Characterization of aqueous silver nitrate solutions for leakage tests

OBJECTIVE: To determine the pH over a period of 168 h and the ionic silver content in various concentrations and post-preparation times of aqueous silver nitrate solutions. Also, the possible effects of these factors on microleakage test in adhesive/resin restorations in primary and permanent teeth were evaluated. MATERIAL AND METHODS: A digital pHmeter was used for measuring the pH of the solutions prepared with three types of water (purified, deionized or distilled) and three brands of silver nitrate salt (Merck, Synth or Cennabras) at 0, 1, 2, 24, 48, 72, 96 and 168 h after preparation, and storage in transparent or dark bottles. Ionic silver was assayed according to the post-preparation times (2, 24, 48, 72, 96, 168 h) and concentrations (1, 5, 25, 50%) of solutions by atomic emission spectrometry. For each sample of each condition, three readings were obtained for calculating the mean value. Class V cavities were prepared with enamel margins on primary and permanent teeth and restored with the adhesive systems OptiBond FL or OptiBond SOLO Plus SE and the composite resin Filtek Z-250. After nail polish coverage, the permanent teeth were immersed in 25% or 50% AgNO3 solution and the primary teeth in 5% or 50% AgNO3 solutions for microleakage evaluation. ANOVA and the Tukey's test were used for data analyses (α=5%). RESULTS: The mean pH of the solutions ranged from neutral to alkaline (7.9±2.2 to 11.8±0.9). Mean ionic silver content differed depending on the concentration of the solution (4.75±0.5 to 293±15.3 ppm). In the microleakage test, significant difference was only observed for the adhesive system factor (p=0.000). CONCLUSIONS: Under the tested experimental conditions and based on the obtained results, it may be concluded that the aqueous AgNO3 solutions: have neutral/alkaline pH and service life of up to 168 h; the level of ionic silver is proportional to the concentration of the solution; even at 5% concentration, the solutions were capable of indicating loss of marginal seal in the composite restorations; the 3-step conventional adhesive system had better performance regarding microleakage in enamel on primary and permanent teeth.

Knoop microhardness and FT-Raman evaluation of composite resins: influence of opacity and photoactivation source

The aim of this study was to evaluate the degree of conversion by Knoop microhardness (KHN) and FT-Raman spectroscopy (FTIR) of one nanofilled (Filtek Supreme-3M-ESPE [FS]) and one microhybrid composite (Charisma-Heraeus-Kulzer [CH]), each with different opacities, namely enamel, dentin, and translucent, which were photo-activated by a quartz-tungsten-halogen lamp (QTH) and a light-emitting diode (LED). Resin was bulk inserted into a disc-shaped mold that was 2.0 mm thick and 4 mm in diameter, obtaining 10 samples per group. KHN and FTIR values were analyzed by two-way ANOVA and Tukey's tests (α = 0.05). Nanofilled resin activated by a LED presented higher microhardness values than samples activated by a QTH for dentin opacity (p < 0.05). The microhybrid resin showed no differences in KHN or FTIR values with different activation sources or opacity. The nanofilled dentin and enamel resins showed lower FTIR values than the translucent resin. The KHN values of the translucent resins were not influenced by the light source.

