979 resultados para Confocal Scanning Laser Microscopy


Relevância:

100.00% 100.00%

Publicador:

Resumo:

Current environmental concerns include the excessive consumption and inefficient use of non-renewable natural resources. The construction industry is considered one of the largest consumers of natural raw materials, significantly contributing to the environmental degradation of the planet. The use of calcareous quarry (RPPC) and porcelain tile polishing residues (RPP) as partial replacements of the cement in mortars is an interesting alternative to minimize the exploration of considerably large amounts of natural resources. The present study aimed at investigating the properties of fresh and hardened mortars produced using residues to replace cement. The residues used were fully characterized to determine their specific mass, unitary mass, particle size distribution and morphology, and composition. The performance of the mortars was compared to that of reference compositions, prepared without residues. A total of 18 compositions were prepared, 16 using residues and 2 reference ones. The mortars were prepared using Portland CP II F 32 cement, CH I hydrated lime, river sand and tap water. The compositions of the mortars were 1:1:6 and 1:0.5:4.5 (vol%), and water to cement ratios of 1.87 and 1.45 were used, respectively. The mortars in the fresh state were evaluated by consistency index, water retention, density of mass and incorporated air content tests. In their hardened state, the mortars were evaluated by apparent mass density, modulus of elasticity, flexural tensile strength, compressive strength and water absorption by capillarity. The mortars were also analyzed by scanning electron microscopy, energy dispersive spectroscopy, X-ray diffraction and fluorescence. Finally, they were classified according to NBR 13281 standards. The mortars prepared using residues partially replacing the cement exhibited lower modulus of elasticity compared to the reference compositions, thus improving the performance in their intended use. On the downside, the water absorption by capillarity was affected by the presence of residues and both the tensile and compressive strength were reduced. However, from the overall standpoint, the replacement of cement by calcareous quarry or porcelain tile polishing residues did not result in significant changes in the properties of the mortars. Therefore, compositions containing these residues can be used in the construction industry

Relevância:

100.00% 100.00%

Publicador:

Resumo:

In this work, was studied the formation of a composite of the refractory metal niobium with copper, through the process of high-energy milling and liquid phase sintering. The HEM can be used to synthesize composite powders with high homogeneity and fine size particle distribution. It may also produce the solid solubility in immiscible systems such as Nb-Cu, or extend the solubility of systems with limited solubility. Therefore, in the immiscible system Cu-Nb, the high-energy milling was successfully used to obtain the composite powder particles. Initially, the formation of composite particles during the HEM and the effect of preparation technique on the microstructure of the material was evaluated. Four loads of Nb and Cu powders containing 20%wt Cu were synthesized by MAE in a planetary type ball mill under different periods of grinding. The influence of grinding time on the metal particles is evaluated during the process by the withdrawal of samples at intermediate times of milling. After compaction under different forces, the samples were sintered in a vacuum furnace. The liquid phase sintering of these samples prepared by HEM produced a homogeneous and fine grained. The composite particles forming the sintered samples are the addition of a hard phase (Nb) with a high melting point, and a ductile phase (Cu) with low melting point and high thermal and electrical conductivities. Based on these properties, the Nb-Cu system is a potential material for many applications, such as electrical contacts, welding electrodes, coils for generating high magnetic fields, heat sinks and microwave absorbers, which are coupled to electronic devices. The characterization techniques used in this study, were laser granulometry, used to evaluate the homogeneity and particle size, and the X-ray diffraction, in the phase identification and to analyze the crystalline structure of the powders during milling. The morphology and dispersion of the phases in the composite powder particles, as well the microstructures of the sintered samples, were observed by scanning electron microscopy (SEM). Subsequently, the sintered samples are evaluated for density and densification. And finally, they were characterized by techniques of measuring the electrical conductivity and microhardness, whose properties are analyzed as a function of the parameters for obtaining the composite

Relevância:

100.00% 100.00%

Publicador:

Resumo:

