Biocompatibility and biomineralization assessment of a new root canal sealer and root-end filling material

Objective: This study investigated the short-term subcutaneous tissue reaction and biomineralization ability of two epoxy-based root canal sealers containing calcium hydroxide (MBP and MBPc) and ProRoot MTA. Materials and methods: Polyethylene tubes containing the materials were implanted into the dorsal connective tissue of Wistar rats (n = 52) for 7 or 30 days; empty implanted tubes served as controls. Specimens were stained with hematoxylin-eosin and von Kossa stain or left unstained for observation under polarized light. Qualitative and quantitative evaluations of all tissue reactions were performed. One-way anova and the Kruskal-Wallis test were used for statistical analysis (P < 0.05). Results: No significant differences were observed among the groups. All three materials induced mild-to-moderate tissue reactions at 7 days, which decreased over time. Dystrophic mineralization and birefringent structures were observed only in the ProRoot MTA ® group. Conclusion: Both MBP and MBPc appear to be biocompatible but do not stimulate biomineralization. © 2012 John Wiley & Sons A/S.

Effect of thermal cycling and disinfection on microhardness of acrylic resin denture base

The purpose of this study was to investigate the effect of thermal cycling and disinfection on the microhardness of acrylic resins denture base. Four different brands of acrylic resins were evaluated: Onda Cryl, QC 20, Classico and Lucitone. Each brand of acrylic resin was divided into four groups (n = 7) according to the disinfection method (microwave, Efferdent, 4% chlorhexidine and 1% hypochlorite). Samples were disinfected during 60 days. Before and after disinfection, samples were thermal cycled between 5-55 °C with 30-s dwell times for 1000 cycles. The microhardness was measured using a microhardener, at baseline (B), after first thermal cycling (T1), after disinfection (D) and after second thermal cycling (T2). The microhardness values of all groups reduced over time. QC-20 acrylic resin exhibited the lowest microhardness values. At B and T1 periods, the acrylic resins exhibited statistically greater microhardness values when compared to D and T2 periods. It can be concluded that the microhardness values of the acrylic resins denture base were affected by the thermal cycling and disinfection procedures. However, all microhardness values obtained herein are within acceptable clinical limits for the acrylic resins. © 2013 Informa UK Ltd.

Effect of immersion cleansers on the bond strength between a denture base resin and acrylic resin teeth

The aim of the present study was to assess the shear bond strength between a heat-polymerized denture base resin and acrylic resin teeth after immersion in different denture cleansers by simulating a 180-day use. Two acrylic teeth (Biotone, Biotone IPN, Dentsply Ind. e Com., Rio de Janeiro, RJ, Brazil) were chosen for bonding to a heat-polymerized denture base resin (Lucitone 550- Dentsply Ind. e Com., Rio de Janeiro, RJ, Brazil). Eighty specimens were produced and divided into eight groups (n=10) according to their experimental condition (distilled water, 2% chlorhexidine digluconate, 1% sodium hypochlorite and Corega Tabs). Shear bond strength tests (MPa) were performed with a universal testing machine at a crosshead speed of 0.5 mm/min. Data were analyzed by two-way analysis of variance (ANOVA) and Student-Newman-Keuls' multiple comparisons post hoc analysis (α=.05). The shear bond strength results revealed statistically significant differences between the groups. For the Biotone IPN tooth, significantly lower shear bond strength values were found for the group immersed in sodium-perborate solution (4.48±2.18 MPa) than for the group immersed in distilled water (control group) (10.83±1.84 MPa). For Biotone, significantly higher bond strength values (10.04±3.28 MPa) were found for the group immersed in Corega Tabs than for the control group (5.45±2.93 MPa). The immersion in denture cleanser solutions was more detrimental to the conventional acrylic denture tooth (Biotone) than to the highly cross-linked denture tooth (Biotone IPN). However, this effect was not observed for the groups immersed in Corega Tabs solution, regardless of the type of denture tooth. © 2013 Elsevier Ltd.

