Absorption and luminescence of the surface states in ZnS nanoparticles

A broad absorption band around 500 nm is observed in ZnS nanoparticles. The absorption becomes more intensive and shifts to the blue as the particle size is decreased. The absorption energy is lower than the band gap of the particles and is considered to be caused by the surface states. This assignment is supported by the results of the fluorescence and of the thermoluminescence of the surface states. Both the absorption and the fluorescence reveal that the surface states are size dependent. The glow peak of the semiconductor particles is not varied as much upon decreasing size, indicating the trap depth of the surface states is not sensitive to the particle size. Considering these results, a new model on the size dependence of the surface states is proposed, which may explain our observations reasonably. (C) 1997 American Institute of Physics.

Thermoluminescence of ZnS nanoparticles

The thermoluminescence (TL) of ZnS nanoparticles is reported. The TL intensity increases as the particle size is decreased. The consistency of the size dependence of the TL with that of the surface fluorescence indicates that the TL may be related to the surface states. TL may be caused by the recombination of carriers released from the surface states or defect sites by heating. Smaller particles have higher surface/volume ratio and more surface states, therefore contain more accessible carriers for TL. Besides, the carrier recombination rate increases upon decreasing size due to the increase of the overlap between the electron and hole wave functions. These two effects may make the TL increase upon decreasing size of the particles. The appearance of TL prior to any radiation reveals that trapped carriers have pre-existed. The investigation of TL may provide some useful information about the surface states that may explain the size dependence of the surface fluorescence. (C) 1997 American Institute of Physics.

Nd3+-doped LaF3 nanoparticles with a larger emission cross-section

A series of Nd3+-doped LaF3 nanoparticles with Nd3+ concentrations from 0.5 to 10 mol% were synthesized. The fluorescence intensity and lifetime of the nanoparticles at various Nd3+ doping concentration were investigated. The nanoparticles displayed strongest fluorescence intensity at 3 mol% Nd3+ concentration. Eighty-eight percentage quantum efficiency was obtained when the Nd3+ concentration was 0.5 mol%. Optical properties of nanoparticles were studied according to Judd-Ofelt theory. A larger emission cross-section, sigma(em), for F-4(3/2) -> I-4(11/2) transition of the Nd3+ ion was obtained as 3.21 x 10(-20) cm(2), which was two times of the currently reported value. The larger emission cross-section and strong fluorescence intensity demonstrate that these nanoparticles are promising materials for laser applications. (C) 2010 Published by Elsevier B. V.

Fabrication of Novel Superhydrophobic Surfaces and Water Droplet Bouncing Behavior - Part 1: Stable ZnO-PDMS Superhydrophobic Surface with Low Hysteresis Constructed Using ZnO Nanoparticles

A superhydrophobic surface has many advantages in micro/nanomechanical applications, such as low adhesion, low friction and high restitution coefficient, etc. In this paper, we introduce a novel and simple route to fabricate superhydrophobic surfaces using ZnO nanocrystals. First, tetrapod-like ZnO nanocrystals were prepared via a one-step, direct chemical vapor deposition (CVD) approach. The nanostructured ZnO material was characterized by scanning electron microscope (SEM) and X-ray diffraction (XRD) and the surface functionalized by aminopropyltriethoxysilane (APS) was found to be hydrophobic. Then the superhydrophobic surface was constructed by depositing uniformly ZnO hydrophobic nanoparticles (HNPs) on the Poly(dimethylsiloxane) (PDMS) film substrate. Water wettability study revealed a contact angle of 155.4 +/- 2 degrees for the superhydrophobic surface while about 110 degrees for pure smooth PDMS films. The hysteresis was quite low, only 3.1 +/- 0.3 degrees. Microscopic observations showed that the surface was covered by micro- and nano-scale ZnO particles. Compared to other approaches, this method is rather convenient and can be used to obtain a large area superhydrophobic surface. The high contact angle and low hysteresis could be attributed to the micro/nano structures of ZnO material; besides, the superhydrophobic property of the as-constructed ZnO-PDMS surface could be maintained for at least 6 months. (C) Koninklijke Brill NV, Leiden, 2010