Yb：YAG晶体的合作发光现象

研究了Yb：YAG晶体的合作发光现象。当用940hm的近红外光激发时，Yb：YAG晶体有明显的上转换蓝色发光。实验发现498nm的蓝色发光强度与激发功率的平方成正比，而且Yb^3＋掺杂浓度越高，蓝色发光越强。分析表明这是Yb^3＋间强的相互作用导致的合作发光，是由于Yb^3＋在共价性的YAG基质中，它的4f^I3电子易于与近邻离子发生相互作用导致的。

Temperature dependence of the 1.03 mu m stimulated emission cross section of Cr : Yb : YAG crystal

The fluorescence emission spectra of Cr:Yb:YAG crystal are measured and the effective stimulated emission cross section of the crystal are obtained from -80 degrees C to +80 degrees C. A linear temperature dependence between -80 degrees C and +80 degrees C is reported for the 1.03 mu m peak stimulated emission cross section of Cr:Yb:YAG crystal. (c) 2004 Elsevier B.V. All rights reserved.

Blue upconversion luminescence generation in Ce3+: Gd2SiO5 crystals by infrared femtosecond laser irradiation

Blue frequency-upconversion fluorescence emission has been observed in Ce3+-doped Gd2SiO5 single crystals, pumped with 120-fs 800 nm IR laser pulses. The observed fluorescence emission peaks at about 440nm is due to 5d -> 4f transition of Ce3+ ions. The intensity dependence of the blue fluorescence emission on the IR excitation laser power obeys the cubic law, demonstrating three-photon absorption process. Analysis suggested that three-photon simultaneous absorption induced population inversion should be the predominant frequency upconversion mechanism. (c) 2006 Optical Society of America.

Temperature dependence of the 1.064-mu m stimulated emission cross-section of Cr : Nd : YAG crystal

The fluorescence emission spectra of Cr:Nd:YAG crystal are measured and the effective stimulated emission cross-section of the crystal is obtained from -80 to +80 degrees C. A linear temperature dependence between -80 and +80 degrees C is reported for the 1.064-mu m peak stimulated emission cross-section of Cr:Nd:YAG crystal. (C) 2005 Elsevier Ltd. All rights reserved.

Three-photon-excited upconversion luminescence of Ce3+: YAP crystal by femtosecond laser irradiation

Infrared to ultraviolet and visible upconversion luminescence was demonstrated in trivalent cerium doped YAlO3 crystal (Ce3+: YAP) under focused infrared femtosecond laser irradiation. The fluorescence spectra show that the upconverted luminescence comes from the 5d-4f transitions of trivalent cerium ions. The dependence of luminescence intensity of trivalent cerium on infrared pumping power reveals that the conversion of infrared radiation is dominated by three-photon excitation process. It is suggested that the simultaneous absorption of three infrared photons pumps the Ce3+ ion into upper 5d level, which quickly nonradiatively relax to lowest 5d level. Thereafter, the ions radiatively return to the ground states, leading to the characteristic emission of Ce3+. (c) 2005 Optical Society of America.

Cooperative and charge transfer luminescence in Yb3+ -doped yttrium aluminum perovskite (YAlO3)

YAlO3 (YAP) crystals with different Yb3+ concentration have been grown by Czochralski method and cooperative fluorescence of Yb3+ ions in YAP crystal was studied under 940-nm infrared (IR) LD excitation at room temperature. The Yb concentration dependence of absorption intensity of IR and charge transfer bands exhibit different features. The green emission band in the region of 480-520nm was assigned to the cooperative deexcitation of two Yb3+ ions. The remaining upconverted emission bands containing various sharp peaks associated with impurity ions were observed and discussed. Charge transfer luminescence of heavily doped 20at% Yb:YAP is strongly temperature dependent and no concentration quenching of the charge transfer luminescence was found through the investigation of different Yb levels samples. (c) 2006 Elsevier B.V. All rights reserved.

红外飞秒激光诱导Ce^3＋掺杂闪烁晶体的上转换发光研究

本文研究了红外飞秒激光照射下Ce^3＋ 掺杂的YAP和LSO两种闪烁晶体的上转换发光现象.实验发现在飞秒激光泵浦下,这两种晶体的荧光均来自于Ce^3＋离子的5d-4f跃迁.荧光强度与泵浦光功率之间的依赖关系揭示了Ce^3＋：YAP和Ce^3＋：LSO晶体的上转换过程皆由三光子吸收过程所主导.分析表明,Ce^3＋：YAP和Ce^3＋：LSO晶体中的三光子吸收是三光子同时吸收.

