Color degradation of acrylic resin denture teeth as a function of liquid diet: ultraviolet-visible reflection analysis

The effect of different beverages on acrylic resin denture teeth color degradation is evaluated. Ten acrylic resin denture teeth brands were evaluated: Art Plus (AP), Biolux (BX), Biotone IPN (BI), Magister (MG), Mondial 6 (MD), Premium 6 (PR), SR Vivodent PE (SR), Trilux (TR), Trubyte Biotone (TB), and Vipi Dent Plus (VP). Teeth were immersed in staining solutions (coffee, cola, and orange juice) or artificial saliva (control) (n = 6) for 1, 7, 15, or 30 days. Specimen colors were evaluated spectrophotometrically based on the Commission Internationale d'Eclairage L*a*b* system. Color differences (Delta E) were calculated between the baseline and post-staining results. Data were evaluated by analysis of variance and Tukey test (alpha = 0.05). BI (1.82 +/- 0.95) and TR (1.78 +/- 0.72) teeth exhibited the greatest Delta E values, while BX (0.88 +/- 0.43) and MD (1.09 +/- 0.44) teeth were the lowest, regardless of solution and measurement period, and were different from BI and TR teeth (P < 0.05). Cola and coffee promoted higher denture teeth color alterations than orange juice and saliva (P < 0.05). Saliva generated the lowest denture teeth color alterations. Greater immersion times caused higher denture teeth color changes. The lifespan of removable dentures and the aesthetic satisfaction of several edentulous patients may be increased with the use of stain-resistant artificial denture teeth. (C) The Authors.

Exposed Collagen In Resin Bonds to Caries-affected Dentin After Dentin Treatment with Aqueous and Alcoholic Chlorhexidine Solutions

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Adhesive bonding of resin composite to various titanium surfaces using diferente metal conditioners and a surface modification system

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Efficacy of Surface Treatments on the Bond Strength of Resin Cements to Two Brands of Zirconia Ceramic

Purpose: To compare the shear bond strength (SBS) of two cements to two Y-TZP ceramics subjected to different surface treatments.Materials and Methods: Zirconia specimens were made from Lava (n = 36) and IPS e.max ZirCAD (n = 36), and their surfaces were treated as follows: no treatment (control), silica coating with 30-mu m silica-modified alumina (Al2O3) particles (CoJet Sand), or coating with liners Lava Ceram for Lava and Intensive ZirLiner for IPS e.max ZirCAD. Composite resin cylinders were bonded to zirconia with Panavia F or RelyX Unicem resin cements. All specimens were thermocycled (6000 cycles at 5 degrees C/55 degrees C) and subjected to SBS testing. Data were analyzed by post-hoc test Tamhane T2 and Scheffe tests (alpha = 0.05). Failure mode was analyzed by stereomicroscope and SEM.Results: With both zirconia brands, CoJet Sand showed significantly higher SBS values than control groups only when used with RelyX Unicem (p = 0.0001). Surface treatment with liners gave higher SBS than control groups with both ceramic brands and cements (p < 0.001). With both zirconia brands, the highest SBS values were obtained with the CoJet and RelyX Unicem combination (> 13.47 MPa). Panavia F cement showed significantly better results when coupled with liner surface treatment rather than with CoJet (p = 0.0001, SBS > 12.23 MPa). In untreated controls, Panavia F showed higher bond strength than RelyX Unicem; the difference was significant (p = 0.016) in IPS e.max ZirCAD. The nontreated specimens and those treated with CoJet Sand exhibited a high percentage of adhesive and mixed A (primarily adhesive) failures, while the specimens treated with liners presented an increase in mixed A and mixed C (primarily cohesive) failures as well as some cohesive failure in the bulk of Lava Ceram for both cements.Conclusion: CoJet Sand and liner application effectively improved the SBS between zirconia and luting cements. This study suggests that different interactions between surface treatments and luting cements yield different SBS: in clinical practice, these interactions should be considered when combining luting cements with surface treatments in order to obtain the maximum bond strength to zirconia restorations.

