Electrostatic layer-by-layer deposition and electrochemical characterization of thin films composed of MnO(2) nanoparticles in a room-temperature ionic liquid

Thin films of MnO(2) nanoparticles were grown using the layer-by-layer method with poly (diallyldimetylammonium) as the intercalated layer. The film growth was followed by UV-vis, electrochemical quartz crystal microbalance (EQCM), and atomic force microscopy. Linear growth due to electrostatic immobilization of layers was observed up to 30 bilayers, but electrical connectivity was maintained only for 12 MnO(2)/PPDA bilayers. The electrochemical characterization of this film in 1-butyl-2,3-dimethyl-imidazolium (BMMI) bis(trifluoromethanesulfonyl)imide (TFSI) (BMMITFSI) with and without addition of a lithium salt indicated a higher electrochemical response of the nanostructured electrode in the lithium-containing electrolyte. On the basis of EQCM experiments, it was possible to confirm that the charge compensation process is achieved mainly by the TFSI anion at short times (<2 s) and by BMMI and lithium cations at longer times. The fact that large ions like TFSI and BMMI participate in the electroneutrality is attributed to the redox reaction that occurs at the superficial sites and to the high concentration of these species compared to that of lithium cations.

The characterisation of the protective film formed by benzotriazole on the 90/10 copper-nickel alloy surface in H2SO4 media

The nature of the protective film formed by benzotriazole (BTAH) on the surface of the 90/10 CuNi alloy in deaerated 0.5 mol L-1 H2SO4 solution containing Fe(III) ions as oxidant was investigated by weight-loss, calorimetric measurements, and by surface-enhanced Raman spectroscopy (SERS). The SERS measurements show that the protective film is composed by the [Cu(I)BTA](n), polymeric complex and that the BTAH molecules are also adsorbed on the electrode surface. A modification of the BET isotherm for adsorption of gases ill solids is proposed to describe the experimental results obtained from weight-loss experiments that suggest an adsorption in multilayers. Electrochemical studies of copper and nickel in 0.5 mol L-1 H2SO4 in presence and absence of BTAH have also been made as an aid to interpret the results. The calculated adsorption free energy of the cuprous benzotriazolate on the surface of the alloy is in accordance with the value for pure copper. (C) 2007 Elsevier Ltd. All rights reserved.

Optical changes and writing on hydrotalcite supported gold nanoparticles

Gold nanoparticles (AuNP) incorporated into hydrotalcite (HT), provide an interesting type of pigment in which temperature can modulate the plasmon resonance and the aggregation phenomenon. As inferred from microscopy techniques, the preferential binding sites are located at the border of the HT external basal surface, leading to aggregates of gold nanoparticles displaying characteristic plasmon resonance and interference bands around 520 and 700 nm, respectively. The thermally induced color changes in the HT-supported gold material arise from the competition between of nanoparticles aggregation and fusion processes, as characterized by TEM and STM. A laser beam can also induce such changes, allowing the writing of optical information on this type of material.

A New Insight on the Preparation of Stabilized Alpha-Nickel Hydroxide Nanoparticles

Nickel hydroxide can provide an outstanding cathode material in alkaline secondary batteries, however the progressive decrease of the charge capacity as a function of the number of oxidation/reduction cycles is a challenging problem to be solved. New improvements on the electrochemical properties of electrode materials can be achieved by exploiting the much better performance of alpha-nickel hydroxide. Such materials were obtained in a stable form by sol-gel method and characterized by thermogravimetric analyses, UV-Vis spectroscopy, X-ray diffractometry, scanning and transmission electron microscopy, cyclic voltammetry and electrochemical quartz crystal microbalance techniques. The results revealed not only the formation of the alpha-Ni(OH)(2) phase, but also a much better electrochemical reversibility and stability as compared with similar materials obtained by electrochemical precipitation method.