Microstructure and laser-induced damage threshold of ZrO2 coatings dependence on annealing temperature

ZrO2 coatings were deposited on different substrates of Yb:YAG and fused silica by electron beam evaporation. After annealed for 12 h at 673 and 1073 K, respectively, weak absorption of coatings was measured by surface thermal lensing (STL) technique, and then laser-induced damage threshold (LIDT) was determined also. The crystalline phase of ZrO2 coatings and the size of the crystal grain were investigated by X-ray diffraction. It was found that microstructure of ZrO2 coatings was dependent on both annealing temperature and substrate structure, and coatings containing monoclinic phases had higher damage threshold than others. Due to the strong absorption of Yb:YAG, damage threshold of coatings on Yb:YAG was much less than that on fused silica. (C) 2004 Elsevier B.V. All rights reserved.

Overcoat dependence of laser-induced damage threshold of 355 nm HR coatings

A series of HR coatings, with and without overcoat, were prepared by electron beam evaporation using the same deposition process. The laser-induced damage threshold (LIDT) was measured by a 355 nm Nd:YAG laser with a pulse width of 8 ns. Damage morphologies of samples were observed by Leica-DMRXE Microscope. The stress was measured by viewing the substrate deformation before and after coatings deposition using an optical interferometer. Reflectance of the samples was measured by Lambda 900 Spectrometer. The theoretical results of electric field distributions of the samples were calculate by thin film design software (TFCalc). It was found that SiO2 overcoat had improved the LIDT greatly, while MgF2 overcoat had little effect on the LIDT because of its high stress in the HR coatings. The damage morphologies were different among HR coatings with and without overcoats. (c) 2005 Elsevier B.V. All rights reserved.

Theoretical analysis of optical properties of dielectric coatings dependence on substrate subsurface defects

A model for refractive index of stratified dielectric substrate was put forward according to theories of inhomogeneous coatings. The substrate was divided into surface layer, subsurface layer and bulk layer along the normal direction of its surface. Both the surface layer (separated into N-1 sublayers of uniform thickness) and subsurface layer (separated into N-2 sublayers of uniform thickness), whose refractive indices have different statistical distributions, are equivalent to inhomogeneous coatings, respectively. And theoretical deduction was carried Out by employing characteristic matrix method of optical coatings. An example of mathematical calculation for optical properties of dielectric coatings had been presented. The computing results indicate that substrate subsurface defects can bring about additional bulk scattering and change propagation characteristic in thin film and Substrate. Therefore, reflectance, reflective phase shift and phase difference of an assembly of coatings and substrate deviate from ideal conditions. The model will provide some beneficial theory directions for improving optical properties of dielectric coatings via substrate surface modification. (c) 2005 Elsevier B.V. All rights reserved.

Thickness dependence of structure and optical properties of silver films deposited by magnetron sputtering

A series of silver films with different thickness were prepared under identical conditions by direct current magnetron sputtering. The optical properties of the silver films were measured using spectrophotometric techniques and the optical constants were calculated from reflection and transmission measurements made at near normal incidence. The results show that the optical properties and constants are affected by films' thickness. Below the critical thickness of 17 nm at which Ag film forms a continuous film, the optical properties and constants vary significantly as the thickness of films increases and then tends to a stable value which is reached at 41 nm. X-ray diffraction measurements were carried out to examine the structure and stress evolution of the Ag films as a function of films' thickness. It was found that the interplanar distance of (111) orientation decreases when the film thickness increases and tends to be close to that of bulk material. The compressive strains also decrease with increasing thickness. (C) 2007 Published by Elsevier B.V.

Working pressure dependence of properties of Al2O3 thin films prepared by electron beam evaporation

The effects of working pressure on properties of Al2O3 thin films are investigated. Transmittance of the Al2O3 thin film is measured by a Lambda 900 spectrometer. Laser-induced damage threshold (LIDT) is measured by a Nd:YAG laser at 355nm with a pulse width of 7ns. Microdefects were observed under a Nomarski microscope. The samples are characterized by optical properties and defect, as well as LIDT under the 355 nm Nd: YAG laser radiation. It is found that the working pressure has fundamental effect on the LIDT. It is the absorption rather than the microdefect that plays an important role on the LID T of Al2O3 thin film.