X-ray reflectivity of zirconia based sol-gel coatings on borosilicate glasses

In this work the technique of X-ray reflectometry was applied to study zirconiumsulfate films deposited by sol-gel dip-coating process on a borosilicate glass surface. The influence of withdrawal speed and temperature of thermal treatment on the film structure are analyzed. The thermal evolution of the density and thickness of the film was compared with these properties measured for a monolithic xerogel by helium picnometry and thermomechanical analysis. The fitting of experimental curves by classical reflectivity model showed the presence of an additional layer at the top surface of the coating. Layer thickness increases with increase of withdrawal speed in agreement with the Landau-Levich model. The apparent and real densities are similar for coatings fired below 400 degrees C, which shows that the films are free of pores. The shrinkage during firing is anisotropic, occurring essentially perpendicular to the coating surface. (C) 1999 Elsevier B.V. B.V. All rights reserved.

Effects of chemical disinfectants on the transverse strength of denture base acrylic resins

The disinfection of dental prostheses by immersion in a chemical solution should be capable of rapid inactivation of pathogenic microorganisms, without causing any adverse effect on the denture base resins. This study evaluated the effect of disinfection immersion on the transverse strength of two heat-cured resins. The denture base resins (Lucitone 550 and QC 20) were polymerized according to the manufacturers' instructions. After polymerization, the specimens were polished, and then stored in water at 37 degreesC for 50 +/- 2 h prior immersion in one of the following solutions for 10 min: 4% chlorhexidine, 1% sodium hypochlorite and 3.78% sodium perborate. The specimens were submitted to disinfection twice, simulating when dentures come from the patient and before being returned to the patient. Ten specimens were made for each group. The transverse strength was evaluated by a 3-point bend test. The flexural strength of the two denture base acrylic resins evaluated remained unaffected after immersion in the three solutions evaluated. In general, the QC 20 resin specimens exhibited lower transverse strength than the Lucitone 550 resin specimens, regardless of immersion solutions.

Kinetic parameters obtained for thermal decomposition of acrylic resins present in commercial paint emulsions

Samples of water based commercial acrylic resin paints were spread in a film form on slides, dried at room temperature and exposed to solar radiation for up to eight months.The characterization and quantification of resins and charges in the white paint emulsion were carried out for the thermal decomposition. Besides this, X-ray diffractometry was used to identify CaCO3 as charge and TiO2 (rutile phase) as pigment.It was observed through thermal techniques similar behavior to the samples even though with varied exposure time.Kinetic studies of the samples allowed to obtain the activation energy (Ea) and Arrhenius parameters (A) to the thermal decomposition of acrylic resin to three different commercial emulsion (called P-1, P-2, P-3) through non-isothermal procedures. The values of E. varied regarding the exposition time (eight months) and solar radiation from 173 to 197 U mol(-1) (P-1 sample), from 175 to 226 W mol(-1) (P-2 sample) and 206 to 197 kJ mol(-1) (P-3 sample).Kinetic Compensation Effect (KCE) observed for samples P-2 and P-3 indicate acrylic resin s present in these may be similar in nature. This aspect could be observed by a small difference in the thermal behavior of the TG curves from P I to P-2 and P-3 sample.The simulated kinetic model to all the samples was the autocatalytic estdk Berggreen.

Fluorescence probe study of the interaction between acrylic acid-co-ethyl methacrylate copolymers and sodium dodecylsulfate

The interaction between sodium dodecylsulfate (SDS) and acrylic acid (AA)-ethyl methacrylate (EMA) copolymers has been investigated using steady state fluorescence and conductimetric measurements to assess the effect of the polymer composition on the aggregation process. Micropolarity studies using the ratio between the emission intensities of the vibronic bands of pyrene (I-1/I-3) and the shift of the fluorescence emission of pyrene-3-carboxaldehyde show, that the interaction of SDS with AA-EMA copolymers occurs at surfactant concentrations smaller than that observed for the pure surfactant in water and depends on the copolymer composition. The increase of ethyl methacrylate in the copolymers lowers the critical aggregation concentration (CAC) due to the larger hydrophobic character of the polymer backbone. The formation of aggregates on the macromolecule is induced mainly, by hydrophobic interactions, but the process is also influenced by the ionic strength due to the counter-ions of the polyelectrolyte.

