Synthesis and sintering of ZrO2-CeO2 powder by use of polymeric precursor based on Pechini process

Nanocrystalline ZrO2-12 mol % CeO2 powders were synthesized using a polymeric precursor method based on the Pechini process. X-ray diffraction (XRD) patterns showed that the method was effective to synthesize tetragonal zirconia single-phase. The mean crystallite size attained ranges from 6 to 15 nm. The BET surface areas were relatively high reaching 97 m(2)/g. Studies by nitrogen adsorption/desorption on powders, dilatometry of the compacts, and transmission electron microscopy (TEM) of the powders, were also developed to verify the particles agglomeration state. Both citric acid : ethylene glycol ratio and calcination temperature affected the powder morphology, which influenced the sinterability and microstructure of the sintered material, as showed by scanning electron microscopy (SEM). (C) 2001 Kluwer Academic Publishers.

Metallic powder injection molding using low pressure

The demand by high performance materials that have to support severe service conditions at a reasonable cost has been forcing the powder metallurgy to improve constantly. The most recent and more important innovation in the area is the process of powder injection.Powder injection molding (PIM) is a technology capable of producing a new range of components from powders. This advanced technology overcomes the existent limitations in the forming of products with complex geometry. The process presents countless variations which are used in the industry today. Invariably, it consists of mixing the powders and a thermo-plastic binder, injecting the mass in the mold in the wanted form, debinding, sintering and making optional secondary operations, as for example, machinery.The purpose of this work is to review the metal injection molding techniques and apply the low pressure injection molding process to family of parts using metallic powder with 10 mum particle size. This work also comments the design and construction of a low pressure injection machine and injection molds. (C) 2001 Elsevier B.V. B.V. All rights reserved.

Thermodynamic and quality properties of lemon juice powder as affected by maltodextrin and Arabic gum

Sorption isotherms of lemon juice (LE) powders with and without additives-18% maltodextrin (MA) or 18% gum Arabic (GA) were determined at 20-50 degrees C. Addition of additives was shown to affect the isotherms in such a way that, at the same water activity, samples LE + GA and LE + MA presented lower equilibrium moisture content and were not so affected by varying temperature. The net isosteric heats of sorption of juice powders with additives were higher (less negative) than those of lemon juice powders, suggesting that there are more active polar sites in the product without addition of GA or MA. In general, the quality properties decreased with the addition of maltodextrin and gum arabic and it was obtained similar values for LE + GA and LE + MA.

Influence of strains and defects on ferroelectric and dielectric properties of thin-film barium-strontium titanates

Pristine, W and Mn 1% doped Ba(0.6)Sr(0.4)TiO(3) epitaxial thin films grown on the LaAlO(3) substrate were deposited by pulsed laser deposition (PLD). Dielectric and ferroelectric properties were determined by the capacitance measurements and X-ray diffraction was used to determine both residual elastic strains and defect-related inhomogeneous strains-by analyzing diffraction line shifts and line broadening, respectively. We found that both elastic and inhomogeneous strains are affected by doping. This strain correlates with the change in Curie-Weiss temperature and can qualitatively explain changes in dielectric loss. To explain the experimental findings, we model the dielectric and ferroelectric properties of interest in the framework of the Landau-Ginzburg-Devonshire thermodynamic theory. As expected, an, elastic-strain contribution due to the epilayer-substrate misfit has an important influence on the free-energy. However, additional terms that correspond to the defect-related inhomogeneous strain had to be introduced to fully explain the measurements.

Effects of powder preparation and sintering procedure on microstructure and dielectric properties of PLZT ceramics

PLZT ceramics belong to one of the very important groups of functional materials that make a basis for the production of a large range of electronic devices. The microstructure and properties of ceramics depend on the powder preparation and thermal processing conditions. Various techniques have been used to obtain chemically homogeneous and fine starting powders. PLZT powders have been prepared by two different production routes: by a modified Pechini method, using a polymeric precursor method (PMM) and by a partial oxalate method. A two-step sintering process, including a hot pressing, was carried out at 1100 and 1200degreesC Distinct phases obtained during the sintering process have been investigated by SEM and EDS techniques and dielectric properties such as permittivity and dielectric loss were measured in a frequency range from 1 to 20 kHz.. A significant difference in microstructure and dielectric properties, depending on powder origin and sintering procedure, has been noticed.