NEAR INFRARED SPECTROSCOPY FOR ESTIMATING SUGARCANE BAGASSE CONTENT IN MEDIUM DENSITY FIBERBOARD

Medium density fiberboard (MDF) is an engineered wood product formed by breaking down selected lignin-cellulosic material residuals into fibers, combining it with wax and a resin binder, and then forming panels by applying high temperature and pressure. Because the raw material in the industrial process is ever-changing, the panel industry requires methods for monitoring the composition of their products. The aim of this study was to estimate the ratio of sugarcane (SC) bagasse to Eucalyptus wood in MDF panels using near infrared (NIR) spectroscopy. Principal component analysis (PCA) and partial least square (PLS) regressions were performed. MDF panels having different bagasse contents were easily distinguished from each other by the PCA of their NIR spectra with clearly different patterns of response. The PLS-R models for SC content of these MDF samples presented a strong coefficient of determination (0.96) between the NIR-predicted and Lab-determined values and a low standard error of prediction (similar to 1.5%) in the cross-validations. A key role of resins (adhesives), cellulose, and lignin for such PLS-R calibrations was shown. PLS-DA model correctly classified ninety-four percent of MDF samples by cross-validations and ninety-eight percent of the panels by independent test set. These NIR-based models can be useful to quickly estimate sugarcane bagasse vs. Eucalyptus wood content ratio in unknown MDF samples and to verify the quality of these engineered wood products in an online process.

In Vitro Adhesion of Streptococcus sanguinis to Dentine Root Surface After Treatment with Er:Yag Laser, Ultrasonic System, or Manual Curette

Objective: The purpose of this in vitro study was to evaluate the dentine root surface roughness and the adherence of Streptococcus sanguinis (ATCC 10556) after treatment with an ultrasonic system, Er:YAG laser, or manual curette. Background Data: Bacterial adhesion and formation of dental biofilm after scaling and root planing may be a challenge to the long-term stability of periodontal therapy. Materials and Methods: Forty flattened bovine roots were randomly assigned to one of the following groups: ultrasonic system (n = 10); Er:YAG laser (n = 10); manual curette (n = 10); or control untreated roots (n = 10). The mean surface roughness (Ra, mu m) of the specimens before and after exposure to each treatment was determined using a surface profilometer. In addition, S. sanguinis was grown on the treated and untreated specimens and the amounts of retained bacteria on the surfaces were measured by culture method. Results: All treatments increased the Ra; however, the roughest surface was produced by the curettes. In addition, the specimens treated with curettes showed the highest S. sanguinis adhesion. There was a significant positive correlation between roughness values and bacterial cells counts. Conclusion: S. sanguinis adhesion was the highest on the curette-treated dentine root surfaces, which also presented the greatest surface roughness.

Er : YAG laser, ultrasonic system, and curette produce different profiles on dentine root surfaces: An in vitro study

Objective: The aim of the present study was to compare the in vitro effects of the Er:YAG laser, an ultrasonic system, and manual curette on dentine root surface by roughness and micro-morphological analysis. Materials and Methods: Thirty-six flattened bovine roots were randomly assigned to one of the following groups: group 1 (n = 12): Er: YAG laser ( 2940 nm), 120 mJ/pulse, 10 Hz, 8.4 J/cm(2); group 2 ( n = 12): ultrasonic system; and group 3 ( n = 12): manual curette. The mean surface roughness (Ra) of each sample was measured using a profilometer before and after the treatments. The micro-morphology of the treated and untreated ( control) root surfaces was evaluated with scanning electron microscopy (SEM) at 50 x and 1000 x magnification. Results: Analysis with the profilometer showed that for equal times of instrumentation, the smoothest surfaces were produced by the Er: YAG laser and the ultrasonic system, followed by the curette ( p < 0.05). Morphological analyses demonstrated that treatment with the Er: YAG laser produced some areas with an irregular surface, craters, and ablation of the intertubular dentin. The smear layer was removed and dentine tubules were opened by both curettes and the ultrasonic system. The micro-morphology of the dentine root surface after ultrasonic treatment, however, demonstrated randomly distributed areas cratering. Conclusion: All instruments increased the roughness of the dentine root surface after treatment; however, the curette produced rougher surfaces than the other devices. SEM analysis revealed distinct root surface profiles produced by the three devices.