The atomic-level structure and chemistry of materials ultimately dictate their observed macroscopic properties and behavior. As such, an intimate understanding of these characteristics allows for better materials engineering and improvements in the resulting devices. In our work, two material systems were investigated using advanced electron and ion microscopy techniques, relating the measured nanoscale traits to overall device performance. First, transmission electron microscopy and electron energy loss spectroscopy (TEM-EELS) were used to analyze interfacial states at the semiconductor/oxide interface in wide bandgap SiC microelectronics. This interface contains defects that significantly diminish SiC device performance, and their fundamental nature remains generally unresolved. The impacts of various microfabrication techniques were explored, examining both current commercial and next-generation processing strategies. In further investigations, machine learning techniques were applied to the EELS data, revealing previously hidden Si, C, and O bonding states at the interface, which help explain the origins of mobility enhancement in SiC devices. Finally, the impacts of SiC bias temperature stressing on the interfacial region were explored. In the second system, focused ion beam/scanning electron microscopy (FIB/SEM) was used to reconstruct 3D models of solid oxide fuel cell (SOFC) cathodes. Since the specific degradation mechanisms of SOFC cathodes are poorly understood, FIB/SEM and TEM were used to analyze and quantify changes in the microstructure during performance degradation. Novel strategies for microstructure calculation from FIB-nanotomography data were developed and applied to LSM-YSZ and LSCF-GDC composite cathodes, aged with environmental contaminants to promote degradation. In LSM-YSZ, migration of both La and Mn cations to the grain boundaries of YSZ was observed using TEM-EELS. Few substantial changes however, were observed in the overall microstructure of the cells, correlating with a lack of performance degradation induced by the H2O. Using similar strategies, a series of LSCF-GDC cathodes were analyzed, aged in H2O, CO2, and Cr-vapor environments. FIB/SEM observation revealed considerable formation of secondary phases within these cathodes, and quantifiable modifications of the microstructure. In particular, Cr-poisoning was observed to cause substantial byproduct formation, which was correlated with drastic reductions in cell performance.

Relevância:

100.00% 100.00%

Publicador:

Resumo:

Continuous Synthesis by Solution Combustion was employed in this work aiming to obtain tin dioxide nanostructured. Basically, a precursor solution is prepared and then be atomized and sprayed into the flame, where its combustion occurs, leading to the formation of particles. This is a recent technique that shows an enormous potential in oxides deposition, mainly by the low cost of equipment and precursors employed. The tin dioxide (SnO2) nanostructured has been widely used in various applications, especially as gas sensors and varistors. In the case of sensors based on semiconducting ceramics, where surface reactions are responsible for the detection of gases, the importance of surface area and particle size is even greater. The preference for a nanostructured material is based on its significant increase in surface area compared to conventional microcrystalline powders and small particle size, which may benefit certain properties such as high electrical conductivity, high thermal stability, mechanical and chemical. In this work, were employed as precursor solution tin chloride dehydrate diluted in anhydrous ethyl alcohol. Were utilized molar ratio chloride/solvent of 0,75 with the purpose of investigate its influence in the microstructure of produced powder. The solution precursor flux was 3 mL/min. Analysis with X-ray diffraction appointed that a solution precursor with molar ratio chloride/solvent of 0,75 leads to crystalline powder with single phase and all peaks are attributed to phase SnO2. Parameters as distance from the flame with atomizer distance from the capture system with the pilot, molar ratio and solution flux doesn t affect the presence of tin dioxide in the produced powder. In the characterization of the obtained powder techniques were used as thermogravimetric (TGA) and thermodiferential analysis (DTA), particle size by laser diffraction (GDL), crystallographic analysis by X-ray diffraction (XRD), morphology by scanning electron microscopy (SEM), transmission electron microscopy (TEM), specific surface area (BET) and electrical conductivity analysis. The techniques used revealed that the SnO2 exhibits behavior of a semiconductor material, and a potentially promising material for application as varistor and sensor systems for gas

Relevância:

100.00% 100.00%

Publicador:

Resumo:

The first part of this thesis deals with the phenomenon of thermoelectricity. It involves the improvement of the thermoelectric properties of silicon using innovative nanostructures. My contribution was to help fabricate these thermoelectric devices, and is the focus of this part of the thesis.

