Influence of cross-head speed on resin-dentin shear bond strength

Objective: To evaluate the influence of different cross-head speeds on shear bond strength test on the dentin surface.Methods: One hundred and twenty extracted bovine incisors were embedded in polystyrene resin. The specimens were prepared by wet grinding with 320-, 400- and 600-grit Al2O3 paper exposing dentin. After the application of the adhesive system Single Bond (3M) to etched dentin, the composite resin Z-100 (3M) was applied and light cured. The specimens were randomly assigned to four groups (n = 30). The shear bond strength tests were performed with an EMIC DL 500 universal testing machine at four different cross-head speeds: 0.50 (A); 0.75 (B); 1.00 (C); and 5.00 mm/min (D).Results: the mean values of shear bond strength in MPa (SD) were: A, 11.78 (3.91); B, 11.82 (4.78); C, 16.32 (6.45); D, 15.46 (5.94). The data were analyzed with one-way ANOVA and Tukey's test (alpha = 0.05). The results indicated that A = B < C = D. The fracture pattern was evaluated by visual analysis in a stereomicroscope (25 x). The percentage of fractures that occurred at the adhesive interface were: A, 92.5%; B, 91.6%; C, 70.0%; D, 47.0%. The Student's t-test to percentages ( = 0.05) indicated that there were no significant differences among A, B and C; A and B differed from D, and there was no significant difference between C and D.Significance: Different cross-head speeds may influence the shear bond strength and the fracture pattern in dentin substrate. Shear bond strength using cross-head speeds of 0.50 and 0.75 mm/min should be preferred. (C) 2001 Academy of Dental Materials. published by Elsevier B.V. Ltd. All rights reserved.

Microleakage of hydrophilic adhesive systems in Class V composite restorations

Purpose: To investigate the microleakage of four hydrophilic adhesive systems: one multiple-bottles (Scotchbond Multi-Purpose Plus); two one-bottle (Single Bond, Stae); and one self-etching (Etch & Prime 3.0). Materials and Methods: 120 bovine incisor teeth were divided into four groups (n = 30) and Class V cavities were prepared at the cemento-enamel junction. The cavities were restored with the adhesive systems and with Z100 composite. The teeth were thermocycled 1,000 times between 5 +/- 2 degreesC and 55 +/- 2 degreesC with a dwell time of 1 min, and then placed in a 2% methylene blue dye (pH 7.0) for 4 hrs, washed and sectioned vertically through the center of the restorations. The qualitative evaluation was made by three examiners who distributed pre-established scores (0-4) for each tooth using a stereomicroscope at x30 magnification. Results: In enamel margins little microleakage was observed and the Kruskal-Wallis analysis did not show differences. In dentin margins the KruskaI-Wallis and multiple comparison analyses were applied: microleakage was significantly greater with Stae (median 3) and Scotchbond MP Plus (median 4). Single Bond (median 1) and Etch & Prime 3.0 (median 2) showed the best results in dentin margins, and the statistical analysis did not demonstrate differences in microleakage among these groups.

Vertical marginal discrepancy of ceramic copings with different ceramic materials finish lines and luting agents: An in vitro evaluation

Statement of problem. Prosthetic restorations that fit poorly may affect periodontal health and occlusion. Studies that have evaluated the accuracy of fit of ceramic restorations before and after cementation assessed primarily intracoronal restorations.Purpose. This in vitro study evaluated the effect of different finish lines, ceramic manufacturing techniques, and luting agents on the vertical discrepancy of ceramic copings.Material and methods. Two stainless steel molars were prepared for complete crowns with 2 different finish lines (heavy chamfer and rounded shoulder); each molar was duplicated to fabricate 90 copings. A total of 180 copings generated 18 groups (n=10 for each finish line-coping material-luting agent combination). Luting agents tested included zinc phosphate, resin-modified glass ionomer (Fuji Plus), and resin composite cements (Panavia F). A metal frame was developed on which to screw the stainless steel model and a ceramic coping; the distance (mum) between 2 predetermined points was measured before and after cementation by a profile projector under a torquing force. A 4-way ANOVA with repeated measurements was performed to assess the influence of each factor in the vertical marginal discrepancy: 3 between-coping factors (finish line-coping material-luting agent) and 1 within-coping factor (before and after cementation) (alpha=.05).Results. Procera copings presented the lowest mean values (P<.05) of vertical marginal discrepancy before and after cementation (25/44 mum) when compared to Empress 2 (68/110 mum) and InCeram Alumina copings (57/117 mum), regardless of any combinations among all finish lines and luting agents tested.Conclusion. Considering each factor separately, the ceramic manufacturing technique appeared to be the most important factor tested for the definitive vertical discrepancy of all-ceramic copings, with lower mean values for Procera copings.

