Effect of temperature on the shear strength of aluminium single lap bonded joints for high temperature applications

An experimental and numerical investigation into the shear strength behaviour of adhesive single lap joints (SLJs) was carried out in order to understand the effect of temperature on the joint strength. The adherend material used for the experimental tests was an aluminium alloy in the form of thin sheets, and the adhesive used was a high-strength high temperature epoxy. Tensile tests as a function of temperature were performed and numerical predictions based on the use of a bilinear cohesive damage model were obtained. It is shown that at temperatures below Tg, the lap shear strength of SLJs increased, while at temperatures above Tg, a drastic drop in the lap shear strength was observed. Comparison between the experimental and numerical maximum loads representing the strength of the joints shows a reasonably good agreement.

Analyse avantages-coûts de la réglementation visant l'accroissement du montant de consignation à 10¢ sur les contenants de boissons gazeuses composés d'aluminium.

Rapport de recherche

Étude critique de la densité électronique et des températures (excitation et ionisation) d'un plasma d'aluminium induit par laser

La caractérisation de matériaux par spectroscopie optique d’émission d’un plasma induit par laser (LIPS) suscite un intérêt qui ne va que s’amplifiant, et dont les applications se multiplient. L’objectif de ce mémoire est de vérifier l’influence du choix des raies spectrales sur certaines mesures du plasma, soit la densité électronique et la température d’excitation des atomes neutres et ionisés une fois, ainsi que la température d’ionisation. Nos mesures sont intégrées spatialement et résolues temporellement, ce qui est typique des conditions opératoires du LIPS, et nous avons utilisé pour nos travaux des cibles binaires d’aluminium contenant des éléments à l’état de trace (Al-Fe et Al-Mg). Premièrement, nous avons mesuré la densité électronique à l’aide de l’élargissement Stark de raies de plusieurs espèces (Al II, Fe II, Mg II, Fe I, Mg I, Halpha). Nous avons observé que les densités absolues avaient un comportement temporel différent en fonction de l’espèce. Les raies ioniques donnent des densités électroniques systématiquement plus élevées (jusqu’à 50 % à 200 ns après l’allumage du plasma), et décroissent plus rapidement que les densités issues des raies neutres. Par ailleurs, les densités obtenues par les éléments traces Fe et Mg sont moindres que les densités obtenues par l’observation de la raie communément utilisée Al II à 281,618 nm. Nous avons parallèlement étudié la densité électronique déterminée à l’aide de la raie de l’hydrogène Halpha, et la densité électronique ainsi obtenue a un comportement temporel similaire à celle obtenue par la raie Al II à 281,618 nm. Les deux espèces partagent probablement la même distribution spatiale à l’intérieur du plasma. Finalement, nous avons mesuré la température d’excitation du fer (neutre et ionisé, à l’état de trace dans nos cibles), ainsi que la température d’ionisation, à l’aide de diagrammes de Boltzmann et de Saha-Boltzmann, respectivement. À l’instar de travaux antérieurs (Barthélémy et al., 2005), il nous est apparu que les différentes températures convergeaient vers une température unique (considérant nos incertitudes) après 2-3 microsecondes. Les différentes températures mesurées de 0 à 2 microsecondes ne se recoupent pas, ce qui pourrait s’expliquer soit par un écart à l’équilibre thermodynamique local, soit en considérant un plasma inhomogène où la distribution des éléments dans la plume n’est pas similaire d’un élément à l’autre, les espèces énergétiques se retrouvant au cœur du plasma, plus chaud, alors que les espèces de moindre énergie se retrouvant principalement en périphérie.

Young’s modulus of silicon nitride used in scanning force microscope cantilevers

The Young’s modulus and Poisson’s ratio of high-quality silicon nitride films with 800 nm thickness, grown on silicon substrates by low-pressure chemical vapor deposition, were determined by measuring the dispersion of laser-induced surface acoustic waves. The Young’s modulus was also measured by mechanical tuning of commercially available silicon nitride cantilevers, manufactured from the same material, using the tapping mode of a scanning force microscope. For this experiment, an expression for the oscillation frequencies of two-media beam systems is derived. Both methods yield a Young’s modulus of 280–290 GPa for amorphous silicon nitride, which is substantially higher than previously reported (E5146 GPa). For Poisson’s ratio, a value of n 50.20 was obtained. These values are relevant for the determination of the spring constant of the cantilever and the effective tip–sample stiffness