Differences in loosely bound fluoride formation and anticaries effect of resin-based fluoride varnishes

International Journal of Paediatric Dentistry 2013; 23: 166-172 Objective. Our in vitro study evaluated calcium fluoride formation in enamel and the anticaries effect of seven resin-based varnishes under cariogenic challenge. Methods. Enamel blocks were subjected to pH cycling. The experimental groups received fluoride varnish application, the positive control received topical fluoride gel treatment, and the negative control did not receive any treatment. The pH cycling surface hardness (SH1) and integrated loss of subsurface hardness (ΔKHN) were then determined. We measured the amount of fluoride released into the demineralizing and remineralizing (DE-RE) solutions used in pH cycling. The fluoride concentration in the enamel was determined 24h after application of the products as loosely bound fluoride and firmly bound fluoride. Results. Higher deposits of loosely bound fluoride were observed for Duofluorid, followed by Biophat. For Duraphat, Bifluorid, Duraflur, and Duofluorid, no difference was observed in the SH1 and ΔKHN values, with the lowest mineral loss compared to the other groups. The Bifluorid and Duofluorid groups released high fluoride amounts into the DE-RE, and statistically significant difference was noted between them. Conclusions. The anticaries effect showed no correlation with higher deposited fluoride amounts, resin type, or fluoride source. © 2012 John Wiley & Sons Ltd, BSPD and IAPD.

Effect of MTA-based sealer on the healing of periapical lesions

Some manufacturers have recently added specific components to improve the ease of handling and insertion material properties of MTA in order to create MTA-based sealers. Objective: The aim of this study was to evaluate the healing of periapical lesions in canine teeth after a single session of endodontic treatment with MTA Fillapex® compared with Sealapex® or Endo-CPM-Sealer®. Material and Methods: Sixty-two root canals were performed on two 1-year-old male dogs. After coronal access and pulp extirpation, the canals were exposed to the oral cavity for 6 months in order to induce periapical lesions. The root canals were prepared, irrigated with a solution of 2.5% sodium hypochlorite and filled with gutta-percha and different sealers, according to the following groups: 1) Sealapex®; 2) Endo-CPM-Sealer®; and 3) MTA Fillapex®. Some teeth with periapical lesions were left untreated for use as positive controls. Healthy teeth were used as negative controls. After 6 months, the animals were sacrificed and serial sections from the roots were prepared for histomorphologic analysis and stained with hematoxylin and eosin and the Brown and Brenn technique. The lesions were scored according to pre-established histomorphologic parameters and the scores statistically analyzed using the Kruskal-Wallis test. Results: All 3 materials produced similar patterns of healing (p>0.05); in particular, persistent inflammation and absence of complete periapical tissue healing were consistently noted. Conclusions: Preparation of the infected root canals followed by filling with the materials studied was insufficient to provide complete healing of the periapical tissues.

Chemical characterization and flexural strength of a denture base acrylic resin with monomer 2-tert-butylaminoethyl methacrylate

Purpose: The objectives of this study were to investigate the flexural strength (FS) and chemical interaction between 2-tert-butylaminoethyl methacrylate (TBAEMA) and a denture base acrylic resin. Materials and Methods: Specimens were divided into five groups according to the concentration of TBAEMA incorporated in acrylic resin Onda-Cryl (0%, 1%, 2%, 3%, 4%) and were submitted to Fourier transform infrared spectroscopy (FTIR), electron spectroscopy for chemical analysis (XPS-ESCA), and differential scanning calorimetry (DSC) analyses. FS of the specimens was tested, and results were analyzed by ANOVA/Tukey's test (α < 0.05). Results: Different nitrogen ratios were observed on specimens' surfaces: 0.36%, 0.54%, 0.35%, and 0.20% for groups 1%, 2%, 3%, and 4%, respectively. FTIR indicated copolymerization of acrylic resin and TBAEMA, and DSC results demonstrated a decrease in glass transition temperature (Tg). Significant differences were found for FS (p < 0.05). The mean values were 91.1 ± 5.5,A 77.0 ± 13.1,B 67.2 ± 12.5,B 64.4 ± 13.0,B and 67.2 ± 5.9B MPa for groups 0%, 1%, 2%, 3% and 4%, respectively (same superscript letters indicate no significant difference). Conclusions: The incorporation of TBAEMA in acrylic resin resulted in copolymerization and the presence of amine groups on specimens' surfaces, and in decreases of Tg and FS. © 2012 by the American College of Prosthodontists.

