Comparison of Physicochemical Surface Conditioning Methods for Adhesion of bis-GMA Resin Cement to Particulate Filler Composite and Surface Characterization

This study compared the effect of physicochemical surface conditioning methods on the adhesion of bis-GMA-based resin cement to particulate filler composite (PFC) used for indirect dental restorations. PFC blocks (N (block)=54, n (block)=9 per group) were polymerized and randomly subjected to one of the following surface conditioning methods: a) No conditioning (Control-C), b) Hydrofluoric acid (HF)etching for 60s (AE60), c) HF for 90s (AE90), d) HF for 120s (AE120), e) HF for 180s (AE180), and f) air-abrasion with 30 mu m silica-coated alumina particles (AB). The conditioned surfaces were silanized with an MPS silane, and an adhesive resin was applied. Resin composite blocks were bonded to PFC using resin cement and photo-polymerized. PFC-cement-resin composite blocks were cut under coolant water to obtain bar specimens (1mmx0.8mm). Microtensile bond strength test (mu TBS)was performed in a universal testing machine (1mm/min). After debonding, failure modes were classified using stereomicroscopy. Surface characterization was performed on a set of separate specimen surfaces using Scanning Electron Microscopy (SEM), X-Ray Dispersive Spectroscopy (XDS), X-Ray Photoelectron Spectroscopy (XPS), and Fourier Transform-Raman Spectroscopy (FT-RS). Mean mu TBS (MPa) of C (35.6 +/- 4.9) was significantly lower than those of other groups (40.2 +/- 5.6-47.4 +/- 6.1) (p<0.05). The highest mu TBS was obtained in Group AB (47.4 +/- 6.1). Prolonged duration of HF etching increased the results (AE180: 41.9 +/- 7), but was not significantly different than that of AB (p>0.05). Failure types were predominantly cohesive in PFC (34 out of 54) followed by cohesive failure in the cement (16 out of 54). Degree of conversion (DC) of the PFC was 63 +/- 10%. SEM analysis showed increased irregularities on PFC surfaces with the increased etching time. Chemical surface analyses with XPS and FT-RS indicated 11-70% silane on the PFC surfaces that contributed to improved bond strength compared to Group C that presented 5% silane, which seemed to be a threshold. Group AB displayed 83% SiO2 and 17% silane on the surfaces.

Effect of simulated intraoral erosion and/or abrasion effects on etch-and-rinse bonding to enamel

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Efeitos da interação e soluções utilizadas na prevenção da formação do precipitado originado pela interação do hipoclorito de sódio e do diglunato de clorexidina e a repercursão sobre a resistência de união de cimento obturador na dentina do canal radicular

Pós-graduação em Odontologia - FOAR

Anatomização de pinos de fibra de vidro: estudo de propriedades mecânicas na interface restauradora adesiva

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Estrutura do esmalte humano e sua interface com sistemas adesivos

Esta tese sistematiza uma série de estudos dedicados à compreensão da interface do esmalte e sistemas adesivos. Para tanto, a estrutura da camada aprismática do esmalte em alta resolução pela microscopia eletrônica de varredura foi avaliada quanto a sua continuidade, espessura, distribuição nas faces coronárias e em fossas e fissuras, predominantemente em dentes decíduos não erupcionados. Foi também analisado pela microscopia eletrônica de varredura os efeitos do condicionamento de diferentes tipos de ácido e, em especial, do ácido fosfórico em diferentes concentrações, metodologias e tempos de aplicação. Estes trabalhos permitiram visualizar as principais ações ácidas desmineralizantes e os tipos de retenções no centro ou periferias dos prismas ou em ambas as regiões, bem como a profundidade e forma dos “tags” resinosos com carga e sem carga na intimidade do esmalte. No caso particular da aplicação dos selantes em fossas e fissuras foi também avaliada comparativamente a eficácia das técnicas invasivas ou não invasivas. Os últimos experimentos foram dedicados ao estudo da microinfiltração de diferentes sistemas adesivos e da resistência destes sistemas adesivos na estrutura do esmalte. Novos estudos merecem dar continuidade à linha de pesquisa de sempre priorizando o propósito de vincular os procedimentos aplicados com uma consistente e indispensável fundamentação de pesquisa básica no interesse da clínica odontopediátrica.