In vitro evaluation of adherence of Candida albicans, Candida glabrata, and Streptococcus mutans to an acrylic resin modified by experimental coatings

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Evaluation of bond strength and thickness of adhesive layer according to the techniques of applying adhesives in composite resin restorations

Adhesive restorations have increasingly been used in dentistry, and the adhesive system application technique may determine the success of the restorative procedure. The aim of this study was to evaluate the influence of the application technique of two adhesive systems (Clearfil SE Bond and Adper Scotchbond MultiPurpose) on the bond strength and adhesive layer of composite resin restorations. Eight human third molars were selected and prepared with Class I occlusal cavities. The teeth were restored with composite using various application techniques for both adhesives, according to the following groups (n = 10): group 1 (control), systems were applied and adhesive was immediately light activated for 20 seconds without removing excesses; group 2, excess adhesive was removed with a gentle jet of air for 5 seconds; group 3, excess was removed with a dry microbrush-type device; and group 4, a gentle jet of air was applied after the microbrush and then light activation was performed. After this, the teeth were submitted to microtensile testing. For the two systems tested, no statistical differences were observed between groups 1 and 2. Groups 3 and 4 presented higher bond strength values compared with the other studied groups, allowing the conclusion that excess adhesive removal with a dry micro-brush could improve bond strength in composite restorations. Predominance of adhesive fracture and thicker adhesive layer were observed via scanning electron microscopy (SEM) in groups 1 and 2. For groups 3 and 4, a mixed failure pattern and thinner adhesive layer were verified. Clinicians should be aware that excess adhesive may negatively affect bond strength, whereas a thin, uniform adhesive layer appears to be favorable. (Quintessence Int 2013;44:9-15)

Evaluation of Resin Bond Strength to Yttria-stabilized Tetragonal Zirconia and Framework Marginal Fit: Comparison of Different Surface Conditionings

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Adhesion of substrate-adherent combinations for early composite repairs: Effect of intermediate adhesive resin application

This study evaluated the effect of intermediate adhesive resin application (IAR) on tensile bond strength (TBS) for early composite repairs in situations where substrate and repair composite bonded together were once of the same kind with the substrate (similar) and once other than the substrate material (dissimilar). Specimens from three types of composites (TPH Spectrum (TPH), Charisma (CHA) and Filtek Z250 (Z250)) were fabricated. The specimens in each composite group (n=72) were randomly divided into six subgroups (n=12). In each composite group, the similar and two dissimilar composites were bonded onto the substrates once using an IAR (Adper Single Bond Plus) and once without. After water storage for I week at 37 degrees C, substrate-adherent combinations were submitted to tensile test. Data were analyzed with three-way ANOVA and Tukey's tests (alpha=0.05). The substrate-adherent combination (p=0.0001), adherent (repair) composite (p=0.0001), and application of IAR (p=0.0001) significantly affected the results. Utilization of IAR improved the repair bond strength for all composite combinations. (C) 2013 Elsevier Ltd. All rights reserved.

Bond Strength of Different Resin Cement and Ceramic Shades Bonded to Dentin

Purpose: To evaluate the microtensile bond strength (MTBS) of ceramic cemented to dentin varying the resin cement and ceramic shades.Materials and Methods: Two VITA VM7 ceramic shades (Base Dentine 0M1 and Base Dentine 5M3) were used. A spectrophotometer was used to determine the percentage translucency of ceramic (thickness: 2.5 mm). For the MTBS test, 80 molar dentin surfaces were etched and an adhesive was applied. Forty blocks (7.2 x 7.2 x 2.5 mm) of each ceramic shade were produced and the ceramic surface was etched (10% hydrofluoric acid) for 60 s, followed by the application of silane and resin cement (A3 yellow and transparent). The blocks were cemented to dentin using either A3 or transparent cement. Specimens were photoactivated for 20 s or 40 s, stored in distilled water (37 degrees C/24 h), and sectioned. Eight experimental groups were obtained (n = 10). Specimens were tested for MTSB using a universal testing machine. Data were statistically analyzed using ANOVA and Tukey's post-hoc tests (alpha <= 0.05).Results: The percentage translucency of 0M1 and 5M3 ceramics were 10.06 (+/- 0.25)% and 1.34 (+/- 0.02)%, respectively. The lowest MTBS was observed for the ceramic shade 5M3. For the 0M1 ceramic, the A3 yellow cement that was photocured for 20 s exhibited the lowest MTBS, while the transparent cement that was photocured for 40 s presented the highest MTBS.Conclusions: For the 2.5-mm-thick 5M3 ceramic restorations, the MTBS of ceramic cemented to dentin significantly increased. The dual-curing cement Variolink II photocured for 40 s is not recommended for cementing the Base Dentine 5M3 feldspathic ceramic to dentin.

