Planar waveguides based on nanocrystalline and Er3+ doped SnO2

Luminescent SnO2: x%mol Er3+ (x=0.1-2.0) thin films have been spin coated on borosilicate and silica substrates from water colloidal suspensions that could be prepared containing up to 40% in weight SnO2 nanocrystalline powders. High Resolution Transmission Electron Microscopy results show the well known SnO2 cassiterite structure and nanocrystallites around 10 nm in diameter, corroborating results from X-ray diffraction. Mono and multi layers have been prepared from the stable colloidal suspensions and films thickness was observed to increase linearly, up to 200 nm, with the colloidal suspensions nanoparticles amount. Excitation and emission spectra have been measured and Er3+ ions were found to be essentially incorporated into the cassiterite structure, substituting for Sn4+, for doping concentration lower than 0.05 mol%. Er3+ ions also appear segregated at the grains surface for higher doping concentration. The optical parameters (refractive index, thickness and propagating modes) of a waveguide sample were measured at 632.8 and 543.4 nm by the prism coupling technique. A monomodal waveguide was obtained with attenuation loss of 3.5 dB/cm along a 2.5 cm optical path.

Electrical properties of screen printed BaTiO3 thick films

The deposition of thick film pastes by screen-printing is a relatively simple and convenient method to produce thicker layers with thickness up to 100 mum. In the present work, the barium titanate thick films were prepared from mechanically activated powders based on BaC03 and TiO2. After mixing, the powders were calcined at low temperature by slow heating and cooling rates. The thick films were deposited on to Al2O3 substrates through hybrid technology. The obtained films were fired at 850 degreesC together with electrode material (silver/palladium). The electrical properties of thick films: dielectric permittivity, dielectric losses, Curie temperature, hysteresis loop were reported. The obtained BT thick films can be applied in as multilayer capacitors or in gas sensor application. (C) 2003 Elsevier Ltd. All rights reserved.

Composites PVDF-TrFE/BT used as bioactive membranes for enhancing bone regeneration

In this paper a piezoelectric composite membranes were developed for charge generator to promoter bone regeneration on defects sites. Is known that the osteogenesis process is induced by interactions between biological mechanisms and electrical phenomena. The membranes were prepared by mixing Barium Titanate (BT) powders and PVDF-TrFE (PVDF:TrFE = 60:40 mol%) on dimethylformamide medium. This precursor solution was dried and crystallized at 100degreesC for 12 hours. Composites membranes were obtained by following methods: solvent casting (SC), spincoating (SP), solvent extraction by water addition (WS) and hot pressing (HP).The microstructural analysis performed by SEM showed connectivity type 3-0 and 3-1 with high homogeneity for samples of ceramic volume fraction major than 0.50. Powder agglomerates within the polymer matrix was evidenced were observed for composites with the BT volume fraction major than 40%. The composite of ceramic fraction of 0.55 presented the best values of remanent polarization (similar to33 muC/cm(2)), but the flexibility of these composites with the larger ceramic fraction was significantly affected.For in vivo evaluation PVDF-TrFE/BT 90/10 membranes with 3cm larger were longitudinally implanted under tibiae of male rabbit. After 21 days the animals were sacrificed. By histological analyses were observed neo formed bone with a high mitotic activity. In the interface bone-membrane was evidenced a pronounced callus formation. These results encourage further applications of these membranes in bone-repair process.

Er3+ as marker for order-disorder determination in the PbTiO3 system

Er3+ ions were added to the PbTiO3 network using the polymeric precursor method to characterize the order-disorder transformation found in this material by means of experimental and theoretical approach. The disordered and ordered material structures were studied by photoluminescence measurements, X-ray diffraction (XRD) and U-V-visible spectroscopy. The Er3+ ions served as a marker to identify the structural short-range order beginning in the PbTiO3 matrix. From photoluminescence results it was concluded that disordered PbTiO3 powders have a certain short range order in the network that are undetected by XRD measurements. The electronic structures were calculated by the ab initio periodic method in DFT level with the non-local B3LYP hybrid approximation for the Ti atom site interpretation using density of states (DOS) results. This analysis enabled understanding that Ti atom sphere coordination can create possible states for radioactive return and trap of electron-holes pair. (c) 2007 Elsevier B.V. All rights reserved.

