Identificación y análisis funcional de genes implicados en la homeostasis de níquel en la bacteria endosimbiótica de leguminosas Rhizobium leguminosarum

La asociación Rhizobium-leguminosa constituye una interacción planta-microorganismo particularmente beneficiosa a nivel medioambiental debido a su capacidad promotora del crecimiento vegetal en condiciones de deficiencia de nitrógeno. Se ha demostrado que una excesiva concentración de metales pesados en el suelo afecta negativamente la competitividad bacteriana y al desarrollo de interacciones diazotróficas eficientes (Chaudri et al., 2000; Pereira et al., 2006). Por otro lado, el suministro de metales como Fe, Mo, Ni o Cu es fundamental para la biosíntesis de enzimas bacterianas relacionadas con el proceso de fijación de nitrógeno que ocurre en el interior de los nódulos de las leguminosas (Moreau et al., 1995). Con objeto de identificar sistemas génicos implicados en la homeostasis de níquel en bacterias endosimbióticas, se ha llevado a cabo una mutagénesis mediante inserción aleatoria de un minitransposón derivado de Tn5 en Rhizobium leguminosarum bv. viciae UPM1137, una cepa capaz de resistir elevadas concentraciones de níquel y cobalto. Como resultado de esta mutagénesis se han obtenido 14 mutantes incapaces de crecer en medios suplementados con NiCl2. La localización de la inserción en estos mutantes muestra que una elevada proporción de los genes afectados codifican proteínas de membrana o proteínas secretadas. En paralelo, se ha obtenido la secuencia del genoma de la cepa UPM1137, lo que permite realizar estudios in silico comparando los genomas disponibles de varias cepas de R. leguminosarum bv. viciae, que presentan una menor sensibilidad a metales. El análisis bioinformático de los genomas secuenciados y la caracterización fenotípica de los mutantes obtenidos permitirá identificar potenciales sistemas de resistencia y su contribución a la homeostasis de metales.

Caracterización de la resistencia a metales pesados de cepas de Rhizobium aisladas de suelos ultramáficos y contaminados

- Caracterización de la resistencia a altas concentraciones de metales, y en especial a níquel y cobalto en las cepas objeto de estudio. - Determinar si existe una posible correlación entre la presencia del sistema hidrogenasa y la resistencia a altas concentraciones de níquel. - Determinar los mecanismos moleculares implicados en la resistencia a níquel en la cepa de Rhizobium leguminosarum más resistente identificada en este estudio.

Identificación y caracterización funcional de sistemas génicos implicados en la homeostasis de níquel en Rhizobium leguminosarum bv. viciae

La homeostasis de metales como níquel, cobalto, cobre o zinc es un proceso delicado en procariotas. Estos metales de transición son, por un lado imprescindibles para el mantenimiento del metabolismo celular, pero por otro muy tóxicos a elevadas concentraciones. Por este motivo, los microorganismos han desarrollado mecanismos para regular su concentración intracelular, tales como bombas de flujo de metales, secuestradores intra y extracelulares o enzimas detoxificadoras.

Caracterização microbiológica, química e presença de poluentes orgânicos em amostras de lodo de esgoto de São Paulo