Bonding of facial silicon with nanoparticles to an acrylic resin substrate

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Efeito do tipo de adesivo e do seu mecanismo de ativação, assim como da viscosidade da resina composta, na resistência de união à dentina antes e após envelhecimento artificial

Pós-graduação em Odontologia Restauradora - ICT

Effect of Er:YAG laser and diamond drill on hybrid layer morphology obtained with self-etch adhesive: analysis by SEM and confocal laser scanning microscopy (CLSM)

This study aimed to evaluate the effect of Er:YAG (L) and diamond drills (DD) on: 1) the microshear bond strength (MPa); 2) the adhesive interface of two-step (TS) – Adper Scotchbond Multipurpose and one-step (OS) adhesives – Adper EasyOne, both from 3M ESPE. Material and methods: According to the preparation condition and adhesives, the samples were divided into four groups: DD_TS (control); DD_OS; L_TS and L_OS. 60 bovine incisors were randomly divided into experimental and groups: 40 for microshear bond strength (n = 10) and 20 for the adhesive interface morphology [6 to measure the thickness of the hybrid layer (HL) and length of tags (t) by CLSM (n = 3); 12 to the adhesive interface morphology by SEM (n = 3) and 2 to illustrate the effect of the instruments on dentine by SEM (n = 1)]. To conduct the microshear bond strength test, four cylinders (0.7 mm in diameter and 1 mm in height with area of adhesion of 0.38 mm) were constructed with resin composite (Filtek Z350 XT – 3M ESPE) on each dentin surface treated by either L or DD and after adhesives application. Microshear bond strength was performed in universal testing machine (EMIC 2000) with load cell of 500 kgf and a crosshead speed of 0.5 mm / min. Adhesive interface was characterized by thickness of hybrid layer (HL) and length of tags (t) in nm, with the aid of UTHSCSA ImageTool software. Results: Microshear bond strength values were: L_TS 34.10 ± 19.07, DD_TS 24.26 ± 9.35, L_OS 33.18 ± 12.46, DD_OS 21.24 ± 13.96. Two-way ANOVA resulted in statistically significant differences only for instruments (p = 0.047). Mann-Whitney identified the instruments which determined significant differences for HL thickness and tag length (t). Concerning to the adhesive types, these differences were only observed for (t). Conclusion: It can be concluded that 1) laser Er:YAG results in higher microshear bond strength values regardless of the adhesive system (TS and OS); 2) the tags did not significant affect the microshear bond strength; 3) the adhesive interface was affected by both the instruments for cavity preparation and the type of adhesive system used.

Influência do agente de união na resistência ao cisalhamento da interface titânio/polímero de vidro

There is little information regarding bond strengths of polyglass to metal alloys. This study evaluated the influence of bonding system on shear bond strength of a composite resin (Artglass/Heraeus Kulzer) to cast titanium (Ti). Twenty metallic structures (4mm in diameter, 5mm thick) of titanium grade I were cast shaped and abraded with 250mm aluminum oxide and separated into two groups. For each group was applied one bonding system (Siloc or Retention Flow) before opaque and dentin polymer superposition. This procedure was managed using teflon matrices. They were manipulated and polymerized according to the manufacturer's recommendations. The samples were stored in distilled water for 24 hours at 37º and thermocycled (5º and 55ºC/500 cycles). Shear bond strength tests were performed by using an Instron Universal testing machine at a crosshead speed of 5mm/min. Results were analyzed statistically with one-way ANOVA (a=0,5) and they indicated that the Retention Flow system was statistically better than Siloc (20.74 MPa and 11.65 MPa , respectively). It was possible to conclude that the bonding agent influenced the adhesion between polymer and cast titanium.

