Low temperature synthesis and hcaracterization of Ag2S1-x Tez(O

A low-temperature route for the synthesis of Ag2S,Ag2Te and their solid solutions Ag2S1-xTex(0 less-than-or-equal-to x less-than-or-equal-to 1) is reported. Ag2S is prepared by the direct addition of silver nitrate solution to thiourea, while Ag2Te is prepared by reacting silver nitrate solution with tellurium in nitric acid and subsequently reducing it with hydrazine hydrate. The solid solutions of Ag2S and Ag2Te are obtained by the addition of nitrate solutions of silver and tellurium to thiourea followed by its reduction with hydrazine hydrate. The method enables the synthesis of low-temperature crystalline phase of Ag2S1-xTex solid solutions. The powder X-ray diffraction studies suggest that the solid solutions of compositions x < 0.3 have a phase akin to alpha-Ag2S and those with compositions x > 0.6 are similar to alpha-Ag2Te. In the intermediate range of compositions (x = 0.4 and 0.5), the solid solutions are found to be mixtures of alpha-Ag2S and alpha-Ag2Te phases which transform totally to alpha-Ag2S phase on prolonged annealing at about 473 K.

Nanocomposites by rapid solidification route

Nanometric aggregates of solids can be classified into two types, nanograined or nanophased materials and nanocomposites. In the present paper after a brief review including the relation between size and boundary fraction, the basic principles that can be utilized to synthesize these materials from liquid route has been discussed. We shall present examples to show that with proper choice of systems and conditions it is possible to obtain nanocomposites in systems showing clustering tendencies in liquid as well as the systems exhibiting ordering tendencies leading to compound formation

Industrial validation of processing maps of 316L stainless steel using hot forging, rolling, and extrusion

The development of microstructure in 316L stainless steel during industrial hot forming operations including press forging (strain rate of 0 . 15 s(-1)), rolling/extrusion (strain rate of 2-8 . 8 s(-1)), and hammer forging (strain rate of 100 s(-1)) at different temperatures in the range 600-1200 degrees C was studied with a view to validating the predictions of the processing map. The results showed that good col relation existed between the regimes indicated in the map and the product microstructures. The 316L stainless steel exhibited unstable flow in the form of flow localisation when hammer forged at temperatures above 900 degrees C, rolled below 1000 degrees C, or press forged below 900 degrees C. All these conditions must therefore be avoided in mechanical processing of the material. Conversely, in order to obtain defect free microstructures, ideally the material should be rolled at temperatures above 1100 degrees C, press forged at temperatures above 1000 degrees C, or hammer forged in the temperature range 600-900 degrees C. (C) 1996 The Institute of Materials.

Mullite-zirconia composites

Mullite-zirconia composite powders were prepared by the combustion of an aqueous heterogeneous redox mixture consisting of Al(NO3)(3), Zr(NO3)(4)/ZrO(NO3)(2), silica fume and urea/diformyl hydrazine at 500 degrees C. X-ray diffraction data showed that a large amount of tetragonal zirconia existed in the composite powders in spite of high temperature calcination. Milled composite powders showed enhanced densification compared to the unmilled powders and the microstructure of the sintered (1600 degrees C) compacts showed the presence of spherical zirconia grains in intergranular positions along with elongated mullite grains.

Correlation of resistivity and microstructure in dilute titaniulll–nitrogen alloy

The precipitation kinetics of the quenched dilute Ti-1.6 at.-%N alloy has been followed by resistivity measurements at 77 K using the four probe method. Resistivity behaviour has been studied for various durations for the alloys aged in the temperature range 273-373 K. The resistivity behaviour has been explained on the basis of the growth and decay of interfacial strain fields associated with the precipitation process. In addition, the resistivity changes have been correlated with transmission electron microscopy observations. (C) 1995 The Institute of Materials.

Rapid microwave assisted synthesis of hydroxyapatite

A fast, efficient and novel method of preparation of hydroxyapatite using microwaves has been described.