Objetivou-se com este trabalho avaliar o potencial agrícola do lodo de esgoto produzido no estado de São Paulo, bem como, verificar a possibilidade de interação entre a composição química e a abundância relativa de bactérias no lodo. Foram realizadas coletas de amostra de lodo de esgoto em 19 estações de tratamento de esgoto, em três épocas distintas. Nas amostras provenientes das três épocas foram determinados as concentrações dos 16 hidrocarbonetos policíclicos aromáticos (HPAs) listados como prioritários no monitoramento ambiental pela USEPA (acenafteno, acenaftileno, antraceno, benzo(a)antraceno, benzo(a)pireno, benzo(b)fluoranteno, benzo(ghi)perileno, benzo(k)fluoranteno, criseno, dibenzo(a,h)antraceno, fenantreno, fluoranteno, fluoreno, indeno(1,2,3-cd)pireno, naftaleno e pireno). Nas amostras da segunda época de coleta, além da presença de HPAs, determinou-se as concentrações de poluentes orgânicos emergentes (hormônios, produtos farmacêuticos e produtos de uso industrial), realizou-se a caracterização completa segundo a Resolução CONAMA 375/2006 (umidade, pH, N-Kjeldahl e inorgânico, carbono orgânico, cálcio, potássio, fósforo, magnésio, enxofre, boro, cobre, ferro, níquel, manganês, molibdênio, selênio, zinco, alumínio, arsênio, bário, cádmio, cromo, chumbo, mercúrio e sódio) e a caracterização da comunidade bacteriana através de metodologia independente de cultivo (sequenciamento illumina). Os macronutrientes em maiores concentrações no lodo de esgoto são: N > Ca > S > P > Mg > K. Os elementos inorgânicos Ni e Zn apresentaram concentração superior à máxima permitida para utilização agrícola pela resolução Conama 375/2006 em 1 e 3 amostras, respectivamente. A substância inorgânica que mais limita o enquadramento do lodo de esgoto como adubo orgânico (Instrução Normativa 27/2006) é o Hg. Os compostos benzilparabeno, bisfenol AF (BPAF), ácido perfluorooctanoico (PFOA) e tetrabromobisfenol A (TBBPA) não foram detectados. Por outro lado, cimetidina, metilparabeno, bisfenol A (BPA) e triclocarban foram detectados nas 19 amostras avaliadas. O composto presente em maior concentração é o triclocarban. As concentrações de hidrocarbonetos policíclicos aromáticos são baixas, de acordo com a norma Europeia. Os filos Proteobacteria e Bacteroidetes estão presentes em maior abundância relativa. Existe uma comunidade bacteriana núcleo nas estações de tratamento de esgoto do estado de São Paulo, composta por 81 gêneros, presentes nas 19 ETEs avaliadas, dos quais, os que estão em maior abundância relativa são Treponema, Clostridium, Propionibacterium, Syntrophus e Desulfobulbus. A elevação do pH a valores próximos de 12 reduz a diversidade microbiana. Considerando a abundância relativa e a composição química do lodo de esgoto, as estações podem ser agrupadas em três grupos distintos, sendo que um deles é influenciado principalmente pelos teores de Ca, Zn e Cu, o outro pelos teores de Fe e S e o terceiro grupo que foi influenciado pelos demais fatores avaliados.

Síntese e caracterização de nanomateriais superparamagnéticos do tipo core-shell para aplicação em catálise e biomedicina