Synergic Reactions in the Estuarine Environment leading to Modulation of Aluminium metal during Transport Processes (in Cochin Estuary)

The research work which was carried out to Synergic Reactions in the Estuarine Environment leading to Modulation of Aluminium metal during Transport Processes (in Cochin Estuary)Estuaries are considered as sink or source for terrestrial and various anthropogenically generated materials. These include naturally occurring elements Al, Si, Fe or trace inorganics or industrial pollutants of different types. There have been reports on both positive and negative impacts by the introduction of above materials into the ecosystem.This thesis deals with the trace metal Aluminium (Al) whose average concentration (about 8%) in the earths crust is surpassed only by that of Oxygen and Silicon. There can be no doubt that most of the land derived materials reaches the ocean through rivers via estuaries. An important aspect noticed here is that the concentration of dissolved Al is much lower in sea water than in river water.On critically analysing Cochin estuary, for the entire cycles, covering monsoon, postmonsoon and premonsoon, the following salient features are documented as hereunder. Dissolved Al exhibits high and variable trends in Cochin estuary, the influencing parameters being salinity, SPM, pH and dissolved Si. A general profile showed removal in upper/mid estuary followed by regeneration in the mid/lower estuary and further decrease seawards in the southern/northem arms.Distribution appears to be a function of freshwater input, the monsoon season exhibiting very high concentrations throughout the estuary. As the river discharge decreased with the progress of seasons, dissolved Al concentration also decreased, the metal limiting itself to the upper and mid estuary.

Influence of Interface Surface Geometries In The Tensile Characteristics Of Friction Welded Joints From Aluminium Alloys

Friction welding is a solid state joining process that produces coalescence in materials, using the heat developed between surfaces through a combination of mechanical induced rubbing motion and applied load. In rotary friction welding technique heat is generated by the conversion of mechanical energy into thermal energy at the interface of the work pieces during rotation under pressure. Traditionally friction welding is carried out on a dedicated machine because of its adaptability to mass production. In the present work, steps were made to modify a conventional lathe to rotary friction welding set up to obtain friction welding with different interface surface geometries at two different speeds and to carry out tensile characteristic studies. The surface geometries welded include flat-flat, flat-tapered, tapered-tapered, concave-convex and convex-convex. A comparison of maximum load, breaking load and percentage elongation of different welded geometries has been realized through this project. The maximum load and breaking load were found to be highest for weld formed between rotating flat and stationary tapered at 500RPM and the values were 19.219kN and 14.28 kN respectively. The percentage elongation was found to be highest for weld formed between rotating flat and stationary flat at 500RPM and the value was 21.4%. Hence from the studies it is cleared that process parameter like “interfacing surface geometries” of weld specimens have strong influence on tensile characteristics of friction welded joints

A Comparative Study Of Tensile And Microstructural Characteristics Of Friction Welded Joints And Conventionally Welded Joints Of Aluminium Alloy 6061

Welding of high strength and low weight materials like Aluminium Alloys without any defects by conventional welding techniques is a major challenge in industries. Hence research on solid state welding techniques like Friction stir welding and Friction welding techniques have got much importance in joining of Aluminium alloys. However most of the industries are not changing conventional techniques as skilled workers are available on that area. Most common conventional welding techniques used for joining of Aluminium alloys are Gas welding and Arc welding. Friction welding is a solid-state welding process that generates heat through mechanical friction between a moving and a stationary component with the addition of a lateral force called “upset” to plast ically displace and fuse the materials. In this work, experimental study on tensile and micro structural characteristics of welded joints formed from conventional welding techniques and Rotary friction welding(suitable for weld specimens with circular cross section) has been carried out and the same were compared. The process parameters for arc welding used was 50-70 Amp reverse polarity DC and electrodes of 2.3mm diameter. In Gas welding, the parameters were oxy acetylene neural flame at 3200°C and 3mm electrodes . In the case of friction welding an axial pressure loading of 3Mpa with 5 MPa as upsetting pressure and 500 rpm were used to obtain good welded joints. Tensile characteristic studies of Arc welded joints and Gas welded joints showed 48% and 60 % variations respectively from the maximum load bearing characteristics of parent metal. In the case of friction welded joint, the variation was found to 46%. Micro structural evaluation of conventionally welded joints exhibited clear distinct zones of various weld regions. In the case of friction welded joint micro structural photographs showed comparable features both in parent metal and welded region. Thus the tensile characteristic study and microstructure evaluations proved that friction welded joints are good in both aspects compared to conventionally welded joints.