Catalytic properties of thioredoxin immobilized on superparamagnetic nanoparticles

Thioredoxin (Trx1), a very important protein for regulating intracellular redox reactions, was immobilized on iron oxide superparamagnetic nanoparticles previously coated with 3-aminopropyltriethoxysilane (APTS) via covalent coupling using the EDC (1-ethyl-3-{3-dimethylaminopropyl}carbodiimide) method. The system was extensively characterized by atomic force microscopy, vibrational and magnetic techniques. In addition, gold nanoparticles were also employed to probe the exposed groups in the immobilized enzyme based on the SERS (surface enhanced Raman scattering) effect, confirming the accessibility of the cysteines residues at the catalytic site. For the single coated superparamagnetic nanoparticle, by monitoring the enzyme activity with the Ellman reagent, DTNB=5,5`-dithio-bis(2-15 nitrobenzoic acid), an inhibitory effect was observed after the first catalytic cycle. The inhibiting effect disappeared after the application of an additional silicate coating before the AFTS treatment, reflecting a possible influence of unprotected iron-oxide sites in the redox kinetics. In contrast, the doubly coated system exhibited a normal in-vitro kinetic activity, allowing a good enzyme recovery and recyclability. (C) 2011 Elsevier Inc. All rights reserved.

New insights on surface-enhanced Raman scattering based on controlled aggregation and spectroscopic studies, DFT calculations and symmetry analysis for 3,6-bi-2-pyridyl-1,2,4,5-tetrazine adsorbed onto citrate-stabilized gold nanoparticles

Asystematic study on the surface-enhanced Raman scattering (SERS) for 3,6-bi-2-pyridyl-1,2,4,5-tetrazine (bptz) adsorbed onto citrate-modified gold nanoparticles (cit-AuNps) was carried out based on electronic and vibrational spectroscopy and density functional methods. The citrate/bptz exchange was carefully controlled by the stepwise addition of bptz to the cit-AuNps, inducing flocculation and leading to the rise of a characteristic plasmon coupling band in the visible region. Such stepwise procedure led to a uniform decrease of the citrate SERS signals and to the rise of characteristic peaks of bptz, consistent with surface binding via the N heterocyclic atoms. In contrast, single addition of a large amount of bptz promoted complete aggregation of the nanoparticles, leading to a strong enhancement of the SERS signals. In this case, from the distinct Raman profiles involved, the formation of a new SERS environment became apparent, conjugating the influence of the local hot spots and charge-transfer (CT) effects. The most strongly enhanced vibrations belong to a(1) and b(2) representations, and were interpreted in terms of the electromagnetic and the CT mechanisms: the latter involving significant contribution of vibronic coupling in the system. Copyright (C) 2010 John Wiley & Sons, Ltd.

Biolabeling with nanoparticles based on Y(2)O(3):Nd(3+) and luminescence detection in the near-infrared

Neodymium based fluorescence presents several advantages in comparison to conventional rare earth or enzyme-substrate based fluorescence emitting sources (e.g.Tb, HRP). Based on this fact we have herein explored a Nd-based fluoroimmunoassay. We efficiently detected the presence of an oxidized low-density lipoprotein (oxLDL) in human plasma a well-known marker for cardiovascular diseases, which causes around 30% of deaths worldwide. Conventional fluoroimmunoassay uses time-resolved luminescence techniques, with detection in the visible range, to eliminate the fluorescence background from the biological specimens. By using an immunoassay based on functionalized Y(2)O(3):Nd(3+) nanoparticles, where the excitation and emission processes in the Nd(3+) ion occur in the near-infrared (NIR) region, we have succeeded in eliminating the interferences from the biological fluorescence background, avoiding the use of time-resolved techniques. This yields higher emission intensity from the Nd(3+)-nanolabels and efficient detection of anti-oxidized low-density lipoproteins (anti-oxLDL) by Y(2)O(3):Nd(3+)-antibody-antigen conjugation, leading to a novel biolabeling method. (C) 2010 Elsevier B.V. All rights reserved.

