Surface integrity analysis when milling ultrafine-grained steels

This paper quantifies the effects of milling conditions on surface integrity of ultrafine-grained steels. Cutting speed, feed rate and depth of cut were related to microhardness and microstructure of the workpiece beneath machined surface. Low-carbon alloyed steel with 10.8 µm (as-received) and 1.7 µm (ultrafine) grain sizes were end milled using the down-milling and dry condition in a CNC machining center. The results show ultrafine-grained workpiece preserves its surface integrity against cutting parameters more than the as-received material. Cutting speed increases the microhardness while depth of cut deepens the hardened layer of the as-received material. Also, deformations of microstructure following feed rate direction were observed in workpiece subsurface.

Influence of the substitutional solute on the mechanical properties of Ti-Nb binary alloys for biomedical use

Titanium alloys are widely used in the manufacture of biomedical implants because they possess an excellent combination of physical properties and outstanding biocompatibility. Today, the most widely used alloy is Ti-6Al-4V, but some studies have reported adverse effects with the long-term presence of Al and V in the body, without mentioning that the elasticity modulus value of this alloy is far superior to the bone. Thus, there is a need to develop new Ti-based alloys without Al and V that have a lower modulus, greater biocompatibility, and similar mechanical strength. In this paper, we investigated the effect of Nb as a substitutional solute on the mechanical properties of Ti-Nb alloys, prepared in an arc-melting furnace and characterized by density, X-ray diffraction, optical microscopy, hardness and elasticity modulus measurements. The X-ray and microscopy measurements show a predominance of the α phase. The microhardness values showed a tendency to increase with the concentration of niobium in the alloy. Regarding the elasticity modulus, it was observed a nonlinear behavior with respect to the concentration of niobium. This behavior is associated with the presence of the α phase.

Properties of experimental resins based on synthesized propoxylated bis-GMA with different propionaldehyde ratios

The effect of different propionaldehyde ratios on the properties of bis-GMA-based comonomers and copolymers diluted with propoxylated bis-GMA (CH3bis-GMA) was evaluated. Five experimental comonomers were prepared combining bis-GMA with CH3bis-GMA and propionaldehyde at 0, 2, 8, 16, 24 mol%. Light polymerization was effected with the use of 0.2 wt. (%) each of camphorquinone and N,N-dimethyl-p-toluidine. Resin degrees of conversion (%DC) were evaluated by FT-IR spectrophotometry and Tg by Differential Scanning Calorimeter. Complex viscosity (η*), the effect of temperature on η*, and Microhardness (H) for dry and wet samples were also determined. Data were analyzed by Student's t-test, one-way ANOVA and Tukey-Kramer test (α = 0.05). The group with 24 mol% additive had a significant increase in %DC and H, and the lowest comonomer Tg and η*. No remarkable variation was noted in copolymers Tg s. All resins presented Newtonian behavior of viscosity, which linearly decreased with increased temperature. The η* decreased sigmoidally as the additive ratio increased.

Influence of HSM cutting parameters on the surface integrity characteristics of hardened AISI H13 steel

The purpose of this study is to evaluate the influence of the cutting parameters of high-speed machining milling on the characteristics of the surface integrity of hardened AISI H13 steel. High-speed machining has been used intensively in the mold and dies industry. The cutting parameters used as input variables were cutting speed (v c), depth of cut (a p), working engagement (a e) and feed per tooth (f z ), while the output variables were three-dimensional (3D) workpiece roughness parameters, surface and cross section microhardness, residual stress and white layer thickness. The subsurface layers were examined by scanning electron and optical microscopy. Cross section hardness was measured with an instrumented microhardness tester. Residual stress was measured by the X-ray diffraction method. From a statistical standpoint (the main effects of the input parameters were evaluated by analysis of variance), working engagement (a e) was the cutting parameter that exerted the strongest effect on most of the 3D roughness parameters. Feed per tooth (f z ) was the most important cutting parameter in cavity formation. Cutting speed (v c) and depth of cut (a p) did not significantly affect the 3D roughness parameters. Cutting speed showed the strongest influence on residual stress, while depth of cut exerted the strongest effect on the formation of white layer and on the increase in surface hardness.

Impact of acquired enamel pellicle modification on initial dental erosion

The acquired enamel pellicle that forms on the tooth surface serves as a natural protective barrier against dental erosion. Numerous proteins composing the pellicle serve different functions within this thin layer. Our study examined the effect of incorporated mucin and casein on the erosion-inhibiting potential of the acquired enamel pellicle. Cyclic acidic conditions were applied to mimic the erosive environment present at the human enamel interface during the consumption of soft drinks. One hundred enamel specimens were prepared for microhardness tests and distributed randomly into 5 groups (n = 20) that received the following treatment: deionized water, humidity chamber, mucin, casein, or a combination of mucin and casein. Each group was exposed to 3 cycles of a 2-hour incubation in human saliva, followed by a 2-hour treatment in the testing solution and a 1-min exposure to citric acid. The microhardness analysis demonstrated that the mixture of casein and mucin significantly improved the erosion-inhibiting properties of the human pellicle layer. The addition of individual proteins did not statistically impact the function of the pellicle. These data suggest that protein-protein interactions may play an important role in the effectiveness of the pellicle to prevent erosion.

