Primate Pulpal Healing after Exposure and TheraCal Application

Aim: The purpose of this in vivo study was to compare the effectiveness of a new light cured resin based dicalcium/tricalcium silicate pulp capping material (TheraCal LC, Bisco), pure Portland cement, resin based calcium hydroxide or glass ionomer in the healing of bacterially contaminated primate pulps. Study design: The experiment required four primates each having 12 teeth prepared with buccal penetrations into the pulpal tissues with an exposure of approximately 1.0 mm. The exposed pulps of the primate teeth were covered with cotton pellets soaked in a bacterial mixture consisting of microorganisms normally found in human pulpal abscesses. After removal of the pellet, hemostasis was obtained and the pulp capping agents applied. The light cured resin based pulp capping material (TheraCal LC) was applied to the pulpal tissue of twelve teeth with a needle tip syringe and light cured for 15 seconds. Pure Portland cement mixed with a 2% Chlorhexidine solution was placed on the exposed pulpal tissues of another twelve teeth. Twelve additional teeth had a base of GIC applied (Triage, Fuji VII GC America) and another twelve had a pulp cap with VLC DYCAL (Dentsply), a light cured calcium hydroxide resin based material. The pulp capping bases were then covered with a RMGI (Fuji II LC GC America). The tissue samples were collected at 4 weeks. The samples were deminerilized, sectioned, stained and histologically graded. Results: There were no statistically significant differences between the groups in regard to pulpal inflammation (H= 0.679, P=1.00). However, both the Portland cement and light cured TheraCal LC groups had significantly more frequent hard tissue bridge formation at 28 days than the GIC and VLC Dycal groups (H= 11.989, P=0.009). The measured thickness of the hard tissue bridges with the pure Portland and light cured TheraCal LC groups were statistically greater than that of the other two groups (H= 15.849, P=0.002). In addition, the occurrence of pulpal necrosis was greater with the GIC group than the others. Four premolars, one each treated according to the protocols were analyzed with a microCT machine. The premolar treated with the light cured TheraCal LC demonstrated a complete hard tissue bridge. The premolar treated with the GIC did not show a complete hard tissue bridge while the premolar treated with VLC Dycal had an incomplete bridge. The pure Portland with Chlorhexidine mixture created extensive hard tissue bridging.Conclusion: TheraCal LC applied to primate pulps created dentin bridges and mild inflammation acceptable for pulp capping.

Iliac osteosynthesis with nylon clamp associated to polymethylmethacrylate bone cement - experimental study in dogs cadavers

Fractures of iliac body are generally consequences of traumas of great impact. These fractures lead to a lack of locomotor response and in specific cases, surgery is needed. Among the possible therapeutic lines, implants become a good option. In this paper, the authors used dog corpses to develop a surgery technique of iliac osteosynthesis, employing nylon clamps and bone cement of polymethylmethacrylate (PMMA). Sixteen hemi pelvises of eight dog corpses, which had its iliac bodies totally fractured previously, were utilized. The osteosynthesis was reached through the implantation of six nylon clamps, distributed equally between the bone fragments. With the use of the nylon clamps there were bone realignment and a contact surface to fixation of the biomaterial. The technique developed in corpses was easily executed, effective in reduction, alignment and stabilization of the fracture. The authors suggest more studies in vitro to evaluate immobilization resistance and functionality in dogs with this condition.

Thickness and marking quality of different occlusal contact registration strips

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Efeito de diferentes espessuras, técnicas de aplicação e protocolos de resfriamento na resistência à fratura da cerâmica de cobertura aplicada sobre infraestrutura de y-tzp

Pós-graduação em Odontologia Restauradora - ICT

Propriedades físico-químicas e mecânicas, potencial bioativo e caracterização da interface dentina-cimento de cimentos endodônticos experimentais à base de cimento Portland associados à radiopacificadores micro e nanoparticulados

Pós-graduação em Odontologia - FOAR

Efeito de protocolos de cimentação na carga de fratura para uma cerâmica de dissilicato de lítio

Pós-graduação em Odontologia Restauradora - ICT

Thickness-dependent piezoelectric behaviour and dielectric properties of lanthanum modified BiFeO3 thin films

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

A combined approach for the treatment of resorbed fresh sockets allowing immediate implant restoration: a 2-year follow-up

