Microwave hydrothermal synthesis, characterisation, and catalytic performance of Zn1-xMnxO in cellulose conversion

Wurtzite-type Zn1-xMnxO (x = 0, 0.03, 0.05, 0.07) nanostructures were successfully synthesised using a simple microwave-assisted hydrothermal route and their catalytic properties were investigated in the cellulose conversion. The morphology of the nanocatalysts is dopant-dependent. Pure ZnO presented multi-plate morphology with a flower-like shape of nanometric sizes, while the Zn0.97Mn0.03O sample is formed by nanoplates with the presence of spherical nanoparticles; the Zn0.95Mn0.05O and Zn0.93Mn0.07O samples are mainly formed by nanorods with the presence of a small quantity of spherical nanoparticles. The catalyst without Mn did not show any catalytic activity in the cellulose conversion. The Mn doping promoted an increase in the density of weak acid sites which, according to the catalytic results, favoured promotion of the reaction. © 2013 Institute of Chemistry, Slovak Academy of Sciences.

Visible to infrared energy conversion in Pr3+-Yb3+ co-doped fluoroindate glasses

Processes involving visible to infrared energy conversion are presented for Pr3+-Yb3+ co-doped fluoroindate glasses. The emission in the visible and infrared regions, the luminescence decay time of the Pr 3+:3P0 → 3H4 (482 nm), Pr3+:1D2 → 3H6 (800 nm), Yb3+:2F5/2 → 2F 7/2 (1044 nm) transitions and the photoluminescence excitation spectra were measured in Pr3+ samples and in Pr3+-Yb 3+ samples as a function of the Yb3+ concentration. In addition, energy transfer efficiencies were estimated from Pr3+: 3P0 and Pr3+:1D2 levels to Yb3+:2F7/2 level. Down-Conversion (DC) emission is observed due to a combination of two different processes: 1-a one-step cross relaxation (Pr3+:3P0 → 1G4; Yb3+:2F7/2 → 2F5/2) resulting in one photon emitted by Pr3+ (1G4 → 3H5) and one photon emitted by Yb3+ (2F7/2 → 2F5/2); 2-a resonant two-step first order energy transfer, where the first part of energy is transferred to Yb3+ neighbor through cross relaxation (Pr3+:3P0 → 1G4; Yb3+:2F7/2 → 2F5/2) followed by a second energy transfer step (Pr 3+:1G4 → 3H4; Yb3+:2F7/2 → 2F5/2). A third process leading to one IR photon emission to each visible photon absorbed involves cross relaxation energy transfer (Pr3+: 1D2 → 3F4; Yb 3+:2F7/2 → 2F5/2). © 2013 Elsevier B.V. All rights reserved.

Análise prognóstica da imunoexpressão de proteínas relacionadas à transição epitelial-mesenquimal nos carcinomas mamários esporádicos de cadelas

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Time reduction of light curing: Influence on conversion degree and microhardness of orthodontic composites

Introduction: The aim of this study was to assess the influence of curing time and power on the degree of conversion and surface microhardness of 3 orthodontic composites. Methods: One hundred eighty discs, 6 mm in diameter, were divided into 3 groups of 60 samples according to the composite used-Transbond XT (3M Unitek, Monrovia, Calif), Opal Bond MV (Ultradent, South Jordan, Utah), and Transbond Plus Color Change (3M Unitek)-and each group was further divided into 3 subgroups (n = 20). Five samples were used to measure conversion, and 15 were used to measure microhardness. A light-emitting diode curing unit with multiwavelength emission of broad light was used for curing at 3 power levels (530, 760, and 1520 mW) and 3 times (8.5, 6, and 3 seconds), always totaling 4.56 joules. Five specimens from each subgroup were ground and mixed with potassium bromide to produce 8-mm tablets to be compared with 5 others made similarly with the respective noncured composite. These were placed into a spectrometer, and software was used for analysis. A microhardness tester was used to take Knoop hardness (KHN) measurements in 15 discs of each subgroup. The data were analyzed with 2 analysis of variance tests at 2 levels. Results: Differences were found in the conversion degree of the composites cured at different times and powers (P < 0.01). The composites showed similar degrees of conversion when light cured at 8.5 seconds (80.7%) and 6 seconds (79.0%), but not at 3 seconds (75.0%). The conversion degrees of the composites were different, with group 3 (87.2%) higher than group 2 (83.5%), which was higher than group 1 (64.0%). Differences in microhardness were also found (P < 0.01), with lower microhardness at 8.5 seconds (35.2 KHN), but no difference was observed between 6 seconds (41.6 KHN) and 3 seconds (42.8 KHN). Group 3 had the highest surface microhardness (35.9 KHN) compared with group 2 (33.7 KHN) and group 1 (30.0 KHN). Conclusions: Curing time can be reduced up to 6 seconds by increasing the power, with a slight decrease in the degree of conversion at 3 seconds; the decrease has a positive effect on the surface microhardness.