Depth of cure of resin composites: is the ISO 4049 method suitable for bulk fill materials?

To evaluate if depth of cure D(ISO) determined by the ISO 4049 method is accurately reflected with bulk fill materials when compared to depth of cure D(new) determined by Vickers microhardness profiles.

Multiscale Characterization of Acrylic Bone Cement Modified with Functionalized Mesoporous Silica Nanoparticles

Acrylic bone cement is widely used to anchor orthopedic implants to bone and mechanical failure of the cement mantle surrounding an implant can contribute to aseptic loosening. In an effort to enhance the mechanical properties of bone cement, a variety of nanoparticles and fibers can be incorporated into the cement matrix. Mesoporous silica nanoparticles (MSNs) are a class of particles that display high potential for use as reinforcement within bone cement. Therefore, the purpose of this study was to quantify the impact of modifying an acrylic cement with various low-loadings of mesoporous silica. Three types of MSNs (one plain variety and two modified with functional groups) at two loading ratios (0.1 and 0.2 wt/wt) were incorporated into a commercially available bone cement. The mechanical properties were characterized using four-point bending, microindentation and nanoindentation (static, stress relaxation, and creep) while material properties were assessed through dynamic mechanical analysis, differential scanning calorimetry, thermogravimetric analysis, FTIR spectroscopy, and scanning electron microscopy. Four-point flexural testing and nanoindentation revealed minimal impact on the properties of the cements, except for several changes in the nano-level static mechanical properties. Conversely, microindentation testing demonstrated that the addition of MSNs significantly increased the microhardness. The stress relaxation and creep properties of the cements measured with nanoindentation displayed no effect resulting from the addition of MSNs. The measured material properties were consistent among all cements. Analysis of scanning electron micrographs images revealed that surface functionalization enhanced particle dispersion within the cement matrix and resulted in fewer particle agglomerates. These results suggest that the loading ratios of mesoporous silica used in this study were not an effective reinforcement material. Future work should be conducted to determine the impact of higher MSN loading ratios and alternative functional groups. (C) 2014 Elsevier Ltd. All rights reserved.

Curing capability of halogen and LED light curing units in deep class II cavities in extracted human molars

Class II cavities were prepared in extracted lower molars filled and cured in three 2-mm increments using a metal matrix. Three composites (Spectrum TPH A4, Ceram X mono M7 and Tetric Ceram A4) were cured with both the SmartLite PS LED LCU and the Spectrum 800 continuous cure halogen LCU using curing cycles of 10, 20 and 40 seconds. Each increment was cured before adding the next. After a seven-day incubation period, the composite specimens were removed from the teeth, embedded in self-curing resin and ground to half the orofacial width. Knoop microhardness was determined 100, 200, 500, 1000, 1500, 2500, 3500, 4500 and 5500 microm from the occlusal surface at a distance of 150 microm and 1000 microm from the metal matrix. The total degree of polymerization of a composite specimen for any given curing time and curing light was determined by calculating the area under the hardness curve. Hardness values 150 microm from the metal matrix never reached maximum values and were generally lower than those 1000 microm from the matrix. The hardest composite was usually encountered between 200 microm and 1000 microm from the occlusal surface. For every composite-curing time combination, there was an increase in microhardness at the top of each increment (measurements at 500, 2500 and 4500 microm) and a decrease towards the bottom of each increment (measurements at 1500, 3500 and 5500 microm). Longer curing times were usually combined with harder composite samples. Spectrum TPH composite was the only composite showing a satisfactory degree of polymerization for all three curing times and both LCUs. Multiple linear regression showed that only the curing time (p < 0.001) and composite material (p < 0.001) had a significant association with the degree of polymerization. The degree of polymerization achieved by the LED LCU was not significantly different from that achieved by the halogen LCU (p = 0.54).

The impact of ozone treatment on enamel physical properties

PURPOSE: To assess the effects of the highly reactive molecule of ozone on sound enamel physical properties and its effects on sealing ability. METHODS: The effect of ozone on sealant tag length, microleakage and unfilled area proportion were evaluated on intact and prepared sound molar fissures. Microhardness, contact angle and acid resistance tests were performed on ground sound smooth surfaces. The samples were treated with ozone for 40 seconds (HealOzone). Control samples were treated with air (modified HealOzone) or left untreated. RESULTS: No statistically significant difference was observed between the control and ozone treated samples in all tests. Prepared fissures exhibited no unfilled areas and a statistically significantly lower microleakage compared to intact fissures. Ozone was shown to dehydrate enamel and consequently enhance its microhardness, which was reversible.