Reactivities of aluminium and aluminium-magnesium alloy powders in polymeric composites

Polymeric compositions containing Al-Mg alloys show higher reactivities, in comparison with similar compositions containing aluminium. This is observed irrespective of the amount of oxidizer, type of oxidizer used, type of polymeric binder, and over a range of the particle sizes of the metal additive. This is evident from the higher calorimetric values obtained for compositions containing the alloy, in comparison to samples containing aluminium. Analysis of the combustion residue shows the increase in calorimetric value to be due to the greater extent of oxidation of the alloy. The interaction between the polymeric binder and the alloy was studied by coating the metal particles with the polymer by a coacervation technique. On ageing in the presence of ammonium perchlorate, cracking of the polymer coating on the alloy was noticed. This was deduced from differential thermal analysis experiments, and confirmed by scanning electron microscopic observations. The increase in stiffness of the coating, leading to cracking, has been traced to the cross-linking of the polymer by magnesium.

Repeated drop weight impacts and post-impact ILSS tests on glass-epoxy composite

E glass epoxy laminates of thicknesses in the range 2-5 mm were subjected to repeated impacts. For each thickness the number of hits to cause tup penetration was determined and the value of this number was higher the larger the thickness of the laminate tested. The C-scan, before and after impact, was done to obtain information regarding flaw distribution. Short beam shear test samples were made from locations at fixed distances from impact point and tested. The samples closer to the zone of impact showed lower strength values. Scanning fractography revealed shear deformation features for these samples and brittle fracture features for the region near the zone of impact.

Differences in the glass-forming ability of rapidly solidified and mechanically alloyed Ti-Ni-Cu alloys

Melt spinning of Ti50Ni50 ? xCux (x = 10, 25, 40) alloys showed that the glass-forming ability is good for Cu-rich compositions and poor for Ni-rich compositions. The results of mechanical alloying experiments in the same system showed a reverse trend as far as the glass-forming ability is concerned. These contradictory results are explained in the light of thermodynamic and kinetic considerations. Crystallization results of the melt spun alloys are also presented.

Study of fracture features in foam bearing glass epoxy composites subjected to repeated impacts

The paper reports the failure features observed in low mass repeatedly (pendulum) impacted glass epoxy composites with and without the mid section having either 2-layers or 3-layers of flexible foam. Features such as through width and inclined cracks as well as adhering of foam observed in the experiments are explained. The significance of the foam material in modifying the impact response of the composite is stressed.

Solid state amorphization in binary Ti---Ni, Ti---Cu and ternary Ti---Ni---Cu system by mechanical alloying

An amorphous phase has been synthesized by mechanical alloying in a planetary mill over a nickel content range of 10�70 at.% in the Ti---Ni system and a copper content range of 10�50 at.% in the Ti---Cu system. In the case of ternary Ti---Ni---Cu alloys the glass-forming composition range has been found to be given by x = 10�20 for Ti60Ni40 ? xCux, x = 10 � 30 for Ti50Ni50 ? xCux and x = 10 � 40 for Ti40Ni60 ? xCux alloys. The difficulty in the amorphization of copper-rich compositions is explained in the light of enthalpy composition diagrams calculated for the ternary solid solution and the amorphous phase.

Synthesis, structure and IR absorption studies of LnBaCuCoO(5) (Ln equal earth) oxides

A series of oxides LnBaCuCoO(5) (Ln = Pr, Nd, Sm, Dy, Gd, Ho and Er) have been synthesized by ceramic method. The oxides crystallize in a tetragonal structure, isostructural to YBaCuCoO5. All the oxides in the series are semiconducting. IR spectra of these oxides show distinct absorption bands at 630 cm(-1), 550 cm(-1) and 330 cm(-1) which are assigned to E, A(2) and A(1) modes respectively. Doping of holes in these oxides, by calcium substitution in Er1-xCaxBaCuCoO5-x (up to x similar or equal to 0.3) was done but, these oxides did not show metallic behaviour.

Transport properties, structure, and radiation induced defect studies in amorphous carbon films

Amorphous conducting carbon films are prepared by plasma assisted chemical vapour deposition and their d.c. conductivity (similar to 100 Scm(-1)) is studied from 300K down to 4.2K. The films were irradiated by high energy ion beam(I+13, 170 MeV) with a dose of 10(13) ions/cm(2). As a result a marked decrease in conductivity by two to three orders in magnitude was observed. The structural changes and the defects in the films caused by ion irradiation are studied using photoluminescence, persistent photoconductivity, and ESR spectroscopy.