Ex Situ Scanning Electrochemical Microscopy (SECM) Investigation of Bismuth- and Bismuth/Lead Alloy Film-Modified Gold Electrodes in Alkaline Medium

Scanning electrochemical microscopy (SECM) in feedback mode was employed to characterise the reactivity and microscopic peculiarities of bismuth and bismuth/lead alloys plated onto gold disk substrates in 0.1 molL(-1) NaOH solutions. Methyl viologen was used as redox mediator, while a platinum microelectrode was employed as the SECM tip. The metal films were electrodeposited ex situ from NaOH solutions containing either bismuth ions only or both bismuth and lead ions. Approach curves and SECM images indicated that the metal films were conductive and locally reactive with oxygen to provide Bi(3+) and Pb(2+) ions. The occurrence of the latter chemical reactions was verified by local anodic stripping voltammetry (ASV) at the substrate solution interface by using a mercury-coated platinum SECM tip. The latter types of measurements allowed also verifying that lead was not uniformly distributed onto the bismuth film electrode substrate. These findings were confirmed by scanning electron microscopy images. The surface heterogeneity produced during the metal deposition process, however, did not affect the analytical performance of the bismuth coated gold electrode in anodic stripping voltammetry for the determination of lead in alkaline media, even in aerated aqueous solutions. Under the latter conditions, stripping peak currents proportional to lead concentration with a satisfactory reproducibility (within 5% RSD) were obtained.

Magnetic coupled electrochemistry: Exploring the use of superparamagnetic nanoparticles for capturing, transporting and concentrating trace amounts of analytes

We propose the use of functionalized superparamagnetic nanoparticles for capturing, and transporting analytes, in association with an external miniature magnet to deposit such nanocarrier species at the electrode surface. This approach can be employed for the electroanalytical determination of chemical species capable of interacting with the nanoparticles, or in the opposite case, to block their response at the electrode surface. The concept was successfully demonstrated by using aminofunctionalized nanoparticles to block the discharge of hexacyanoferrate(II) ions, and to enhance the signals of aquapentacyanoferrate(II) ions via coordination to the surface amino groups. Selective analysis was also performed for silver ions, surpassing the stripping methods in terms of versatility and usefulness. (C) 2010 Elsevier B.V. All rights reserved.

Ligand-Assisted Preparation of Palladium Supported Nanoparticles: a Step toward Size Control

Supported nanoparticles (SNPs) with narrow size distribution were prepared by H(2) reduction of Pd(2+) previously bound, to ligand-modified silica surfaces. Interestingly, the size of the Pd SNPs was tuned by the ligand grafted on the support surface. Amino- and ethylenediamino-functionalized supports formed Pd(0) SNPs of ca. 6 and 1 nm, respectively. The catalytic properties of both Pd(0) SNPs were investigated.

Effect of mechanical coating with Ni and Ni-5% Al on the structure and electrochemical properties of the Mg-50% Ni alloy

The Mg-Ni metastable alloys (with amorphous or nanocrystalline structures) are promising candidates for anode application in nickel-metal hydride rechargeable batteries due to its large hydrogen absorbing capacity, low weight, availability, and relative low price. In spite of these interesting features, improvement on the cycle life performance must be achieved to allow its application in commercial products. In the present paper, the effect of mechanical coating of a Mg-50 at.% Ni alloy with Ni and Ni-5 at.% Al on the structure, powder morphology, and electrochemical properties is investigated. The coating additives, Mg-Ni alloy and resulting nanocomposites (i.e., Mg-Ni alloy + additive) were investigated by means of X-ray diffraction and scanning electron microscopy. The Mg-Ni alloy and nanocomposites were submitted to galvanostatic cycles of charge and discharge to evaluate their electrode performances. The mechanical coating with Ni and Ni-5% Al increased the maximum discharge capacity of the Mg-Ni alloy from of 221 to 257 and 273 mA h g(-1), respectively. Improvement on the cycle life performance was also achieved by mechanical coating.