Aqueous solution behavior of thermosensitive (N-isopropylacrylamide-acrylic acid-ethyl methacrylate) terpolymers

A series of N-isopropylacrylamide (NIPAM)-acrylic acid-ethyl methacrylate terpolymers with varied monomer compositions was prepared by radical polymerization. The solution behavior of these polymers was studied in dilute aqueous solution using spectrophotometry, fluorescence spectroscopy and high-sensitivity differential scanning calorimetry. The results obtained revealed that the lower critical solution temperatures depend strongly on the copolymer composition, solution pH and ionic strength. At a high pH, the ionization of acrylic acid (AA) units leads to an increase in solution cloud points (T-c). Solutions of polymers containing 10% or less of AA display a constant T-c for pH above 5.5, with 15% there is a continuous increase in T-c with pH and, for higher AA contents, no clouding was observed within the studied temperature range. Fluorescence probe studies were conducted by following the I (1)/I (3) ratio of pyrene vibronic bands and the emission of anilinonaphtalene sulfonic acid, sodium salt (ANS), both approaches revealing the existence of hydrophobic domains for polymers with higher ethyl methacrylate content at temperatures lower than T-c, suggesting some extent of aggregation and/or a coil-to-globule transition. Scanning calorimetry measurements showed an endothermic transition at temperatures agreeing with the previously detected cloud points. Moreover, the transition curves became broader and with a smaller transition enthalpy, as both the AA content and the solution pH were increased. These broader transitions were interpreted to be the result of a wider molecular distribution upon polymer ionization, hence, displaying varied solution properties. The decrease in transition enthalpy was rationalized as a consequence of reminiscent hydration of NIPAM units, even after phase separation, owing to the presence of electric charges along the polymer chain.

Effect of microwave sterilization and water storage on the Vickers hardness of acrylic resin denture teeth

Statement of problem. Acrylic resin denture teeth soften upon immersion in water, and the heating generated during microwave sterilization may enhance this process.Purpose. Six brands of acrylic resin denture teeth were investigated with respect to the effect of microwave sterilization and water immersion on Vickers hardness (VHN).Material and Methods. The acrylic resin denture teeth (Dentron [D], Vipi Dent Plus [V], Postaris [P], Biolux [B], Trilux [T], and Artiplus [A]) were embedded in heat-polymerized acrylic resin within polyvinylchloride tubes. For each brand, the occlusal surfaces of 32 identical acrylic resin denture posterior teeth were ground flat with 1500-grit silicon carbide paper and polished on a wet polishing wheel with a slurry of tin oxide. Hardness tests were performed after polishing (control group, C) after polishing followed by 2 cycles of microwave sterilization at 650 W for 6 minutes (MwS group), after polishing followed by 90-day immersion in water (90-day Wim group), and after polishing followed by 90-day storage in water and 2 cycles of microwave sterilization (90-day Wim + MwS group). For each specimen, 8 hardness measurements were made and the mean was calculated. Data were analyzed with a 2-way analysis of variance followed by the Bonferroni procedure to determine any significance between pairs of mean values (alpha=.01).Results: Mircrowave sterilization of specimens significantly decreased (P <.001) the hardness of the acrylic resin denture tooth specimens P (17.8 to 16.6 VHN, V (18.3 to 15.8 VHN), T (17.4 to 15.3 VHN), B (16.8 to 15.7 VHN), and A (17.3 to 15.7 VHN). For all acrylic resin denture teeth, no significant differences in hardness were found between the groups Mws, 90-day Wim, and 90-day Wim + MwS, with the exception of the 90-day Wim + MwS tooth A specimens (14.4 VHN), which demonstrated significant lower mean values (P <.001) than the 90-day Wim (15.8 VHN) and MwS (15.7 VHN) specimens.Conclusions. For specimens immersed in water for 90 days, 2 cycles of microwave sterilization had no effect on the hardness of most of the acrylic resin denture teeth.

Composite occlusal surfaces for acrylic resin denture teeth

Acrylic resin denture teeth often exhibit rapid occlusal wear, which may lead to a loss of chewing efficiency and a loss of vertical dimension of occlusion. The use of metal occlusal surfaces on the acrylic resin denture teeth will minimize occlusal wear. Several articles have described methods to construct metal occlusal surfaces; however, these methods are time-consuming, costly, and sometimes considered to be unesthetic. These methods also require that the patient be without the prosthesis for the time necessary to perform the laboratory procedures. This article presents a quick, simple, and relatively inexpensive procedure for construction of composite occlusal surfaces on complete and partial dentures.