As diversas aplicações tecnológicas de nanopartículas magnéticas (NPM) vêm intensificando o interesse por materiais com propriedades magnéticas diferenciadas, como magnetização de saturação (MS) intensificada e comportamento superparamagnético. Embora MNP metálicas de Fe, Co e bimetálicas de FeCo e FePt possuam altos valores de MS, sua baixa estabilidade química dificulta aplicações em escala nanométrica. Neste trabalho foram sintetizadas NPM de Fe, Co, FeCo e FePt com alta estabilidade química e rigoroso controle morfológico. NPM de óxido metálicos (Fe e Co) também foram obtidas. Dois métodos de síntese foram empregados. Usando método baseado em sistemas nanoheterogêneos (sistemas micelares ou de microemulsão inversa), foram sintetizadas NPM de Fe3O4 e Co metálico. Foram empregados surfactantes cátion-substituídos: dodecil sulfato de ferro(III) (FeDS) e dodecil sulfato de cobalto(II) (CoDS). Para a síntese das NPM, foram estudados e determinados a concentração micelar crítica do FeDS em 1-octanol (cmc = 0,90 mmol L-1) e o diagrama de fases pseudoternário para o sistema n-heptano/CoDS/n-butanol/H2O. NPM esferoidais de magnetita com3,4 nm de diâmetro e comportamento quase-paramagnético foram obtidas usando sistemas micelares de FeDS em 1-octanol. Já as NPM de Co obtidas via microemulsão inversa, apesar da larga distribuição de tamanho e baixa MS, são quimicamente estáveis e superparamagnéticas. O segundo método é baseado na decomposição térmica de complexos metálicos, pelo qual foram preparadas NPM esféricas de FePt e de óxidos metálicos (Fe3O4, FeXO1-X, (Co,Fe)XO1-X e CoFe2O4) com morfologia controlada e estabilidade química. O método não mostrou a mesma efetividade na síntese de NPM de FeAg e FeCo: a liga FeAg não foi obtida enquanto que NPM de FeCo com estabilidade química foram obtidas sem controle morfológico. NPM de Fe e FeCo foram preparadas a partir da redução térmica de NPM de Fe3O4 e CoFe2O4, as quais foram previamente recobertas com sílica. A sílica previne a sinterização inter-partículas, além de proporcionar caráter hidrofílico e biocompatibilidade ao material. As amostras reduzidas apresentaram aumento dos valores de MS (entre 21,3 e 163,9%), o qual é diretamente proporcional às dimensões das NPM. O recobrimento com sílica foi realizado via hidrólise de tetraetilortosilicato (TEOS) em sistema de microemulsão inversa. A espessura da camada de sílica foi controlada variando-se o tempo de reação e as concentrações de TEOS e de NPM, sendo então proposto um mecanismo do processo de recobrimento. Algumas amostras receberam um recobrimento adicional de TiO2 na fase anatase, para o qual foi empregado etilenoglicol como solvente e ligante para formação de glicolato de Ti como precursor. A espessura da camada de TiO2 (2-12 nm) é controlada variando as quantidades relativas entre NPM e o precursor de Ti. Ensaios de hipertermia magnética foram realizados para as amostras recobertas com sílica. Ensaios de hipertermia magnéticas mostram grande aumento da taxa de aquecimento das amostras após a redução térmica, mesmo para dispersões diluídas de NPM (0,6 a 4,5 mg mL-1). Taxas de aquecimento entre 0,3 e 3,0oC min-1 e SAR entre 37,2 e 96,3 W g-1. foram obtidos. A atividade fotocatalítica das amostras recobertas foram próximas à da fase anatase pura, com a vantagem de possuir um núcleo magnético que permite a recuperação do catalisador pela simples aplicação de campos magnéticos externos. Os resultados preliminares dos ensaios de hipertermia magnética e fotocatálise indicam um forte potencial dos materiais aqui relatados para aplicações em biomedicina e em fotocatálise.

Efeito da temperatura de revenimento sobre o grau de sensitização e resistência à corrosão por pite de aços inoxidáveis supermartensíticos contendo 13% Cr, 5% Ni, com e sem adições de Nb e Mo.