The second part and primary focus of this thesis is the analysis of thin films using scanning probe techniques. These surface techniques include atomic force microscopy, electric force microscopy, Kelvin probe force microscopy, and scanning tunneling microscopy. The thin films studied are graphene and molybdenum disulfide, two remarkable materials that display unique two-dimensional qualities. These materials are shown to be useful in studying the properties of adsorbates trapped between them and the substrate on which they rest. Moreover, these adsorbed species are seen to affect the structural and electronic properties of the thin films themselves. Scanning probe analyses are particularly useful in elucidating the properties of these materials, as surface effects play a significant role in determining their characteristics.

The final part of this thesis is concerned with the study of Akt in live cells using protein capture agents previously developed by my colleagues. The activation and degradation of Akt is investigated using various biological assays, including Western blots, in vitro kinase assays, and cell viability assays. Finally, the usefulness of synthetic capture agents in perturbing protein pathways and as delivery agents is assessed and analyzed.

Relevância:

100.00% 100.00%

Publicador:

Resumo:

The refractory metal carbides have proven important in the development of engineering materials due to their properties such as high hardness, high melting point, high thermal conductivity and high chemical stability. The niobium carbide presents these characteristics. The compounds of niobium impregnated with copper also have excellent dielectric and magnetic properties, and furthermore, the Cu doping increases the catalytic activity in the oxidation processes of hydrogen. This study aimed to the synthesis of nanostructured materials CuNbC and niobium and copper oxide from precursor tris(oxalate) oxiniobate ammonium hydrate through gas-solid and solid-solid reaction, respectively. Both reactions were carried out at low temperature (1000°C) and short reaction time (2 hours). The niobium carbide was produced with 5 % and 11% of copper, and the niobium oxide with 5% of copper. The materials were characterized by X-Ray Diffraction (XRD), Rietveld refinement, Scanning Electron Microscopy (SEM), X-Ray Fluorescence Spectroscopy (XRF), infrared spectroscopy (IR), thermogravimetric (TG) and differential thermal analysis (DTA , BET and particle size Laser. From the XRD analysis and Rietveld refinement of CuNbC with S = 1.23, we observed the formation of niobium carbide and metallic copper with cubic structure. For the synthesis of mixed oxide made of niobium and copper, the formation of two distinct phases was observed: CuNb2O6 and Nb2O5, although the latter was present in small amounts

Relevância:

100.00% 100.00%

Publicador:

Resumo:

The coatings mortars are essential elements of building structures because they execute an important role in protecting walls and are particularly exposed to aggressive action responsible for its degradation over time. The importance of wall coverings has been the subject of discussion and analysis in the conservation and rehabilitation of old buildings. Are sometimes removed and replaced with inappropriate solutions of constructive point of view or architecture. The most commonly used coatings on walls of old buildings is based on traditional hydraulic lime mortars. The present study aims at the formulation of new lime- based mortars and aerial fine aggregate, in order to contribute to a better field of conservation and restoration mortar coating of old buildings. Residue was used for polishing porcelain as fine aggregate, replacing the aggregate (sand), in percentages 05-30% by mass. We conducted a thorough evaluation of the mortar properties in fresh and hardened state by comparing the performance of the same with a reference mortar. The residue used was characterized as the density, bulk density, and particle size laser, scanning electron microscopy, X-ray diffraction and X-ray fluorescence. Formulations were produced 7, 6 with residue and one commonly used formulation, which served as a reference. In the formulations of lime mortars air (hydrated lime powder CH-I) has been adopted a stroke volume (1:3) with constant binder, was varied and the water / binder and aggregate and waste. For evaluation of mortars fresh, proceeded to consistency analysis, specific gravity, water retention and air content embedded. In the hardened state assays were performed in specific gravity, water retention, modulus of elasticity, tensile strength in bending, compressive strength, water absorption by capillary action, adhesion, tensile strength, resistance to shrinkage and salts by of crystallization trials with resources chloride solution, nitrate and sulfate all sodium in prismatic at 90 days of age, in addition to the micro structural analysis of mortars. Based on the results we can see that the mortar formulated with 10% content of waste and the reference free retraction feature more stable closer to neutrality. The composition of 10% was obtained better performance against the action of the salt crystallization. The mortar with 15% residue obtained better density, lower air content embedded and high capacity for water retention developing good workability. The replacement of 20% of waste generates a satisfactory utilization of resistance to compression, flexion and traction grip the base. And, finally, it can be seen that the mortar with 10, 15 and 20% residual show, in principle, good suitability as coatings, thus enabling a final result consistent with durability, workability and aesthetics developing therefore a material with better performance to repair or replace existing mortars in old buildings