Introduction: The demand for optimal esthetics has increased with the advance of the implant dentistry and with the desire for easier, safer and faster technique allowing predictable outcomes. Thus, the aim of this case report was to describe a combined approach for the treatment of a periodontally compromised tooth by means of atraumatic tooth extraction, immediate flapless implant placement, autogenous block and particulate bone graft followed by connective tissue graft and immediate provisionalization of the crown in the same operatory time. Case Report: A 27-year-old woman underwent the proposed surgical procedures for the treatment of her compromised maxillary right first premolar. The tooth was removed atraumatically with a periotome without incision. A dental implant was inserted 3 mm apical to the cement-enamel junction of the adjacent teeth enabling the ideal tridimensional implant position. An osteotomy was performed in the maxillary tuber for block bone graft harvesting that allowed the reconstruction of the alveolar buccal plate. Thereafter, an autogenous connective tissue graft was placed to increase both the horizontal and vertical dimensions of the alveolar socket reaching the patient functional and esthetic expectations. Conclusion: This treatment protocol was efficient to create a harmonious gingival architecture with sufficient width and thickness, maintaining the stability of the alveolar bone crest yielding excellent aesthetic results after 2-years of follow-up. We suggest that this approach can be considered a viable alternative for the treatment of periodontally compromised tooth in the maxillary esthetic area enhancing patient comfort and satisfaction.

Incorporation of chlorhexidine gluconate or diacetate into a glass-ionomer cement: porosity, surface roughness, and anti-biofilm activity

To evaluate the porosity, surface roughness and anti-biofilm activity of a glass-ionomer cement (GIC) after incorporation of different concentrations of chlorhexidine (CHX) gluconate or diacetate. Methods: For the porosity and surface roughness tests, 10 test specimens were fabricated of the GIC Ketac Molar Easy Mix (KM) and divided into the following groups: Control, GIC and 0.5% CHX diacetate; GIC and 1.0% CHX diacetate; GIC and 2.0% CHX diacetate; GIC and 0.5% CHX gluconate; GIC and 1.0% CHX gluconate; GIC and 2.0% CHX gluconate. To evaluate porosity, the test specimens were fractured. The fragments were photographed by scanning electron microscopy (SEM), and the images analyzed with the aid of the software program Image J. The surface roughness (Ra) was obtained by the mean value of three readouts performed on the surface of each specimen, always through the center. To analyze the anti-biofilm activity, strains of S. mutans ATCC 35688 were used, and the groups control and GIC +CHX diacetate 1% were divided as follows: GIC (1 day); GIC (7 days), GIC (14 days), GIC (21 days); GIC+CHX (1 day), GIC+CHX (7 days), GIC+CHX (14 days), GIC+CHX (21 days); GIC+ CHX (1 day), GIC+ CHX (7 days), GIC+ CHX (14 days) and GIC+ CHX (21 days) using 10 test specimens per group. For biofilm growth, the specimens were placed in a vertical position in 24-well plates and incubated overnight 10 times. The culture medium was renewed every 24 hours. The suspension was diluted and seeded on BHI agar for quantification of the bacteria present. For evaluation of all the tests the two-way ANOVA was used, and if necessary, the Tukey test was applied, with a level of significance of 5%. Results: Regarding GIC porosity, the ANOVA showed that the presence of CHX increased the porosity (P< 0.001) proportionally to the increase in concentrations (P= 0.001), without however, presenting interaction between material and concentration (P= 0.705). Regarding the number of pores, a significant increase in pores was observed with the increase in CHX concentration (P= 0.003). The surface roughness test demonstrated no statistically significant effect as to increase or reduction in roughness at any of the CHX concentrations used (P> 0.05). Anti-biofilm activity analysis pointed out a significant effect of the factors material (P= 0.006) and time (P< 0.001), with CHX diacetate CHX presenting greater effectiveness in reducing microorganisms.

Repair of Bone Defects Filled with New Calcium Aluminate Cement (EndoBinder)

The aim of this study was to evaluate and compare the repair of bone defects filled with calcium aluminate cement (EndoBinder), mineral trioxide aggregate (MTA), and calcium hydroxide. Methods After mixing, the cements were inserted into bone defects (3.3 mm) mechanically created in the right and left tibias of 30 rats (Rattus norvegicus, Wistar). In the control group, the bone defects were filled with blood clot of the animal itself. After time intervals of 7, 30, and 90 days had elapsed, bone tissue biopsies (n = 5) were surgically obtained and submitted to laboratory processing. The response of bone tissue in contact with the materials was microscopically analyzed. The percentage of neoformed bone tissue in the defect was determined by means of planimetry counting points superimposed on the histologic image. Results Significant increase in the percentage of neoformed bone tissue was observed throughout the experimental periods in all groups (P < .05). For the cements EndoBinder and MTA (30 and 90 days), these percentage values were statistically higher than those of the control group (P < .05); however, they were similar to those of calcium hydroxide (P > .05). Conclusions EndoBinder and MTA allowed complete repair of bone defects created in rat tibias.