Natale und neonatale Zähne

Natal teeth have been defined as teeth which are present at birth, while neonatal teeth erupt during the first 30 days. Their occurrence is rare, the prevalence ranges from 1:2000 to 1:3000 with a higher frequency in the lip and palate clefts and syndroms. In about 85% natal or neonatal teeth are lower central incisors (60% in pairs), rare are upper teeth, molars and multiple teeth. In almost 90% they are part of the deciduous dentition. A lot of possible causes of early eruption are discussed, but only the relation to hereditary factors seems to be evident. An autosomal dominant trait is often described. The appearance of these teeth is dependent on the degree of maturity, but most of the time it is loose, small, discoloured and hypoplastic. Histologically, enamel hypoplasia with normal prism structure is apparent. No significant disturbances of the dentin structures are observed, only cervically dentin becomes atubular with spaces and enclosed cells. A large vascular pulp and failure of root formation are further investigations. Our microhardness measurements showed values from 24.3-32.4 KHN for enamel and 48.3-62.2 KHN for dentin, while normal deciduous teeth have an enamel hardness of 322.0 +/- 17.5 KHN. The thickness of enamel was never more than 280 microm compared to up to 1200 microm in normal teeth. This shows the retarded development of natal and neonatal teeth, because mineralization has not finished at the time of birth. In accordance with developmental age tooth structure and appearence are normal. In consideration of complications as Riga-Fede-disease, feeding problems, possibility of infection and hypermobility most of the time extraction is the treatment of choice, but in the interest of protecting the child this decision should be made carefully.

Impact of different toothpastes on the prevention of erosion

The aim of the present study was to test the impact of different toothpastes on the prevention of erosion. Enamel demineralization and remineralization were monitored using surface microhardness (SMH) measurements. Human enamel specimens were treated following two different procedures: (1) incubation in toothpaste slurry followed by acid softening and artificial saliva exposure; (2) acid softening followed by incubation in toothpaste slurry and artificial saliva exposure. For the control procedure, toothpaste treatment was excluded. The following toothpastes were tested: Zendium, Sensodyne Proschmelz (Pronamel), Prodent Rocket Power, Meridol and Signal active. Normalized SMH values compared to the baseline (= 1.00) after 1-hour artificial saliva exposure for procedure 1 (respectively for procedure 2) were as follows (mean: 95% CI): Sensodyne Proschmelz 0.97: 0.93, 1.00 (0.92: 0.90, 0.94), Zendium 0.97: 0.94, 1.00 (0.89: 0.83, 0.95), Meridol 0.97: 0.94, 1.00 (0.94: 0.92, 0.96), Signal active 0.94: 0.91, 0.97 (0.95: 0.91, 0.99), Prodent Rocket Power 0.92: 0.90, 0.94 (0.93: 0.89, 0.97) and control 0.91: 0.88, 0.94. Further exposure to artificial saliva for up to 4 h showed no significant improvement of SMH. Regression analyses revealed a significant impact of the applied procedure. Incubation in toothpaste slurries before the acid challenge seems to be favorable to prevent erosion. None of the tested toothpastes showed statistically significant better protection than another against an erosive attack.

Processing and mechanical properties of cast aluminum containing scandium, zirconium, and ytterbium

A series of aluminum alloys containing additions of scandium, zirconium, and ytterbium were cast to evaluate the effect of partial ytterbium substitution for scandium on tensile behavior. Due to the high price of scandium, a crucible-melt interaction study was performed to ensure no scandium was lost in graphite, alumina, magnesia, or zirconia crucibles after holding a liquid Al-Sc master alloy for 8 hours at 900 °C in an argon atmosphere. The alloys were subjected to an isochronal aging treatment and tested for conductivity and Vickers microhardness after each increment. For scandium-containing alloys, peak hardnesses of 520-790 MPa, and peak tensile stresses of 138-234 MPa were observed after aging from 150-350 °C for 3 hours in increments of 50 °C, and for alloys without scandium, peak hardnesses of 217-335 MPa and peak tensile stresses of 45-63 MPa were observed after a 3 hour, 150 °C aging treatment. The hardness and tensile strength of the ytterbium containing alloy was found to be lower than in the alloy with no ytterbium substitution.

