the cases for a given pavement site as long as the threshold minimum value of the coherence function is greater than 0.90.

Effect of high gold salt concentrations on the size and polydispersity of gold nanoparticles prepared by an extended Turkevich-Frens method

The Turkevich-Frens synthesis starting conditions are expanded, ranging the gold salt concentrations up to 2 mM and citrate/gold(III) molar ratios up to 18:1. For each concentration of the initial gold salt solution, the citrate/gold(III) molar ratios are systematically varied from 2:1 to 18:1 and both the size and size distribution of the resulting gold nanoparticles are compared. This study reveals a different nanoparticle size evolution for gold salt solutions ranging below 0.8 mM compared to the case of gold salt solutions above 0.8 mM. In the case of Au3+]<0.8 mM, both the size and size distribution vary substantially with the citrate/gold(III) ratio, both displaying plateaux that evolve inversely to Au3+] at larger ratios. Conversely, for Au3+]>= 0.8 mM, the size and size distribution of the synthesized gold nanoparticles continuously rise as the citrate/gold(III) ratio is increased. A starting gold salt concentration of 0.6 mM leads to the formation of the most monodisperse gold nanoparticles (polydispersity index<0.1) for a wide range of citrate/gold(III) molar ratios (from 4:1 to 18:1). Via a model for the formation of gold nanoparticles by the citrate method, the experimental trends in size could be qualitatively predicted:the simulations showed that the destabilizing effect of increased electrolyte concentration at high initial Au3+] is compensated by a slight increase in zeta potential of gold nanoparticles to produce concentrated dispersion of gold nanoparticles of small sizes.

Electrothermal Ageing of Epoxy Nanocomposites

Constant stress accelerated ageing experiments were conducted on unfilled epoxy and epoxy alumina nanocomposites with different filler loadings of 0.1, 1 and 5 wt%. Electrical (6 kV/mm), thermal (60 degrees C) and combined electrothermal (6 kV/mm and 60 degrees C) ageing experiments were performed for a duration of 250 h. The leakage current through the samples were continuously monitored and the variation in the tan delta values with ageing duration was also monitored. It was observed that the increase in the tan delta value with ageing duration was less for the epoxy alumina nanocomposites as compared to the unfilled epoxy. Dielectric spectroscopy measurements were performed on the samples before and after the ageing in the frequency range of 10(-2) to 10(6) Hz. The permittivity and tan delta values were found to increase in the low frequency range. The volume resistivity of unfilled epoxy and epoxy alumina nanocomposites were also measured before and after the ageing. The volume resistivity improved marginally for the thermally aged samples, but reduced for the electrically aged and the electrothermally aged samples. The decrease in the value of volume resistivity was more for the multistress aged unfilled epoxy samples as compared to the multistress aged epoxy alumina nanocomposites. It was also observed that the unfilled epoxy samples having a higher value of tan delta failed first. The time to failure of the samples showed an increasing trend with an increase in the nano filler loading of epoxy alumina nanocomposites.

Eulerian two-phase flow simulation and experimental validation of semisolid slurry generation process using cooling slope

Experimental and numerical studies of slurry generation using a cooling slope are presented in the paper. The slope having stainless steel body has been designed and constructed to produce semisolid A356 Al alloy slurry. The pouring temperature of molten metal, slope angle of the cooling slope and slope wall temperature were varied during the experiment. A multiphase numerical model, considering liquid metal and air, has been developed to simulate the liquid metal flow along the cooling channel using an Eulerian two-phase flow approach. Solid fraction evolution of the solidifying melt is tracked at different locations of the cooling channel following Schiel's equation. The continuity, momentum and energy equations are solved considering thin wall boundary condition approach. During solidification of the melt, based on the liquid fraction and latent heat of the alloy, temperature of the alloy is modified continuously by introducing a modified temperature recovery method. Numerical simulations has been carried out for semisolid slurry formation by varying the process parameters such as angle of the cooling slope, cooling slope wall temperature and melt superheat temperature, to understand the effect of process variables on cooling slope semisolid slurry generation process such as temperature distribution, velocity distribution and solid fraction of the solidifying melt. Experimental validation performed for some chosen cases reveals good agreement with the numerical simulations.

