Chemical characterization and bioactivity of epoxy resin and Portland cement-based sealers with niobium and zirconium oxide radiopacifiers

The purpose of this study was to characterize and to evaluate the bioactivity potential of experimental root canal sealers (ES) based on Portland cement, epoxy resin with nano- and micro-particles of niobium or zirconium oxide used as radiopacifiers in comparison to AH Plus and MTA Fillapex. Methods Specimens of the sealers (10 mm in diameter × 1 mm thick) were prepared and the radiopacity was evaluated according to ISO 6876 (2012) specifications. Characterization of the sealers was performed under the scanning electron microscope (SEM) immediately after setting and after immersion for 28 days in Hank's balanced salt solution (HBSS). In addition X-ray energy dispersive spectroscopy (EDS), X-ray diffraction (XRD) and Fourier transform infrared (FT-IR) spectroscopy were also performed. The pH and calcium ion release were measured after 1, 7, 14, 21 and 28 days after completion of seating using a digital pH meter and an atomic absorption spectrophotometer, respectively. Results The experimental sealers exhibited an average radiopacity of 2.5 mm thickness of aluminum, which was similar to MTA Fillapex (P > 0.05) and inferior to AH Plus (P < 0.05). AH Plus did not show bioactivity. Although the experimental sealers did not exhibit the formation of hydration product, they encouraged the deposition of crystalline spherical structures of calcium deficient phosphate. The highest pH and calcium release values were observed with the experimental sealers (P < 0.01). ES-Nb-micro was the only sealer to present hexagonal shaped crystal deposition. Significance Novel root canal sealers based on a mixture of Portland cement, epoxy resin and radiopacifier exhibited a degree of bioactivity although no evidence of cement hydration was demonstrated on material characterization. The radiopacifier particle size had limited effect on the sealer microstructure and chemical properties.

Fibras alimentares: efeito na farinha, reologia das massas, qualidade e taxa de envelhecimento de pães

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Extração e caracterização de amido de quinoa, cañihua e Mirabilis jalapa

Pós-graduação em Engenharia e Ciência de Alimentos - IBILCE

Estudo das propriedades mecânicas do concreto com adição de cinza de casca de arroz

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Thermal and spectroscopic study of the 3,4-(methylenedioxy) cinnamate compounds of transition metals in the solid state

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

The water effect on allosteric regulation of hemoglobin probed in water glucose and water glycine solutions

We have previously proposed a role of hydration in the allosteric control of hemoglobin based on the effect of varying concentrations of polyols and polyethers on the human hemoglobin oxygen affinity and on the solution water activity (Colombo, M. F., Rau, D. C., and Parsegian, V. A. (1992) Science 256, 655-659). Here, the original analyses are extended to test the possibility of concomitant solute and water allosteric binding and by introducing the bulk dielectric constant as a variable in our experiments. We present data which indicate that glycine and glucose influence HbA oxygen affinity to the same extent, despite the fact that glycine increases and glucose decreases the bulk dielectric constant of the solution. Furthermore, we derive an equation linking changes in oxygen affinity to changes in differential solute and water binding to test critically the possibility of neutral solute heterotropic binding. Applied to the data, these analyses support our original interpretation that neutral solutes act indirectly on the regulation of allosteric behavior of hemoglobin by varying the chemical potential of water in solution. This leads to a displacement of the equilibrium between Hb conformational states in proportion to their differential hydration.

Protective efficacy of psidium cattleianum (Sabine) and myracrodruon urundeuva (Allemao) leaf extracts against caries development in rats

This study evaluated the influence of Psidium cattleianum Sabine (Myrtaceae) and Myracrodruon urundeuva Allemão (Anacardiaceae) aqueous extracts on S. mutans counts and dental enamel micro-hardness of rats submitted to a cariogenic challenge. Sixty Wistar rats were distributed in three groups and received water (control) or aqueous extracts of Psidium cattleianum or Myracrodruon urundeuva as hydration solution. Initially the animals had their sublingual and submandibular salivary glands surgically removed and the parotid ducts ligated. Then the rats were inoculated with 106 CFU of Streptococcus mutans ATCC 35668 and were fed with a cariogenic diet. To detect and quantify the presence of S. mutans, oral biofilms were sampled and microbial DNA was extracted and submitted to amplification by means of real-time PCR (Polymerase Chain Reaction). After seven weeks the animals were sacrificed and enamel demineralization was analyzed by cross-sectional micro-hardness. Both extracts produced a significant reduction on S. mutans counts and decreased the enamel demineralization. It can be concluded that the extracts tested had a significant effect on S. mutans in oral biofilm of the rats, decreasing S. mutans accumulation and enamel demineralization.

