Gamma phases in Cu-Al alloys and the influence of a square shaped phase in the electrochemical behavior of a Cu-13.6wt% Al alloy

The electrochemical behavior of Cu-xAl alloys, with 11 wt%less than or equal to x less than or equal to 15wt%, in 0.5 M H2SO4 was studied by means of open-circuit potential decay measurements, quasi-stationary and fast cyclic voltammetry, and electrochemical impedance spectroscopy. Some of the alloys (x less than or equal to 14%), when quenched formed martensitic structures. Alloys with greater than or equal to 13% showed a little square-shaped phase when quenched from temperatures around 800 degrees C. It was observed that in sulfuric medium, these formations were dealuminized differently than the martensitic phase. The values of the rest potentials are more influenced by the heat treatment rather than by the alloy composition. An anodic Tafel slope of ca. 60 mV/decade was observed for all the alloys, independently of the heat treatment. This is explained in terms of a competition between two processes: copper oxidation and copper(I) deproportionation. In the cyclic voltammetric experiments it was observed an anodic current peak, related with copper oxidation with a possible formation of some interfacial species, and a cathodic current peak during the reverse potential scan, associated with the reduction of soluble species and/or of the film. The AC Impedance data were interpreted in terms of electric equivalent circuits.

Development of Ti-Mo alloys for biomedical applications: Microstructure and electrochemical characterization

Ti-Mo alloys from 4 to 20 Mo wt.% were arc-melted. Their compositions and surfaces were analyzed by EDX, XRF and SEM. The Mo mapping shows a homogeneous distribution for all alloys. The XRD analysis showed that the crystal structure of the alloys is sensitive to the Mo concentration; a mixture of the hexagonal alpha' and orthorhombic alpha '' phases was observed for the Ti-4Mo alloy, and the alpha '' phase is observed almost exclusively when the concentration of Mo added to the Ti reaches 6%. A significant retention of the beta phase is observed for the alloy containing 10% Mo, while at higher Mo concentrations (15% and 20%), retention of phase beta is only verified. Preliminary electrochemical studies have indicated a valve-metal behavior and good corrosion resistance in aerated Ringer solution for all alloys. (c) 2006 Published by Elsevier B.V.

Cobalt(II) and nickel(II) complexes with djenkolic acid

Cobalt(II) and nickel(II) djenkolates CoC7H12N2O4S2. H2O (I) and NiC7H12N2O4S2. H2O (II) were synthesized by the reaction of potassium djenkolate with the respective chlorides. LR spectra suggested coordination via the COO- and NH2 groups for the ligands in both compounds. Visible absorption spectra confirmed the octahedral structure of the complexes. X-ray powder diffraction patterns were indexed in the orthorhombic and monoclinic unit cells with parameters: a = 11.35, b = 7.35, c = 6.85 Angstrom for I and a = 11.54, b = 7.45, c = 6.90 Angstrom, beta = 94.95 degrees for II.

All electron fully relativistic Dirac-Fock calculation for darmstadtium carbide using prolapse free basis set

For the first time, ab inito all electron fully relativistic and correlated Dirac-Fock calculations with prolapse free basis set are reported for a Super Heavy Element. We investigated the relativistic effects on bonding and on some spectroscopic constants for the darmstadtium carbide and our results at DF/CCSD(T) with a prolapse free basis set suggest for R-e, omega(e) and D-e the values of 174 pm, 1114 cm(-1) and 7.29 eV, respectively. These values are very similar to the values for PtC found on literature. It was also found that prolapse free basis set may be important to estimate the dissociation energy using Relativistic 4-components correlated methods. (c) 2007 ELsevier B.V. All rights reserved.

Anelastic relaxation processes due oxygen in Nb-3.1 at.% Ti alloys

In the last 50 years several studies have been made to understand the relaxation mechanisms of the heavy interstitial atoms present in transition metals and their alloys. Internal friction measurements have been carried out in a Nb-Ti alloy containing 3.1 at.% of Ti produced by the Materials Department of Chemical Engineering Faculty of Lorena (Brazil), with several quantities of oxygen in solid solution using a torsion pendulum. These measurements have been performed by a torsion pendulum in the temperature range from 300 to 700 K with an oscillation frequency between 0.5 and 10 Hz. The experimental results show complex internal friction spectra that have been resolved, into a series of Debye peaks corresponding to different interactions. For each relaxation process it was possible to obtain the height and temperature of the peak, the activation energy and the relaxation time of the process. (C) 2003 Elsevier B.V. All rights reserved.

