Microstructure and grain boundary microanalysis of X70 pipeline steel

Grain boundaries (GBs), particularly ferrite: ferrite GBs, of X70 pipeline steel were characterized using analytical electron microscopy (AEM) in order to understand its intergranular stress corrosion cracking (IGSCC) mechanism(s). The microstructure consisted of ferrite (alpha), carbides at ferrite GBs, some pearlite and some small precipitates inside the ferrite grains. The precipitates containing Ti, Nb, V and N were identified as complex carbo-nitrides and designated as (Ti, Nb, WC, N). The GB carbides occurred (1) as carbides along ferrite GBs, (2) at triple points, and (3) at triple points and extending along the three ferrite GBs. The GB carbides were Mn rich, were sometimes also Si rich, contained no micro-alloying elements (Ti, Nb, V) and also contained no N. It was not possible to measure the GB carbon concentration due to surface hydrocarbon contamination despite plasma cleaning and glove bag transfer from the plasma cleaner to the electron microscope. Furthermore, there may not be enough X-ray signal from the small amount of carbon at the GBs to enable measurement using AEM. However, the microstructure does indicate that carbon does segregate to alpha : alpha GBs during microstructure development. This is particularly significant in relation to the strong evidence in the literature linking the segregation of carbon at GBs to IGSCC. It was possible to measure all other elements of interest. There was no segregation at alpha : alpha GBs, in particular no S, P and N, and also no segregation of the micro-alloying elements, Ti, Nb and V. (C) 2003 Kluwer Academic Publishers.

Comparative atmospheric corrosion of primary and cold rolled copper in Australia

Atmospheric corrosion tests, according to ASTM G50, have been carried out in Queensland, Australia, at three different sites representing three different environmental conditions. A range of materials including primary copper (electrosheet) and electrolytic tough pitch (traditional cold rolled) copper have been exposed. Data is available for five exposure periods over a three year time span. X-Ray Diffraction has been used to determine the composition of the corrosion products. Corrosion rates have been determined for each material at each of the exposure sites and are compared with corrosion rates obtained from other long term atmospheric corrosion test programs. Primary copper sheet (electrosheet) behaves like traditionally produced cold rolled copper (C11000) sheet but with an increased corrosion rate. This difference between the rolled copper samples and the primary copper samples is probably due to a combination of factors related to the difference in crystallographic texture of the underlying copper, the morphology and texture of the cuprite layer, the surface roughness of the sheets, and the differences in mass. These factors combine together to provide an increased oxidation rate and TOW for the electrosheet material and which is significantly higher at the more tropical sites. For a sulfate environment (Urban) the initial corrosion product is cuprite with posnjakite and brochantite also occurring at longer exposures. Posnjakite is either washed away or converted to brochantite during further exposure. The amount of brochantite increases with exposure time and forms the blue-green patina layer. For a chloride environment (Marine) the initial corrosion product is cuprite with atacamite also occurring at longer exposures.

Mechanical alloying of MoSi2 with ternary alloying elements. Part 2 - computer simulation

A computer model of the mechanical alloying process has been developed to simulate phase formation during the mechanical alloying of Mo and Si elemental powders with a ternary addition of Al, Mg, Ti or Zr. Using the Arhennius equation, the model balances the formation rates of the competing reactions that are observed during milling. These reactions include the formation of tetragonal C11(b) MOSi2 (t-MoSi2) by combustion, the formation of the hexagonal C40 MoSi2 polymorph (h-MoSi2), the transformation of the tetragonal to the hexagonal form, and the recovery of t-MoSi2 from h-MoSi2 and deformed t-MoSi2. The addition of the ternary additions changes the free energy of formation of the associated MoSi2 alloys, i.e. Mo(Si, Al)(2), Mo(Mg, Al)(2), (Mo, Ti)Si-2 (Mo, Zr)Si-2 and (Mo, Fe)Si-2, respectively. Variation of the energy of formation alone is sufficient for the simulation to accurately model the observed phase formation. (C) 2003 Elsevier B.V. All rights reserved.