Studies on the Aging Characteristics of Base Oil with Amine Based Antioxidant in Steel-on-Steel Lubricated Sliding

An industrial base oil, a blend of different paraffin fractions, is heated to 130 degrees C (1) in the ambient and (2) for use as a lubricant in a steel pin on a steel disk sliding experiment. The base oil was tested with and without test antioxidants: dimethyl disulfide (DMDS) and alkylated diphenylamine (ADPA). Primary and secondary oxidation products were monitored continuously by FTIR over a 100 h period. In addition, friction and wear of the steel pin were monitored over the same period and the chemical transformation of the pin surface was monitored by XPS. The objective of this work is to observe the catalytic action of the steel components on the oil aging process and the efficacy of the antioxidant to reduce oxidation of oil used in tribology as a lubricant. Possible mechanistic explanations of the aging process as well as its impact on friction and wear are discussed.

Organophotocatalysis in nanostructured soft gel materials as tunable reaction vessels: comparison with homogeneous and micellar solutions

Riboflavin tetraacetate-catalyzed aerobic photooxidation of 1-(4-methoxyphenyl)ethanol was investigated as a model reaction under blue visible light in different soft gel materials, aiming to establish their potential as reaction vessels for photochemical transformations. Three strategies involving different degrees of organization of the catalyst within the gel network were explored, and the results compared to those obtained in homogeneous and micellar solutions. In general, physical entrapment of both the catalyst and the substrate under optimized concentrations into several hydrogel matrices (including low-molecular-weight and biopolymer-based gels) allowed the photooxidation with conversions between 55 and 100% within 120 min (TOF similar to 0.045-0.08 min(-1); k(obs) similar to 0.011-0.028 min(-1)), albeit with first-order rates ca. 1-3-fold lower than in solution under comparable non-stirred conditions. Remarkably, the organogel made of a cyclohexane-based bisamide gelator in CH3CN not only prevented the photodegradation of the catalyst but also afforded full conversion in less than 60 min (TOF similar to 0.167 min(-1); k(obs) similar to 0.073 min(-1)) without the need of additional proton transfer mediators (e. g., thiourea) as it occurs in CH3CN solutions. In general, the gelators could be recycled without detriment to their gelation ability and reaction rates. Moreover, kinetics could be fine-tuned according to the characteristics of the gel media. For instance, entangled fibrillar networks with relatively high mechanical strength were usually associated with lower reaction rates, whereas wrinkled laminated morphologies seemed to favor the reaction. In addition, the kinetics results showed in most cases a good correlation with the aeration efficiency of the gel media.

Accelerated multistress aging of polymer nanocomposites and its condition monitoring

In recent years, the time dependant maintenance of expensive high voltage power equipments is getting replaced by condition based maintenance so as to detect apriori an impending failure of the equipment. For condition based maintenance, most monitoring systems concentrate on the electrical quantities such as measurement and evaluation of partial discharges, tan delta, tip-up test, dielectric strength, insulation resistance, polarization and depolarization current. However, in the case of equipments being developed with novel nanodielectric insulating materials, the variation in these parameters before an impending failure is not available. Hence in this work, accelerated electrothermal aging studies have been conducted on unfilled epoxy as well as epoxy nanocomposite samples of 5 wt% filler loading, and the tan d values were continuously monitored to obtain the condition of the samples under study. It was observed that those samples whose tan d increased at a rapid rate failed first.

SASW evaluation of asphaltic and cement concrete pavements using different heights of fall for a spherical mass

A number of spectral analysis of surface wave tests were performed on asphaltic and cement concrete pavements by dropping freely a 6.5kg spherical mass, having a radius of 5.82cm, from a height (h) of 0.51.5m. The maximum wavelength ((max)), up to which the shear wave velocity profile can be detected with the usage of surface wave measurements, increases continuously with an increase in h. As compared to the asphaltic pavement, the values of (max) and (min) become greater for the chosen cement concrete pavement, where (min) refers to the minimum wavelength. With h=0.5m, a good assessment of the top layers of both the present chosen asphaltic and the cement concrete pavements, including soil subgrade, can be made. For a given h, as compared to the selected asphaltic pavement, the first receiver in case of the chosen cement concrete pavement needs to be placed at a greater distance from the source. Inverse analysis has also been performed to characterise the shear wave velocity profile of different layers of the pavements.