The effect of multisubstitution on the thermoelectric properties of chalcogenide-based Cu2.1Zn0.9Sn1-xInxSe4 (0 <= x <= 0.1)

Quinary chalcogenide compounds Cu2.1Zn0.9Sn1-xInxSe4 (0 <= x <= 0.1) were prepared by melting (1170K) followed by annealing (773 K) for 172 h. Powder X-ray diffraction (XRD) data accompanied by electron probe microanalysis (EPMA) and Raman spectra of all the samples confirmed the formation of a tetragonal kesterite structure with Cu2FeSnS4-type. The thermoelectric properties of all the samples were measured as a function of temperature in the range of 300-780K. The electrical resistivity of all the samples exhibits metallic-like behavior. The positive values of the Seebeck coefficient and the Hall coefficient reveal that holes are the majority charge carriers. The codoping of copper and indium leads to a significant increase of the electrical resistivity and the Seebeck coefficient as a function of temperature above 650 K. The thermal conductivity of all the samples decreases with increasing temperature. Lattice thermal conductivity is not significantly modified as the doping content may infer negligible mass fluctuation scattering for copper/zinc and indium/tin substitution. Even though, the power factors (S-2/rho) of indium-doped samples Cu2.1Zn0.9Sn1-xInxSe4 (x = 0.05, 0.075) are almost the same, the maximum zT = 0.45 at 773K was obtained for Cu2.1Zn0.9Sn0.925In0.075Se4 due to its smaller value of thermal conductivity. (C) 2013 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim

Periodically Clickable Polyesters: Study of Intrachain Self-Segregation Induced Folding, Crystallization, and Mesophase Formation

A series of polyesters based on 2-propargyl-1,3-propanediol or 2,2-dipropargyl-1,3-propanediol or 2-allyl-2-propargyl-1,3-propanediol and 1,20-eicosanedioic acid were prepared by solution polycondensation using the corresponding diacid chloride; these polyesters were quantitatively ``clicked'' with a fluoroalkyl, azide, namely CF3(CF2)(7)CH2CH2N3, to yield polyesters carrying long-chain alkylene segments in the backbone and either one or two perfluoroalkyl segments located at periodic intervals along the polymer chain. The immiscibility of the alkylene and fluoroalkyl segments causes the polymer chains to fold in a zigzag fashion to facilitate the segregation of these segments; the folded chains further organize in the solid state to form a lamellar structure with alternating domains of alkyl (HC) and fluoroalkyl (FC) segments. Evidence for the self-segregation is provided by DSC, SAXS, WAXS, and TEM studies; in two of the samples, the DSC thermograms showed two distinct endotherms associated with the melting of the individual domains, while the WAXS patterns confirm the existence of two separate peaks corresponding to the interchain distances within the crystalline lattices of the HC and FC domains. SAXS data, on the other hand, reveal the formation of an extended lamellar morphology with an interlamellar spacing that matches reasonably well with those estimated from TEM studies. Interestingly, a smectic-type liquid crystalline phase is observed at temperatures between the two melting transitions. These systems present a unique opportunity to develop interesting nanostructured polymeric materials with precise control over both the domain size and morphology; importantly, the domain sizes are far smaller than those typically observed in traditional block copolymers.

Topological Excitations in Semiconductor Heterostructures

Topological defects play an important role in the melting phenomena in two-dimensions. In this work, we report experimental observation of topological defect induced melting in two-dimensional electron systems (2DES) in the presence of strong Coulomb interaction and disorder. The phenomenon is characterised by measurement of conductivity which goes to zero in a Berezinskii-Kosterlitz-Thouless like transition. Further evidence is provided via low-frequency conductivity noise measurements.

A composition-dependent ``re-entrant'' crystallographic phase transition in the substitutional metal acetylacetonate complex (Cr1-xGax)(acac)(3)

The formation of a complete solid solution between acetylacetonate (acac) complexes of chromium and gallium, (Cr1-x,Ga-x)(acac)(3) for 0.1 melting point, making it a substitutional complex. Whereas the pure complexes (i.e. the end members of the solid solution, x = 0 and x = 1) are both centro-symmetric, a composition-dependent crystallographic phase transition to a non-centrosymmetric structure is found to occur for compositions with 0.4 < x < 0.9. Such a ``re-entrant'' crystallographic transition is interpreted to be due to the drive to overcome the disorder present in certain centrosymmetric chromium-rich compositions, by going over to a non-centrosymmetric structure with a doubling of the unit cell. The substitutional complex is shown to lead to a substitutional oxide with the beta-gallate structure. (C) 2014 Elsevier Ltd. All rights reserved.

