Characterisation of montmorillonites simultaneously modified with an organic dye and an ammonium salt at different dye/salt ratios. Properties of these modified montmorillonites EVA nanocomposites

In this work, a sodium montmorillonite (Na+-Mt) was modified with two molecules simultaneously, an organic dye, methylene blue (MB), and ethyl hexadecyl dimethyl ammonium (EHDDMA). The synthesised organo-montmorillonites (OMt) combining different proportions of the two molecules were thoroughly characterised and mixed with ethylene vinyl acetate copolymer (EVA) in order to check the ability of these OMt as pigments and reinforcing additives. The synthesised OMt combining both surfactants, MB and EHDDMA, present higher interlayer distances than those with only MB, which were employed in previous works as nanopigments. When these OMt were incorporated in the EVA matrix, the obtained clay polymer nanocomposites (CPN) showed a high exfoliation degree of the OMt in the polymer, in such a way that at 80% of the cationic exchange capacity (CEC) of the Mt exchanged with EHDDMA, most of the OMt was exfoliated. Moreover, all the obtained CPN showed an increase in the Young's Moduli compared to the EVA reference, and especially those containing higher amounts of MB. The thermal stability of the CPN also increases with the MB content, compared to other CPN including conventional surfactants. The hiding power and colouring power achieved in the CPN are higher even with a much lower load of MB when EHDDMA is exchanged in the Mt.

Protein Hydrolysis and Nitrogen Remobilisation in Plant Life and Senescence

In plant cells, as in all other cells, proteins are submitted to permanent turnover, and the intracellular content of a given protein depends on its rate of both synthesis and degradation. The life time of most proteins is shorter than that of the cell. Thus, in young leaves of Lemna minor, the average half-life of protein was estimated to be 7 days, and it was shorter under stress conditions (Davies 1982). Such observations mean that nitrogen and amino acid fluxes are both cylic and permanent. Although protein turnover may appear wasteful, in terms of energy, numerous studies have shown that proteolysis provides multiple functions in cell physiology, and is an essential regulatory mechanism of cell metabolism and development.

Summary report : detoxification of Navy red dye by microwave plasma /

Mode of access: Internet.

Kinetics of the hydrolysis of N-trifluoroacetylamino acids /

"September 23, 1955."

The manual of colours and dye wares : their properties, applications, valuation, impurities and sophistications : for the use of dyers, printers, drysalters, brokers, etc. /

Includes index.

The hydrolysis of Iodine and a reaction with "Propanol".

Mode of access: Internet.

The dye binding of milk proteins

"Literature cited": p. 42-43.

Degradation of azo-dye Orange II by a photoassisted Fenton reaction using a novel composite of iron oxide and silicate nanoparticles as a catalyst

A novel nanocomposite of iron oxide and silicate, prepared through a reaction between a solution of iron salt and a dispersion of Laponite clay, was used as a catalyst for the photoassisted Fenton degradation of azo-dye Orange II. This catalyst is much cheaper than the Nafion-based catalysts, and our results illustrate that it can significantly accelerate the degradation of Orange II under the irradiation of UV light (lambda = 254 nm). An advantage of the catalyst is its long-term stability that was confirmed through using the catalyst for multiple runs in the degradation of Orange II. The effects of the H2O2 molar concentration, solution pH, wavelength and power of the LTV light, catalyst loading, and initial Orange II concentration on the degradation of Orange 11 were studied in detail. In addition, it was also found that discoloration of Orange 11 undergoes a faster kinetics than mineralization of Orange II and 75% total organic carbons of 0.1 mM Orange II can be eliminated after 90 min in the presence of 1.0 g of Fe-nanocomposite/L, 4.8 mM H2O2, and 1 x 8W UVC.

Reactions of fac-[PtMe2(OMe)(H2O)3]+ with halide ions: effect of halide trans effect on methoxide hydrolysis

A solution of fac-[PtMe2(OMe)(H2O)(3)](+) (1) in aqueous perchloric acid underwent very slow hydrolysis of the Pt-OMe bond, over many, weeks. When chloride was added to a solution of 1, two interconverting isomers of [PtMe2(OMe)Cl(H2O)(2)] (with chloride trans to methyl) were formed, and with excess chloride, [PtMe2(OMe)Cl-2(H2O)](-) (both chloride ligands trans to methyl). This solution was stable at ambient temperature, but on heating, methanol was formed and [PtMe2Cl2(H2O)(2)] (both chloride ligands cis to methyl) was produced in the solution. It is proposed that this reaction proceeds via an intermediate complex with chloride bound trans to methoxide. Concentration gave solid [{PtMe2Cl2}n], whose identity was confirmed by conversion to [PtMe(2)Cl(2)py(2)] (pyridine, py, trans to methyl). With bromide and iodide, methoxide hydrolysis occurred at ambient temperature, more slowly with bromide than with iodide, to form solid [{PtMe2X2}(n)] without significant concentrations of [PtMe2X2(H2O)(2)] formed as an intermediate. The greater tendency for Pt-OMe bond to hydrolyse trans to halide compared with 1 was ascribed to the higher trans effect of the halide ligand compared with that of water. (C) 2003 Elsevier Science B.V. All rights reserved.

A Two-Step Sol–Gel Method for Synthesis of Nanoporous TiO2

This article reports a study of the effects of synthesis parameters on the preparation and formation of mesoporous titania nanopowders by employing a two-step sol-gel method. These materials displayed crystalline domains characteristic of anatase. The first step of the process involved the hydrolysis of titanium isopropoxide in a basic aqueous solution mediated by neutral surfactant. The solid product obtained from step 1 was then treated in an acidified ethanol solution containing the same titanium precursor to thicken the pore walls. Low pH and higher loading of the Ti precursor in step 2 produced better mesoporosity and crystallinity of titanium dioxide polymorphs. The resultant powder exhibited a high surface area (73.8 m(2)/g) and large pore volume (0.17 cm(3)/g) with uniform mesopores. These materials are envisaged to be used as precursors for mesoporous titania films as a wide band gap semiconductor in dye-sensitized nanocrystalline TiO2 solar cells.

Hydrothermal seeded synthesis of mesoporous titania for application in dye-sensitised solar cells (DSSCs)

A modified-templated- hydrothermal technique was used to prepare mesoporous titania powders through the interaction of tiny anatase seeds (