Relevância:

100.00% 100.00%

Publicador:

Resumo:

In this work was used a plasma torch of non transferred arc with argon as work gas, using a power supply with maximum DC current of 250 A and voltage of 30 V to activate the plasma and keep it switched on. The flame temperature was characterized by optical emission spectroscopy, through Boltzmann-plot-method. The torch has been used like igniter in the aluminothermic reduction of the mixture tantalum oxide and aluminum, seeking to obtain metallic tantalum. In heating of the reagents only one particle will be considered to study interactions between plasma-particle, seeking to determinate its fusion and residence time. The early powders were characterized by laser granulometry, scanning electron microscopy (SEM) and X-ray diffraction analysis. The final product of this reaction was characterized by SEM and X-ray diffraction. Crystallite size was calculated by the Scherrer equation and microdeformation was determined using Willamsom-Hall graph. With Rietveld method was possible to quantify the percentile in weight of the products obtained in the aluminothermic reaction. Semi-quantitative chemical analysis (EDS) confirmed the presence of metallic tantalum and Al2O3 as products of the reduction. As was waited the particle size of the metallic tantalum produced, presents values in nanometric scale due the short cooling time of those particles during the process

Relevância:

100.00% 100.00%

Publicador:

Resumo:

The structural characteristics of liposomes have been widely investigated and there is certainly a strong understanding of their morphological characteristics. Imaging of these systems, using techniques such as freeze-fracturing methods, transmission electron microscopy, and cryo-electron imaging, has allowed us to appreciate their bilayer structures and factors which can influence this. However, there are few methods which all us to study these systems in their natural hydrated state; commonly the liposomes are visualized after drying, staining, and/or fixation of the vesicles. Environmental Scanning Electron Microscopy (ESEM) offers the ability to image a liposome in its hydrated state without the need for prior sample preparation. Within our studies we were the first to use ESEM to study liposomes and niosomes and we have been able to dynamically follow the hydration of lipid films and changes in liposome suspensions as water condenses on to, or evaporates from, the sample in real time. This provides insight into the resistance of liposomes to coalescence during dehydration, thereby providing an alternative assay of liposome formulation and stability.

Relevância:

100.00% 100.00%

Publicador:

Resumo:

This paper presents the results of a multidisciplinary and multi-analytical study of the amber beads, red pigments, lithic arrowheads and selected ceramics from the Museum of Évora’s collection of the Zambujeiro Dolmen. Amber beads were studied by Attenuated Total Reflectance Fourier Transformed Infrared Spectroscopy (ATR-FTIR) and Pyrolysis coupled to Gas Chromatography and Mass Spectrometry (Py-GC/MS) to confirm their chemical nature and provenance. The red pigments, frequently found in funerary Neolithic context of the Iberian Peninsula, were studied with micro-Raman, and Scanning Electron Microscopy coupled to Energy Dispersive X-Ray Spectroscopy (SEM-EDS) to identify their chemical nature and provenance. The lithic arrowheads were analysed by portable X-Ray Fluorescence (p-XRF), micro X-Ray Diffraction (XRD), SEM-EDS, and Laser Ablation Inductively Coupled Plasma Mass Spectrometry (LA-ICP-MS). The ceramic materials were studied to infer provenance and production technology by p-XRF, XRD and SEM-EDS; ceramic contents were evaluated by GC/MS. The studies have shown that while some materials travel hundreds or thousands of kilometres to arrive to the Zambujeiro Dolmen, local materials were also used in the items selected by the communities to honour their deceased.

