Selective corrosion of 550 degrees C aged Cu10Ni-3Al-1.3Fe alloy in NaCl aqueous solution

This work studied the electrochemical behavior of a solution treated or 550 degrees C aged Cu10Ni-3Al-1.3Fe alloy, in 0.01 M NaCl aqueous solution, through potentiodynamic polarization in both stagnant condition or under erosion process. Results showed the occurrence of a passivity break potential (E(pb)), related to the beginning of the denickelification process, which occurred as a localized attack under stagnant electrolyte. Under erosion conditions localized denickelification was not observed, despite of the presence of E(pb). This could indicate that selective corrosion of Ni, which caused the observed E(pb), occurred as a dissolution-redeposition process, with removal of the Cu deposits during erosion process. (C) 2011 Elsevier Ltd. All rights reserved.

Corrosion Versus Mechanical Tests for Indirect Detection of Alpha Prime Phase in UNS S32520 Super Duplex Stainless Steel

Alpha prime formation leads to material embrittlement and deterioration of corrosion resistance. In the present study, the mechanical and corrosion behavior of super duplex stainless steel UNS S32520 aged at 475 degrees C from 0.5 h to 1,032 h was evaluated using microhardness measurements, Charpy impact tests, electrochemical impedance spectroscopy, and cyclic polarization curves. The sensibility of these tests to the effects of alpha prime phase was investigated. The microhardness test showed a gradual increase in hardness with aging time, whereas the impact tests revealed losses of about 80% in the energy absorption capacity for the material aged for 12 h in comparison with the solution-annealed samples. The most responsive analysis was the impact test, which indirectly revealed the presence of this deleterious phase in samples aged for 0.5 h. The electrochemical impedance spectroscopy and polarization tests were not highly sensitive to the alpha prime phase unless these are present in large amounts in the stainless steel.

Controlling the luminescence properties of poly(p-phenylene vinylene) entrapped in Langmuir and Langmuir-Blodgett films of stearic acid

Properties of hybrid films can be enhanced if their molecular architecture is controlled. In this paper, poly (p-phenylene vinylene) was mixed with stearic acid in order to form stable hybrid Langmuir monolayers. Surface properties of these films were investigated with measurements of surface pressure, and also with polarization modulation infrared reflection-absorption spectroscopy (PM-IRRAS). The films were transferred from the air-water interface to solid supports through the Langmuir-Blodgett technique, and the viability of the film as optical device was investigated with fluorescence spectroscopy. Comparing the fluorescent spectra for the polymer in solution, as a casting film, and as an LB film, the emission bands for LB films were narrower and appeared at lower wavelengths. The interactions between the film components and the design for the LB film may take advantage of the method to immobilize luminescent polymers in mixed ultrathin films adsorbed in solid matrices. (C) 2011 Elsevier B.V. All rights reserved.

Corrosion behavior of Eurofer 97 and ODS-Eurofer alloys compared to traditional stainless steels

In the present work, the corrosion resistance of ferritic-martensitic EUROFER 97 and ODS-EUROFER steels was tested in solutions containing NaCl or H(2)SO(4) and KSCN, both at 25 degrees C. The results were compared to those of AISI 430 ferritic and AISI 410 martensitic conventional stainless steels. The as-received samples were tested by electrochemical techniques, specifically, electrochemical impedance spectroscopy, potentiodynamic polarization curves, and double-loop electrochemical potentiokinetic reactivation tests. The surfaces were observed by scanning electron microscopy after exposure to corrosive media. The results showed that EUROFER 97 and ODS-EUROFER alloys present similar corrosion resistance but lower than ferritic AISI 430 and martensitic 410 stainless steels.