Microtensile bond strength of resin cements to caries-affected dentin

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Evaluation of the chemical interaction between carbon nanotubes functionalized with TGDDM tetrafunctional resin and hardener DDS

In this work, the chemical interaction between carbon nanotubes (MWCNT) functionalized with acyl chloride (SOCl2) and polymer chain tetrafuncional N,N,N′,N′-tetraglycidyl-4,4′- diaminodiphenylmethane (TGDDM) and hardener 4,4′diaminodiphenyl sulfone (DDS) has been monitored by Fourier transform infrared spectroscopy (FTIR) with a attenuated total reflectance (ATR) coupled. MWCNT were obtained from the pyrolysis of a mixture of camphor and ferrocene into a oven. The functionalization process was done by oxidative treatment in order to incorporate carboxylic group over the walls of MWCNT, before to be used SOCl2. The functionalized carbon nanotubes were evaluated by X-ray photoelectron spectroscopy (XPS), Raman and transmission electron microscopy (TEM). Nanostructured composites were processed by using epoxy resin with MWCNT in varying percentages. In this work it was observed that different percentages of functionalized nanotubes modify the interaction between the composite matrix and curing agent, where can be observed that in specimens with content less than 1 wt% MWCNT the chemical bond occurs preferentially from the opening of the SO double bond of the hardener and when is used MWCNT content higher than 1 wt% there is little chemical interaction with the SO bond of the hardener and most MWCNT binds to amine. © 2013 Elsevier Ltd.

Effect of diamond-like carbon thin film coated acrylic resin on candida albicans biofilm formation

Purpose: The purpose of this study was to evaluate the effect of diamond-like carbon thin films doped and undoped with silver nanoparticles coating poly(methyl methacrylate) (PMMA) on Candida albicans biofilm formation. The control of biofilm formation is important to prevent oral diseases in denture users. Materials and Methods: Forty-five PMMA disks were obtained, finished, cleaned in an ultrasonic bath, and divided into three groups: Gc, no surface coating (control group); Gdlc, coated with diamond-like carbon film; and Gag, coated with diamond-like carbon film doped with silver nanoparticles. The films were deposited using a reactive magnetron sputtering system (physical vapor deposition process). The specimens were characterized by optical profilometry, atomic force microscopy, and Rutherford backscattering spectroscopy analyses that determined differences in chemical composition and morphological structure. Following sterilization of the specimens by γ-ray irradiation, C. albicans (ATCC 18804) biofilms were formed by immersion in 2 ml of Sabouraud dextrose broth inoculated with a standardized fungal suspension. After 24 hours, the number of colony forming units (cfu) per specimen was counted. Data concerning biofilm formation were analyzed using ANOVA and the Tukey test (p < 0.05). Results: C. albicans biofilm formation was significantly influenced by the films (p < 0.00001), reducing the number of cfu, while not affecting the roughness parameters (p > 0.05). The Tukey test showed no significant difference between Gdlc and Gag. Films deposited were extremely thin (∼50 nm). The silver particles presented a diameter between 60 and 120 nm and regular distribution throughout the film surface (to Gag). Conclusion: Diamond-like carbon films, doped or undoped with silver nanoparticles, coating the base of PMMA-based dentures could be an alternative procedure for preventing candidosis in denture users. © 2013 by the American College of Prosthodontists.

Effect of carbamide peroxide bleaching gel on composite resin flexural strength and microhardness

This study investigated the effect of 16% carbamide peroxide (Whiteness Perfect/FGM) on the Vickers microhardness and flexural strength of the restorative composites Filtek Z100 (hybrid), Filtek Z350 (nanofill), Brilliant (micro-hybrid) and Opallis (micro-hybrid). Discshaped (4×2 mm; n=5) and bar-shaped (12×2×1 mm; n=10) specimens of each restorative material were randomly divided into 2 groups: (G1) 16 weeks stored in distilled water; (G2) 16 weeks stored in distilled water, with 16% carbamide peroxide application during 6 h per day for the last 4 weeks. The mechanical properties were evaluated using a Vickers microhardness tester and a mechanical testing machine. Data were analyzed by twoway ANOVA and Tukey's (HSD) post-hoc test (α=0.05). Filtek Z100 presented the highest microhardness value, followed by Filtek Z350 and finally by Brilliant and Opallis (p=0.00). Filtek Z100 and Brilliant exhibited the highest flexural strength value, followed by Filtek Z350 and Opallis (p=0.00). Bleaching treatment decreased significantly microhardness of Brilliant and Opallis (p=0.00). The flexural strength of all studied materials was not affected by the home bleaching (p=0.28).