Relevância:

100.00% 100.00%

Publicador:

Resumo:

This study presents results on a developed methodology to characterize ground layers in Portuguese workshops. In this work a set of altarpieces of the 15th and 16th centuries, assigned to Coimbra painting workshop was studied, overall the masters Vicente Gil (doc. Coimbra 1498–1525), Manuel Vicente (doc. Coimbra 1521–1530) and Bernardo Manuel (act. c. 1559–94), father, son and grandson, encompassing from late gothic to mannerist periods. The aim of the study is to compare ground layers, fillers and binders of Coimbra workshop, and to correlate their characteristics to understand the technical evolution of this family of painters, using complementary microscopic techniques. The cross-sections from the groups of paintings were examined by optical microscopy and the results were integrated through the analysis obtained by μ-X–ray diffraction, scanning electron microscopy with energy dispersive X–ray Spectrometry, μ-confocal Raman and occasionally with μ-Fourier transform infrared spectroscopy imaging. Ground layers are of calcium sulfate, present as gesso grosso (mainly anhydrite with small amounts of gypsum) in the first and last phases of the workshop and gesso mate (mainly gypsum with small amounts of anhydrite) in an intermediate period. Binders have protein and oleic characteristics.

Relevância:

100.00% 100.00%

Publicador:

Resumo:

Le attività di ricerca svolte nel corso del dottorato di ricerca, sono state focalizzate principalmente sullo studio dell’evoluzione microstrutturale, delle proprietà meccaniche e tribologiche di una particolare lega da fonderia, EV31A, con alte percentuali di terre rare (Nd e Gd > 4% in peso). Le analisi microstrutturali sono state eseguite tramite microscopia ottica (OM), elettronica in scansione (SEM) ed elettronica in trasmissione (TEM), mentre le proprietà meccaniche sono state determinate attraverso prove di trazione e prove di fatica a flessione rotante. Al fine di incrementare le proprietà tribologiche delle leghe di magnesio è stata valutata l’efficacia del trattamento PEO sia sulla lega EV31A, sia sulle più comuni leghe AZ80 e AZ91D, effettuando test tribologici in modalità pattino su cilindro (Block on Ring). Infine è stato condotto uno studio sull’efficacia del trattamento di fusione superficiale laser (LSM), analizzandone gli effetti sia sull’evoluzione microstrutturale, sia sulle proprietà meccaniche e sulla resistenza a corrosione. Le attività svolte nel corso del dottorato di ricerca sono state svolte presso il Dipartimento di Ingegneria Industriale DIN della Scuola di Ingegneria e Architettura dell’Università di Bologna sotto la supervisione della Prof. ssa Lorella Ceschini.

Relevância:

100.00% 100.00%

Publicador:

Resumo:

A general description of the work presented in this thesis can be divided into three areas of interest: micropore fabrication, nanopore modification, and their applications. The first part of the thesis is related to the novel, reliable, cost-effective, potable, mass-productive, robust, and ease of use micropore flowcell that works based on the RPS technique. Based on our first goal, which was finding an alternate materials and processes that would shorten production times while lowering costs and improving signal quality, the polyimide film was used as a substrate to create precise pores by femtosecond laser, and the resulting current blockades of different sizes of the nanoparticles were recorded. Based on the results, the device can detecting nano-sized particles by changing the current level. The experimental and theoretical investigation, scanning electron microscopy, and focus ion beam were performed to explain the micropore's performance. The second goal was design and fabrication of a leak-free, easy-to-assemble, and portable polymethyl methacrylate flowcell for nanopore experiments. Here, ion current rectification was studied in our nanodevice. We showed a self-assembly-based, controllable, and monitorable in situ Poly(l-lysine)- g-poly(ethylene glycol) coating method under voltage-driven electrolyte flow and electrostatic interaction between nanopore walls and PLL backbones. Using designed nanopore flowcell and in situ monolayer PLL-g-PEG functionalized 20±4 nm SiN nanopores, we observed non-sticky α-1 anti-trypsin protein translocation. additionally, we could show the enhancement of translocation events through this non-sticky nanopore, and also, estimate the volume of the translocated protein. In this study, by comparing the AAT protein translocation results from functionalized and non-functionalized nanopore we demonstrated the 105 times dwell time reduction (31-0.59ms), 25% amplitude enhancement (0.24-0.3 nA), and 15 times event’s number increase (1-15events/s) after functionalization in 1×PBS at physiological pH. Also, the AAT protein volume was measured, close to the calculated AAT protein hydrodynamic volume and previous reports.