O desenvolvimento dos aços inoxidáveis Super-Martensíticos (SM) nasce da necessidade de implementar novas tecnologias, mais econômicas e amigáveis ao meio ambiente. Os aços inoxidáveis SM são uma derivação dos aços inoxidáveis martensíticos convencionais, diferenciando-se basicamente no menor teor de carbono, na adição de Ni e Mo. Foram desenvolvidos como uma alternativa para aços inoxidáveis duplex no uso de dutos para a extração de petróleo offshore em meados dos anos 90. Para que esses aços apresentem as propriedades mecânicas de resistência à tração e tenacidade é necessário que sejam realizados tratamentos de austenitização, seguido de têmpera, e de revenimento, onde, particularmente para este último, há várias opções de tempos e temperaturas. Como os tratamentos térmicos geram as propriedades mecânicas através de transformações de fase (precipitação) podem ocorrer alterações da resistência à corrosão. São conhecidos os efeitos benéficos da adição de Nb em aços inoxidáveis tradicionais. Por isso, o objetivo desta pesquisa foi estudar aços inoxidáveis SM contendo Nb. Foi pesquisada a influência da temperatura de revenimento sobre a resistência à corrosão de três aços inoxidáveis SM, os quais contêm 13% Cr, 5% Ni, 1% a 2% Mo, com e sem adições de Nb. No presente trabalho, foram denominados de SM2MoNb, SM2Mo e SM1MoNb, que representam aços com 2% Mo, 1% Mo e 0,11% Nb. Dado que os principais tipos de corrosão para aços inoxidáveis são a corrosão por pite (por cloreto) e a corrosão intergranular (sensitização), optou-se por determinar os Potenciais de Pite (Ep) e os Graus de Sensitização (GS) em função da temperatura de revenimento. Os aços passaram por recozimento a 1050°C por 48 horas, para eliminação de fase ferrita delta. Em seguida foram tratados a 1050 °C por 30 minutos, com resfriamento ao ar, para uniformização do tamanho de grão. A estrutura martensítica obtida recebeu tratamentos de revenimento em temperaturas de: 550 °C, 575 °C, 600 °C, 625 °C, 650 °C e 700 °C, por 2 horas. O GS foi medido através da técnica de reativação eletroquímica potenciodinâmica na versão ciclo duplo (DL-EPR), utilizando-se eletrólito de 1M H2SO4 + 0,01M KSCN. Para determinar o Ep foram realizados ensaios de polarização potenciodinâmica em 0,6M NaCl. Os resultados obtidos foram discutidos através das variações microestruturais encontradas. Foram empregadas técnicas de microscopia ótica (MO), microscopia eletrônica de varredura (MEV), simulação termodinâmica de fases através do programa Thermo-Calc e determinação de austenita revertida mediante difração de raios X (DRX) e ferritoscópio. A quantificação da austenita por DRX identificou que a partir de 600 °C há formação desta fase, apresentando máximo em 650 °C, e novamente diminuindo para zero a 700 °C. Por sua vez, o método do ferritoscópio detectou austenita nas condições em que a analise de DRX indicou valor nulo, sendo as mais críticas a do material temperado (sem revenimento) e do aço revenido a 700 °C. Propõe-se que tais diferenças entre os dois métodos se deve à morfologia fina da austenia retida, a qual deve estar localizada entre as agulhas de martensita. Os resultados foram discutidos em termos da precipitação de Cr23C6, Mo6C, NbC, fase Chi, austenita e ferrita, bem como das consequências do empobrecimento em Cr e Mo, gerados por tais microconstituintes. São propostos três mecanismos para explicar a sensitização: o primeiro é devido a precipitação de Cr23C6, o segundo a precipitação de fase Chi (rica em Cr e Mo) e o terceiro é devido a formação de ferrita durante o revenimento. O melhor desempenho quanto ao GS foi obtido para os revenimentos a 575 °C e 600°C, por 2 horas. Os resultados de Ep indicaram que o aço SM2MoNb, revenido a 575°C, tem o melhor desempenho quanto à resistência à corrosão por cloreto. Isso associado ao baixo GS coloca este aço, com este tratamento térmico, numa posição de destaque para aplicações onde a resistência à corrosão é um critério de seleção de material, uma vez que, segundo a literatura a temperatura de 575 °C está no intervalo de temperaturas de revenimento onde são obtidas as melhores propriedades mecânicas.

