Desenvolvimento e caracterização de ligas de Co-Cr-Mo

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Propriedades mecânicas, físico-químicas e biológica de adesivo experimental com incorporação de epigalocatequina-3-galato

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Avaliação da bioatividade de revestimentos produzidos sobre Tântalo por oxidação eletrolítica assistida por plasma

Pós-graduação em Ciência e Tecnologia de Materiais - FC

Caracterização da liga Ti-15Zr visando aplicações biomédicas

With advances in health care, has been na increase of demand for material that could replace the functions of the human body parts, thus evolved biomedic prosthesis which today are responsible for the constant improvement of the quality of life. The Titanium alloys are widely used as implants due to its properties, like high mechanical resistance, biocompatibility and corrosion resistance, and the addition alloying elements like Zirconium, may improve some of those properties. Such properties are related to the microstructure and consequently to the type of processing performed. The purpose of this dissertation was to characterize the experimental alloy Ti15Zr after route of processsing and heat treatment in order to extend the knowledge about this alloy. The latter has been abtained by fusion of pure metals in a arc melting furnace with an inert argon atmosphere. The material has been homogenized in a tube furnace at 950ºC for 24h and cold worked by swaging, after that, bars with 10 mm of diameter were obtained by the process of rotary forging. The samples were solubilized at 900º C for 2 hours and quenched in water. After that, 4 samples were submitted to the aging, at 400º C, 450º C, 500º C and 550º C. The microstructure and phase analysis was done by optical microscopy and X-rays diffraction (XRD), the mechanical characterization was carried out by microhardness test and finally, evaluation of corrosion resistance of the alloy by electrochemical tests. The XRD and the optical microscopy made it possible to analyze that the heat treatment influenced the phase shifting from α to α', and probably affected the alloy hardness, at the first aged sample at 500º Chas been a sudden increase in the value of hardness, probably by appearance of omega phase, unwanted phase to the medical application duo to great fragility, and finally ... (Complete abstract click electronic access below)

Avaliação da bioatividade de revestimentos produzidos sobre Tântalo por oxidação eletrolítica assistida por plasma

Pós-graduação em Ciência e Tecnologia de Materiais - FC

Caracterização da liga Ti-15Zr visando aplicações biomédicas

With advances in health care, has been na increase of demand for material that could replace the functions of the human body parts, thus evolved biomedic prosthesis which today are responsible for the constant improvement of the quality of life. The Titanium alloys are widely used as implants due to its properties, like high mechanical resistance, biocompatibility and corrosion resistance, and the addition alloying elements like Zirconium, may improve some of those properties. Such properties are related to the microstructure and consequently to the type of processing performed. The purpose of this dissertation was to characterize the experimental alloy Ti15Zr after route of processsing and heat treatment in order to extend the knowledge about this alloy. The latter has been abtained by fusion of pure metals in a arc melting furnace with an inert argon atmosphere. The material has been homogenized in a tube furnace at 950ºC for 24h and cold worked by swaging, after that, bars with 10 mm of diameter were obtained by the process of rotary forging. The samples were solubilized at 900º C for 2 hours and quenched in water. After that, 4 samples were submitted to the aging, at 400º C, 450º C, 500º C and 550º C. The microstructure and phase analysis was done by optical microscopy and X-rays diffraction (XRD), the mechanical characterization was carried out by microhardness test and finally, evaluation of corrosion resistance of the alloy by electrochemical tests. The XRD and the optical microscopy made it possible to analyze that the heat treatment influenced the phase shifting from α to α', and probably affected the alloy hardness, at the first aged sample at 500º Chas been a sudden increase in the value of hardness, probably by appearance of omega phase, unwanted phase to the medical application duo to great fragility, and finally ... (Complete abstract click electronic access below)

Detorque evaluation of dental abutment screws after immersion in a fluoridated artificial saliva solution