EROSION-CORROSION SYNERGISM OF AN AISI 410 MARTENSITIC STAINLESS STEEL

In this work, the behavior of an AISI 410 martensitic stainless steel under corrosion-erosion conditions is evaluated. Quenched and tempered samples were used for the wear test, using a low velocity jet-like device connected to a potentiostat. Potentiodynamic polarization curves were obtained with the electrolyte in static state, with flow conditions and under corrosion-erosion, adding quartz particles to the electrolyte. In addition, mass loss measurements under erosion and corrosion-erosion conditions were carried out. The topography of the surfaces was examined after the wear tests, using optical and scanning electron microscopy. This information, together with the results of mass losses and the electrochemical tests were used to establish the degradation mechanisms of the stainless steels under different testing conditions. The results showed that synergism is a significant part of the degradation process of this steel (66.5%) and that the mass removal process of steel was controlled by corrosion assisted by erosion.

Effect of cerium (IV) ions on the anticorrosion properties of siloxane-poly(methyl methacrylate) based film applied on tin coated steel

This work investigates the influence of the addition of cerium (IV) ions on the anticorrosion properties of organic-inorganic hybrid coatings applied to passivated tin coated steel. In order to evaluate the specific effect of cerium (IV) addition on nanostructural features of the organic and inorganic phases of the hybrid coating, the hydrolytic polycondensation of silicon alkoxide and the radical polymerization of the methyl methacrylate (MMA) function were induced separately. The corrosion resistance of the coatings was evaluated by means of linear polarization, Tafel type curves and electrochemical impedance measurements. The impedance results obtained for the hybrid coatings were discussed based on an electrical equivalent circuit used to fit the experimental data. The electrochemical results clearly showed the improvement of the protective properties of the organic-inorganic hybrid coating mainly when the cerium (IV) was added to the organic phase solution precursor, which seemed to be due to the formation of a more uniform and densely reticulated siloxane-PMMA film. (C) 2010 Elsevier Ltd. All rights reserved.

Use of SECM to study the electrochemical behavior of DIN 1.4575 superferritic stainless steel aged at 475 degrees C

In order to lower the excessive costs of metallic prosthesis materia Is alternatives to Ti and Ti alloys have been searched. in this study, the corrosion resistance of the DIN 1.4575 superferritic stainless steel, either solution annealed or solution annealed and aged at 475 degrees C for periods varying from 100 to 1080 h, was investigated by electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization methods in Hanks` solution. The solution annealed and the aged for 1080 h samples were also tested using scanning electrochemical microscopy (SECM) in a 0.1 mol/L NaCl solution at 25 degrees C. The EIS results showed that the corrosion resistance of the DIN 1.4575 steel decreases with heat treatment time at 475 degrees C probably due to alpha prime formation. Besides the diminution of the overall impedance values, the low frequency limit of the Nyquist diagrams show a progressive change from an almost capacitive response to a resistive behavior as the heat treatment time increases. Pitting corrosion resistance also decreased with aging time at 475 degrees C.

Dodigen 213-N as corrosion inhibitor for ASTM 1010 mild steel in 10% HCL

This article describes a study of the behavior of a mixture of amines and amides, commercially known as Dodigen 213-N (D-213 N), as a corrosion inhibitor for ASTM 1010 mild steel in 10% w/w HCl solution. The concentration range used was 1 x 10(-5) M to 8 x 10(-4) M. The weight loss and electrochemical techniques used were corrosion potential measurement, anodic and cathodic polarization curves, and electrochemical impedance spectroscopy (EIS). The solution temperature was 50 +/- A 1 A degrees C and it was naturally aerated. The corrosion potential values shifted to slightly more positive values, thus indicating mixed inhibitor behavior. The anodic and cathodic polarization curves showed that D-213 N is an effective corrosion inhibitor, since both the anodic and the cathodic reactions were polarized in comparison with those obtained without inhibitor. For all concentrations the cathodic polarization curves were more polarized than the anodic ones. The inhibition efficiency was in the range 75-98%, calculated from values of weight loss and corrosion current density, i (corr), obtained by extrapolation of Tafel cathodic linear region.