Avaliação in vitro da resistência de união de dois sistemas adesivos dentinários à dentina bovina antes e após a termociclagem: teste de cisalhamento e análise estereomicroscópia

Pós-graduação em Odontologia Restauradora - ICT

Resistência ao cisalhamento de diferentes sistemas adesivos no esmalte dental

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Pré tratamento dentinário influência do condicionamento ácido, irradiação laser e hipermineralização na resistência ao cisalhamento de sistema adesivo multi uso

The disadvantages generated by the acid etching of the dentin, such as an increase in its permeability, in the surface moisture and in the potential to denature the external dentinal collagen, the formation of a fragility zone and the citotoxicity of the adhesive monomers; which are all aggravated by the depth of the dentin, have stimulated new and different treatment philosophies of the dentin. The purpose of the present study, therefore, was to investigate the effects of three dentin treatments: laser irradiation, acid etching and hypermineralization, in the shear bond strength of the SMP Plus bonding system. Sixty bovine incisors were extracted and randomly selected immediatly alter the animal's death. They were kept frozen (-18°C) for no longer than 14 days. After buccal dentinal surface had been exposed, X-Rays were taken to control the dentin thickness. The specimens were separated into two groups: (1) Control, kept in distilled water at 4ºC; (2) Mineralized, kept in hypermineralized solution at 4°C for 14 days. Each group was divided into three sub-groups according to the type of dentin treatment used: group F - followed the manufacturer instructions (acid-etching + primer + bond), group AL (acid-etching + primer + bond + laser) and group LA (laser + (laser + acid-etching + primer + bond). A composite resin standard cylinder (Z100-3M) was bond to the dentinal surface and the shear bond strength performed on a Universal lnstron machine 4301, with 500 Kg load and at 0,5mm/min. speed. The analysis of variance (ANOVA) determined that the treatments influenced the shear bond strength values (p<0,05) with the following average shearing load at failure: AL (9,96 MPa), F (7,28MPa) e LA (4,87 MPa). The interaction between the two factors analyzed Group (control and mineralized) and treatment (F, AL, LA) also influenced the shear bond strength (p<0,05). The highest values were obtained...

Análise da interface adesiva entre pinos de fibra de vidro e dentina intrarradicular submetida à irrigação com diferentes agentes condicionantes

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Propriedades mecânicas, físico-químicas e biológica de adesivo experimental com incorporação de epigalocatequina-3-galato

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Sistemi adesivi con applicazioni in campo biomedicale

Polymeric adhesives have been used for many applications like suture and embolization, instead of classic surgical methods or as for dental uses. In this work both subjects have been investigated and the results separated in two parts. In the first, new dentinal adhesives with different polymerizable groups (methacrylic or vinyl-ethereal) were synthesized. A low sensitivity to hydrolysis and equal or enhanced properties, compared to existing commercial products, were considered essentials. Moreover, these monomers need to polymerize by radical photopolymerization and functional groups of different characteristics were tested. All these products were characterized by microtensile bond strength test to determine the bonding strength between the adhesive and tooth. Concerning embolization, cyanoacrylates are nowadays the most-used adhesives in surgery. Thus, they must respond to several requirements. For instance, polymerization time and adhesive strength need to be low, to avoid diffusion of the products in the body and adhesion to the catheter. In order to overcome these problems we developed new cyanoacrylates, which practically instantly polymerize upon contact with blood but do not demonstrate strong adhesion to the catheter, thank to the presence of fluorine atoms, linked to the ester chain. The synthesis of these products was carried out in several steps, such as the depolymerization of the corresponding oligomers at high temperature in acid conditions. Two types of adhesion strengths were determined. Bonding strength between human veins and a microcatheter was determined in vitro by using organic materials as the most realistic model. Another test, on two layers of skin, was conducted to verify the possible use of these new cyanoacrylates as a glue for sutures. As a conclusion, we were able to demonstrate that some of the prepared monomers posses adhesive strength and polymerization time lower than the commercial product Glubran2.