Purpose: Implant-abutment connections still present failures in the oral cavity due to the loosening of mechanical integrity by detorque and corrosion of the abutment screws. The objective of this study was to evaluate the detorque of dental abutment screws before and after immersion in fluoridated solutions. Materials and Methods: Five commercial implant-abutment assemblies were assessed in this investigation: (C) Conex˜aoR , (E) EmfilsR , (I) INPR , (S) SINR , and (T) Titanium FixR . The implants were embedded in an acrylic resin and then placed in a holding device. The abutments were first connected to the implants and torqued to 20Ncmusing a handheld torque meter. The detorque values of the abutments were evaluated after 10 minutes. After applying a second torque of 20 Ncm, implant-abutment assemblies were withdrawn every 3 hours for 12 hours in a fluoridated solution over a period of 90 days. After that period, detorque of the abutments was examined. Scanning electronicmicroscopy (SEM) associated to energy dispersive spectroscopy (EDS) was applied to inspect the surfaces of abutments. Results: Detorque values of systems C, E, and I immersed in the fluoridated solution were significantly higher than those of the initial detorque. ANOVA demonstrated no significant differences in detorque values between designs S and T. Signs of localized corrosion could not be detected by SEM although chemical analysis by EDS showed the presence of elements involved in corrosive processes. Conclusion: An increase of detorque values recorded on abutments after immersion in fluoridated artificial saliva solutions was noticed in this study. Regarding chemical analysis, such an increase of detorque can result from a corrosion layer formed between metallic surfaces at static contact in the implant-abutment joint during immersion in the fluoridated solutions.

Residual stresses in Y-TZP crowns due to changes in the thermal contraction coefficient of veneers

Objective. To test the hypothesis that the difference in the coefficient of thermal contraction of the veneering porcelain above (˛liquid) and below (˛solid) its Tg plays an important role in stress development during a fast cooling protocol of Y-TZP crowns. Methods. Three-dimensional finite element models of veneered Y-TZP crowns were developed. Heat transfer analyses were conducted with two cooling protocols: slow (group A) and fast (groups B–F). Calculated temperatures as a function of time were used to determine the thermal stresses. Porcelain ˛solid was kept constant while its ˛liquid was varied, creating different ˛/˛solid conditions: 0, 1, 1.5, 2 and 3 (groups B–F, respectively). Maximum ( 1) and minimum ( 3) residual principal stress distributions in the porcelain layer were compared. Results. For the slowly cooled crown, positive 1 were observed in the porcelain, orientated perpendicular to the core–veneer interface (“radial” orientation). Simultaneously, negative 3 were observed within the porcelain, mostly in a hoop orientation (“hoop–arch”). For rapidly cooled crowns, stress patterns varied depending on ˛/˛solid ratios. For groups B and C, the patterns were similar to those found in group A for 1 (“radial”) and 3 (“hoop–arch”). For groups D–F, stress distribution changed significantly, with 1 forming a “hoop-arch” pattern while 3 developed a “radial” pattern. Significance. Hoop tensile stresses generated in the veneering layer during fast cooling protocols due to porcelain high ˛/˛solid ratio will facilitate flaw propagation from the surface toward the core, which negatively affects the potential clinical longevity of a crown.

Pozolanicidade dos resíduos industriais, lã de vidro e lã cerâmica

As fibras cerâmicas se caracterizam por ser um material leve, com alto grau de pureza, baixo armazenamento de calor, baixa condutividade térmica, resistência a choque térmico e alta resistência à corrosão em altas temperaturas. Essas características levam a uma grande procura das indústrias mínero-metalúrgicas e de outros setores para revestimentos de distribuidores, muflas, fornos de aquecimentos, entre outros. Após utilização no processo, por perderem sua capacidade de isolamento, os resíduos gerados precisam de destinação. Esse trabalho enfoca, especificamente, resíduos de lã cerâmica e lã de vidro. Pelo fato de a composição das fibras cerâmicas ser rica em sílica e alumina, efetuou-se uma investigação acerca da atividade pozolânica das mesmas com a cal e o cimento, especificamente CPV ARI, CPII E32 e CPIII 32RS, para avaliação da perspectiva de reciclagem em possível incorporação no concreto.