Synthesis and thermal characterization of luminescent powers of terbium(III) with mixed ligands

This work deals with the synthesis and thermal decomposition of complexes of general formula: Ln(beta-dik)(3)L (where Ln=Tb(+3), beta-dik=4,4,4-trifluoro-1-phenyl-1,3butanedione(btfa) and L=1,10-fenantroline(phen) or 2,2-bipiridine(bipy). The powders were characterized by melting point, FTIR spectroscopy, LTV-visible, elemental analysis, scanning differential calorimeter(DSC) and thermogravimetry(TG). The TG/DSC curves were obtained simultaneously in a system DSC-TGA, under nitrogen atmosphere. The experimental conditions were: 0.83 ml.s(-1) carrier gas flow, 2.0 +/- 0.5 mg samples and 10 degrees C.min(-1) heating rate. The CHN elemental analysis of the Tb(btfa)(3)bipy and Tb(btfa)(3)phen complexes, are in good agreement with the expected values. The IR spectra evinced that the metal ion is coordinated to the ligands via C=O and C-N groups. The TG/DTG/DSC curves of the complexes show that they decompose before melting. The profiles of the thermal decomposition of the Tb(btfa)3phen and Tb(btfa)3bipy showed six and five decomposition stages, respectively. Our data suggests that the thermal stability of the complexes under investigation followed the order: Tb(btfa)(3)phen < Tb(btfa)(3)bipy.

Photoluminescence in disordered Zn2TiO4

In this work, the polymeric precursor method Was used to obtain disordered Zn2TiO4 powders, either Undoped or doped with Sn4+, Cr3+ and V5+, to be applied its photoluininescent material. The characterization was undertaken by means of thermal analysis (TG and DTA), X-ray diffraction (XRD), infrared spectroscopy (IR) and photoluminescence (PL). Previous works stated that titanate octahedra containing a short Ti-O distance show efficient luminescence at roorn temperature if these octahedra are isolated from each other. In the present work, the phenomenon was observed in condensed octahedra, sharing edges. The room temperature PL noticed in undoped Zn2TiO4 had its intensity increased by the dopant addition-the increase was of about 300% for V5+ doping 400% for Cr3+ and 800% for Sn4+. (c) 2005 Elsevier B.V. All rights reserved.

Small angle X-ray scattering study of surface modified tin oxide nanoparticles prepared by sol-gel route

The surface properties of SnO2 nanoparticles were modified by grafting ionic (Tiron (R). (OH)(2)C6H2(SO3Na)(2)(H2O)-H-.) or non-ionic (Catechol (R). C6H4-1,2-(OH)(2)) capping Molecules during aqueous sol-gel processing to improve the redispersibility of powdered xerogel. The effect of the amount of grafted organic molecules on the redispersibility of powders in aqueous solution at several basic pH values was Studied. The nanostructural features of the colloidal suspensions were analyzed by small angle X-ray scattering (SAXS) measurements. Irrespective of the nature and amount of grafted molecules, complete redispersion was obtained in aqueous solution at pH = 13. The redispersion at pH = 11 results in a mixture of dispersed primary particles and aggregates. The proportion of well dispersed nanoparticles and aggregates (and their average size) can be tuned by the quantity of grafted ionic molecules.

Color and structural analysis of CoxZn7-xSb2O12 pigments

The polymeric precursor method was successfully used to synthesize CoxZn7-xSbO12 (x = 0-7) powders. Pigments were evaluated using colorimetry, X-ray diffraction, UV-vis and infrared spectroscopy. The optical band gap values vary with the Co2+ substitution. These results suggest that the concomitant presence of Co and Zn in the spinel lattice leads to the rupture of the Vegard law, as well as other properties of the studied system, such as unit cell volume. The Co-richer samples display a higher absorbance than the Co-lean samples. The high absorption of the Co7Sb2O12 sample at most of the visible region makes this compound a candidate for a black pigment. It was shown that color depends on the site where the chromophore ion is located, in agreement with the ligand field theory. (c) 2006 Elsevier Ltd. All rights reserved.