SYNTHESIS OF ULTRA-FINE CRYSTALLINE ZRXTI1-XO4 POWDER BY POLYMERIC PRECURSOR METHOD

Reactive ZrxTi1-xO4 (x=0.65, 0.50 and 0.35) powder was prepared by the polymeric precursor method. Studies by X-ray diffraction (XRD), nitrogen adsorption/desorption, and thermogravimetric analysis (TG) showed that powders with high crystallinity (>90%) and high surface areas (>40 m(2)/g) are obtained after calcination at 700 degrees C for 3 h. Infrared spectroscopy and XRD results showed that these titanates nucleate from the amorphous phase with no intermediate phases, at low temperature (450 degrees C).

Visible PL phenomenon at room temperature in disordered structure of SrWO4 powder

The SrWO4 (SWO) powders were synthesized by the polymeric precursor method and annealed at different temperatures. The SWO structure was obtained by X-ray diffraction and the corresponding photoluminescence (PL) spectra was measured. The PL results reveal that the structural order-disorder degree in the SWO lattice influences in the PL emission intensity. Only the structurally order-disordered samples present broad and intense PL band in the visible range. To understand the origin of this phenomenon, we performed quantum-mechanical calculations with crystalline and order-disordered SWO periodic models. Their electronic structures were analyzed in terms of band structure. The appearance of localized levels in the band gap of the order-disordered structure was evidenced and is a favorable condition for the intense PL to occur.

Analytical procedure for total mercury determination in fishes and shrimps by chronopotentiometric stripping analysis at gold film electrodes after microwave digestion

A method for the total mercury determination in fish and shrimps employing chronopotentiometric stripping analysis on gold film electrodes is described. Fish and shrimp tissues were digested using a microwave oven equipped with closed vessels. We developed a microwave heating program which decomposed all the samples employing diluted nitric acid and hydrogen peroxide. The proposed method was validated by analyzing a certified reference material and then applied for different fish species from fresh water and seawater acquired in local markets of São Paulo city, Brazil. The Brazilian legislation establishes 0.5 and 1 mg per kilogram of fish as upper limit of mercury for omnivorous and predator species, respectively. Except for blue shark tissues, the mercury content was situated below 0.5 mu g g(-1) for all the analyzed samples. The detection limit of the proposed method was calculated as 5 ng g(-1) of sample utilizing 5 minutes of electrodeposition (+300 mV vs. Ag/AgCl) on the gold electrode. (c) 2006 Elsevier Ltd. All rights reserved.

Characterization and application of PZT/PU and graphite doped PZT/PU composite

Composites, made of lead zirconate titanate (PZT) ceramic powder and castor oil-based polyurethane (PU), were prepared in the film form. The films were obtained in the thickness range 100-300 mum using up to 50/50 vol.% of ceramic. Another composite (PZT/C/PU) was obtained by adding a small amount (1.0 vol.%) of graphite (C) to the PZT/PU composite. By increasing the conductivity of PU-containing graphite, polarization of PZT could be carried out with better efficiency. A comparison of piezo- and pyroelectric activities and spatial distribution of polarization between graphite doped and undoped composites reveal the advantages of using semiconductor filler. These composites were used as sensors to detect acoustic emission (AE). The detection was made using two simulated sources of AE, i.e., ball bearing drop and pencil lead break. PZT/C/PU composite was able to detect both flexural and extensional components of wave vibration. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Processing and properties of Ag/BSCCO PIT tapes containing different proportions of silver metal powder

Monofilamentary tapes (150 pm thickness) were prepared by swaging and rolling silver tubes containing the Bi:2212 ceramic (granulation below 20 mum) and the silver powder (about 0.8 mum). The study has been made, among other samples, on tapes with nominal proportions of 0, 10 and 20 wt.% of silver. The samples were characterized by SEM, and by electrical measurements under varying applied magnetic field. The measurements of J(c) showed that the addition of 10 wt.% silver powder is very beneficent to this property, doubling the obtained values at 60 K, while the 20 wt.% tape presented very low J(c). The tape with no silver content showed to have a J(c) as high as 2.2 x 10(5) A/cm(2), at 4.2 K, zero applied magnetic field. (C) 2004 Elsevier B.V. All rights reserved.