Can Heat Treatment Procedures of Pre-hydrolyzed Silane Replace Hydrofluoric Acid in the Adhesion of Resin Cement to Feldspathic Ceramic?

Purpose: To evaluate the influence of heat treatment (HT) procedures of a pre-hydrolyzed silane on bond strength of resin cement to a feldspathic ceramic.Materials and Methods: Ceramic and composite blocks (N = 30) were divided into six groups (n = 5) and subjected to the following conditioning procedures: G1: 9.6% hydrofluoric acid (HF) for 20 s + silane (RelyX Ceramic Primer, 3M ESPE) + resin cement (Panavia F2.0, Kuraray) (control); G2: HF (20 s) + silane + heat treatment in furnace (HTF) (100 degrees C, 2 min) + resin cement; G3: silane + HTF + resin cement; G4-HF (20 s) + silane + heat treatment with hot air (HTA) (50 +/- 5 degrees C for 1 min) + resin cement; G5: silane + HTA + resin cement; G6: silane + resin cement. The microtensile bond strength (MTBS) test was performed using a universal testing machine (1 mm/min). After debonding, the substrate and adherent surfaces were analyzed using a stereomicroscope and SEM to categorize the failure types. The data were statistically evaluated using one-way ANOVA and Tukey's test (5%).Results: The control group (G1) showed no pre-test failures and presented significantly higher mean MTBS (16.01 +/- 1.12 MPa) than did other groups (2.63 +/- 1.05 to 12.55 +/- 1.52 MPa) (p = 0.0001). In the groups where HF was not used, HTF (G3: 12.55 +/- 1.52 MPa) showed significantly higher MTBS than did HTA (G5: 2.63 +/- 1.05 MPa) (p < 0.05). All failure types were mixed, ie, adhesive between the resin cement and ceramic accompanied by cohesive failure in the cement.Conclusion: Heat treatment procedures for the pre-hydrolyzed silane either in a furnace or with the application of hot air cannot replace the use of HF gel for the adhesion of resin cement to feldspathic ceramic. Yet when mean bond strengths and incidence of pre-test failures are considered, furnace heat treatment delivered the second best results after the control group, being considerably better than hot air application.

Effect of Post-silanization Heat Treatments of Silanized Feldspathic Ceramic on Adhesion to Resin Cement

Purpose: To evaluate the effect of post-silanization heat treatment of a silane agent and rinsing with hot water of silanized CAD/CAM feldspathic ceramic surfaces on the microtensile bond strength between resin cement and the ceramic, before and after mechanical cycling.Materials and Methods: Blocks measuring 10 x 5.7 x 3.25 mm(3) were produced from feldspathic ceramic cubes (VITA Mark II, VITA Zanhfabrik). Each ceramic block was duplicated in composite resin using a template made of polyvinylsiloxane impression material. Afterwards, ceramic and corresponding resin composite blocks were ultrasonically cleaned and randomly divided according to the 5 strategies used for conditioning the ceramic surface (n = 10): GHF: etching with hydrofluoric acid 10% + rinsing with water at room temperature + silanization at 20 degrees C; G20: silanization; G77: silanization + oven drying at 77 degrees C; G20r: silanization + hot water rinsing; G77r: silanization + oven drying at 77 C + hot water rinsing. The resin and ceramic blocks were cemented using a dual-curing resin cement. Every group was divided in two subgroups: aging condition (mechanical cycling, designated as a) or non-aging (designated as n). All the bonded assemblies were sectioned into microsticks for microtensile bond strength (mu TBS) testing. The failure mode of the tested specimens was assessed and mu TBS data were statistically analyzed in two ways: first 2-way ANOVA (GHF, G20 and G77 in non-aging/aging conditions) and 3-way ANOVA (temperature x rinsing x aging factors, excluding GHF), followed by Tukey's test (p = 0.05).Results: The 2-way ANOVA revealed that the mu TBS was significantly affected by the surface treatment (p < 0.001) but not by aging (p = 0.68), and Tukey's test showed that G77-n/G77-a (18.0 MPa) > GHF-n/GHF-a (12.2 MPa) > G20-n/G20-a (9.1 MPa). The 3-way ANOVA revealed that the mu TBS was significantly affected by the heat treatment and rinsing factors (p < 0.001), but not affected by aging (p = 0.36). The rinsing procedure decreased, while oven drying increased the bond strengths. Group G77, in both non-aging and aging conditions (18.6-17.4 MPa), had the highest bond values. Failure modes were mainly mixed for all groups.Conclusion: Oven drying at 77 degrees C improved the bond strength between the resin cement and feldspathic ceramic, but hot water rinsing reduced the bond strength and should not be recommended.