Synthesis and luminescence properties of water dispersible Eu3+-doped boehmite nanoparticles

Nanocrystallized boehmite gamma-AlOOH center dot nH(2)O had been synthesized by spray-drying (SD) of a solution of aluminium tri-sec-butoxide peptized by nitric acid. The sub-micronic spherical particles obtained had an average diameter of 500 nm and were built of 100 nm or less platelet-like sub-particles. The average crystallite size calculated from XRD was 1.6 nm following the b axis (i.e. one unit cell) and 3-4 nm perpendicular to b. As a result of the nanometric sizes of crystallites, there was a large surface free for water adsorption and it was found to be n = 1.18 +/- 0.24H(2)O per AlOOH. The SD spheres spontaneously dispersed in water at room temperature and formed stable-over months-suspensions with nanometre-size particles (25-85 nm). Luminescent europium-doped nanocrystallized boehmites AlOOH: Eu (Al0.98Eu0.02OOH center dot nH(2)O) were synthesized the same way by SD and demonstrated the same crystallization properties and morphologies as the undoped powders. It is inferred from the Eu3+ luminescence spectroscopy that partly hydrated europium species are immobilized on the boehmite nanocrystals where they are directly bonded to alpha(OH) groups of the AlOOH surface. The europium coordination is schematically written [Eu3+(OH)(alpha)(H2O)(7-alpha/2)]. The europium-doped boehmite from SD spontaneously dispersed in water: the luminescence spectroscopy proves that most of the Eu3+ ions were detached from the NPs during water dispersion. The AlOOH: Eu nanoparticles were modified by the amine acid asparagine (ASN). The modification aimed to render the NPs compatible for further bio-functionalization. After surface modification, the NPs easily dispersed in water; the luminescence spectra after dispersion prove that the Eu3+ ions were held at the boehmite surface.

Synthesis of SnO2 by chemical routes and its use in varistors production

Tin oxide, SnO2. is a very used compound in industry and one of its uses is as varistor. For the current requirements of the technology is necessary a strict control of the chemical purity and the particle size of the raw material; for that reason the great interest that exists at the moment to develop synthesis methods that allow to get these requirements. In this work, ceramic powders of the Sn-Co-Nb-Ti-Al system using the controlled precipitation and polymeric precursor (Pechini) methods were synthesized. The raw material obtained was characterized using X-ray diffraction (XRD), thermal analysis (DTA/FG) and scanning electron microscopy (SEM). The sintering samples shown a good varistor behavior with non-linear coefficient (alpha) values similar to 22, and Er 2083 V/cm(2). (c) 2007 Elsevier Ltd. All rights reserved.

Microwave synthesis of YAG : Eu by sol-gel methodology

Yttrium-aluminum oxides are interesting compounds and they have been extensively used as host for lasers and phosphors, due to their stable physical and chemical properties. The fabrication of yttrium-aluminum garnet (YAG) has been investigated thoroughly. Single-crystal YAG is expensive and to produce it a new way has been investigated. This process consists of modifying the methodology of reagents mixture and the process of heating them. The microwave irradiation is used to heat-treat the oxide mixture. The traditional synthesis of YAG powders occurs through the reaction of aluminum and yttrium powders at high temperatures. With this work we investigated the preparation of YAG by non-hydrolytic sol-gel route as an alternative methodology to obtain yttrium-aluminum matrix from inorganic precursors (yttrium and aluminum chloride). The preparation of the gel was carried out in an oven-dried glassware. The AlCl3, YCl3 and ethanol were reacted in reflux under argon atmosphere. Europium III chloride was added as a structural probe. The powder was dried and heat-treated in modified microwaves. The samples were pre-treated at 50 and 800 C during I h and then heated in microwaves for 30 s, 2 and 4 min. The formation process and structure of the powders were studied by means of X-ray diffraction (XRD), photoluminescence (PL) and transmission electronic microscopy (TEM). XRD presents only picks corresponding to the YAG phase and confirmed by TEM. PL date showed that the YAG phase was formed in 2 min with the samples pre-treated at 50 C. For the samples pretreated at 800 degrees C, the YAG phase appears in 30s. The excitation spectra present a maximum of 394 nm corresponding to the L-5(6) level and emission spectra of Eu III ion present bands characteristic transitions arising from the D-5(0) -> F-7(J) (J= 1, 2, 3, 4) monifolds excited at their maximum. The magnetic dipole D-5(0) -> F-7(1) transition presents more intensity than the electric dipole D-5(0) -> F-7(2) transition. This methodology showed efficiency in obtaining YAG phase. (c) 2006 Elsevier B.V. All rights reserved.

