以（CH3）2Si（OC2H5）2为前驱体，采用溶胶-凝胶与有机合成相结合的方法，制得稳定性良好的涂膜液。采用旋转涂膜法在掺钕磷酸盐激光玻璃棒端面涂制防潮膜，膜层固化后透过率达96．5％，获得的膜层表面粗糙度优良，均方根表面粗糙度（RMS）为1．659nm，平均粗糙度（RA）平均为1．321nm；在激光波长1053nm，脉冲宽度1 ns条件下膜层的激光破坏闽值可达10～14 J／cm^2。经过“神光Ⅱ”高功率激光器物理实验运行，膜层使用期为五年，并且已经在我国“神光Ⅲ”原型装置上试用。

Second-harmonic generation in Ge20As25S55 glass irradiated by an electron beam

Second-harmonic generation was observed in Ge(20)AS(25)S(55) chalcogenide glass irradiated by an electron beam. The second-harmonic intensity increased with increasing electron-beam current and accelerating voltage. The second-harmonic generation in Ge20As25S55 glass was caused by the space-charge electrostatic field that was generated by irradiation of an electron beam. Second-order nonlinearity chi ((2)) as great as 0.8 pm/V was obtained. The results of measurements of thermally stimulated depolarization current indicated that the glass was poled in the thin layers of its surface (several micrometers) and that the nonlinearity was stable. (C) 2001 Optical Society of America.

PIXE and ICP-AES analysis of early glass unearthed from Xinjiang (China)

Early glasses (about 1066 BC-220 AD) unearthed from Xinjiang of China were chemically characterized by using PIXE and ICP-AES. It was found that these glasses were basically attributed to PbO-BaO-SiO2 system, K2O-SiO2 system, Na2O-CaO-SiO2 system and Na2O-CaO-PbO-SiO2 system. The results from the cluster analysis showed that some glasses had basically similar recipe and technology. The PbO-BaO-SiO2 glass and the K2O-SiO2 glass were thought to come from the central area and the south of ancient China, respectively. The part of the Na2O-CaO-SiO2 glass (including the Na2O-CaO-PbO-SiO2 glass) might be imported from Mesopotamia, while the other part might be locally produced. (c) 2005 Elsevier B.V. All rights reserved.

Effects of sensing temperature on the NO2-sensing properties of octa-iso-pentyloxymetallonaphthalocyanine spin-coated films

A kind of 1,6,10,15,19,24,28,33-octa-iso-pentyloxy-2,3-metallonaphthalocyanines complexes MNc(iso-PeO)(8) (M = Co, Cu, Pd) are used as spincoating film-forming materials. The surface morphologies of the films prepared were studied first. These films were then used for the experiments of NO2 sensing. The effects of sensing temperature as well as the NO concentration on the sensing properties were studied. The experimental results showed that the three MNc(iso-PeO)(8) films were uniform, smooth and dense. Due to the different metal ions (M) on the center of naphthalocyanine, the CoNc(iso-PeO)(8) film had a higher film resistance and response-recovery rate in the NO2 sensing experiments. On the contrary, the response to NO2 of the PdNc(iso-PeO)(8) and CuNc(iso-PeO)(8) films were superior to that of CoNc(iso-PeO)(8). By varying the sensing temperature, it was found that the elevation of sensing temperature could improve the sensing response, recovery ratio, and sensitivity of the sensing films. At high concentrations of NO2, the response time became shorter. (c) 2007 Elsevier B.V. All rights reserved.

Nd-glass belt lasers with improved beam quality

Nd-doped phosphate glass belt lasers pumped by laser diodes are demonstrated. The Nd-glass belt with a large cross-section and a small Fresnel number is air-cooled to provide around 18-W continuous wave (CW) output power with a beam quality factor of My2

Numerical research of heat generation in flashlamp-pumped Nd : glass disk amplifiers

The heat generation in a flashlamp-pumped Nd:glass disk amplifier is studied by the simulation of the whole pumping process, which is based on the ray-tracing method. The results of temperature rise distribution as well as gain distribution are presented. The evolution of heat generation in disk during the pumping process is discussed in detail. Some main factors related with the thermal effect, such as the quantum efficiency, fluorescence lifetime, and pulse duration, are investigated through studying the ratio of the heat generation to energy storage in the gain medium. The influence of each parameter on heat generation is studied carefully, and the results provide ways to decrease the heat generation during the pumping process. (c) 2005 Society of Photo-Optical Instrumentation Engineers.

Temperature characteristics of optical parameters of phthalocyanine LB films and spin-coated films

The LB films and spin-coated films of tetra-neopentoxy phthalocyanine zinc (TNPPcZn) were prepared and annealed at different temperatures. Their refractive index (n) and extinction coefficient (k) were measured by p-polarized reflectance. The similar value of n and k, as well as similar changing tendency of it and k at varied annealing temperatures, was found between LB films and spin-coated films. In addition, the absorption curves of TNPPcZn LB films and spin-coated films in visible range at different annealing temperature were investigated. The results indicate that the changing tendency of the extinction coefficient of two kinds of TNPPcZn films obtained from two methods mentioned above were coincident. When the annealing temperature increased to 150 degrees C, the monomers of TNPPcZn films transformed to aggregates, n(f) and k(f) of the films increased. Further, n(f) and k(f) decreased as aggregates changed back to monomers again at the annealing temperature of 300 degrees C. The experimental results coincide well with the theoretical analysis. (C) 2004 Elsevier B.V. All rights reserved.

Effect of Fe impurity on the optical loss of Nd-doped phosphate laser glass

The optical loss coefficient at 1053-nm wavelength, influenced by Fe ions in N31-type Nd-doped phosphate laser glass, was determined precisely and analyzed in detail. It is found that the optical loss coefficient per unit of Fe concentration (cm^(-1)/ppmw) increases with Fe concentration in the range of 0---300 ppmw, but it approaches a constant as the Fe concentration is larger than 300 ppmw. Such a concentration effect is due to a shift in the redox equilibrium between Fe3+ and Fe2+ ions in the glass. The effect of oxygen pressure, temperature, and variable valence states of other metal ions in glass samples on the optical loss is also discussed.

Er3+ and Yb3+ codoped phosphate laser glass for high power flashlamp pumping

A novel Vb(3+)-Er-(3+) codoped phosphate glass for high power flashlamp pumping and high repetition rate laser at 1.54 mu m, designated EAT5-2, is developed. The weight-loss rate of is 1.3 x 10(-5) gcm(-2) h(-1) in boiling water, which is comparable to Kigre's QX-Er glass. Some spectroscopic parameters are analysed by Judd-Ofelt theory and McCumber theory The emission cross section is calculated to be 0.73 x 10(-20) cm(2). The thermo-mechanical properties of EAT5-2 are modified after an ion-exchange chemical strengthening process in a KNO3/NaNO3 molten salt bath. The thresholds for optical damage from the flashlamp pumping are tested on glass rods. A repetition rate of 15 Hz is achieved for chemically strengthened glass. The laser experimental results at. 1.54 mu m from flashlamp pumping are also reported.