Study of ethanol electro-oxidation in acid environment on Pt(3)Sn/C anode catalysts prepared by a modified polymeric precursor method under controlled synthesis conditions

A carbon-supported binary Pt(3)Sn catalyst has been prepared using a modified polymeric precursor method under controlled synthesis conditions This material was characterized using X-ray diffraction (XRD). and the results indicate that 23% (of a possible 25%) of Sn is alloyed with Pt, forming a dominant Pt(3)Sn phase. Transmission election microscopy (TEM) shows good dispersion of the electrocatalyst and small particle sizes (3 6 nm +/- 1 nm) The polarization curves for a direct ethanol fuel cell using Pt(3)Sn/C as the anode demonstrated Improved performance compared to that of a PtSn/C E-TEK. especially in the intrinsic resistance-controlled and mass transfer regions. This behavior is probably associated with the Pt(3)Sn phase. The maximum power density for the Pt(3)Sn/C electrocatalyst (58 mW cm(-2)) is nearly twice that of a PtSn/C E-TEK electrocatalyst (33 mW cm(-2)) This behavior is attributed to the presence of a mixed Pt(9)Sn and Pt(3)Sn alloy phase in the commercial catalysts (C) 2009 Elsevier B V All rights reserved

Electrochemical Behaviour of the AA2024 Aluminium Alloy Modified with Self-Assembled Monolayers/Polyaniline Double Films

The electrochemical characteristics of the AA2024 aluminium alloy modified with octadecyltrimethoxysilane (ODTMS) + polyaniline (PANi) and propiltrimethoxysilane (PTMS) + (PANi) were studied in the present work. The results show that the different protective coatings shift the values of corrosion and pit potentials to more positive values making the system nobler and indicate that the double film ODTMS + PANi present the best protection against corrosion characteristics, that is probably due to the two contributions: anodic protection associated with the barrier effect.

The origin of the molecular interaction between amino acids and gold nanoparticles: A theoretical and experimental investigation

This study describes the synthesis of novel biological hybrid materials, where 3D structures were obtained using gold nanoparticles (AuNps) and methionine (Met) in a one-step procedure in aqueous media. The type of nanostructure can be controlled by tuning the intermolecular interactions between Met and AuNp, which strongly depends on the pH used for the synthesis. Computational simulation using the density-functional theory (DFT) showed that the AuNp - Met 3D structures are formed upon reorientation of Met molecules so that the backbone amine groups interact via H-bonds. These findings were experimentally confirmed using FTIR and UV-vis spectroscopy. Crown Copyright (C) 2008 Published by Elsevier B. V. All rights reserved.

Formation Mechanism via a Heterocoagulation Approach of FePt Nanoparticles Using the Modified Polyol Process

Herein, we report a new approach of an FePt nanoparticle formation mechanism studying the evolution of particle size and composition during the synthesis using the modified polyol process. One of the factors limiting their application in ultra-high-density magnetic storage media is the particle-to-particle composition, which affects the A1-to-L1(0) transformation as well as their magnetic properties. There are many controversies in the literature concerning the mechanism of the FePt formation, which seems to be the key to understanding the compositional chemical distribution. Our results convincingly show that, initially, Pt nuclei are formed due to reduction of Pt(acac)(2) by the diol, followed by heterocoagulation of Fe cluster species formed from Fe(acac)(3) thermal decomposition onto the Pt nuclei. Complete reduction of heterocoagulated iron species seems to involve a CO-spillover process, in which the Pt nuclei surface acts as a heterogeneous catalyst, leading to the improvement of the single-particle composition control and allowing a much narrower compositional distribution. Our results show significant decreases in the particle-to-particle composition range, improving the A1-to-L1(0) phase transformation and, consequently, the magnetic properties when compared with other reported methods.