Effect of Resin Cement Type on the Microtensile Bond Strength to Lithium Disilicate Ceramic and Dentin Using Different Test Assemblies

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Effect of Surface Conditioning Modalities on the Repair Bond Strength of Resin Composite to the Zirconia Core / Veneering Ceramic Complex

Purpose: This study evaluated the effect of different surface conditioning protocols on the repair strength of resin composite to the zirconia core / veneering ceramic complex, simulating the clinical chipping phenomenon.Materials and Methods: Forty disk-shaped zirconia core (Lava Zirconia, 3M ESPE) (diameter: 3 mm) specimens were veneered circumferentially with a feldspathic veneering ceramic (VM7, Vita Zahnfabrik) (thickness: 2 mm) using a split metal mold. They were then embedded in autopolymerizing acrylic with the bonding surfaces exposed. Specimens were randomly assigned to one of the following surface conditioning protocols (n = 10 per group): group 1, veneer: 4% hydrofluoric acid (HF) (Porcelain Etch) + core: aluminum trioxide (50-mu m Al2O3) + core + veneer: silane (ESPE-Sil); group 2: core: Al2O3 (50 mu m) + veneer: HF + core + veneer: silane; group 3: veneer: HF + core: 30 mu m aluminum trioxide particles coated with silica (30 mu m SiO2) + core + veneer: silane; group 4: core: 30 mu m SiO2 + veneer: HF + core + veneer: silane. Core and veneer ceramic were conditioned individually but no attempt was made to avoid cross contamination of conditioning, simulating the clinical intraoral repair situation. Adhesive resin (VisioBond) was applied to both the core and the veneer ceramic, and resin composite (Quadrant Posterior) was bonded onto both substrates using polyethylene molds and photopolymerized. After thermocycling (6000 cycles, 5 degrees C-55 degrees C), the specimens were subjected to shear bond testing using a universal testing machine (1 mm/min). Failure modes were identified using an optical microscope, and scanning electron microscope images were obtained. Bond strength data (MPa) were analyzed statistically using the non-parametric Kruskal-Wallis test followed by the Wilcoxon rank-sum test and the Bonferroni Holm correction (alpha = 0.05).Results: Group 3 demonstrated significantly higher values (MPa) (8.6 +/- 2.7) than those of the other groups (3.2 +/- 3.1, 3.2 +/- 3, and 3.1 +/- 3.5 for groups 1, 2, and 4, respectively) (p < 0.001). All groups showed exclusively adhesive failure between the repair resin and the core zirconia. The incidence of cohesive failure in the ceramic was highest in group 3 (8 out of 10) compared to the other groups (0/10, 2/10, and 2/10, in groups 1, 2, and 4, respectively). SEM images showed that air abrasion on the zirconia core only also impinged on the veneering ceramic where the etching pattern was affected.Conclusion: Etching the veneer ceramic with HF gel and silica coating of the zirconia core followed by silanization of both substrates could be advised for the repair of the zirconia core / veneering ceramic complex.