Effect of morphology on electrical treeing in low density polyethylene nanocomposites

Influence of polymer morphology on the inception and the growth of electrical trees in unfilled low density polyethylene (LDPE) as well as LDPE filled with 1, 3 and 5% by weight nanoalumina samples stressed with 50 Hz ac voltage has been studied. It is seen that there is a significant improvement in tree inception voltage with filler loading in LDPE filled with nanoparticles. Tree inception voltage increased with the filler loading up to 3% by weight nanoalumina loading and showed a reduction at 5% by weight loading. Change in tree growth patterns from branch to bush as well as a slower tree growth with increase in filler loading in LDPE alumina nanocomposites were observed. The degree of crystallinity and change in crystalline morphology induced by the presence of alumina nanoparticles in LDPE was studied using differential scanning calorimetry (DSC) and scanning electron microscopy (SEM). DSC results show a similar melting behaviour for both unfilled LDPE and LDPE nanocomposites. However, there is a reduction in the degree of crystallinity for LDPE filled with 5% by weight nanoalumina. An increase in lamellae packing with increase in filler loadings and a highly disordered spherulitic structure for LDPE filled with 5% by weight nanoalumina was observed from the SEM images. The slow propagation of tree growth as well as reduction in tree inception voltage with increase in filler loadings were attributed to the morphological changes observed in the LDPE nanocomposites.

Solubility-Hardness Correlation in Molecular Crystals: Curcumin and Sulfathiazole Polymorphs

Curcumin and sulfathiazole exist as three and five polymorphs, respectively. We correlate solubility and mechanical properties in these polymorphic systems. It is seen that hardness (H) is inversely proportional to the solubility of a polymorph. H of the polymorphs is explained on the basis of slip planes in the crystal structure, the Schmid factor (m), and the relative orientation of molecules with respect to the nanoindenter direction. Effectively, H is a useful parameter (compared to melting point, T-m, and density, rho) that correlates well with the solubility of a polymorph. Such a correlation is helpful in systems like curcumin and sulfathiazole in which the Gibbs free energy of the polymorphs are close to one another. To summarize, a softer polymorph is more soluble.

In the Sense of Transcription Regulation by G-Quadruplexes: Asymmetric Effects in Sense and Antisense Strands

G-Quadruplexes occupy important regulatory regions in the genome. DNA G-quadruplexes in the promoter regions and RNA quadruplexes in the UTRs (untranslated regions) have been individually studied and variously implicated at different regulatory levels of gene expression. However, the formation of G-quadruplexes in the sense and antisense strands and their corresponding roles in gene regulation have not been studied in much detail. In the present study, we have elucidated the effect of strand asymmetry in this context. Using biophysical methods, we have demonstrated the formation of stable G-quadruplex structure in vitro using CD and UV melting. Additionally, ITC was employed to demonstrate that a previously reported selective G-quadruplex ligand was able to bind and stabilize the G-quadruplex in the present sequence. Further, we have shown using reporter constructs that although the DNA G-quadruplex in either strand can reduce translation efficiency, transcriptional regulation differs when G-quadruplex is present in the sense or antisense strand. We demonstrate that the G-quadruplex motif in the antisense strand substantially inhibits transcription, while when in the sense strand, it does not affect transcription, although it does ultimately reduce translation. Further, it is also shown that the G-quadruplex stabilizing ligand can enhance this asymmetric transcription regulation as a result of the increased stabilization of the G-quadruplex.

Comprehending the Formation of Eutectics and Cocrystals in Terms of Design and Their Structural Interrelationships

The phenomenon of cocrystallization, which encompasses the art of making multicomponent organic solids such as cocrystals, solid solutions, eutectics, etc. for novel applications, has been less studied in terms of reliably and specifically obtaining a desired cocrystallization product and the issues that govern their formation. Further, the design, structural, and functional aspects of organic eutectics have been relatively unexplored as compared to solid solutions and cocrystals well-established by crystal engineering principles. Recently, eutectics were proposed to be designable materials on par with cocrystals, and herein we have devised a systematic approach, based on the same crystal engineering principles, to specifically and desirably make both eutectics and cocrystals for a given system. The propensity for strong homomolecular synthons over weak heteromolecular synthons and vice versa during supramolecular growth was successfully utilized to selectively obtain eutectics and cocrystals, respectively, in two model systems and in two drug systems. A molecular level understanding of the formation of eutectics and cocrystals and their structural interrelationships which is significant from both fundamental and application viewpoints is discussed. On the other hand, the obscurity in establishing a low melting combination as a eutectic or a cocrystal is resolved through phase diagrams.