Validação de protocolo sensorial para avaliação de carne bovina

Beef quality control, particularly its sensory characteristics, is an important factor for producers and retailers in order to satisfy consumer’s choices. Sensory analysis is an important tool to evaluate attributes that cannot be measured by easily available instrumental techniques, as well as texture – tenderness and juiciness – whose human perception is more complete, through trained panels. The aim of this study was evaluate the use of a beef sensory analysis protocol in three different laboratories. Six commercial samples of different brands of aged beef and 14 samples from crossbred animals (Bonsmara × Nelore - 7 and Canchim × Nelore - 7), aged during 14 days were analyzed. The samples were distributed to each participant laboratory, where 7 to 12 panelists were trained. A sheet containing a 9 cm non-structured scale with 14 attributes was used. The attributes were brown colour (CMAR); aponevrosis (PNAP); hydration degree (GH); characteristic beef aroma (SCCB); salty taste (SS); liver flavour (SF); fat flavour (SG); metallic flavour (SM); tenderness (MZ); juiciness (SL); fibrosity (FBS) and liver texture (SF). Obtained data was analyzed using analysis of variance and principal component analysis (PCA). The results showed that there was no interaction between samples and laboratories, indicating that all of them responded in a similar manner in relation to the samples, except PNAP attribute, which was expected as meat is very non-uniform normally. Samples were well differentiated in all laboratories as it could be observed in PCA graphs. With proper training it is possible to use a standard protocol for beef sensory analysis.

Desenvolvimento de hidrogéis nanoestruturados baseados em polissacarídeo e zeólita para aplicação em sistemas de liberação controlada

Pós-graduação em Ciência dos Materiais - FEIS

Mejillonesite, a new acid sodium, magnesium phosphate mineral, from Mejillones, Antofagasta, Chile

Mejillonesite, ideally NaMg(2)(PO(3)OH)(PO(4))(OH)center dot H(5)O(2), is a new mineral approved by the CNMNC (IMA 2010-068). It occurs as isolated crystal aggregates in thin zones in fine-grained opal-zeolite aggregate on the north slope of Cerro Mejillones, Antofagasta, Chile. Closely associated minerals are bobierrite, opal, clinoptilolite-Na, clinoptilolite-K, and gypsum. Mejillonesite forms orthorhombic, prismatic, and elongated thick tabular crystals up to 6 mm long, usually intergrown in radiating aggregates. The dominant form is pinacoid {100}. Prisms {hk0}, {h0l}, and {0kl} are also observed. The crystals are colorless, their streak is white, and the luster is vitreous. The mineral is transparent. It is non-fluorescent under ultraviolet light. Mohs' hardness is 4, tenacity is brittle. Cleavage is perfect on {100}, good on {010} and {001}, and fracture is stepped. The measured density is 2.36(1) g/cm(3); the calculated density is 2.367 g/cm(3). Mejillonesite is biaxial (-), alpha= 1.507(2), beta= 1.531(2), gamma= 1.531(2), 2V(meas) = 15(10)degrees, 2V(calc) = 0 degrees (589 nm). Orientation is X= a, Z= elongation direction. The mineral is non-pleochroic. Dispersion is r> v, medium. The IR spectrum contains characteristic bands of the Zundel cation (H(5)O(2)(+), or H(+)center dot 2H(2)O) and the groups P-OH and OH(-). The chemical composition is (by EDS, H(2)O by the Alimarin method, wt%): Na(2)O 9.19, MgO 26.82, P(2)O(5) 46.87, H(2)O 19, total 101.88. The empirical formula, based on 11 oxygen atoms, is Na(0.93)Mg(2.08)(PO(3)OH)(1.00) (PO(4)) (OH)(0.86) .0.95H(5)O(2) The strongest eight X-ray powder-diffraction lines [d in angstrom(I)(hkl)] are: 8.095(100)(200), 6.846(9) (210), 6.470(8)(111), 3.317(5)(302), 2.959(5)(132), 2.706(12)(113), 2.157(19)(333), and 2.153(9) (622). The crystal structure was solved on a single crystal (R = 0.055) and gave the following data: orthorhombic, Pbca, a = 16.295(1), b = 13.009(2), c = 8.434(1) angstrom, V= 1787.9(4) angstrom(3), Z = 8. The crystal structure of mejillonesite is based on a sheet (parallel to the b-c plane) formed by two types of MgO(6) octahedra, isolated tetrahedra PO(4) and PO(3)OH whose apical vertices have different orientation with respect to the sheet. The sheets are connected by interlayer, 5-coordinated sodium ions, proton hydration complexes, and hydroxyl groups. The structure of mejillonesite is related to that of angarfite, NaFe(5)(3+)(PO(4))(4)(OH)(4).4H(2)O and bakhchisaraitsevite, Na(2)Mg(5)(PO(4))(4)center dot 7H(2)O.

Characterization and properties of blended cement matrices containing activated bamboo leaf wastes

The worldwide production of bamboo generates large volumes of leaf wastes, which are deposited in landfills or burned in an uncontrolled manner, with negative effects in the environment. The ash obtained by calcining of the bamboo leaf waste, shows good qualities as supplementary cementing material for the production of blended cements. The current paper shows a detailed scientific study of a Brazilian bamboo leaf ash (BLA) calcined at 600 degrees C in small scale condition, by using different techniques (XRF, XRD, SEM/EDX, FT-IR, TG/DTG) and technical study in order. to analyse the behaviour of this ash in blended cements elaborated with 10% and 20% by mass of BLA. The results stated that this ash shows a very high pozzolanic activity, with a reaction rate constant K of the order of 10(-1)/h and type I CSH gel was the main hydrated phase obtained from pozzolanic reaction. The BLA blended cements (10% and 20%) complied with the physical and mechanical requirements of the existing European standards. (c) 2012 Elsevier Ltd. All rights reserved.