Effect of the Etching Duration and Ultrasonic Cleaning on Microtensile Bond Strength Between Feldspathic Ceramic and Resin Cement

This study assessed the effect of different etching durations of feldspathic ceramic with hydrofluoric acid (HF) and ultrasonic cleaning of the etched ceramic surface on the microtensile bond strength stability of resin to a feldspathic ceramic. The research hypotheses investigated were: (1) different etching times would not affect the adhesion resistance and (2) ultrasonic cleaning would improve the adhesion. Ceramic blocks (6 x 6 x 5 mm) (N = 48) were obtained. The cementations surfaces were duplicated in resin composite. The six study groups (n = 8) were: G1Etching with 10% aqueous HF (30 s) + silane; G 210% HF (1 min) + silane; G3-10% HF (2 min) + silane; G4-10% HF (30 s) + ultrasonic cleaning (4 min) in distilled water + silane; G5-10% HF (1 min) + ultrasonic cleaning + silane; G6-10% HF (2 min) ultrasonic cleaning + silane. The cemented blocks were sectioned into microbars for the microtensile test. The etching duration did not create significant difference among the groups (p = .156) but significant influence of ultrasonic cleaning was observed (p = .001) (Two-way ANOVA and Tukey's test, p > 0.05). All the groups after ultrasonic cleaning presented higher bond strength (19.38-20.08 MPa) when compared with the groups without ultrasonic cleaning (16.2117.75 MPa). The bond strength between feldspathic ceramic and resin cement was not affected by different etching durations using HF. Ultrasonic cleaning increased the bond strength between ceramic surface and resin cement, regardless of the etching duration.

Influence of air-particle deposition protocols on the surface topography and adhesion of resin cement to zirconia

Objectives: This study evaluated the influence of air-particle abrasion protocols on the surface roughness (SR) of zirconia and the shear bond strength (SBS) of dual-polymerized resin cement to this ceramic. Materials and methods. Sintered zirconia blocks (n = 115) (Lava, 3M ESPE) were embedded in acrylic resin and polished. The specimens were divided according to the 'particle type' (Al: 110 mu m Al2O3; Si: 110 mu m SiO2) and 'pressure' factors (2.5 or 3.5 bar) (n = 3 per group): (a) Control (no air-abrasion); (b) Al2.5; (c) Si2.5; (d) Al3.5; (e) Si3.5. SR (Ra) was measured 3-times from each specimen after 20 s of air-abrasion (distance: 10 mm) using a digital optical profilometer. Surface topography was evaluated under SEM analyses. For the SBS test, 'particle type', 'pressure' and 'thermocycling' (TC) factors were considered (n = 10; n = 10 per group): Control (no air-abrasion); Al2.5; Si2.5; Al3.5; Si3.5; Control(TC); Al2.5(TC); Si2.5(TC); Al3.5(TC); Si3.5(TC). After silane application, resin cement (Panavia F2.0) was bonded and polymerized. Specimens were thermocycled (6.000 cycles, 5-55 degrees C) and subjected to SBS (1 mm/min). Data were analyzed using ANOVA, Tukey's and Dunnett tests (5%). Results. 'Particle' (p = 0.0001) and 'pressure' (p = 0.0001) factors significantly affected the SR. All protocols significantly increased the SR (Al2.5: 0.45 +/- 0.02; Si2.5: 0.39 +/- 0.01; Al3.5: 0.80 +/- 0.01; Si3.5: 0.64 +/- 0.01 mu m) compared to the control group (0.16 +/- 0.01 mu m). For SBS, only 'particle' factor significantly affected the results (p = 0.015). The SiO2 groups presented significantly higher SBS results than Al2O3 (Al2.5: 4.78 +/- 1.86; Si2.5: 7.17 +/- 2.62; Al3.5: 4.97 +/- 3.74; Si3.5: 9.14 +/- 4.09 MPa) and the control group (3.67 +/- 3.0 MPa). All TC specimens presented spontaneous debondings. SEM analysis showed that Al2O3 created damage in zirconia in the form of grooves, different from those observed with SiO2 groups. Conclusions. Air-abrasion with 110 mu m Al2O3 resulted in higher roughness, but air-abrasion protocols with SiO2 promoted better adhesion.