SCC initiation for X65 pipeline steel in the "high" pH carbonate/bicarbonate solution

The initiation of stress corrosion cracking (SCC) was studied using scanning electron microscope observations of linearly increasing stress test specimens. SCC initiation from the following surfaces was studied: (i) initiation from the commercial pipe surface covered by the Zn coating, (ii) initiation from a mechanically polished surface with a deformed layer, and (iii) initiation from an electro-polished surface. SCC initiation involved different features for these surfaces as follows. (i) For the Zn coated commercial pipe surface, a crack in the Zn coating led to the dissolution of the deformed layer and when the deformed layer was penetrated, intergranular SCC initiation became possible. (ii) For a mechanically polished surface with a deformed layer, cracks in the surface oxide concentrated the anodic dissolution to such an extent that there was transgranular SCC in the deformed layer. SCC was intergranular when the deformed layer had been penetrated. Transgranular stress corrosion cracks were stopped at ferrite grain boundaries (GBs) oriented perpendicular to the SCC propagation direction. (iii) For an electro-polished surface, the surface oxide film was cracked at many locations, but intergranular SCC only propagated into the steel when the oxide crack corresponded to a GB. An oxide crack away from a GB is expected to be healed. The observed SCC initiation mechanism was not associated with simple preferential chemical attack of the ferrite GBs. (C) 2003 Elsevier Ltd. All rights reserved.

Phase-equilibrium data and liquidus for the system "MnO"-CaO-Al2O3-SiO2 at Al2O3/SiO2 of 0.55 and 0.65

Phase-equilibrium data and liquidus isotherms for the system MnO-CaO-(Al2O3 + SiO2) at silicomanganese alloy saturation have been determined in the temperature range of 1373 to 1723 K. The results are presented in the form of the pseudoternary sections MnO-CaO-(Al2O3 + SiO2) with Al2O3/SiO2 weight ratios of 0.55 and 0.65. The primary-phase fields have been identified in this range of conditions.

Stress crrosion cracking fracture mechanisms in rock bolts

Rock bolts have failed by Stress Corrosion Cracking (SCC). This paper presents a detailed examination of the fracture surfaces in an attempt to understand the SCC fracture mechanism. The SCC fracture surfaces, studied using Scanning Electron Microscopy (SEM), contained the following different surfaces: Tearing Topography Surface (TTS), Corrugated Irregular Surface (CIS) and Micro Void Coalescence (MVC). TTS was characterised by a ridge pattern independent of the pearlite microstructure, but having a spacing only slightly coarser than the pearlite spacing. CIS was characterised as porous irregular corrugated surfaces joined by rough slopes. MVC found in the studied rock bolts was different to that in samples failed in a pure ductile manner. The MVC observed in rock bolts was more flat and regular than the pure MVC, being attributed to hydrogen embrittling the ductile material near the crack tip. The interface between the different fracture surfaces revealed no evidence of a third mechanism involved in the transition between fracture mechanisms. The microstructure had no effect on the diffusion of hydrogen nor on the fracture mechanisms. The following SCC mechanism is consistent with the fracture surfaces. Hydrogen diffused into the material, reaching a critical concentration level. The thus embrittled material allowed a crack to propagate through the brittle region. The crack was arrested once it propagated outside the brittle region. Once the new crack was formed, corrosion reactions started producing hydrogen that diffused into the material once again. (C) 2003 Kluwer Academic Publishers.

Understanding magnesium corrosion - A framework for improved alloy performance

The purpose of this paper is to provide a succinct but nevertheless complete mechanistic overview of the various types of magnesium corrosion. The understanding of the corrosion processes of magnesium alloys builds upon our understanding of the corrosion of pure magnesium. This provides an understanding of the types of corrosion exhibited by,magnesium alloys, and also of the environmental factors Of most importance. This deep understanding is required as a foundation if we are to produce magnesium alloys much more resistant to corrosion than the present alloys. Much has already been achieved, but there is vast scope for improvement. This present analysis can provide a foundation and a theoretical framework for further, much needed research. There is still vast scope both for better fundamental understanding of corrosion processes, engineering usage of magnesium, and also on the corrosion protection of magnesium alloys in service.