Repair bond strength of a resin composite to alumina-reinforced feldspathic ceramic

This study compared the microtensile bond strength of a repair resin to an alumina-reinforced feldspathic ceramic (Vitadur-alpha, Vita) after 3 surface conditioning methods: Group 1, etching with 9.6% hydrofluoric acid for 1 minute plus rinsing and drying, followed by application of silane for 5 minutes; group 2, airborne particle abrasion with 110-mm aluminum oxide using a chairside air-abrasion device followed by silane application for 5 minutes; group 3, chairside tribochemical silica coating with 30-mu m SiOx followed by silane application for 5 minutes (N = 30). Group 1 presented the highest mean bond strength (19.7 +/- 3.8 MPa), which was significantly higher than those of groups 2 (10 +/- 2.6 MPa) and 3 (10.4 +/- 4 MPa) (P <.01). Scanning electron microscope analysis of the failure modes demonstrated predominantly mixed types of failures, with adhesive and/or cohesive failures in all experimental groups.

Influence of ceramic surface conditioning and resin cements on microtensile bond strength to a glass ceramic

Statement of problem. It is not clear how different glass ceramic surface pretreatments influence the bonding capacity of various luting agents to these surfaces.Purpose. The purpose of this study was to evaluate the microtensile bond strength (mu TBS) of 3 resin cements to a lithia disilicate-based ceramic submitted to 2 surface conditioning treatments.Material and methods. Eighteen 5 X 6 X 8-mm ceramic (IPS Empress 2) blocks were fabricated according to manufacturer's instructions and duplicated in composite resin (Tetric Ceram). Ceramic blocks were polished and divided into 2 groups (n=9/treatment): no conditioning (no-conditioning/control), or 5% hydrofluoric acid etching for 20 seconds and silanization for 1 minute (HF + SIL). Ceramic blocks were cemented to the composite resin blocks with I self-adhesive universal resin cement (RelyX Unicem) or 1 of 2 resin-based luting agents (Multilink or Panavia F), according to the manufacturer's instructions. The composite resin-ceramic blocks were stored in humidity at 37 degrees C for 7 days and serially sectioned to produce 25 beam specimens per group with a 1.0-mm(2) cross-sectional area. Specimens were thermal cycled (5000 cycles, 5 degrees C-55 degrees C) and tested in tension at 1 mm/min. Microtensile bond strength data (MPa) were analyzed by 2-way analysis of variance and Tukey multiple comparisons tests (alpha=.05). Fractured specimens were examined with a stereomicroscope (X40) and classified as adhesive, mixed, or cohesive.Results. The surface conditioning factor was significant (HF+SIL > no-conditioning) (P<.0001). Considering the unconditioned groups, the mu TBS of RelyX Unicem was significantly higher (9.6 +/- 1.9) than that of Multilink (6.2 +/- 1.2) and Panavia F (7.4 +/- 1.9). Previous etching and silanization yielded statistically higher mu TBS values for RelyX Unicem (18.8 +/- 3.5) and Multilink (17.4 +/- 3.0) when compared to Panavia F (15.7 +/- 3.8). Spontaneous debonding after thermal cycling was detected when luting agents were applied to untreated ceramic surfaces.Conclusion. Etching and silanization treatments appear to be crucial for resin bonding to a lithia disilicate-based ceramic, regardless of the resin cement used.

EPR investigation of the influence of side chain protecting groups on peptide-resin solvation of the Asx and Glx model containing peptides

In spite of all progressive efforts aiming to optimize SPPS, serious problems mainly affecting the assembly of aggregating sequences have persisted. Following the study intended to unravel the complex solvation phenomenon of peptide-resin beads, the XING and XAAAA model aggregating segments were labeled with a paramagnetic probe and studied via EPR spectroscopy. Low and high substituted resins were also comparatively used, with the X residue being Asx or Glx containing the main protecting groups used in the SPPS. Notably, the cyclo-hexyl group used for Asp and Glu residues in Boc-chemistry induced greater chain immobilization than its tert-butyl partner-protecting group of the Fmoc strategy. Otherwise, the most impressive peptide chain immobilization occurred when the large trytil group was used for Asn and Gln protection in Fmoc-chemistry. These surprising results thus seem to stress the possibility of the relevant influence of the amino-acid side chain protecting groups in the overall peptide synthesis yield. (C) 2007 Elsevier Ltd. All rights reserved.