Nanostructuring of p- and n-type skutterudites reaching figures of merit of approximately 1.3 and 1.6, respectively

Thermoelectric (TE) conversion of waste heat into useful electricity demands optimized thermal and electrical transport in the leg material over a wide temperature range. In order to gain a reasonably high figure of merit (ZT) as well as high thermal electric conversion efficiency, various conditions of the starting material were studied: industrially produced skutterudite powders of p-type DDy(Fe1-xCox)(4)Sb-12 (DD: didymium) and n-type (Mm, Sm)(y)Co4Sb12 (Mm: mischmetal) were used. After a rather fast reaction-melting technique, the bulk was crushed and sieved with various strainers in order to obtain particles below the respective mesh sizes, followed by ball-milling under three different conditions. The dependence of the TE properties (after hot pressing) on the micro/nanosized particles, grains and crystallites was investigated. Optimized conditions resulted in an increase of ZT for bulk material to current record-high values: from ZT similar to 1.1 to ZT similar to 1.3 at 775 K for p-type and from ZT similar to 1.0 to ZT similar to 1.6 at 800 K for n-type, resulting in respective efficiencies (300-850 K) of eta > 13% and eta similar to 16%. (C) 2014 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Substitution-Modulated Anticancer Activity of Half-Sandwich Ruthenium(II) Complexes with Heterocyclic Ancillary Ligands

Ten new organometallic half-sandwich ruthenium complexes with heterocyclic ligands have been synthesized (H1-H10). The substituents on the ancillary heterocyclic ligands were varied to understand the effect of substitution on anticancer activity. The crystallographic characterization of five complexes confirms that they adopt three-legged piano-stool structures and are stabilized by intramolecular hydrogen bonding. Complexes H2 and H3 also exhibit halogen bonding in the solid state. In aqueous media, the complexes form dinuclear ruthenium species. Complex H1 with a noncytotoxic heterocycle, 6-fluoro-2-mercaptobenzothiazole, and complex H11 with the unsubstituted 2-mercaptobenzothiazole are the most active against A2780 and KB cell lines. The substitution of the H atoms on the ancillary ligand with Cl or Br atoms leads to a decrease in the anticancer activity. With the exception of fluorine-substituted H5, the complexes with mercaptobenzoxazole (H6-H9) are inactive against all of the tested cell lines. Ruthenium complexes with mercaptonaphthimidazole (H10) and mercaptobenzimidazole (H13) do not show any anticancer activity. The active complexes show a biphasic melting curve when incubated with calf thymus (CT) DNA. These complexes only inhibit thioredoxin reductase (TrxR) enzyme activity to a small extent. The substitution of hydrogen atoms with fluorine atoms in the aromatic heterocyclic ligands on organometallic half-sandwich ruthenium complexes has the most beneficial effect on their anticancer activity.

Effect of High-Pressure Torsion on Texture, Microstructure, and Raman Spectroscopy: Case Study of Fe- and Te-Substituted CoSb3

Fe0.05Co0.95Sb2.875Te0.125, a double-element-substituted skutterudite, was prepared by induction melting, annealing, and hot pressing (HP). The hot-pressed sample was subjected to high-pressure torsion (HPT) with 4 GPa pressure at 673 K. X-ray diffraction was performed before and after HPT processing of the sample; the skutterudite phase was observed as a main phase, but an additional impurity phase (CoSb2) was observed in the HPT-processed sample. Surface morphology was determined by high-resolution scanning electron microscopy. In the HP sample, coarse grains with sizes in the range of approximately 100 nm to 300 nm were obtained. They changed to fine grains with a reduction in grain size to 75 nm to 125 nm after HPT due to severe plastic deformation. Crystallographic texture, as measured by x-ray diffraction, indicated strengthening of (112), (102) poles and weakening of the (123) pole of the HPT-processed sample. Raman-active vibrational modes showed a peak position shift towards the lower energy side, indicating softening of the modes after HPT. The distortion of the rectangular Sb-Sb rings leads to broadening of Sb-Sb vibrational modes due to local strain fluctuation. In the HPT process, a significant effect on the shorter Sb-Sb bond was observed as compared with the longer Sb-Sb bond.

