Bifunctional Au@Pt hybrid nanorods

The controlled synthesis of bifunctional Au@Pt hybrid nanorods has been realized through a simple wet chemical approach. Transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), and UV-vis-near infrared spectroscopy (UV-vis-NIR) were employed to characterize the obtained hybrid nanorods. TEM results indicate that the thickness of Pt nanoislands on the surfaces of gold nanorods can be easily tunable via controlling the molar ratio of An nanorods to the H2PtCl6. These Au@Pt hybrid nanorods have dual functions, which can be used not only for surface enhanced Raman spectroscopy (SERS), but also to exhibit good catalytic activity for 02 reduction. It is expected that these hybrid nanorods can be used as new functional building blocks to assemble novel three-dimensional (31)) complex multicomponent nanostructures, which are believed to be useful for electrochemical nanodevices.

A general route to transform normal hydrophilic cloths into superhydrophobic surfaces

Herein, we describe a simple and inexpensive method for forming superhydrophobic cloths with the highest water contact angle of close to 180 degrees, in which normal commercial cloths serving as pristine materials are modified with suitable gold micro/nanostructures.

Preparation of novel silver-gold bimetallic nanostructures by seeding with silver nanoplates and application in surface-enhanced Raman scattering

Novel silver-gold bimetallic nanostructures were prepared by seeding with silver nanoplates in the absence of any surfactants. During the synthesis process, it was found that the frameworks of silver nanoplates were normally kept though the basal plane of silver nanoplates became rugged. The real morphology of these nanostructures depended on the molar ratio of gold ions to the seed particles. When the molar ratio of gold ions to silver atoms increased from 0.5 to 4, porous or branched silver-gold bimetallic nanostructures could be made. The growth mechanism was qualitatively discussed based on template-engaged replacement reactions and seed-mediated deposition reactions. Due to the unusual structures, they exhibited interesting optical properties. Moreover, they were shown to be an active substrate for surface-enhanced Raman scattering measurements.

Shape-gradient composite surfaces: Water droplets move uphill

The approach of water droplets self-running horizontally and uphill without any other forces was proposed by patterning the shape-gradient hydrophilic material (i.e., mica) to the hydrophobic matrix (i.e., wax or low-density polyethylene (LDPE)). The shape-gradient composite surface is the best one to drive water droplet self-running both at the high velocity and the maximal distance among four different geometrical mica/wax composite surfaces. The driving force for the water droplets self-running includes: (1) the great difference in wettability of surface materials, (2) the low contact angle hysteresis of surface materials, and (3) the space limitation of the shape-gradient transportation area. Furthermore, the average velocity and the maximal distance of the self-running were mainly determined by the gradient angle (alpha), the droplet volume, and the difference of the contact angle hysteresis. Theoretical analysis is in agreement with the experimental results.

Interfacial supramolecular self-assembled monolayers of C-60 by thiolated beta-cyclodextrin on gold surfaces via monoanionic C-60

The supramolecular self-assembled monolayers (SAMs) of C-60 by thiolated beta-cyclodextrin (CD) on gold surfaces were constructed for the first time using C-60 monoanion. The results indicate that monoanionic C-60 plays a crucial role in the formation of the C-60-containing self-assembled monolayers. The generation of C-60 monoanion and the formation process of C-60 SAMs were monitored in-situ by UV-visible and near-IR spectroscopy. The resulting C-60 SAMs were fully characterized by spectroscopic ellipsometry (SE), cyclic voltammetry, X-ray photoelectron spectroscopy (XPS), and water contact angle measurements. After the immobilization of C-60 by the SAMs of thiolated beta-CD, the film thickness increased by approximately 1 nm from 0.8 to 1.8 nm as determined by SE, demonstrating the formation of the supramolecular self-assembled monolayers of thiolated beta-CD/C-60. The new C-60 SAMs exhibited one quasi-reversible redox couple at half wave potential of -0.57 V vs SCE in aqueous solution containing 0.1 M KCl. The surface coverage of C-60 on the gold surfaces was estimated to be 1.1 x 10(-10) mol cm(-2). The XPS showed the assembly of C-60 over the thiolated beta-CD SAMs.