Influence of human saliva on the development of artificial erosions

It was hypothesized that saliva from patients with erosion exhibits lower protective efficacy compared to saliva from patients without erosion, based on in vitro enamel softening studies. A total of 645 enamel specimens were distributed among seven experimental groups. Saliva was gathered from each of 10 volunteers without clinical signs of dental erosion and from 10 patients exhibiting severe erosive defects. Aliquots of 50 ml of saliva from each patient were mixed with sour drops or citric acid, respectively. Pooled saliva, sour drops and citric acid mixed with water served as controls. The enamel specimens were soaked in the respective mixture for 5 min and were subsequently incubated in pure saliva for 2 min. This cycle was repeated three times, then the specimens were kept in 100 ml of saliva for 8 h. Surface microhardness was evaluated at the beginning of the experiment and after each cycle. During the experiments, microhardness decreased significantly in all groups except for the pure saliva group. For sour drops and citric acid mixed with saliva from patients without erosion, the final microhardness was higher compared to the mixture of the two erosive compounds with saliva from patients with erosion. The storage of saliva for 8 h resulted in a certain amount of rehardening, with the highest level of rehardening being observed in the group that was least demineralized (sour drops plus saliva from patients without erosion). It is concluded that salivary components play a crucial role in the development of dental erosion.

A new optical detection method to assess the erosion inhibition by in vitro salivary pellicle layer

OBJECTIVES Application of the recently developed optical method based on the monitoring of the specular reflection intensity to study the protective potential of the salivary pellicle layer against early enamel erosion. METHODS The erosion progression was compared between two treatment groups: enamel samples coated by the 15 h-in vitro-formed salivary pellicle layer (group P, n=90) and the non-coated enamel surfaces (control group C, n=90). Different severity of the erosive impact was modelled by the enamel incubation in 1% citric acid (pH=3.6) for 2, 4, 8, 10 or 15 min. Erosion quantification was performed by the optical method as well as by the microhardness and calcium release analyses. RESULTS Optical assessment of the erosion progression showed erosion inhibition by the in vitro salivary pellicle in short term acidic treatments (≤ 4 min) which was also confirmed by microhardness measurements proving significantly less (p<0.05) enamel softening in the group P at 2 and 4 min of erosion compared to the group C. SEM images demonstrated less etched enamel interfaces in the group P at short erosion durations as well. CONCLUSIONS Monitoring of the specular reflection intensity can be successfully applied to quantify early erosion progression in comparative studies. In vitro salivary pellicle (2h) provides erosion inhibition but only in short term acidic exposures. CLINICAL SIGNIFICANCE The proposed optical technique is a promising tool for the fast and non-invasive erosion quantification in clinical studies.

Combined effect of a fluoride-, stannous- and chitosan-containing toothpaste and stannous-containing rinse on the prevention of initial enamel erosion-abrasion.

OBJECTIVES The aim of this study was to assess the preventive effect of a fluoride-, stannous- and chitosan-containing (F/Sn/chitosan-) toothpaste (TP) on initial enamel erosion and abrasion. METHODS In total, 150 human premolar enamel specimens were ground, polished and divided into 5 toothpaste/rinse groups (n=30): (G1) placebo-TP/tap water, (G2) sodium fluoride (NaF-) TP/tap water, (G3) F/Sn/chitosan-TP/tap water, (G4) F/Sn/chitosan-TP/Sn-rinse, (G5) NaF-TP/NaF-rinse. The 8-day erosion-abrasion cyclic treatment (one cycle/day) consisted of incubating the samples in artificial saliva (30min), then submitting the samples to toothbrush abrasion (2min incubation in toothpaste slurry; brushing with 20 toothbrush strokes) and rinsing (2min; 10ml) with the respective solution: tap water (G1-G3), Sn-rinse (G4) or NaF-rinse (G5). Afterwards, the samples were submitted to erosion (2min; 30ml 1% citric acid, pH=3.6). Surface microhardness (SMH) was measured initially and after every abrasion and erosion treatment. Enamel substance loss was calculated after each abrasion. Non-parametric ANOVA followed by Wilcoxon rank tests were used for analysis. RESULTS G1 presented the greatest SMH decrease, while G4 presented the least SMH decrease (p<0.001). G3 had a similar SMH decrease to G2 and G5. Substance loss was significantly lower in G4 than all other groups (p<0.05), closely followed by G3. Both G2 and G5 showed similar calculated enamel substance loss to G1. CONCLUSION The treatment with F/Sn/chitosan-TP and tap water provided a similar SMH decrease to both NaF-TP groups, but significantly lower substance loss. F/Sn/Chitosan-TP and Sn-rinse showed a better preventive effect, which promoted less SMH decrease and reduced substance loss. CLINICAL SIGNIFICANCE The toothpaste containing fluoride, stannous and chitosan shows promising results in reducing substance loss from erosion and abrasion. The combination of this toothpaste with the stannous-containing rinse showed even better prevention against erosion-abrasion.