Dissolution, recovery and fade of Sr master alloys in Al-7Si-0.5Mg casting alloys

A number of commercial Al-Sr master alloys of differing Sr content and product form have been added to Al-7Si-0.5Mg casting alloy melts and held at constant temperature for periods up to 7 hours following the addition. The master alloys were added to achieve a specific Sr target level of 200 ppm, and the melts were held at various temperatures (most at 710ºC, but also 670, 690, 740 and 770ºC). A total of thirty six melt trials were conducted and during each trial chill-cast disc samples were taken throughout for subsequent chemical analysis. The Sr concentration versus time data of each trial has been considered in terms of Sr dissolution/recovery behaviour, as well as Sr loss/fade. Trends in the data are identified and discussed, and implications for industrial practices are suggested.

Recent advances in understanding the eutectic solidification in Al-Si foundry alloys

The formation of the Al-Si eutectic is generally the final stage of the solidification process of Al-Si foundry alloys. This means that it can be expected to have a significant impact on the feeding of a casting, and consequently the formation of casting defects, in particular porosity. Understanding and controlling the eutectic solidification process are therefore very important. This paper reviews the recent advances and unique techniques used in improving our understanding of both eutectic nucleation and growth. The role of different modifiers in controlling the eutectic solidification mechanisms is presented and the relationship between eutectic solidification mechanisms and porosity formation is outlined. This new approach to aluminium foundry alloy metallurgy is likely to form the basis for further optimisation of alloy performance and master alloys for the future.

Cracking in the welding of cupro-nickel alloys

The problem of variation in weld crack susceptibility caused by small variations in alloy and impurity elements for the 70-30 cupro-nickel alloy has been investigated. Both wrought and cast versions of the alloy have been studied, the main techniques employed being the Varestraint test and weld thermal simulation. In the wrought alloys, cracking has been found to occur mainly in the weld metal, whilst in the cast alloys cracking is extensive in both weld metal and heat affected zone. The previously reported effects of certain impurities (P,S,Si) in increasing cracking have been confirmed, and it has also been shown that Ti and Zr may both have a crack promoting effect at levels commonly found in cupro-nickels, whilst C can interact with several of the other elements investigated to produce a beneficial effect. The testing carried out using the weld thermal simulator has shown that a relationship does exist between hot ductility and weld cracking. In particular, the absence of the peak in ductility in the range 1100°C-900°C on cooling from a temperature near to the solidus is indicative of a highly crack susceptible alloy. Principal practical implications of the investigation concern the relationship of weld metal cracking to alloy composition, especially the level of certain impurities. It would appear that the upper limits permitted by the alloy specifications are unrealistically high. The introduction of lower impurity limits would alleviate the current problems of variability in resistance to cracking during welding.