The β to α phase transition of tantalum coatings deposited by modulated pulsed power magnetron sputtering

Tantalum coatings are of particular interest today as promising candidates to replace potentially hazardous electrodeposited chromium coatings for tribological and corrosion resistant applications, such as the internal lining on large-caliber gun barrels. Tantalum coatings have two crystalline phases, α-Ta (body-centered-cubic) and β-Ta (metastable tetragonal) that exhibit relatively different properties. Alpha-Ta is typically preferred for wear and corrosion resistant applications and unfortunately, is very difficult to deposit without the assistance of substrate heating or post-annealing treatments. Furthermore, there is no general consensus on the mechanism which causes α or β to form or if there is a phase transition or transformation from β → α during coating deposition. In this study, modulated pulsed power (MPP) magnetron sputtering was used to deposit tantalum coatings with thicknesses between 2 and 20 μm without external substrate heating. The MPP Ta coatings showed good adhesion and low residual stress. This study shows there is an abrupt β → α phase transition when the coating is 5–7 μm thick and not a total phase transformation. Thermocouple measurements reveal substrate temperature increases as a function of deposition time until reaching a saturation temperature of ~ 388 °C. The importance of substrate temperature evolution on the β → α phase transition is also explained.

Strategie di conservazione per bronzi esposti all'aperto: studio di metodologie di pulitura, patinazione e consolidamento

Con l’aumento dell’acidità e degli inquinanti nelle deposizioni umide, la corrosione atmosferica dei bronzi esposti all’aperto è stata accelerata e la stabilità della patina di prodotti di alterazione, che solitamente protegge parzialmente il substrato metallico, risulta compromessa. La patina costituisce il supporto reale nelle condizioni d’impiego dell’inibitore o del protettivo, il quale viene applicato in seguito ad una pulitura del manufatto corroso che non espone il metallo nudo. L’inibitore attualmente più utilizzato, benzotriazolo (BTA), risulta non totalmente adeguato nei confronti del bronzo, tossico per l’ambiente e sospetto cancerogeno per l’uomo. Occorre quindi sviluppare soluzioni alternative per la conservazione dei bronzi all’aperto: a questo scopo, il presente lavoro di tesi si è sviluppato in tre fasi: (i) patinazione via invecchiamento artificiale accelerato, simulando la pioggia battente (dropping test) e la pioggia stagnante (wet&dry) su campioni di bronzo quaternario Cu-Sn-Zn-Pb, al fine di produrre un substrato rappresentativo, diversificando le patine prodotte dalle due geometrie di esposizione, sul quale possa essere applicato un inibitore o protettivo. La patinazione artificiale ha permesso di riprodurre efficacemente le due tipologie di patine naturali: le superfici patinate in pioggia battente hanno mostrato il tipico arricchimento in Stagno dovuto alla decuprificazione, mentre le superfici patinate in pioggia stagnante hanno presentato la comparsa dei tipici prodotti precursori dei solfati basici. (ii) pulitura di una patina naturale su bronzo quaternario (fontana del XVII sec.) mediante sabbiatura criogenica (dry-ice blasting), al fine di verificare l’efficienza di questa tecnica per preparare le superfici patinate all’applicazione di un inibitore o protettivo e il suo eventuale utilizzo in sostituzione alle tecniche tradizionali. La sabbiatura criogenica si è tuttavia dimostrata non selettiva nei confronti dei depositi calcarei, dimostrandosi non utilmente applicabile. (iii) protezione di superfici di bronzo quaternario, patinate artificialmente simulando la pioggia battente, mediante un trattamento innovativo di biopatinazione ottenuto applicando il ceppo fungino Beauveria Bassiana, potenzialmente in grado di convertire in ossalati i prodotti di corrosione della patina naturale. Lo scopo è quello di valutare l’efficienza protettiva della biopatina in seguito ad un invecchiamento accelerato simulante la pioggia battente. La biopatinazione è risultata applicabile anche a superfici arricchite in Stagno artificialmente (dropping test), ma la biopatina ottenuta non si è mostrata in grado di limitare i fenomeni corrosivi. Si ritengono necessarie ulteriori prove per valutarne l’efficienza a più lungo termine.

Obturaciones protegidas

Se presenta una técnica combinada (directa–indirecta) para la restauración de elementos dentarios posteriores que combina las ventajas de las obturaciones convencionales con las de las incrustaciones metálicas y no metálicas.