PHYSIOLOGICAL QUALITY OF OSMOPRIMED EGGPLANT SEEDS

Eggplant seeds germination can be slow and uneven, justifying the use of pre-germinative treatments to improve the performance of seed lots. One option of treatment is the controlled hydration of seeds by priming. In this way, this study aimed to evaluate the performance of eggplant seeds cv. Embu submitted to different methodologies of priming. The seeds used in the experiment were stored in cold chamber (15 degrees C and 55% RH) in paper bags. The research was carried out at Central Laboratory of Seeds/UFLA. The seeds were submitted to the priming in aerated solutions varying the following factors: temperature (15 degrees C and 25 degrees C), time (24, 48 and 72 hours) and solution (water, PEG, KNO3 and PEG+KNO3). Seeds were washed in running water and dried at 30 degrees C, until the return to the initial moisture content, around 10%. The variables analyzed were percentage of germination, percentage of emergence, speed index of emergence and electrical conductivity. The treatments were arranged in a completely randomized design, according to a factorial arrangement 2x3x4+1 (control - seeds without priming). The results showed that priming improves the vigour of eggplant seeds with no effect on viability; the priming in water or KNO3 is efficient to improve the seed vigour and priming in water or KNO3 may use temperature of 15 degrees C or 25 degrees C for 24, 48 or 72 hours.

Effect of EVA on the fresh properties of cement paste

The improved workability effect of latex in dry mortars has not been fully clarified. The purpose of this research was to investigate the influence cif the EVA copolymer on the cement hydration and on the rheological properties of cement pastes. The results pointed to a minor influence of EVA on cement hydration and to a ball-bearing effect. In fact, the shear thinning behavior of reference paste at 15 min after mixing changed to shear thickening owing to the EVA addition. This behavior could be explained by the decrease in the interparticle separation distance as consequence of the solid content increase in case of shearing detachment of weakly adhered EVA particles from the cement particles surfaces. The expected EVA plasticizing effect was observed at 60 min. Such behavior points to the stabilization of EVA on the cement particles surfaces, thus resulting in a steric barrier effect. (C) 2011 Elsevier Ltd. All rights reserved.

Effect of cations/polycations on the efficiency of formation of a hybrid bilayer membrane that mimics the inner mitochondrial membrane

We aim in this study to characterize the effect of cations and polycations on the formation of hybrid bilayer membranes (HBMs), especially those that mimic the inner mitochondrial membrane (IMM), with a proper composition of phosphatidylcholine (PC), phosphatidylethanolamine (PE) and cardiolipin (CL) adsorbed on an alkanethiol monolayer. HBMs are versatile membrane mimetics that show promising results in sensor technology. Its formation depends on the fusion of vesicles on hydrophobic surfaces, a process that is not well understood at the molecular level. Our results showed to which extend and in which condition the presence of cations and polycations facilitate the formation of HBMs. The required time for lipid layer formation was reduced several times and the lipid layer reaches the expected thickness of 19.5 +/- 1.8 angstrom, in contrast to only 2 +/- 1.5 angstrom usually observed in the absence of cations. In the presence of specific concentrations of spermine and Ca2+ the amount of adsorbed phospholipids on the thiol layer increased nearly 70% compared to that observed when Na+ was used at concentrations 10 times higher. Divalent cations and polycations adsorb specifically on the lipid headgroups destabilizing the hydration forces, facilitating the process of vesicle fusion and formation of lipid monolayers. The concepts and conditions described in the manuscript will certainly help the development of the field of membrane biosensors. (C) 2011 Elsevier B.V. All rights reserved.

Efficacy of Cosmetic Formulations Containing Dispersion of Liposome with Magnesium Ascorbyl Phosphate, Alpha-Lipoic Acid and Kinetin

The present study aimed to evaluate the photoprotective effects of cosmetic formulations containing a dispersion of liposome with magnesium ascorbyl phosphate (MAP), alpha-lipoic acid (ALA) and kinetin, as well as their effects on the hydration and viscoelastic skin properties. The photoprotection was determined in vitro (antioxidant activity) and in vivo on UV-irradiated hairless mouse skin. The hydration effects were performed with the application of the formulations under study on the forearm of human volunteers and skin conditions were analyzed before and after a single application and daily applications during 4 weeks in terms of transepidermal water loss (TEWL), skin moisture and viscoelastic properties. The raw material under study possessed free-radical scavenging activity and the formulation with it protected hairless mouse skin barrier function against UV damage. After 4 weeks of application on human skin, the formulation under study enhanced stratum corneum skin moisture and also showed hydration effects in deeper layers of the skin. Thus, it can be concluded that the cosmetic formulation containing a dispersion of liposome with MAP, ALA and kinetin under study showed photoprotective effects in skin barrier function as well as pronounced hydration effects on human skin, which suggests that this dispersion has potential antiaging effects.