Magnetische Kopplungen in magneto-optischen Speicherschichten

Im Rahmen dieser Arbeit wurden magneto-optische Speicherschichten und ihre Kopplungen untereinander untersucht. Hierzu wurden zum Einen die für die magneto-optische Speichertechnologie "klassischen" Schichten aus RE/TM-Legierungen verwendet, zum Anderen aber auch erfolgreich Granate integriert, die bisher nicht in diesem Anwendungsgebiet verwendet wurden. Einleitend werden die magneto-optischen Verfahren, die resultierenden Anforderungen an die dünnen Schichten und die entsprechenden physikalischen Grundlagen diskutiert. Außerdem wird auf das Hochfrequenz-Sputtern von RE/TM-Legierungen eingegangen und die verwendeten magneto-optischen Messverfahren werden erläutert [Kap. 2 & 3]. Die Untersuchungen an RE/TM-Schichten bestätigen die aus der Literatur bekannten Eigenschaften. Sie lassen sich effektiv, und für magneto-optische Anwendungen geeignet, über RF-Sputtern herstellen. Die unmittelbaren Schicht-Parameter, wie Schichtdicke und Terbium-Konzentration, lassen sich über einfache Zusammenhänge einstellen. Da die Terbium-Konzentration eine Änderung der Kompensationstemperatur bewirkt, lässt sich diese mit Messungen am Kerr-Magnetometer überprüfen. Die für die Anwendung interessante senkrechte magnetische Anisotropie konnte ebenfalls mit den Herstellungsbedingungen verknüpft werden. Bei der Herstellung der Schichten auf einer glatten Glas-Oberfläche (Floatglas) zeigt die RE/TM-Schicht bereits in den ersten Lagen ein Wachstumsverhalten, das eine senkrechte Anisotropie bewirkt. Auf einer Quarzglas- oder Keramik-Oberfläche wachsen die ersten Lagen in einer durch das Substrat induzierten Struktur auf, danach ändert sich das Wachstumsverhalten stetig, bis eine senkrechte Anisotropie erreicht wird. Dieses Verhalten kann auch durch verschiedene Pufferschichten (Aluminium und Siliziumnitrid) nur unwesentlich beeinflusst werden [Kap. 5 & Kap. 6]. Bei der direkten Aufbringung von Doppelschichten, bestehend aus einer Auslese-Schicht (GdFeCo) auf einer Speicherschicht (TbFeCo), wurde die Austausch-Kopplung demonstriert. Die Ausleseschicht zeigt unterhalb der Kompensationstemperatur keine Kopplung an die Speicherschicht, während oberhalb der Kompensationstemperatur eine direkte Kopplung der Untergitter stattfindet. Daraus ergibt sich das für den MSR-Effekt erwünschte Maskierungsverhalten. Die vorher aus den Einzelschichten gewonnen Ergebnisse zu Kompensationstemperatur und Wachstumsverhalten konnten in den Doppelschichten wiedergefunden werden. Als Idealfall erweist sich hier die einfachste Struktur. Man bringt die Speicherschicht auf Floatglas auf und bedeckt diese direkt mit der Ausleseschicht [Kap. 7]. Weiterhin konnte gezeigt werden, dass es möglich ist, den Faraday-Effekt einer Granatschicht als verstärkendes Element zu nutzen. Im anwendungstauglichen, integrierten Schichtsystem konnten die kostengünstig, mit dem Sol-Gel-Verfahren produzierten, Granate die strukturellen Anforderungen nicht erfüllen, da sich während der Herstellung Risse und Löcher gebildet haben. Bei der experimentellen Realisierung mit einer einkristallinen Granatschicht und einer RE/TM-Schicht konnte die prinzipielle Eignung des Schichtsystems demonstriert werden [Kap. 8].

Modification and Analysis of Group-13-Nitride Semiconductor Surfaces: Influence of Adsorbates on Device Characteristics and Processing