El fosfato de calcio amorfo y su papel en la remineralización de lesiones incipientes de esmalte

Con el conocimiento actual de la enfermedad de caries, los conceptos de tratamientos, originalmente invasivos y mutilantes, fueron evolucionando conjuntamente al conocerse que dicha lesión surge a raíz del desequilibrio producido en el proceso fisiológico desmineralización-remineralización (DES/REM) 10. Con la consolidación de la odontología adhesiva, la terapéutica actual se basa en 3 objetivos primordiales: diagnóstico precoz, tratamientos preventivos no invasivos o de invasión mínima y máxima conservación de los tejidos dentarios. La remineralización es un proceso de precipitación de calcio, fosfatos y otros iones en la superficie o dentro del esmalte parcialmente desmineralizado. En este artículo haremos una reseña de los métodos terapéuticos actuales de los que disponemos para realizar dicha remineralización.

Soluções de reabilitação e reforço com GFRP: aplicações na Região Autónoma da Madeira

Este trabalho consiste na apresentação de técnicas de reabilitação e reforço e a sua adaptação ao GFRP (Glass Fiber Reinforced Polymer). O foco incidiu sobre as estruturas degradadas pela corrosão das armaduras, e apresenta-se uma vasta gama de técnicas de intervenção. Encamisamento, proteção eletroquímica, adição de armaduras são as técnicas mais desenvolvidas ao longo do trabalho. São ainda abordados os tipos de produtos de recobrimento, as técnicas de aplicação do recobrimento, bem como as ferramentas com maior utilidade para a reabilitação e reforço. De seguida faz-se um breve resumo das características e potencialidades do material GFRP, aborda-se alguns dos principais fornecedores, fazendo uma descrição dos produtos comercializados por estes, e ainda uma análise de preços por metro linear de varão GFRP. Por fim apresenta-se um levantamento fotográfico realizado na Região Autónoma da Madeira, de estruturas que apresentem sinais claros de corrosão das armaduras, com o objetivo de perceber a aplicabilidade dos varões de GFRP na reabilitação das mesmas. Apresenta-se ainda, uma possível técnica de reabilitação/reforço para todos os casos apresentados, utilizando os varões de GFRP. O levantamento fotográfico tem ainda o objetivo de perceber as principais causas de deterioração de estruturas na região, e de criar uma base de estruturas a necessitar de intervenção urgente.

Avaliação de massa e rugosidade superficial de pastilhas de Ti-6Al-4V com aplicação de nanopartículas de prata submetidos ao teste de escovação

Este estudo teve por objetivo avaliar a variação da massa e rugosidade de pastilhas de Ti-6Al-4V com e sem aplicação superficial de nanopartículas de prata coloidal (BSafe®) de dimensões 1,5 cm; 0,5 cm e 0,2 cm, submetidas à teste de escovação e imersão pelo período experimental de 10 anos. No teste de escovação, quinze espécimes de Ti-6Al-4V (TE), quinze com B-Safe® (BE) e quinze de PMMA (PE) como controle foram subdivididos em três condições de escovação: dentifrício comum (DC), dentifrício experimental (DE) e controle com água destilada (H2O) por 200 mil ciclos em máquina de escovação. Os resultados foram submetidos ao teste ANOVA a 2 critérios (condição de escovação e ciclos) e teste de Tukey (α=0,05) para comparações múltiplas. Foi observada variação de massa apenas quando a condição de escovação foi DC nos espécimes do grupo PE e TE. Houve diferença estatisticamente significante nos valores da variação de rugosidade no grupo TE e PE quando a condição de escovação foi DC; no grupo BE, houve diferença quando a condição foi DC e DE, porém em DE houve redução dos valores médios. No teste de imersão, objetivando analisar a ação dos dentifrícios sem o atrito das cerdas, seis espécimes de Ti-6Al-4V (TI) e seis com B-Safe® (BI) foram subdivididos em três condições de imersão: DC, DE e H2O pelo período de 244 horas. Os resultados foram submetidos ao teste t de student pareado. Não foi observada diferença estatística entre as variações de massa e rugosidade de nenhum dos corpos de prova após o teste. Complementar aos ensaios, foi realizado um protocolo de desinfecção com terapia fotodinâmica com azul de metileno pelo período de 4 semanas nos espécimes escovados. Após todos os testes, foi realizada espectrometria de energia dispersiva de raios-X (EDS) para caracterização dos elementos químicos presentes nos espécimes, onde não se observou variações. Os resultados sugerem que o DE é mais indicado para utilização com implantes, enquanto DC apresenta um poder abrasivo capaz de danificar a superfície do Ti-6Al- 4V. Não foi observado nenhum indício de corrosão em nenhum grupo testado.