Simultaneous determination of zinc, copper, lead, and cadmium in fuel ethanol by anodic stripping voltammetry using a glassy carbon-mercury-film electrode

A new, versatile, and simple method for quantitative analysis of zinc, copper, lead, and cadmium in fuel ethanol by anodic stripping voltammetry is described. These metals can be quantified by direct dissolution of fuel ethanol in water and subsequent voltammetric measurement after the accumulation step. A maximum limit of 20% (v/v) ethanol in water solution was obtained for voltammetric measurements without loss of sensitivity for metal species. Chemical and operational optimum conditions were analyzed in this study; the values obtained were pH 2.9, a 4.7-mum thickness mercury film, a 1,000-rpm rotation frequency of the working electrode, and a 600-s pre-concentration time. Voltammetric measurements were obtained using linear scan (LSV), differential pulse (DPV), and square wave (SWV) modes and detection limits were in the range 10(-9)-10(-8) mol L-1 for these metal species. The proposed method was compared with a traditional analytical technique, flame atomic absorption spectrometry (FAAS), for quantification of these metal species in commercial fuel ethanol samples.

Prediction of cassava starch edible film properties by chemometric analysis of infrared spectra

Cassava starch has been shown to make transparent and colorless flexible films without any previous chemical treatment. The functional properties of edible films are influenced by starch properties, including chain conformation, molecular bonding, crystallinity, and water content. Fourier-transform infrared (FTIR) spectroscopy in combination with attenuated total reflectance (ATR) has been applied for the elucidation of the structure and conformation of carbohydrates. This technique associated with chemometric data processing could indicate the relationship between the structural parameters and the functional properties of cassava starch-based edible films. Successful prediction of the functional properties values of the starch-based films was achieved by partial least squares regression data. The results showed that presence of the hydroxyl group on carbon 6 of the cyclic part of glucose is directly correlated with the functional properties of cassava starch films.

Sugarcane molasses and yeast powder used in the Fructooligosaccharides production by Aspergillus japonicus-FCL 119T and Aspergillus niger ATCC 20611

Different concentrations of sucrose (3-25% w/v) and peptone (2-5% w/v) were studied in the formulation of media during the cultivation of Aspergillus japonicus-FCL 119T and Aspergillus niger ATCC 20611. Moreover, cane molasses (3.5-17.5% w/v total sugar) and yeast powder (1.5-5% w/v) were used as alternative nutrients for both strains' cultivation. These media were formulated for analysis of cellular growth, P-Fructosyltransferase and Fructooligosaccharides (FOS) production. Transfructosylating activity (U-t) and FOS production were analyzed by HPLC. The highest enzyme production by both the strains was 3% (w/v) sucrose and 3% (w/v) peptone, or 3.5% (w/v) total sugars present in cane molasses and 1.5% (w/v) yeast powder. Cane molasses and yeast powder were as good as sucrose and peptone in the enzyme and FOS (around 60% w/w) production by studied strains.

Microstructure and dielectric properties of (Ba,Sr)TiO3 thin film produced by the polymeric precursor method

BaxSr1-xTiO3 (x = 0.6) (BST) thin films were successfully prepared on a Pt(111)/TiO2/SiO2/Si(100) substrate by spin coating, using the polymeric precursor method. BST films with a perovskite single phase were obtained after heat treatment at 700 degrees C. The multilayer BST thin films had a granular structure will a grain size of approximately 60 nm. A 480-nm-thick film was obtained by carrying out five cycles of the spin-coating/heating process. Scanning electron microscopy and atomic force microscopy analyses showed that the thin films had a smooth, dense, crack-free surface with low surface roughness (3.6 nm). At room temperature and at a frequency of 100 kHz, the dielectric constant and the dissipation factor were, respectively, 748 and 0.042. The high dielectric constant value was due to the high microstructural quality and chemical homogeneity of the thin films obtained by the polymeric precursor method.

Sintering of ultrafine undoped SnO2 powder

The sintering process of nanometric undoped SnO2 powder was studied. No macroscopic shrinkage was observed during the sintening process. Grain growth kinetics investigation showed that surface diffusion is the dominant mechanism in the temperature range 500-1300 degreesC. For temperatures higher than 1300 degreesC, high weight loss was measured, suggesting evaporation-condensation as the dominant mass-transport mechanism. Thermogravimetric analysis (TG) and mass spectroscopy studies showed that the surface contamination of the SnO2 particles by chemical species like H2O, OH- and CO2, has a strong influence on the role of mass transport controlled by surface diffusion. (C) 2001 Elsevier B.V. Ltd. All rights reserved.