The effect of the CaO/SiO2 ratio on the phase equilibria in the ZnO-“Fe2O3”-(PbO + CaO + SiO2) system in air: CaO/SiO2 = 0.1, PbO/(CaO + SiO2) = 6.2, and CaO/SiO2 = 0.6, PbO/(CaO + SiO2) = 4.3

Experimental studies on phase equilibria in the multi-component system PbO-ZnO-CaO-SiO2-FeO-Fe2O3 in air have been conducted to characterize the phase relations of a complex slag system used in the oxidation smelting of lead and in typical lead blast furnace sinters. The liquidus in two pseudoternary sections ZnO-Fe2O3-(PbO + CaO + SiO2) with the CaO/SiO2 weight ratio of 0.1 and the PbO/(CaO + SiO2) weight ratio of 6.2, and with CaO/SiO2 weight ratio of 0.6 and the PbO/(CaO + SiO2) weight ratio of 4.3, have been constructed.

Crystallographyof Mg17Al12 precipitates in AZ91D alloy

Kikuchi diffraction was used to accurately determine the orientation relationship (OR) between Mg17Al12 precipitates and matrix in an AZ91D alloy. For both continuous and discontinuous precipitations, the Burgers OR and the Potter OR were equally observed. The lattice parameter of Mg17Al12 associated with the former is bigger than that of the latter. (C) 2002 Acta Materialia Inc. Published by Elsevier Science Ltd. All rights reserved.

Boron solubility in Fe-Cr-B cast irons

Boron solubility in the as-cast and solution treated martensite of Fe-Cr-B cast irons, containing approximately 1.35 wt.% of boron, 12 wt.% of chromium, as well as other alloying elements, has been investigated using conventional microanalysis. The significant microstructural variations after tempering at 750 degreesC for 0.5-4 h, compared with the original as-cast and solution treated microstructures, indicated that the matrix consisted of boron and carbon supersaturated solid solutions. The boron solubility detected by electron microprobe was between 0.185-0.515 wt.% for the as-cast martensite and 0.015-0.0589 wt.% for the solution treated martensite, much higher than the accepted value of 0.005 wt.% in pure iron. These remarkable increases are thought to be associated with some metallic alloying element addition, such as chromium, vanadium and molybdenum, which have atomic diameters larger than iron, and expand the iron lattice to sufficiently allow boron atoms to occupy the interstitial sites in iron lattice. (C) 2002 Elsevier Science B.V. All rights reserved.

Morphology and crystallography of Mg24Y5 precipitate in Mg-Y alloy

Orientation relationships between Mg24Y5 precipitates and matrix in a Mg-Y alloy were accurately determined using Kikuchi line diffraction. The Burgers relationship with habit planes of {10 (1) over bar0}(H) and {31 (4) over bar0}(H) were observed for all precipitates. Compared with the Mg17Al12 precipitate in AZ91, the precipitation hardening effect in this alloy was significantly increased. (C) 2002 Acta Materialia Inc. Published by Elsevier Science Ltd. All rights reserved.

Martensite Crystallography - the apparent controversy between the infinitesimal deformation approach and the phenomenological theory of martensitic transformations

The aim of this article is to demonstrate that the apparent controversy between the infinitesimal deformation (ID) approach and the phenomenological theory of martensitic transformations (PTMTs) in predicting the crystallographic characteristics of a martensitic transformation is entirely based on unjustified approximations associated with the way in which the ID calculations are performed. When applied correctly, the ID approach is shown to be absolutely identical to the PTMT. Nevertheless, there may be some advantages in using the ID approach. In particular, it is somewhat simpler than the PTMT; it is based on a physical concept that is easier to understand and, most important, it may provide a tool for investigating some of the features of martensitic transformations that have eluded explanation via the PTMT.

The effect of iron on liquid film migration and sintering of an Al-Cu-Mg alloy

Analytical transmission electron microscopy indicates that liquid film migration occurs during sintering of an Al-Cu-Mg alloy, that intragranular liquid pools develop from migrating films and that iron segregates to these pools. It is suggested that a high localised iron concentration retards the liquid film migration rate by reducing the coherency strain in the retreating grain, causing a region of the film to detach from the boundary, thus forming an intragranular pool in the advancing grain. Alloys with low iron levels develop few intragranular pools and have high sintered densities. (C) 2003 Acta Materialia Inc. Published by Elsevier Science Ltd. All rights reserved.