Micropatterning of metal films coated on polymer surfaces with epoxy mold and its application to organic field effect transistor fabrication

In this letter, a simple and versatile approach to micropatterning a metal film, which is evaporated on a Si substrate coated with polymer, is demonstrated by the use of a prepatterned epoxy mold. The polymer interlayer between the metal and the Si substrate is found important for the high quality pattern. When the metal-polymer-Si sandwich structure is heated with the temperature below T-m but above T-g of the polymer, the plastic deformation of the polymer film occurs under sufficiently high pressure applied. It causes the metal to crack locally or weaken along the pattern edges. Further heating while applying a lower pressure results in the formation of an intimate junction between the epoxy stamp and the metal film. Under these conditions the epoxy cures further, ensuring adhesion between the stamp and the film. The lift-off process works because the adhesion between the epoxy and the metal film is stronger than that between the metal film and the polymer. A polymer field effect transistor is fabricated in order to demonstrate potential applications of this micropatterning approach.

Superhydrophobic PTFE surfaces by extension

A rather simple but yet effective way to achieve a superhydrophobic film by extending a Teflon film is proposed. The water contact angle can be increased from 118 to 165degrees by extending to ca. 190%. The fibrous crystals and the increasing distance between the fibrous crystals are believed responsible for the high water-contact angle. It indicates that the density of the aligned microstructures is very important for the superhydrophobicity.

Pt nanoparticles: Heat treatment-based preparation and Ru(bpy)(3)(2+)-mediated formation of aggregates that can form stable films on bare solid electrode surfaces for solid-state electrochemiluminescence detection

A simple thermal process for the preparation of small Pt nanoparticles is presented, carried out by heating a H-2-PtCl6/3- thiophenemalonic acid aqueous solution. The following treatment of such colloidal Pt solution with Ru( bpy)(3)(2+) causes the assembly of Pt nanoparticles into aggregates. Most importantly, directly placing such aggregates on bare solid electrode surfaces can produce very stable films exhibiting excellent electrochemiluminescence behaviors.

Wettability of zinc oxide surfaces with controllable structures

Zinc oxide (ZnO) surfaces with controllable structures (i.e, microstructure, nanostructure, and micronanobinary structure) have been created by controlling pH at < 4 or > 10.5 in the Zn(gray) + H2O2 reaction. The resulting surface shows superhydrophobicity. It is found that the water contact angle (CA) of the surface with micronanobinary structure is greater than that of nanostructure and that of nanostructure is greater than that of the microstructure. Theoretical analysis is completely in agreement with the experimental results.

Surface-enhanced Raman scattering of silver-gold bimetallic nanostructures with hollow interiors

Surface-enhanced Raman scattering (SERS) activity of silver-gold bimetallic nanostructures (a mean diameter of similar to 100 nm) with hollow interiors was checked using p-aminothiophenol (p-ATP) as a probe molecule at both visible light (514.5 nm) and near-infrared (1064 nm) excitation. Evident Raman peaks of p-ATP were clearly observed, indicating the enhancement Raman scattering activity of the hollow nanostructure to p-ATP. The enhancement factors (EF) at the hollow nanostructures were obtained to be as large as (0.8 +/- 0.3)x10(6) and (2.7 +/- 0.5)x10(8) for 7a and 19b (b(2)) vibration mode, respectively, which was 30-40 times larger than that at silver nanoparticles with solid interiors at 514.5 nm excitation. EF values were also obtained at 1064 nm excitation for 7a and b(2)-type vibration mode, which were estimated to be as large as (1.0 +/- 0.3)x10(6) and (0.9 +/- 0.2)x10(7), respectively. The additional EF values by a factor of similar to 10 for b(2)-type band were assumed to be due to the chemical effect. Large electromagnetic EF values were presumed to derive from a strong localized plasmas electromagnetic field existed at the hollow nanostructures.

Synthesis of Pt/Ag bimetallic nanorattle with Au core

A straightforward combination of the seeding growth method and replacement reaction allowed for the formation of a nanorattle composed of a gold core and Pt/Ag shell. The size, structure, and composition of the Pt/Ag rattle-type nanostructure were confirmed by scanning electron microscopy, transmission electron microscopy and X-ray photoelectron spectrometry.

Macroporous fluoropolymeric films templated by silica colloidal assembly: A possible route to super-hydrophobic surfaces

A super-hydrophobic surface was obtained on a three-dimensional (313) polyvinylidene fluoride (PVDF) macroporous film. The porous films were fabricated through self-assembled silica colloidal templates. The apparent water contact angle of the surface can be tuned from 106 degrees to 153 degrees through altering the sintering temperature and the diameter of the colloidal templates. A composite structure of micro-cavities and nanoholes on the PVDF surface was responsible for the super-hydrophobicity. The wettability of the porous surfaces was described by the use of the Cassie-Baxter model and Wenzel's equation.