Microstructural Features of Hot Deformed Nb-1Zr-0.1C Alloy

Niobium-based alloys are well-established refractory materials; as a result of their high melting temperature and good creep properties, these alloys find their applications in nuclear reactors. The present study deals with a microstructural response of these materials during hot working. The evolution of microstructure and texture during high-temperature deformation has been investigated in the temperature range 1500-1700A degrees C and strain rate range of 0.001-0.1 s(-1). For each deformed sample, the microstructure has been examined in detail. The microstructural features clearly revealed the formation of a substructure and the occurrence of dynamic recrystallization in a proper temperature-strain rate window. At low strain rates, the necklace structure formation was more prominent.

Polymorphism and Phase Transformation Behavior of Solid Forms of 4-Amino-3,5-dinitrobenzamide

We report the preparation, analysis, and phase transformation behavior of polymorphs and the hydrate of 4-amino-3,5-dinitrobenzamide. The compound crystallizes in four different polymorphic forms, Form I (monoclinic, P2(1)/n), Form II (orthorhombic, Pbca), Form III (monoclinic, P2(1)/c), and Form IV (monoclinic, P2(1)/c). Interestingly, a hydrate (triclinic, P (1) over bar) of the compound is also discovered during the systematic identification of the polymorphs. Analysis of the polymorphs has been investigated using hot stage microscopy, differential scanning calorimetry, in situ variable-temperature powder X-ray diffraction, and single-crystal X-ray diffraction. On heating, all of the solid forms convert into Form I irreversibly, and on further heating, melting is observed. In situ single-crystal X-ray diffraction studies revealed that Form II transforms to Form I above 175 degrees C via single-crystal-to-single-crystal transformation. The hydrate, on heating, undergoes a double phase transition, first to Form III upon losing water in a single-crystal-to-single-crystal fashion and then to a more stable polymorph Form I on further heating. Thermal analysis leads to the conclusion that Form II appears to be the most stable phase at ambient conditions, whereas Form I is more stable at higher temperature.

Multidimensional free energy surface of unfolding of HP-36: Microscopic origin of ruggedness

The protein folding funnel paradigm suggests that folding and unfolding proceed as directed diffusion in a multidimensional free energy surface where a multitude of pathways can be traversed during the protein's sojourn from initial to final state. However, finding even a single pathway, with the detail chronicling of intermediates, is an arduous task. In this work we explore the free energy surface of unfolding pathway through umbrella sampling, for a small globular a-helical protein chicken-villin headpiece (HP-36) when the melting of secondary structures is induced by adding DMSO in aqueous solution. We find that the unfolding proceeds through the initial separation or melting of aggregated hydrophobic core that comprises of three phenylalanine residues (Phe7, Phe11, and Phe18). This separation is accompanied by simultaneous melting of the second helix. Unfolding is found to be a multistage process involving crossing of three consecutive minima and two barriers at the initial stage. At a molecular level, Phe18 is observed to reorient itself towards other hydrophobic grooves to stabilize the intermediate states. We identify the configuration of the intermediates and correlate the intermediates with those obtained in our previous works. We also give an estimate of the barriers for different transition states and observe the softening of the barriers with increasing DMSO concentration. We show that higher concentration of DMSO tunes the unfolding pathway by destabilizing the third minimum and stabilizing the second one, indicating the development of a solvent modified, less rugged pathway. The prime outcome of this work is the demonstration that mixed solvents can profoundly transform the nature of the energy landscape and induce unfolding via a modified route. A successful application of Kramer's rate equation correlating the free energy simulation results shows faster rate of unfolding with increasing DMSO concentration. This work perhaps presents the first systematic theoretical study of the effect of a chemical denaturant on the microscopic free energy surface and rates of unfolding of HP-36. (C) 2014 AIP Publishing LLC.

Phase Diagram Study of Succinonitrile-Vanillin Organic Alloy System

Phase diagram studies of succinonitrile-vanillin system show the formation of 2:1 congruent melting type compound. Crystallization velocities of pure components, succinonitrile-vanillin complex, and two eutectics have been determined at different undercoolings. On the basis of heat of fusion measurements, excess thermodynamic functions have been calculated. Microstructural studies revealed that impurities modify the morphology. FTIR spectral studies and computer simulation have shown the existence of hydrogen bonding in the eutectics and the congruent melting compound. On the basis of experimental results, the mechanism of formation of eutectics and its solidification behavior are discussed.