Electrochemical study of modified cerium-silane bi-layer on Al alloy 2024-T3

In this paper, the performance of bis-1, 2-(triethoxysilyl) ethane (BTSE) as a pre-treatment to protect the AA 2024-T3 against corrosion has been investigated by electrochemical impedance spectroscopy (EIS), potentiodynamic polarization curves, and the scanning vibrating electrode technique (SVET). The microstructural and morphological characterizations were carried out via scanning electron microscopy and atomic force microscopy and the chemical composition evaluated using contact angle measurements and X-ray photoelectron spectroscopy (XPS). The electrochemical results showed that the additives improved the anticorrosion properties of the coating. The chemical characterization indicated that additives contribute to an increased degree of surface coverage, as well as to a more complete reticulation. The SVET results evidenced the self-healing abilities of Ce ions. (C) 2009 Elsevier Ltd. All rights reserved.

Influence of cerium (IV) ions on the mechanism of organosilane polymerization and on the improvement of its barrier properties

In this work, the effect of cerium (IV) ammonium nitrate (CAN) addition on the polymerization of bis-[triethoxysilyl]ethane (BTSE) film applied on carbon steel was studied. The electrochemical characterization of the films was carried out in 0.1 mol L(-1) NaCl solution by open-circuit potential measurements, anodic and cathodic polarization curves and electrochemical impedance spectroscopy (EIS). Morphological and chemical characterization were performed by atomic force microscopy (AFM), contact angle measurements, infrared-spectroscopy, nuclear magnetic resonance and thermogravimetric analysis. The results have clearly shown the improvement on the protective properties of the Ce(4+) modified film as a consequence of the formation of a more uniform and densely reticulated silane film. A mechanism is proposed to explain the accelerating role of Ce(4+) ions on the cross-linking of the silane layer. (C) 2008 Elsevier Ltd. All rights reserved.

Electrochemical study of modified non-functional bis-silane layers on Al alloy 2024-T3

In the last few years great efforts have been made in order to find and to develop environmentally friendly substitutes for Cr6+ pre-treatments applied on aluminium alloys used in the aircraft industry. Among the potential substitutes, silane layers have attracted considerable interest from researchers and from the industry. The present work investigates the anti-corrosion behaviour of (bis-1, 2-(triethoxysilyl) ethane (BTSE)) silane layers modified with Ce ions and/or silica nanoparticles applied on Al alloy 2024-T3 substrates. The corrosion behaviour was investigated in 0.1 M NaCl solution via d.c. polarization and electrochemical impedance spectroscopy (EIS). Contact angle measurements and XPS were used to assess information on the chemistry of the silane pre-treated surfaces. The results have shown that the introduction of additives improves the corrosion protection properties of the silane layer. (c) 2008 Elsevier Ltd. All rights reserved.

Corrosion behavior of carbon steel protected with single and bi-layer of silane films filled with silica nanoparticles

The electrochemical behaviour of carbon steel coated with bis-[trimethoxysilylpropyl]amine (BTSPA) filled with silica nanoparticles in naturally aerated 0.1 mol L-1 NaCl solutions was evaluated. The coating was prepared by adding different concentrations of silica nanoparticles (100, 200, 300, 400 and 500 ppm) to the hydrolysis solution and then a second layer without silica nanoparticles was applied. The electrochemical behavior of the coated steel was evaluated by means of open-circuit potential (E-OC), electrochemical impedance spectroscopy (EIS) and polarization curves. Surface characterization was made by atomic force microscopy (AFM), and its hydrophobicity assessed by contact angle measurements. EIS diagrams have shown an improvement of the barrier properties of the silane layer with the silica addition, which was further improved on the bi-layer system. However, a dependence on the filler concentration was verified, and the best electrochemical response was obtained for samples modified with 300 ppm of silica nanoparticles. AFM images have shown a homogeneous distribution of the silica nanoparticles on the sample surface; however particles agglomeration was detected, which degraded the corrosion protection performance. The results were explained on the basis of the improvement of the barrier properties of the coating due to the filler addition and on the onset of defective regions on the more heavily filled coatings allowing easier electrolyte penetration. (C) 2007 Elsevier B.V. All rights reserved.