Im Rahmen dieser interdisziplinären Doktorarbeit wird eine (Al)GaN Halbleiteroberflächenmodifikation untersucht, mit dem Ziel eine verbesserte Grenzfläche zwischen dem Material und dem Dielektrikum zu erzeugen. Aufgrund von Oberflächenzuständen zeigen GaN basierte HEMT Strukturen üblicherweise große Einsatzspannungsverschiebungen. Bisher wurden zur Grenzflächenmodifikation besonders die Entfernung von Verunreinigungen wie Sauerstoff oder Kohlenstoff analysiert. Die nasschemischen Oberflächenbehandlungen werden vor der Abscheidung des Dielektrikums durchgeführt, wobei die Kontaminationen jedoch nicht vollständig entfernt werden können. In dieser Arbeit werden Modifikationen der Oberfläche in wässrigen Lösungen, in Gasen sowie in Plasma analysiert. Detaillierte Untersuchungen zeigen, dass die inerte (0001) c-Ebene der Oberfläche kaum reagiert, sondern hauptsächlich die weniger polaren r- und m- Ebenen. Dies kann deutlich beim Defektätzen sowie bei der thermischen Oxidation beobachtet werden. Einen weiteren Ansatz zur Oberflächenmodifikation stellen Plasmabehandlungen dar. Hierbei wird die Oberflächenterminierung durch eine nukleophile Substitution mit Lewis Basen, wie Fluorid, Chlorid oder Oxid verändert, wodurch sich die Elektronegativitätsdifferenz zwischen dem Metall und dem Anion im Vergleich zur Metall-Stickstoff Bindung erhöht. Dies führt gleichzeitig zu einer Erhöhung der Potentialdifferenz des Schottky Kontakts. Sauerstoff oder Fluor besitzen die nötige thermische Stabilität um während einer Silicium-nitridabscheidung an der (Al)GaN Oberfläche zu bleiben. Sauerstoffvariationen an der Oberfläche werden in NH3 bei 700°C, welches die nötigen Bedingungen für die Abscheidung darstellen, immer zu etwa 6-8% reduziert – solche Grenzflächen zeigen deswegen auch keine veränderten Ergebnisse in Einsatzspannungsuntersuchungen. Im Gegensatz dazu zeigt die fluorierte Oberfläche ein völlig neues elektrisches Verhalten: ein neuer dominanter Oberflächendonator mit einem schnellen Trapping und Detrapping Verhalten wird gefunden. Das Energieniveau dieses neuen, stabilen Donators liegt um ca. 0,5 eV tiefer in der Bandlücke als die ursprünglichen Energieniveaus der Oberflächenzustände. Physikalisch-chemische Oberflächen- und Grenzflächenuntersuchung mit XPS, AES oder SIMS erlauben keine eindeutige Schlussfolgerung, ob das Fluor nach der Si3N4 Abscheidung tatsächlich noch an der Grenzfläche vorhanden ist, oder einfach eine stabilere Oberflächenrekonstruktion induziert wurde, bei welcher es selbst nicht beteiligt ist. In beiden Fällen ist der neue Donator in einer Konzentration von 4x1013 at/cm-2 vorhanden. Diese Dichte entspricht einer Oberflächenkonzentration von etwa 1%, was genau an der Nachweisgrenze der spektroskopischen Methoden liegt. Jedoch werden die elektrischen Oberflächeneigenschaften durch die Oberflächenmodifikation deutlich verändert und ermöglichen eine potentiell weiter optimierbare Grenzfläche.

Concentration of aluminium in breast cyst fluids collected from women affected by gross cystic breast disease

Gross cystic breast disease (GCBD) is the most common benign breast disorder, but the molecular basis of cyst formation remains to be identified. If the use of aluminium-based antiperspirant salts is involved in the etiology of gross breast cyst formation, it might be expected that aluminium would be at elevated levels in human breast cyst fluid (BCF). Aluminium was measured by ICP-MS in 48 samples of BCF, 30 samples of human blood serum and 45 samples of human breast milk at different stages of lactation (colostrum, intermediate, mature). The median level of aluminium in apocrine type I BCF (n:= 27, 150 mu g I-1) was significantly higher than in transuclative type II BCF (n = 21, 32 mu g I-1; P < 0.0001). By comparison, aluminium measurements gave a median concentration of 6 mu g I-1 in human serum and 25 mu g I-1 in human breast milk, with no difference between colostrum, intermediate and mature milk. Levels of aluminium were significantly higher in both types of BCF than in human serum (P < 0.0001). However when compared with human breast milk, aluminium levels were only significantly higher in apocrine type I BCF (P < 0.0001) and not in transudative type II BCF (P = 0.152). It remains to be identified why such high levels of aluminium were found in the apocrine type I BCF and from where the aluminium originated. However, if aluminium-based antiperspirants are found to be the source and to play any causal role in development of breast cysts, then it might become possible to prevent this common breast disorder. Copyright (C) 2008 John Wiley & Sons, Ltd.