Relevância:

100.00% 100.00%

Publicador:

Resumo:

Batteries should be refined depending on their application for a future in which the sustainable energy demand increases. On the one hand, it is fundamental to improve their safety, prevent failures, increase energy density, and reduce production costs. On the other hand, new battery materials and architecture are required to satisfy the growing demand. This thesis explores different electrochemical energy storage systems and new methodologies to investigate complex and dynamic processes. Lithium-ion batteries are described in all their cell components. In these systems, this thesis investigates negative electrodes. Both the development of new sustainable materials and new in situ electrode characterization methods were explored. One strategy to achieve high-energy systems is employing lithium metal anodes. In this framework, ammonium hexafluorophosphate is demonstrated to be a suitable additive for stabilizing the interphase and preventing uncontrolled dendritic deposition. Deposition/stripping cycles, electrochemical impedance spectroscopy, in situ optical microscopy, and operando confocal Raman spectroscopy have been used to study lithium metal-electrolyte interphase in the presence of the additive. Redox Flow Batteries (RFBs) are proposed as a sustainable alternative for stationary applications. An all-copper aqueous RFB (CuRFB) has been studied in all its aspects. For the electrolyte optimization, spectro-electrochemical tests in diluted solution have been used to get information on the electrolyte’s electrochemical behaviour with different copper complexes distributions. In concentrated solutions, the effects of copper-to-ligand ratios, the concentration, and the counter-ion of the complexing agent were evaluated. Electrode thermal treatment was optimized, finding a compromise between the electrochemical performance and the carbon footprint. On the membrane side, a new method for permeability studies was designed using scanning electrochemical microscopy (SECM). The Cu(II) permeability of several membranes was tested, obtaining direct visualization of Cu(II) concentration in space. Also, two spectrophotometric approaches were designed for SoC monitoring systems for negative and positive half-cells.

Relevância:

100.00% 100.00%

Publicador:

Resumo:

The mesoporous SBA-15 silica with uniform hexagonal pore, narrow pore size distribution and tuneable pore diameter was organofunctionalized with glutaraldehyde-bridged silylating agent. The precursor and its derivative silicas were ibuprofen-loaded for controlled delivery in simulated biological fluids. The synthesized silicas were characterized by elemental analysis, infrared spectroscopy, (13)C and (29)Si solid state NMR spectroscopy, nitrogen adsorption, X-ray diffractometry, thermogravimetry and scanning electron microscopy. Surface functionalization with amine containing bridged hydrophobic structure resulted in significantly decreased surface area from 802.4 to 63.0 m(2) g(-1) and pore diameter 8.0-6.0 nm, which ultimately increased the drug-loading capacity from 18.0% up to 28.3% and a very slow release rate of ibuprofen over the period of 72.5h. The in vitro drug release demonstrated that SBA-15 presented the fastest release from 25% to 27% and SBA-15GA gave near 10% of drug release in all fluids during 72.5 h. The Korsmeyer-Peppas model better fits the release data with the Fickian diffusion mechanism and zero order kinetics for synthesized mesoporous silicas. Both pore sizes and hydrophobicity influenced the rate of the release process, indicating that the chemically modified silica can be suggested to design formulation of slow and constant release over a defined period, to avoid repeated administration.