Characterization of bismuth titanate ceramics derived by mechanochemical synthesis

Bismuth titanate, Bi(4)Ti(3)O(12) (BIT) nanosized powders have been successfully synthesized via high energy mechanochemical activation. The phase formation of BIT, crystal structure, microstructure, crystallite size and specific surface area were followed by XRD, scanning electron microscopy (SEM) and the BET specific surface area measurements. The BIT milled 2 h shows the orthorhombic crystalline structure with small amount of amorphous phase. The microstructure of Bi(4)Ti(3)O(12) ceramics sintered at 1000 degrees C for 12h exhibit plate-like grain structure.

Synthesis and photoluminescence study of La1.8Eu0.2O3 coating on nanometric alpha-Al2O3

In this work the La1.8Eu0.2O3 coating on nanometric alpha-alumina, alpha-Al2O3@La1.8Eu0.2O3, was prepared for the first time by a soft chemical method. The powder was heat-treated at 100, 400, 800 and 1200 degrees C for 2 h. X-ray powder diffraction patterns (XRD), transmission electronic microscopy (TEM), emission and excitation spectra, as well as Eu3+, lifetime were used to characterize the material and to follow the changes in structure as the heating temperature increases. The Eu3+ luminescence data revealed the characteristic transitions D-5(0) --> F-7(J) (J = 0, 1 and 3) of Eu3+ at around 580, 591 and 613 nm, respectively, when the powders were excited by 393 nm. The red color of the samples changed to yellow when the powder was annealed at 1200 degrees C. The decrease in the (D-5(0) --> F-7(2))/(D-5(0) --> F-7(1)) ratio from around 5.0 for samples heated at lower temperatures to 3.1 for samples annealed at 1200 degrees C is consistent with a higher symmetry of the Eu3+ at higher temperature. The excitation spectra of the samples also confirms this change by the presence of a more intense and broad band at around 317 nm, instead of the presence of the characteristic peak at 393 mn, which corresponds to the F-7(0) --> L-5(6) transition of the Eu3+. The lifetimes of the D-5(0) --> F-7(2) transition of Eu3+ for the samples heat-treated at 100, 400, 800 and 1200 degrees C was evaluated as 0.57, 0.72, 0.43 and 0.31 ms, respectively. (C) 2006 Elsevier Ltd. All fights reserved.

Effect of ceria content on the sintering of ZrO2 based ceramics synthesized from a polymeric precursor

Zirconia-ceria powders with ceria concentration varying from 0 to 12 mol% were synthesized using a polymeric precursor route based on the Pechini process. Powder characteristics were evaluated with regard to the crystallite size, BET surface area, phase distribution, nitrogen adsorption/desorption behavior, and agglomeration state. Sintering was studied considering the shrinkage rate, densification, grain size, and phase evolution. It was demonstrated that the synthesis method is effective to prepare nanosized powders of tetragonal zirconia single-phase. Sinterability mainly depended on the agglomeration state of powders and the monoclinic phase content, fully tetragonal zirconia ceramic, with grain size of 2.4 mu m, was obtained after addition of at least 9 mol% ceria and sintering at 1500 degrees C for 4 h. (C) 2000 Elsevier B.V. Ltd. All rights reserved.

Structural and electrical characterization of semiconducting barium-lead-titanate ceramics

BaTiO3 is usually doped to achieve the temperature stability required by device applications, as well as to obtain a large positive temperature coefficient anomaly of resistivity (PTCR). Uniform distribution of dopants among the submicron dielectric particles is the key for optimal control of grain size and microstructure to maintain a high reliability. The system Ba0.84Pb0.16TiO3 was synthesized from high purity BaCO3, TiO2, PbO oxide powders as raw materials. Sb2O3, MnSO4 and ZnO were used as dopants and Al2O3, TiO2 and SiO2 as grain growth controllers. Phase composition was analyzed by using XRD and the microstructure was investigated by SEM. EDS attached to SEM was used to analyze phase composition specially related to abnormal grain growth. Electrical resistivities were measured as a function of temperature and the PTCR effect characterized by an abrupt increase on resistivity.