Evaluation of the Bond Strength Between a Composite Resin and Enamel Submitted to Bleaching Treatment and Etched with Er:YAG Laser

Background: The use of laser irradiation for dental surface treatment may increase tooth-composite bond strength. Its use on bleached teeth may decrease the waiting time between bleaching and restorative procedures. Objective: This study aimed to evaluate the bond strength between a composite resin and bovine enamel bleached with 35% hydrogen peroxide and etched with Er:YAG laser. Materials and Methods: Thirty bovine teeth were randomly divided into six groups (n = 5): G1, unbleached and restored 24 h after storage in artificial saliva, etching with 35% phosphoric acid (PA) (control); G2, unbleached and restored 24 h after storage in artificial saliva, etching with Er:YAG laser and 35% PA; G3, bleached and restored immediately afterward, etching with 35% PA; G4, bleached and restored 24 h after bleaching, etching with 35% PA; G5, bleached and restored immediately afterward, etching with Er:YAG and 35% PA laser; G6, bleached and restored 24 h after bleaching, etching with Er:YAG laser and 35% PA. Bond strength was quantitatively evaluated by microtensile test (1.0 mm/min). Data were submitted to statistical analysis using ANOVA and Tukey tests (alpha - 0.05). Results: Bond strength values (MPa) were G1, 26.17 +/- 4.44; G2, 28.87 +/- 3.94; G3, 17.25 +/- 4.58; G4, 21.93 +/- 5.02; G5, 16.69 +/- 2.31; and G6, 29.06 +/- 8.31. There was no statistically significant difference among groups G1, G2, and G6 (p - 0.119), which presented higher bond strength than group G4, followed by groups G3 and G5. Conclusion: Er:YAG irradiation of bleached surfaces may favor bonding procedures when performed 24 h after bleaching.

Apical Leakage of Three Resin-Based Endodontic Sealers after 810-nm-Diode Laser Irradiation

Objective: To evaluate the influence of 810-nm-diode laser irradiation, applied before root canal filling, on apical sealing ability of three different resin-based sealers (AH Plus, EndoRez, and RealSeal). Background: Lasers have been widely used in endodontics. The dentin wall changes caused by laser irradiation could improve the sealing ability of endodontic cements. Methods: Sixty single-rooted human teeth were divided into six groups, according to the endodontic sealer used and previous 810-nm-diode laser irradiation. The protocol for laser irradiation was 2.5W in a continuous wave, in scanning mode, with four irradiations per tooth. After sample preparation, they were analyzed according to apical leakage with silver nitrate impregnation. Results: The RealSeal sealer achieved minimum leakage rates (1.24 mm), with significant differences at the 1% level (Tukey's test, p < 0.01) from AH Plus (1.84 mm) in nonirradiated groups. When the laser was used, there were also significant differences at the 5% level (p < 0.05) between irradiated groups (1.31 and 1.78 mm, respectively). Conclusion: The 810-nm-diode laser irradiation did not promote significant differences in apical leakage.

Effect of a Single Application of TiF(4) and NaF Varnishes and Solutions Combined with Nd:YAG Laser Irradiation on Enamel Erosion in Vitro

Objective: This in vitro study aimed to analyze the influence of neodymium-doped yttrium aluminum garnet (Nd:YAG) laser irradiation on the efficacy of titanium tetrafluoride (TiF(4)) and sodium fluoride (NaF) varnishes and solutions to protect enamel against erosion. Background data: The effect of Nd:YAG laser irradiation on NaF and AmF was analyzed; however, there is no available data on the interaction between Nd:YAG laser irradiation and TiF(4). Methods: Bovine enamel specimens were pre-treated with NaF varnish, TiF(4) varnish, NaF solution, TiF(4) solution, placebo varnish, Nd:YAG (84.9 J/cm(2)), Nd:YAG prior to or through NaF varnish, Nd:YAG prior to or through TiF(4) varnish, Nd:YAG prior to or through NaF solution, Nd:YAG prior to or through TiF(4) solution, and Nd:YAG prior to or through placebo varnish. Controls remained untreated. Ten specimens in each group were then subjected to an erosive demineralization (Sprite Zero, 4x90 s/day) and remineralization (artificial saliva, between the erosive cycles) cycling for 5 days. Enamel loss was measured profilometrically (mu m). Additionally, treated but non-eroded specimens were additionally analyzed by scanning electron microscope (SEM) (each group n-2). The data were statistically analyzed by ANOVA and Tukey's post-hoc test (p < 0.05). Results: Only TiF(4) varnish (1.8 +/- 0.6 mu m), laser prior to TiF(4) varnish (1.7 +/- 0.3 mu m) and laser prior to TiF(4) solution (1.4 +/- 0.3 mu m) significantly reduced enamel erosion compared to the control (4.1 +/- 0.6 mu m). SEM pictures showed that specimens treated with TiF(4) varnish presented a surface coating. Conclusions: Nd:YAG laser irradiation was not effective against enamel erosion and it did not have any influence on the efficacy of F, except for TiF(4) solution. On the other hand, TiF(4) varnish protected against enamel erosion, without the influence of laser irradiation.