Air abrasion before and/or after zirconia sintering: surface characterization, flexural strength, and resin cement bond strength

The purpose of this in vitro study was to evaluate the effect of air-abrasion/zirconia sintering order on the yttria partially stabilized tetragonal zirconia polycrystal (Y-TZP) surface characterization (roughness, morphology, and phase transformation), flexural strength (FS), and shear bond strength (SBS) to a resin cement. Y-TZP specimens were air abraded with 50-μm Al2O3 particles after (AS), before (BS), or before and after zirconia sintering (BAS). For roughness (Ra), 30 block specimens (12×12×3.0 mm; n=10) had their surfaces analyzed by a profilometer. Next, on the air-abraded surfaces of these specimens, composite resin discs (n=30) were bonded with RelyX ARC. The bonded specimens were stored for 24 hours in distilled water at 37°C before shear testing. Failure mode was determined with a stereomicroscope (20×). The surface morphology (n=2) was evaluated by SEM (500×). For the four-point flexural strength test (EMIC DL2000), 39 bar-shaped specimens (20×4.0×1.2 mm; n=13) were air abraded according to the three conditions proposed, and an additional group (nonabraded) was evaluated (n=13). The quantitative analysis of phase transformation (n=1) was completed with Rietveld refinement with X-ray diffraction data. Ra (μm) and SBS (MPa) data were analyzed by one-way analysis of variance (ANOVA) and the Tukey test (α=0.05). Pearson correlation analysis was used to determine if there was a correlation between roughness and SBS. For FS (MPa) data, one-way ANOVA and the Dunnett C-test (α=0.05) were used. The air-abrasion/zirconia sintering order influenced significantly (p<0.001) Ra, SBS, and FS. The BS and AS groups presented the highest (1.3 μm) and the lowest (0.7 μm) Ra. The highest SBS (7.0 MPa) was exhibited by the BAS group, followed by the AS group (5.4 MPa) and finally by the BS group (2.6 MPa). All groups presented 100% adhesive failure. A weak correlation (r=−0.45, p<0.05) was found between roughness and SBS. The air-abrasion/zirconia sintering order provided differences in the surface morphology. The nonabraded (926.8 MPa) and BS (816.3 MPa) groups exhibited statistically similar FS values but lower values than the AS (1249.1 MPa) and BAS (1181.4 MPa) groups, with no significant difference between them. The nonabraded, AS, BS, and BAS groups exhibited, respectively, percentages of monoclinic phase of 0.0 wt%, 12.2 wt%, 0.0 wt%, and 8.6 wt%. The rougher surface provided by the air-abrasion before zirconia sintering may have impaired the bonding with the resin cement. The morphological patterns were consistent with the surface roughness. Considering the short-term SBS and FS, the BAS group exhibited the best performance. Air abrasion, regardless of its performance order, provides tetragonal to monoclinic transformation, while sintering tends to zero the monoclinic phase content.

Effect of particle size on the flexural strength and phase transformation of an airborne-particle abraded yttria-stabilized tetragonal zirconia polycrystal ceramic.