O contributo da refeição escolar para a ingestão de minerais: estudo preliminar

O almoço escolar constitui uma oportunidade importante para a aprendizagem de hábitos alimentares saudáveis, sendo as refeições escolares equilibradas associadas ao aumento da concentração dos alunos na sala de aula, melhores resultados académicos e redução do número de dias em que as crianças ficam doentes. Os minerais constituem um grupo fundamental de nutrientes, não podem ser sintetizados pelo organismo e, por isso, têm que ser fornecidos pela alimentação. Este trabalho tem como objetivo determinar a composição em minerais, de refeições escolares colhidas em escolas do 1º ciclo do ensino básico público, na região metropolitana de Lisboa, de modo a avaliar os seu contributo para a dose diária recomendada. Foram analisadas 13 refeições constituidas por: sopa, prato principal de carne ou peixe, acompanhamento, salada, sobremesa e pão de mistura. As amostras foram submetidas a uma digestão ácida por micro-ondas. Os minerais Cobre, Manganês, Ferro, Zinco, Magnésio, Cálcio, Fósforo, Sódio e Potássio, foram determinados por espectrometria de emissão atómica acoplada com plasma indutivo (ICP-OES).Entre os minerais analisados, o Sódio e Potássio foram os mais abundantes, com teores entre 190 - 268 mg/100 g e 46,9 - 193 mg/100 g, respetivamente. Verificou-se que as refeições analisadas contribuem com mais de 50% da dose diária recomendada para o Sódio e 100% da dose diária recomendada para o Potássio. Relativamente ao Cálcio e Ferro as refeições analisadas fornecem 11% e 12 % da dose diária recomendada. O almoço escolar deve fornecer os nutrientes essenciais e, simultaneamente, permitir o desenvolvimento de preferências alimentares saudáveis, variadas e equilibradas. Este estudo permitiu conhecer o perfil de minerais do almoço, servido em escolas na região metropolitana de Lisboa. Este diagnóstico da situação poderá fundamentar a elaboração de programas de intervenção em saúde e de educação alimentar.

Obtenção de Mo2C com adição de Co por reação gás-sólido em reator de leito fixo

Sulfur compounds emissions have been, on the late years, subject to more severe environmental laws due to its impact on the environment (causing the acid rain phenomena) and on human health. It has also been object of much attention from the refiners worldwide due to its relationship with equipment’s life, which is decreased by corrosion, and also with products’ quality, as the later may have its color, smell and stability altered by the presence of such compounds. Sulfur removal can be carried out by hydrotreating (HDT) which is a catalytic process. Catalysts for HDS are traditionally based on Co(Ni)-Mo(W)/Al2O3. However, in face of the increased contaminants’ content on crude oil, and stricter legislation on emissions, the development of new, more active and efficient catalysts is pressing. Carbides of refractory material have been identified as potential materials for this use. The addition of a second metal to carbides may enhance catalytic activities by increasing the density of active sites. In the present thesis Mo2C with Co addition was produced in a fixed bed reactor via gas-solid reaction of CH4 (5%) and H2(95%) with a precursor made of a mix of ammonium heptamolybdate [(NH4)6[Mo7O24].4H2O] and cobalt nitrate[Co(NO3)2.6H2O] at stoichiometric amounts. Precursors’ where analyzed by XRF, XRD, SEM and TG/DTA. Carboreduction reactions were carried out at 700 and 750°C with two cobalt compositions (2,5 and 5%). Reaction’s products were characterized by XRF, XRD, SEM, TOC, BET and laser granulometry. It was possible to obtain Mo2C with 2,5 and 5% cobalt addition as a single phase at 750°C with nanoscale crystallite sizes. At 700°C, however, both MoO2 and Mo2C phases were found by XRD. No Co containing phases were found by XRD. XRF, however, confirmed the intended Co content added. SEM images confirmed XRD data. The increase on Co content promoted a more severe agglomeration of the produced powder. The same effect was noted when the reaction temperature was increased. The powder synthesized at 750°C with 2,5% Co addition TOC analysis indicated the complete conversion from oxide material to carbide, with a 8,9% free carbon production. The powder produced at this temperature with 5% Co addition was only partially converted (86%)

Síntese de carreadores de oxigênio à base de Ni e Co para estudo do processo de Chemical Looping usando CH4 como combustível