Effect of Nd:YAG Irradiation and Fluoride Application on Dentine Resistance to Erosion in Vitro

Objective: In this paper we evaluated the effect of two fluoridated agents and Nd:YAG irradiation separately and in combination on dentine resistance to erosion. Background Data: The morphological changes in dentin induced by laser treatment may reduce the progression of erosive lesions. Due to the possibility of a synergistic effect of laser with fluoride, this study was conducted. Materials and Methods: Eighty bovine dentine samples (4 x 4 mm) were randomly divided into eight groups, according to the following treatments: G1: untreated (control); G2: acidic phosphate fluoride gel (APF 1.23%) for 4 min; G3: fluoride varnish (NaF 2.26%) for 6 h; G4: 0.5 W Nd: YAG laser (250 mu sec pulse, 10 Hz, 35 J/cm(2), 30 sec); G5: 0.75 W Nd: YAG laser (52.5 J/cm(2)); G6: 1.0 W Nd: YAG laser (70 J/cm(2)); G7: APF + 0.75 W Nd: YAG laser; and G8: NaF + 0.75 W Nd: YAG laser. After the treatments, half of each dentine surface was protected with nail varnish. The samples were stored in artificial saliva (30 mL/sample) for 24 h and submitted to four erosive 1-min cycles. Between the erosive attacks, the blocks were maintained in artificial saliva for 59 min. The erosive wear was evaluated by profilometry. Results: The mean wear (+/- SD, mu m) was: G1: 1.20 +/- 0.20; G2: 0.47 +/- 0.06; G3: 0.81 +/- 0.11; G4: 1.47 +/- 0.32; G5: 1.52 +/- 0.24; G6: 1.49 +/- 0.30; G7: 0.49 +/- 0.11; and G8: 1.06 +/- 0.31 (Tukey's test, p < 0.05). Conclusions: Laser irradiation was not able to reduce dentine erosion. However, fluoride application was able to increase the dentine's resistance to erosion, and APF showed better results than fluoride varnish.

Ultra-Structural Changes at the Apical Stop Irradiated with CO(2) Laser

Objective: This study evaluated ultra-structural dentine changes at the apical stop after CO(2) laser irradiation used during biomechanical preparation. Background: Most studies evaluating the sealing efficiency of CO(2) lasers have been carried out after apical root canal resections and retro-filling procedures. Methods: Sixty human canines were prepared with #1 to #6 Largo burs. The apical stops were established at 1 mm (n = 30) and 2 mm (n = 30) from the apex. Final irrigation was performed with 1% NaOCl and 15% EDTA followed by 20 ml of distilled and deionized water. Specimens were subdivided into three subgroups (n = 10 for each stop distance): GI-no radiation (n = 20); GII-3W potency (n = 20), GIII-5W potency (n = 20). After preparation, specimens were evaluated by scanning electron microscopy, with ultra-structural changes classified according to a scoring system based on six qualitatively different outcomes. Results: Statistical analysis using the Mann-Whitney test confirmed more intense results for the specimens irradiated at 5 W potency than at 3 W (p<0.0001). The Kruskal-Wallis test indicated that when using the same potencies (3 or 5 W) at 1 and 2 mm from the apex, there were no statistically significant differences in ultra-structural changes. Conclusions: Our results showed that ultra-structural changes ranged from smear layer removal to dentine fusion. As laser potency was increased from 3 to 5 W, ultra-structural changes included extensive fused lava-like areas sealing the apical foramen.