Repair bond strength of microhybrid, nanohybrid and nanofilled resin composites: Effect of substrate resin type, surface conditioning and ageing

Objectives: This study evaluated the microtensile bond strength (MTBS) of non-aged and aged resin-based composites (RBC) (nanohybrid and nanofilled) after two surface conditioning methods, repaired using the composite of the same kind or a microhybrid composite. Materials and methods: Nanohybrid (Tetric EvoCeram-TE) and nanofilled (Filtek Supreme-FS) RBC blocks (5 × 5 × 6 mm) (N = 128) were fabricated and randomly divided into two groups: (a) no ageing (control group) and (b) ageing (5.000 thermocycling, 5-55 °C). RBC surfaces were polished by up to 1,200-grit silicone carbide papers and conditioned with either (a) air abrasion with 30-μm SiO2 particles (CoJet Sand) for 4 s + silane coupling agent (ESPE-Sil) + adhesive resin (VisioBond) (n = 16) or (b) adhesive application only (Multilink A+B for TE; Adper ScotchBond 1XT for FS) (n = 16). In half of the groups, repair resin of the same kind with the RBC and, in the other half, a different kind of composite (microhybrid, Quadrant Anterior Shine-AS) with its corresponding adhesive (Quadrant UniBond) was used. The specimens were submitted to MTBS test (0.5 mm/min). Data were analysed using three-way ANOVA and Tukey's tests. Degree of conversion (DC) of non-aged and aged resin composites (TE, FS) (n = 3 per group) was measured by micro-Raman analyses. Results: RBC type (p = 0.001) and ageing affected the MTBS results significantly (p = 0.001). Surface conditioning type did not show significant difference (p = 0.726), but less number of pre-test failures was experienced with the CoJet system compared to adhesive resin application only. Repair strength on aged TE showed significantly less (p < 0.05) MTBS than for FS. FS repaired with the same kind of RBC and adhesive resin presented the highest cohesive failures (43 %). DC was higher for TE (71 %) than for FS (58 %) before ageing. Conclusion: On the aged RBCs, less favourable repair strength could be expected especially for nanohybrid composite. For repair actions, RBC surface conditioning could be accomplished with either adhesive resin application only or with CoJet system, providing that the latter resulted in less pre-test failures. Clinical relevance: Clinicians could condition the resin surface prior to repair or relayering with either CoJet system or adhesive resin application only, depending on the availability of the system. © 2012 Springer-Verlag Berlin Heidelberg.

Randomized controlled clinical trial evaluating connective tissue graft plus resin-modified glass ionomer restoration for the treatment of gingival recession associated with non-carious cervical lesion: 2-year follow-up

Background: The aim of this clinical study is to evaluate the 2-year term results of gingival recession (GR) associated with non-carious cervical lesions (NCCLs) treated by connective tissue graft (CTG) alone or in combination with a resin-modified glass ionomer restoration (CTG+R). Methods: Thirty-six patients with Miller Class I buccal GR associated with NCCLs completed the follow-up. The defects were randomly assigned to receive either CTG or CTG+R. Bleeding on probing (BOP), probing depth (PD), relative GR, clinical attachment level (CAL), and cervical lesion height coverage were measured at baseline, 6 months, 1 year, and 2 years after treatment. Results: Both groups showed statistically significant gains in CAL and soft-tissue coverage. The differences between groups were not statistically significant in BOP, PD, relative GR, or CAL after 2 years. Cervical lesion height coverage was 79.31% ± 18.51% for CTG and 71.95% ± 13.25% for CTG+R (P >0.05). Estimated root coverage was 91.56% ± 11.74% for CTG and 93.29% ± 7.97% for CTG+R (P ≥0.05). Conclusions: Within the limits of the present study, it can be concluded that both procedures provide comparable soft tissue coverage after 2 years of follow-up.