Increasing energy demand is being met largely by fossil fuel reserves, which emit CO2, SOx gases and various other pollutants. So does the search for fuels that emit fewer pollutants and have the same energy efficiency. In this context, hydrogen (H2) has been increasingly recognized as a potential carrier of energy for the near future. This is because the H2 can be obtained by different routes and has a wide application area , in addition to having clean burning, generating only H2O as a product of combustion , and higher energy density per unit mass . The Chemical Looping Reforming process (CLR) has been extensively investigated in recent years, it is possible to regenerate the catalyst by applying cycles of reduction and oxidation. This work has as main objective to develop catalysts based on nickel and cobalt to study the reactivity of reform with chemical recycling process. The catalysts were prepared by three different methods: combustion assisted by microwave, wet impregnation and co-precipitation. All catalysts synthesized have the same amount by weight of the active phases (60% w / w). The other 40 % m/m consists in La2O3 (8% w / w), Al2O3 (30% w / w) and MgO (2%). Oxygen carriers have been named as follows: N or C, nickel or cobalt, followed by the number 3 or 6, meaning 30 to 60% of active phase in the oxide form and C, CI or CP, which means self-combustion assisted by microwave, self-combustion assisted by microwave followed by wet impregnation and co-precipitation. The oxygen carriers were then characterized by the techniques of X-ray diffraction (XRD), surface area (BET), temperature programmed reduction (TPR) and scanning electron microscopy (SEM). The characterization results showed that the different synthesis methods have led to obtaining different morphologies and structures. Redox tests using CH4 as reducing agent and sintetic air as oxidant agent was done with N6C and C6C, N6CI and C6CI and N6CP and C6CP oxygen carriers. The tests revealed different behaviors, depending on active phase and on synthesis procedure. N6C oxygen carrier produced high levels of H2. The C6CI oxygen carrier produced CO2 and H2O without carbon deposits.

Síntese e caracterização de PSFC (Pr0,5Sr0,5Fe1-xCuxO3-δ, sendo x=0,2 e x=0,4) para aplicação como catodo de células a combustível de óxido sólido

The PSFC (Pr0.5Sr0.5Fe1-xCuxO3-δ) is a new mixed oxide perovskite and has been studied and evaluated the cathode materials for intermediate temperature solid oxide fuel cells (IT-SOFCs), mainly due to its good compatibility with the electrolyte (CGO) and its high ionic conductivity and electronic in intermediate temperature. In this work, PSFC powders with two different compositions (Pr0,5Sr0,5Fe0,8Cu0,2O3- PSFC5582 and Pr0,5Sr0,5Fe0,6Cu0,4O3-PSFC5564) were synthesized by the citrate method using a new route. The powders obtained were characterized by thermal analysis (Differential Scanning Calorimetry and Thermogravimetry), and the material calcined at 800, 900 and 1000 °C for 5h were analyzed by X-ray diffractometry (XRD), with the Rietveld refinement of the diffraction data and dilatometry. PSFC5582 composite films were obtained by screen printing of powder calcined at 1000 °C. The films were deposited on substrate ceria doped with gadolinia (CGO) and then sintered at 1050 °C for 2h. The electrochemical performance of the electrodes was evaluated by impedance spectroscopy and the interface electrode/electrolyte was observed by scanning electron microscopy (SEM). The specific resistance area (ASR) was 0.44 Ω.cm² at 800 °C, slightly lower than those reported in the literature for cathodes containing cobalt. The thermal expansion coefficients of both the PSFC compositions were obtained and varied between 13 and 15 x 10-6 °C-1 , in a temperature range of 200 to 650 °C, demonstrating the good thermal compatibility of cathodes with Ce0,9Gd0,1O1,95 electrolytes (CET = 12 x 10-6 °C).