Adhesion of Endodontic Sealers to Human Root Dentine Submitted to Different Surface Treatments

Objective: To evaluate the adhesion of the endodontic sealers Epiphany, Apexit Plus, and AH Plus to root canal dentin submitted to different surface treatments, by using the push-out test. Methods: One hundred twenty-eight root cylinders obtained from maxillary canines were embedded in acrylic resin, had the canals prepared, and were randomly assigned to four groups (n = 32), according to root dentin treatment: (I) distilled water (control), (II) 17% EDTAC, (III) 1% NaOCl and (IV) Er:YAG laser with 16-Hz, 400-mJ input (240-mJ output) and 0.32-J/cm(2) energy density. Each group was divided into four subgroups (n = 8) filled with Epiphany (either dispensed from the automix syringe supplied by the manufacturer or prepared by hand mixing), Apexit Plus, or AH Plus. Data (MPa) were analyzed by ANOVA and Tukey's test. Results: A statistically significant difference (p < 0.01) was found among the root-canal sealers, except for the Epiphany subgroups, which had statistically similar results to each other (p > 0.01): AH Plus (4.77 +/- 0.85), Epiphany/hand mixed (3.06 +/- 1.34), Epiphany/automix syringe (2.68 +/- 1.35), and Apexit Plus (1.22 +/- 0.33). A significant difference (p < 0.01) was found among the dentin surface treatments. The highest adhesion values were obtained with AH Plus when root dentin was treated with Er: YAG laser and 17% EDTAC. Epiphany sealer presented the lowest adhesion values to root dentin treated with 17% EDTAC. Conclusions: The resin-based sealers had different adhesive behaviors, depending on the treatment of root canal walls. The mode of preparation of Epiphany (automix syringe or hand mixing) did not influence sealer adhesion to root dentin.

Influence of pulse repetition rate on temperature rise and working time during composite filling removal with the Er : YAG laser

Objective: The purpose of this study was to assess the efficacy of Er:YAG laser energy for composite resin removal and the influence of pulse repetition rate on the thermal alterations occurring during laser ablation. Materials and Methods: Composite resin filling was placed in cavities (1.0 mm deep) prepared in bovine teeth and the specimens were randomly assigned to five groups according to the technique used for composite filling removal. In group I (controls), the restorations were removed using a high-speed diamond bur. In the other groups, the composite fillings were removed using an Er: YAG laser with different pulse repetition rates: group 2-2 Hz; group 3-4 Hz; group 4-6 Hz; and group 5-10 Hz. The time required for complete removal of the restorative material and the temperature changes were recorded. Results: Temperature rise during composite resin removal with the Er: YAG laser occurred in the substrate underneath the restoration and was directly proportional to the increase in pulse repetition rate. None of the groups had a temperature increase during composite filling removal of more than 5.6 degrees C, which is considered the critical point above which irreversible thermal damage to the pulp may result. Regarding the time for composite filling removal, all the laser-ablated groups (except for group 5 [10 Hz]) required more time than the control group for complete elimination of the material from the cavity walls. Conclusion: Under the tested conditions, Er: YAG laser irradiation was efficient for composite resin ablation and did not cause a temperature increase above the limit considered safe for the pulp. Among the tested pulse repetition rates, 6 Hz produced minimal temperature change compared to the control group (high-speed bur), and allowed composite filling removal within a time period that is acceptable for clinical conditions.