Setting Time Affects In Vitro Biological Properties of Root Canal Sealers

Introduction: Biocompatibility of root canal sealers is important because of the long-term contact of their eluates and/or degradation products with periapical tissues. The literature still lacks studies about the genotoxic effects of these materials and the influence of setting time on biological properties. The cytotoxicity and genotoxicity of an epoxy resin-based sealer (AH Plus), a single methacrylate-based sealer (EndoRez), and a silicone-based sealer (RoekoSeal) were assessed. Methods: Chinese hamster fibroblasts (V79) were cultured and exposed to different dilutions of extracts from the sealers that were left to set for 0, 12, and 24 hours before contact with culture medium. Cell viability was measured by the methyl-thiazol-diphenyltetrazolium assay. Genotoxicity was assessed by the comet assay. Data were statistically analyzed by Kruskal-Wallis and Dunn tests (P < .05). Results: Root canal sealers were statistically more cytotoxic than the untreated control group, except for the silicon-based sealer. Cell viability ranking was the following (from the most to the least cytotoxic): methacrylate-based > epoxy resin-based > silicone-based. The setting time influenced the epoxy resin-based sealer cytotoxicity (decreased at 12 hours) and the general genotoxicity (increased at 24 hours). DNA damage ranking was the following (from the most to the least genotoxic): methacrylate-based > silicone-based = epoxy resin-based. Conclusions: The setting time had influence on the cytotoxicity of the epoxy resin-based sealer and genotoxicity of all tested sealers. The methacrylate-based sealer was the most cytotoxic, and the silicone-based sealer was not cytotoxic. Genotoxicity was observed for all sealers. © 2013 American Association of Endodontists.

Si-based thin film coating on Y-TZP: Influence of deposition parameters on adhesion of resin cement

This study evaluated the influence of deposition parameters for Si-based thin films using magnetron sputtering for coating zirconia and subsequent adhesion of resin cement. Zirconia ceramic blocks were randomly divided into 8 groups and specimens were either ground finished and polished or conditioned using air-abrasion with alumina particles coated with silica. In the remaining groups, the polished specimens were coated with Si-based film coating with argon/oxygen magnetron discharge at 8:1 or 20:1 flux. In one group, Si-based film coating was performed on air-abraded surfaces. After application of bonding agent, resin cement was bonded. Profilometry, goniometry, Energy Dispersive X-ray Spectroscopy and Rutherford Backscattering Spectroscopy analysis were performed on the conditioned zirconia surfaces. Adhesion of resin cement to zirconia was tested using shear bond test and debonded surfaces were examined using Scanning Electron Microscopy. Si-based film coating applied on air-abraded rough zirconia surfaces increased the adhesion of the resin cement (22.78 ± 5.2 MPa) compared to those of other methods (0-14.62 MPa) (p = 0.05). Mixed type of failures were more frequent in Si film coated groups on either polished or air-abraded groups. Si-based thin films increased wettability compared to the control group but did not change the roughness, considering the parameters evaluated. Deposition parameters of Si-based thin film and after application of air-abrasion influenced the initial adhesion of resin cement to zirconia. © 2013 Elsevier B.V. All rights reserved.

The impact of hydrofluoric acid etching followed by unfilled resin on the biaxial strength of a glass-ceramic

Objectives: To evaluate the null hypotheses that hydrofluoric (HF) acid etching time would neither decrease the biaxial flexural strength of a glass-based veneering ceramic nor enhance it after silane and unfilled resin (UR) applications. Methods: Disc-shaped IPS e.max ZirPress specimens were allocated into 12 groups: G1-control (no-etching), G2-30 s, G3-60 s, G4-90 s, G5-120 s, G6-60 s + 60 s. Groups (G7-G12) were treated in the same fashion as G1-G6, but followed by silane and UR applications. Surface morphology and roughness (Ra and Rq) of the ceramics were assessed by means of scanning electron microscopy (SEM) and profilometry, respectively. Flexural strength was determined by biaxial testing. Data were analyzed by two-way ANOVA and the Sidak test (α = 0.05). Weibull statistics were estimated and finite element analysis (FEA) was carried out to verify the stress concentration end areas of fracture. Results: The interaction (etching time vs. surface treatment) was significant for Ra (p = 0.008) and Rq (0.0075). Resin-treated groups presented significantly lower Ra and Rq than non-treated groups, except for the 60 s group (p < 0.005). SEM revealed that etching affected the ceramic microstructure and that the UR was able to penetrate into the irregularities. A significant effect of etching time (p = 0.029) on flexural strength was seen. G7-G12 presented higher strength than G1-G6 (p < 0.0001). None of experimental groups failed to show 95% confidence intervals of σ 0 and m overlapped. FEA showed lower stress concentration after resin treatment. Significance: HF acid etching time did not show a damaging effect on the ceramic flexural strength. Moreover, the flexural strength could be enhanced after UR treatment. © 2013 Academy of Dental Materials.