Statement of problem Because airborne-particle abrasion is an efficient method of improving the bond at the zirconia-cement interface, understanding its effect on the strength of yttria-stabilized tetragonal zirconia polycrystal is important. Purpose The purpose of this study was to evaluate the effect of the particle size used for airborne-particle abrasion on the flexural strength and phase transformation of a commercially available yttria-stabilized tetragonal zirconia polycrystal ceramic. Material and Methods For both flexural strength (20.0 × 4.0 × 1.2 mm) (n=14) and phase transformation (14.0-mm diameter × 1.3-mm thickness) (n=4), the zirconia specimens were made from Lava, and their surfaces were treated in the following ways: as-sintered (control); with 50-μm aluminum oxide (Al2O3) particles; with 120-μm Al2O3 particles; with 250-μm Al2O3 particles; with 30-μm silica-modified Al2O3 particles (Cojet Sand); with 120-μm Al2O3 particles, followed by 110-μm silica-modified Al2O3 particles (Rocatec Plus); and with Rocatec Plus. The phase transformation (%) was assessed by x-ray diffraction analysis. The 3-point flexural strength test was conducted in artificial saliva at 37°C in a mechanical testing machine. The data were analyzed by 1-way ANOVA and the Tukey honestly significant difference post hoc test (α=.05). Results Except for the Cojet Sand group, which exhibited statistically similar flexural strength to that of the as-sintered group and for the group abraded with 250-μm Al2O3 particles, which presented the lowest strength, airborne-particle abrasion with the other particle sizes provided the highest values, with no significant difference among them. The as-sintered specimens presented no monoclinic phase. The groups abraded with smaller particles (30 μm and 50 μm) and those treated with the larger ones (110 μm and/or 120 μm particles and 250 μm) exhibited percentages of monoclinic phase that varied from 4% to 5% and from 8.7% to 10%. Conclusions Except for abrasion with Cojet Sand, depending on the particle size, zirconia exhibited an increase or a decrease in its flexural strength. Airborne-particle abrasion promoted phase transformation (tetragonal to monoclinic), and the percentage of monoclinic phase varied according to the particle size.

Interference of the assessment method in pH values of an epoxy-based cement

Introduction: Alkalinization potential is a fundamental property of endodontic epoxy-based cements containing calcium hydroxide. Studies have shown discrepant pH results for same materials at different evaluation periods. A possible reason accounting for these differences may be the assessment procedures. Objective: To evaluate the pH value of an epoxy-based cement (Sealer 26) in different periods of analysis, using two assessment methods. Material and methods: Sealer 26 was manipulated and immediately placed into polyethylene tubes (n=10, each group) and immersed in distilled water. In G1, the tubes were kept in the same water during all experiment; and in G2, the tubes were removed and placed into another flask with an equal amount of water after the pH evaluation. The pH of these solutions was measured at 24 hours, 7, 14 and 28 days. Analysis were made within the same group according to the experimental periods and between groups in each experimental period. Data were submitted to ANOVA (α = 5%) and t test, respectively. Results: For G1 and G2, all periods showed different pH values (p < 0.05), except between 14 and 28 days (p > 0.05) and between 7 and 14 days (p > 0.05), respectively. In each period, no significant differences were observed between the groups. Conclusion: The method to obtain the pH values in different experimental periods no interfered in the final results. However, difference was observed when the results were analyzed at same group.

Evaluation of the physicochemical properties and push-out bond strength of mta-based root canal cement

Aim: This study investigated the flowability, setting time, pH, calcium release and bond strength of a MTA-based cement (MTA Fillapex®) compared to AH Plus and Sealapex. Materials and methods: For the flowability test, the ISO 6876:2001 specification was utilized and for the setting time test, the ASTM C266-03 specification was utilized. For the pH and calcium release measurements, 10 samples were prepared for each group and analyzed for several different periods. For the push-out test, dentin disks were distributed into three groups, according to the cement utilized and into three subgroups, according to the root third (n = 10). After obturation, the specimens underwent push-out testing. The data were compared statistically using a significance level of 5%. Results: The flowability of all materials was found to be similar (p > 0.05). The setting times were different among the groups tested (MTA Fillapex < Sealapex < AH Plus) (p < 0.05). At days 7 and 28, the MTA Fillapex presented the higher pH values (p < 0.05). At 24 hours and at 14 days, the calcium release of the MTA Fillapex was similar to that of Sealapex (p > 0.05). AH Plus presented the lowest pH and calcium release values (p < 0.05). In all root thirds, the adhesion to the dentin of the MTA Fillapex and Sealapex were significantly lower than that of AH Plus (p < 0.05). Conclusion: MTA Fillapex and Sealapex presented several similar properties and both were found to be different than AH Plus. Clinical significance: This study evaluated the physicochemical and mechanical properties of new MTA-based root canal cement, in order to use this scaler in root canal fillings. MTA Fillapex showed satisfactory properties for clinical use.

Indirect resin onlay cemented with self-adhesive resin cement: a comprehensive clinical overview

Advances in adhesive technology and esthetic dental materials have permitted clinicians to perform conservative preparation of the dentition for onlay restorations. Indirect resin onlays are a great alternative to dental crowns for reestablishment the function and esthetic in teeth with great destruction.