Thermal behavior of alpha-(Cu-Al-Ag) alloys

Thermal behavior of alpha-(Cu-Al-Ag) alloys, i.e. alloys with composition less than about 8.5 mass% Al, was studied using differential scanning calorimetry (DSC), differential thermal analysis (DTA), scanning electron microscopy (SEM), energy dispersive X-ray analysis (EDX) and X-ray diffractometry (XRD). The results indicated that the presence of silver introduces new thermal events ascribed to the formation of a silver-rich phase and, after addition higher amounts than 8 mass% Ag to the Cu-8 mass% Al alloy it is possible to observe the formation of the gamma(1) phase (Al4Cu9), which is only observed in alloys containing minimum of 9 mass% Al. These results may be attributed to some Ag characteristics and its interaction with Cu and Al.

Stress-induced ordering due heavy interstitial atoms in Nb-0.3 wt.% Ti alloys

The mechanical properties of metals with bee structure, such as niobium and their alloys, are changed of a significant way by the introduction of heavy interstitial elements. These interstitial elements (oxygen, for example) present in the metallic matrix occupy octahedral sites and constitute an elastic dipole of tetragonal symmetry and might produce anelastic relaxation. Polycrystalline samples of Nb-0.3 wt.% Ti (Nb-Ti) alloy with oxygen in solid solution were analysed. The anelastic spectroscopy measurements had been made in a torsion pendulum, with frequencies in the Hz range, in a temperature range between 300 and 700 K. The results showed thermally activated relaxation structures were identified four relaxation process attributed to stress-induced ordering of single oxygen, nitrogen and carbon atoms around niobium and stress-induced ordering of single oxygen atoms around titanium atoms. (c) 2005 Elsevier B.V. All rights reserved.

Effect of Ag concentration on the thermal behavior of the Cu-10 mass% Al and Cu-11 mass% Al alloys

In this work the effect of Ag concentration on the thermal behavior of the Cu-10 mass% Al and Cu-11 mass% Al alloys with additions of 4, 6, 8 and 10 mass% Ag was studied using differential scanning calorimetry (DSC), in situ X-ray diffractometry (XRD) and scanning electron microscopy (SEM). The results showed that for the Cu-10 mass% Al alloy Ag addition induce the beta'(1) phase formation and for the Cu-11 mass% Al alloy these additions increase the amount of martensite formed on quenching and decrease the stability range of this phase on heating.

Electrochemical behavior of cobalt oxide coatings on cold-rolled steel in alkaline sodium sulfate

The electrochemical behavior of a coating of cobalt oxide on cold-rolled steel in alkaline sodium sulfate was Studied using the electrochemical techniques of open-circuit potential measurements and electrochemical impedance spectroscopy. The coating was prepared at different annealing temperatures ranging from 350 to 750 degreesC and characterized by SEM, EDX and XRD. Below 550 degreesC the composition of the coating was basically of Co3O4. At 750 degreesC CoO was formed and big cracks appeared on the film exposing an inner layer of iron oxides. Analysis of the EIS data is very difficult because of the complexity of the interface structure. It can be inferred that the charge transfer resistance of the coatings prepared at 350 and 450 C were higher than those for the coatings prepared at temperatures above 550 degreesC. (C) 2002 Published by Elsevier B.V. Ltd.

Completeness of beta-phase decomposition reaction in Cu-Al-Ag alloys

The completeness of beta-phase decomposition reaction in the Cu-11wt%Al-xwt%Ag alloys (x = 0, 1, 2, and 3) was studied using differential scanning calorimetry (DSC), X-ray diffractometry (XRD), and optical microscopy (OM). The results indicated that beta-phase transformations are highly dependent on cooling rate and on the presence of Ag. on slow cooling, the silver presence prevents the beta- and beta(1)-phase decomposition; thus, inducing the martensitic phase formation. After rapid cooling, a new thermal event is observed and the reverse martensitic transformation is shifted to lower temperatures.

Determination of cobalt marker in cow ruminal fluid by EDXRF and SRTXRF

This article describes a comparison of conventional energy-dispersive X-ray fluorescence (EDXRF) and synchrotron radiation total-reflection X-ray fluorescence (SRTXRF) for Co determination in ruminal fluid from Holstein cow. This element is used as marker for animal nutrition studies. For EDXRF, 200 mu l of the sample were dried on 6.35 mu m Mylar filmat 60 degrees C. The excitation was carried out using an X-ray tube with Mo target and Zr filter operated at 30 kV/ 20 mA. For SRTXRF, 10 mu l of the samplewere pipetted on a Lucite carrier and dried at 60 degrees C. In both the techniques, Ga was used as internal standard and the acquisition time was 200 s. The trueness of both techniques was evaluated through the standard addition method, the recoveries obtained by SRTXRF and EDXRF were 76 and 99%, and the limits of detection, 13 and 240 mu g l(-1), respectively. Copyright (C) 2011 John Wiley & Sons, Ltd.