Cr3C2-NiCr and WC-Ni thermal spray coatings as alternatives to hard chromium for erosion-corrosion resistance

Cr3C2-NiCr and WC-Ni coatings are widely used for wear applications at high and room temperature, respectively. Due to the high corrosion resistance of NiCr binder, Cr3C2-NiCr coatings are also used in corrosive environments. The application of WC-Ni coatings in corrosive media is 14 not recommended due to the poor corrosion resistance of the (pure Ni) metallic matrix. It is well known that the addition of Cr to the metallic binder improves the corrosion properties. Erosion-corrosion performance of thermal spray coatings is widely influenced by ceramic phase composition, the size of ceramic particles and also the composition of the metallic binder. In the present work, two types of HVOF thermal spray coatings (Cr3C2-NiCr and WC-Ni) obtained with different spray conditions were studied and compared with conventional micro-cracked hard chromium coatings. Both as-sprayed and polished samples were tested under two erosion-corrosion conditions with different erosivity. Tungsten carbide coatings showed better performance under the most erosive condition, while chromium carbide coatings were superior under less erosive conditions. Some of the tungsten carbide coatings and hard chromium showed similar erosion-corrosion behaviour under more and less erosive conditions. The erosion-corrosion and electrochemical results showed that surface polishing improved the erosion-corrosion properties of the thermally sprayed coatings. The corrosion behaviour of the different coatings has been compared using Electrochemical Impedance Spectroscopy (EIS) and polarization curves. Total material loss due to erosion-corrosion was determined by weight loss measurements. An estimation of the corrosion contribution to the total weight loss was also given. (c) 2007 Elsevier B.V. All rights reserved.

Study of an alternative phosphate sealer for replacement of hexavalent chromium

This study evaluates the possibility of replacing the hexavalent chromium passivation treatment used as a sealer after phosphating of carbon steel (SAE 1010) by a treatment with niobium ammonium oxalate (Ox). Samples of carbon steel (SAE 1010) after being phosphated in a zinc phosphate bath (PZn + Ni) were immersed in solution of niobium ammonium oxalate (250 mg L(-1) of Nb) either at pH 3.0 or pH 8.0. A passivation treatment with a solution with CrO(3) (200 mg L(-1) of Cr(6+)) was also used for reference. The corrosion resistance of the phosphated samples after passivation treatments was analyzed in a NaCl 0.5 mol L(-1) solution using electrochemical impedance spectroscopy (EIS) and anodic polarization curves. Salt spray tests were also performed to evaluate their corrosion resistance. The results showed that the highest corrosion resistance was obtained by passivation in a solution with (250 mg L(-1) of Nb) at pH 8.0. (C) 2010 Elsevier B.V. All rights reserved.

Effect of Charge Asymmetry on Adsorption and Phase Separation of Polyampholytes on Silica and Cellulose Surfaces

The relation between the properties of polyampholytes in aqueous solution and their adsorption behaviors on silica and cellulose surfaces was investigated. Four polyampholytes carrying different charge densities but with the same nominal ratio of positive to negative segments and two structurally similar polyelectrolytes (a polyacid and a polybase) were investigated by using quartz crystal microgravimetry using silica-coated and cellulose-coated quartz resonators. Time-resolved mass and rigidity (or viscoelasticity) of the adsorbed layer was determined from the shifts in frequency (Delta f) and energy dissipation (Delta D) of the respective resonator. Therefore, elucidation of the dynamics and extent of adsorption, as well as the conformational changes of the adsorbed macromolecules, were possible. The charge properties of the solid Surface played a crucial role in the adsorption of the studied polyampholytes, which was explained by the capability of the surface to polarize the polyampholyte at the interface. Under the same experimental conditions, the polyampholytes had a higher nominal charge density phase-separated near the interface, producing a soft, dissipative, and loosely bound layer. In the case of cellulose substrates, where adsorption was limited, electrostatic and polarization effects were concluded to be less significant.