Síntese e caracterização de nanopartículas magnéticas de Co e Ni com aplicação em magneto hipertermia

Nanoparticles are importante for the study of new phenomena and for the development of new applications. Metallic magnetic nanoparticles like Cobalt and Nickel are important for their applications in nanoscience and nanotechnology. In this work, we report on the synthesis and characterization of Ni and Co nanoparticles. The nanoparticles were prepared by the modi- ed sol-gel method and were formed in the pore-network of the biopolymer quitosan. The reduction occurred in absence of H2 ux. The metallic particles and their monoxides have a face-centered- cubic structure. The metallic particles sizes ranged from 59 to 77 nm and from 19 to 50 nm for Ni and Co, respectively. Their monoxides chemically passivated the metallic cores, and after several weeks we have not observed further increase in oxidation. The synthesis method was tuned to obtain mainly the ferromagnetic phase. The system behaves like a core/shell structure with a ferromagnetic core and an antiferromagnetic shell. Exchange bias e ect was observed at temperatures below the Néel temperature. Both systems were submitted to an alternated magnetic eld and the heat released by the particles increased the temperature to 140°C in an interval of 5 min. Similar studies in samples dispersed in water increased the temperatures to 40-59°C, these results suggest that these materials are candidates for magnetic hyperthermia.

Modificação do eletrodo AWS E7018 com adição de filmes finos externos de PVC e Al, para soldagem de aço C-Mn

This paper suggests modifications in coating of electrodes providing an alternative for execution of welding with low hydrogen electrode AWS E7018 without having to dry it, reducing thus the cost and time of manufacturing of high resistance welds. The welds in this research were developed with basic coated electrodes (hygroscopic) – SMAW process – externally painted with aluminum spray paint for high temperatures or wrapped with thin plastic films (PVC) and aluminum foil films used commonly for food protection. The basic premise is that establishing a barrier between the atmosphere and the electrode coating could reduce the effects of high hygroscopicity presented by coatings of low hydrogen, minimizing this way the main source of supply of hydrogen to the fusion pool during welding. It is also expected that the addition of new materials from the electrode coating to the fusion pool would induce metallurgical changes in the deposited metal and, as a consequence, modifications in its mechanical properties. This research dealt with measuring the dissolved hydrogen in the deposited metal after welding with modified electrodes, evaluating the influence of these changes in the produced microstructures and in the mechanical properties of the resulting weld, and comparing the obtained results with the standard welding procedures and with the recently developed waterproof electrodes. The results obtained in most samples welded with modified electrodes showed increased mechanical resistance and increased tenacity due to the increased percentage of acicular ferrite in metal deposited without significant elevation of hardness, when compared with the traditional welding with AWS E7018 electrode and with ELBRÁS BRH4R waterproof electrode. The diffusing hydrogen measured in the modified electrodes was kept inside the parameters defined by international codes.

Modificação do eletrodo AWS E7018 com adição de filmes finos externos de PVC e Al, para soldagem de aço C-Mn

This paper suggests modifications in coating of electrodes providing an alternative for execution of welding with low hydrogen electrode AWS E7018 without having to dry it, reducing thus the cost and time of manufacturing of high resistance welds. The welds in this research were developed with basic coated electrodes (hygroscopic) – SMAW process – externally painted with aluminum spray paint for high temperatures or wrapped with thin plastic films (PVC) and aluminum foil films used commonly for food protection. The basic premise is that establishing a barrier between the atmosphere and the electrode coating could reduce the effects of high hygroscopicity presented by coatings of low hydrogen, minimizing this way the main source of supply of hydrogen to the fusion pool during welding. It is also expected that the addition of new materials from the electrode coating to the fusion pool would induce metallurgical changes in the deposited metal and, as a consequence, modifications in its mechanical properties. This research dealt with measuring the dissolved hydrogen in the deposited metal after welding with modified electrodes, evaluating the influence of these changes in the produced microstructures and in the mechanical properties of the resulting weld, and comparing the obtained results with the standard welding procedures and with the recently developed waterproof electrodes. The results obtained in most samples welded with modified electrodes showed increased mechanical resistance and increased tenacity due to the increased percentage of acicular ferrite in metal deposited without significant elevation of hardness, when compared with the traditional welding with AWS E7018 electrode and with ELBRÁS BRH4R waterproof electrode. The diffusing hydrogen measured in the modified electrodes was kept inside the parameters defined by international codes.