The knowledge conversion SECI process as innovation indicator analysis factor

It highlights the innovation importance in the current society and presents innovation indicators applied in 125 countries. We made an analysis in the 80 variables distributed through seven GII pillars, trying to identify the direct, indirect or null incidences of the knowledge conversion way described by the SECI Process. The researched revealed the fact that knowledge management, in this case specifically the knowledge conversion SECI Process, is present in the variables that, according to the GII, make clear innovative activity in countries.

Sprayed films of europium complexes toward light conversion devices

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Conversion between basic density and apparent density at any moisture content in Eucalyptus grandis

Wood basic density (BD) is related to other wood characteristics and its determination is important in forest inventory, though BD must be differentiated from the apparent density (AD), which relates to the moisture content (MC) of wood. The aim of this study is to demonstrate a reliable conversion from BD to AD for any MC of Eucalyptus grandis wood based on two exponential and linear models that relate volumetric shrinkage to MC. To this end, wood specimens were submitted to drying and the volumetric shrinkage was determined as a function of MC. The two models proved to be efficient in the conversion of BD to AD and vice versa.

Use of surgery and carboplatin in feline malignant mammary gland neoplasms with advanced clinical staging

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Infrared to visible up-conversion in biocellulose yttrium vanadate nanoparticle composite membranes. Demonstration of chloroaluminum phthalocyanine light emission under up-converted light excitation

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Long-term surface hardness and monomer conversion of a nonofilled and a microhybrid composite resin

Objective: This study aims to evaluate the degree of conversion (DC) and hydrolytic degradation through the Vickers hardness test (HV) of a nanofilled (Filtek™ Z-250, 3M) and a microhybrid (Filtek™Supreme-XT, 3M) composite resin. Materials and methods: Eight disk-shaped specimens (4 mm diameter × 2 mm thick, ISO 4049) of each material were prepared for each test. Composites were inserted into single increment in a metallic matrix and light-cured for 40 seconds. VH readings were performed for each specimen at predetermined intervals: immediately after polymerization (control), 1, 2, 3, 7, 14, 21, 30 and 180 days. After curing, initial hardness measurements were performed and the specimens were immersed in artificial saliva at 37°C. For DC (%), specimens were ground, pressed with KBr and analyzed by FT-IR spectrophotometer. Results: Student t-test showed that there was no difference between the resins for DC (p = 0.252). ANOVA analysis revealed that Z-250 VH means were all greater than S-XT, for both top and bottom surfaces, whatever the storage-period in artificial saliva (p < 0.001). After 180 days of storage, the hardness obtained for S-XT was similar with that at the baseline, for both top and bottom surfaces. While for Z-250 hardness was not significantly different from baseline only for top surface, but there was a significant decrease observed in hardness for bottom surface. Conclusion: The materials tested showed no evidence of hydrolytic degradation in a significant way, in a 6-month storagetime in artificial saliva. Nanofilled resin presents a monomer conversion comparable to the conventional microhybrid.

Degree of conversion of different composite resins photo-activated with light-emitting diode and argon ion laser

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Greenhouse gas balance in the conversion from extensive pasture to other agricultural systems in Andean region of Colombia

Pós-graduação em Agronomia (Ciência do Solo) - FCAV

Non-hematopoietic PAR-2 is essential for matriptase-driven pre-malignant progression and potentiation of ras-mediated squamous cell carcinogenesis

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

The effect of polymerization mode on monomer conversion, free radical entrapment, and interaction with hydroxyapatite of commercial self-adhesive cements

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)