Ultrastructural analysis of root canal dentine irradiated with 980-nm diode laser energy at different parameters

Objective: The purpose of this in vitro study was to investigate using the scanning electron microscope (SEM) the ultrastructural morphological changes of the radicular dentine surface after irradiation with 980-nm diode laser energy at different parameters and angles of incidence. Background Data: There have been limited reports on the effects of diode laser irradiation at 980 nm on radicular dentin morphology. Materials and Methods: Seventy-two maxillary canines were sectioned and roots were biomechanically prepared using K3 rotary instruments. The teeth were irrigated with 2 mL of distilled water between files and final irrigation was performed with 10 mL of distilled water. The teeth were then randomly divided into five groups (n = 8 each) according to their diode laser parameters: Group 1: no irradiation (control); group 2: 1.5 W/continuous wave (CW) emission (the manufacturer's parameters); group 3: 1.5 W/100 Hz; group 4: 3 W/CW; and group 5: 3 W/100 Hz. Laser energy was applied with helicoid movements (parallel to the canal walls) for 20 sec. Eight additional teeth for each group were endodontically prepared and split longitudinally and irradiation was applied perpendicularly to the root surface. Results: Statistical analysis showed no difference between the root canal thirds irradiated with the 980-nm diode laser, and similar results between the parameters 1.5 W/CW and 3 W/100 Hz (p > 0.05). Conclusion: When considering different output powers and delivery modes our results showed that changes varied from smear layer removal to dentine fusion.

Effect of Er:YAG Laser Parameters on Ablation Capacity and Morphology of Primary Enamel

Objective: The purpose of this study was to evaluate the ablation capacity of different energies and pulse repetition rates of Er:YAG laser energy on primary molar enamel, by assessing mass loss and by analyzing the surface morphology with scanning electron microscopy. Background Data: Previous studies have demonstrated the capacity of the Er:YAG laser to ablate enamel substrate. Methods: Forty-two sound primary molars were bisected in a mesiodistal direction. The enamel surfaces were flattened and their initial mass (in milligrams) was obtained. An area of 4 mm(2) was delimited. The specimens were randomly assigned to 12 groups according to the combination of energy (160, 200, 250, and 300 mJ) and pulse repetition rate (2, 3, and 4 Hz). Er: YAG laser irradiation was performed on each specimen for 20 sec. After irradiation, the final mass was obtained and specimens were prepared for examination with scanning electron microscopy. The data obtained by subtracting the final mass from the initial mass were statistically analyzed using ANOVA and the Tukey test (p < 0.05). Results: The pulse repetition rate of 4 Hz provided greater mass loss, different from that seen with 2 Hz, and similar to that seen with 3 Hz. The energy level of 300 mJ resulted in greater mass loss, similar to that seen with 200 and 250 mJ. Scanning electron photomicrographs showed that there was non-selective enamel removal, with fused and cracked areas in all specimens. Conclusion: The parameters of 200 mJ and 2 Hz produced a good ablation rate with fewer surface alterations in primary molar enamel.

Three-dimensional finite element thermal analysis of dental tissues irradiated with Er,Cr:YSGG laser

In the present study, a finite element model of a half-sectioned molar tooth was developed in order to understand the thermal behavior of dental hard tissues (both enamel and dentin) under laser irradiation. The model was validated by comparing it with an in vitro experiment where a sound molar tooth was irradiated by an Er,Cr:YSGG pulsed laser. The numerical tooth model was conceived to simulate the in vitro experiment, reproducing the dimensions and physical conditions of the typical molar sound tooth, considering laser energy absorption and calculating the heat transfer through the dental tissues in three dimensions. The numerical assay considered the same three laser energy densities at the same wavelength (2.79 mu m) used in the experiment. A thermographic camera was used to perform the in vitro experiment, in which an Er, Cr: YSGG laser (2.79 mu m) was used to irradiate tooth samples and the infrared images obtained were stored and analyzed. The temperature increments in both the finite element model and the in vitro experiment were compared. The distribution of temperature inside the tooth versus time plotted for two critical points showed a relatively good agreement between the results of the experiment and model. The three dimensional model allows one to understand how the heat propagates through the dentin and enamel and to relate the amount of energy applied, width of the laser pulses, and temperature inside the tooth. (C) 2008 American Institute of Physics. [DOI: 10.1063/1.2953526]