Efeito da adição de WC e Co na sinterização e propriedades mecânicas da alumina

Composites based on alumina (Al2O3), tungsten carbide (WC) and cobalt (Co) exhibit specific properties such as low density, high oxidation resistance, high melting point and high chemical inertia. That composite shows to be a promising material for application in various fields of engineering. In this work, the mechanical properties of the composite (Al2O3 – WC – Co), particularly density and hardness, were evaluated according to the effects of the variables of powder processing parameters, green compact and sintered. Powder composites with the composition of 80 wt% Al2O3, 18 wt% WC and 2 wt% Co were processed by high energy ball milling in a planetary mill for 50 hours as well as mixed by manual mixing in a glass vessel with the same proportion. Samples were collected (2, 10, 20, 30, 40 and 50 hours) during the milling process. Then, the powders were compacted in a cylindrical die with 5 mm in diameter in a uniaxial press with pressures of 200 and 400 MPa. The sintering was in two stages: first, the solid phase sintering was performed at 1126 and 1300 °C for 1 hour with a heating rate of 10 °C/min in a resistive furnace under argon atmosphere for green samples compacted in 200 and 400 MPa; the second sintering was performed on dilatometer in solid phase at 1300 °C for green sample compacted in 200 MPa, another sintering also was performed on dilatometer, this time in liquid phase at 1550 °C for green samples compacted in 200 and 400 MPa, with the same parameters used in resistive furnace. The raw materials were characterized by X – ray diffraction (XRD), X – ray fluorescence (XRF), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and laser particlemeter. The sintered samples were subjected to microhardness testing. The results showed that high energy milling achieved to the objectives regarding the particle size and the dispersion of composite phases. However, the hardness did not achieve to significant results, this is an indication that the composite has low fracture toughness.

Efeito da adição de WC e Co na sinterização e propriedades mecânicas da alumina

Composites based on alumina (Al2O3), tungsten carbide (WC) and cobalt (Co) exhibit specific properties such as low density, high oxidation resistance, high melting point and high chemical inertia. That composite shows to be a promising material for application in various fields of engineering. In this work, the mechanical properties of the composite (Al2O3 – WC – Co), particularly density and hardness, were evaluated according to the effects of the variables of powder processing parameters, green compact and sintered. Powder composites with the composition of 80 wt% Al2O3, 18 wt% WC and 2 wt% Co were processed by high energy ball milling in a planetary mill for 50 hours as well as mixed by manual mixing in a glass vessel with the same proportion. Samples were collected (2, 10, 20, 30, 40 and 50 hours) during the milling process. Then, the powders were compacted in a cylindrical die with 5 mm in diameter in a uniaxial press with pressures of 200 and 400 MPa. The sintering was in two stages: first, the solid phase sintering was performed at 1126 and 1300 °C for 1 hour with a heating rate of 10 °C/min in a resistive furnace under argon atmosphere for green samples compacted in 200 and 400 MPa; the second sintering was performed on dilatometer in solid phase at 1300 °C for green sample compacted in 200 MPa, another sintering also was performed on dilatometer, this time in liquid phase at 1550 °C for green samples compacted in 200 and 400 MPa, with the same parameters used in resistive furnace. The raw materials were characterized by X – ray diffraction (XRD), X – ray fluorescence (XRF), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and laser particlemeter. The sintered samples were subjected to microhardness testing. The results showed that high energy milling achieved to the objectives regarding the particle size and the dispersion of composite phases. However, the hardness did not achieve to significant results, this is an indication that the composite has low fracture toughness.